Functional thin films fabricated by plasma polymerization and their biological applications

Plasma polymerization technique is widely accepted as an effective and simple method for the preparation of functional thin films. By careful choice of precursors and deposition parameters, plasma polymers bearing various functional groups could be easily obtained. In this work, I explored the deposition of four kinds of plasma polymerised functional thin films, including the protein-resistant coatings, the thermosensitive coatings, as well as, the coatings bearing amine or epoxide groups. The deposited plasma polymers were characterized by various techniques, such as X-ray photoelectron spectroscopy, atom force microscopy, Fourier transform infrared spectroscopy, surface plasmon resonance spectroscopy, optical waveguide spectroscopy, and so on. As expected, high retention of various functional groups could be achieved either at low plasma input power or at low duty cycle (duty cycle = Ton/(Ton+Toff)). The deposited functional thin films were found to contain some soluble materials, which could be removed simply by extraction treatment. Besides the thermosentive plasma polymer (see Chapter 9), other plasma polymers were used for developing DNA sensors. DNA sensing in this study was achieved using surface plasmon enhanced fluorescence spectroscopy. The nonfouling thin films (i.e., ppEO2, plasma polymerization of di(ethylene glycol) monovinyl ether) were used to make a multilayer protein-resistant DNA sensor (see Chapter 5). The resulted DNA sensors show good anti-fouling properties towards either BSA or fibrinogen. This sensor was successfully employed to discriminate different DNA sequences from protein-containing sample solutions. In Chapter 6, I investigated the immobilization of DNA probes onto the plasma polymerized epoxide surfaces (i.e., ppGMA, plasma polymerization of glycidyl methacrylate). The ppGMA prepared at a low duty cycle showed good reactivity with amine-modified DNA probes in a mild basic environment. A DNA sensor based on the ppGMA was successfully used to distinguish different DNA sequences. While most DNA detection systems rely on the immobilization of DNA probes onto sensor surfaces, a new homogeneous DNA detection method was demonstrated in Chapter 8. The labeled PNA serves not only as the DNA catcher recognizing a particular target DNA, but also as a fluorescent indicator. Plasma polymerized allylamine (ppAA) films were used here to provide a positively charged surface.

Internal characteristics, chemical compounds and spectroscopy of sapphire as single crystals

In this study more than 450 natural sapphire samples (most of basaltic type) collected from 19 different areas were examined. They are from Dak Nong, Dak Lak, Quy Chau, two unknown sources from the north (Vietnam); Bo Ploi, Khao Ploi Waen (Thailand); Ban Huay Sai (Laos); Australia; Shandong (China); Andapa, Antsirabe, Nosibe (Madagascar); Ballapana (Sri Lanka); Brazil; Russia; Colombia; Tansania and Malawi. rnThe samples were studied on internal characteristics, chemical compositions, Raman-, luminescence-, Fourier transform infrared (FTIR)-, and ultraviolet-visible-near infrared (UV-Vis-NIR)- spectroscopy. The internal features of these sapphire samples were observed and identified by gemological microscope, con focal micro Raman and FTIR spectroscopy. The major and minor elements of the samples were determined by electron probe microanalysis (EPMA) and the trace elements by laser ablation inductively coupled plasma mass spectrometry (LA-ICP-MS). rnThe structural spectra of sapphire were investigated by con focal Raman spectroscopy. The FTIR spectroscopy was used to study the vibration modes of OH-groups and also to determine hydrous mineral inclusions in sapphire. The UV-Vis-NIR absorption spectroscopy was used to analyze the cause of sapphire color. rnNatural sapphires contain many types of mineral inclusions. Typically, they are iron-containing inclusions like goethite, ilmenite, hematite, magnetite or silicate minerals commonly feldspar, and often observed in sapphires from Asia countries, like Dak Nong, Dak Lak in the south of Vietnam, Ban Huay Sai (Laos), Khao Ploi Waen and Bo Ploi (Thailand) or Shandong (China). Meanwhile, CO2-diaspore inclusions are normally found in sapphires from Tansania, Colombia, or the north of Vietnam like Quy Chau. rnIron is the most dominant element in sapphire, up to 1.95 wt.% Fe2O3 measured by EPMA and it affects spectral characteristics of sapphire.rnThe Raman spectra of sapphire contain seven peaks (2A1g + 5Eg). Two peaks at about 418.3 cm-1 and 577.7 cm-1 are influenced by high iron content. These two peaks shift towards smaller wavenumbers corresponding to increasing iron content. This shift is showed by two equations y(418.3)=418.29-0.53x andy(577.7)=577.96-0.75x, in which y is peak position (cm-1) and x is Fe2O3 content (wt.%). By exploiting two these equations one can estimate the Fe2O3 contents of sapphire or corundum by identifying the respective Raman peak positions. Determining the Fe2O3 content in sapphire can help to distinguish sapphires from different origins, e.g. magmatic and metamorphic sapphire. rnThe luminescence of sapphire is characterized by two R-lines: R1 at about 694 nm and R2 at about 692 nm. This characteristic is also influenced by high iron content. The peak positions of two R-lines shift towards to smaller wavelengths corresponding to increasing of iron content. This correlation is showed by two equations y(R_2 )=692.86-0.049x and y(R_1 )=694.29-0.047x, in which y is peak position (nm) of respective R-lines and x is Fe2O3 content (wt.%). Two these equations can be applied to estimate the Fe2O3 content of sapphire and help to separate sapphires from different origins. The luminescence is also applied for determination of the remnant pressure or stress around inclusions in Cr3+-containing corundum by calibrating a 0-pressure position in experimental techniques.rnThe infrared spectra show the presence of vibrations originating from OH-groups and hydrous mineral inclusions in the range of 2500-4000 cm-1. Iron has also an effect upon the main and strongest peak at about 3310 cm-1. The 3310 cm-1 peak is shifted to higher wavenumber when iron content increases. This relationship is expressed by the equation y(3310)=0.92x+3309.17, in which y is peak position of the 3310 cm-1 and x is Fe2O3 content (wt.%). Similar to the obtained results in Raman and luminescence spectra, this expression can be used to estimate the Fe2O3 content and separate sapphires from different origins. rnThe UV-Vis-NIR absorption spectra point out the strong and sharp peaks at about 377, 387, and 450 nm related to dispersed Fe3+, a broad band around 557 and 600 nm related to intervalence charge transfer (IVCT) Fe2+/Ti4+, and a broader band around 863 nm related to IVCT of Fe2+/Fe3+. rnGenerally, sapphires from different localities were completely investigated on internal features, chemical compounds, and solid spectral characteristics. The results in each part contribute for identifying the iron content and separate sapphires from different localities order origins. rn