Structuring of polymer surface by evaporation of sessile microdrops

In this thesis, we investigated the evaporation of sessile microdroplets on different solid substrates. Three major aspects were studied: the influence of surface hydrophilicity and heterogeneity on the evaporation dynamics for an insoluble solid substrate, the influence of external process parameters and intrinsic material properties on microstructuring of soluble polymer substrates and the influence of an increased area to volume ratio in a microfluidic capillary, when evaporation is hindered. In the first part, the evaporation dynamics of pure sessile water drops on smooth self-assembled monolayers (SAMs) of thiols or disulfides on gold on mica was studied. With increasing surface hydrophilicity the drop stayed pinned longer. Thus, the total evaporation time of a given initial drop volume was shorter, since the drop surface, through which the evaporation occurs, stays longer large. Usually, for a single drop the volume decreased linearly with t1.5, t being the evaporation time, for a diffusion-controlled evaporation process. However, when we measured the total evaporation time, ttot, for multiple droplets with different initial volumes, V0, we found a scaling of the form V0 = attotb. The more hydrophilic the substrate was, the more showed the scaling exponent a tendency to an increased value up to 1.6. This can be attributed to an increasing evaporation rate through a thin water layer in the vicinity of the drop. Under the assumption of a constant temperature at the substrate surface a cooling of the droplet and thus a decreased evaporation rate could be excluded as a reason for the different scaling exponent by simulations performed by F. Schönfeld at the IMM, Mainz. In contrast, for a hairy surface, made of dialkyldisulfide SAMs with different chain lengths and a 1:1 mixture of hydrophilic and hydrophobic end groups (hydroxy versus methyl group), the scaling exponent was found to be ~ 1.4. It increased to ~ 1.5 with increasing hydrophilicity. A reason for this observation can only be speculated: in the case of longer hydrophobic alkyl chains the formation of an air layer between substrate and surface might be favorable. Thus, the heat transport to the substrate might be reduced, leading to a stronger cooling and thus decreased evaporation rate. In the second part, the microstructuring of polystyrene surfaces by drops of toluene, a good solvent, was investigated. For this a novel deposition technique was developed, with which the drop can be deposited with a syringe. The polymer substrate is lying on a motorized table, which picks up the pendant drop by an upward motion until a liquid bridge is formed. A consecutive downward motion of the table after a variable delay, i.e. the contact time between drop and polymer, leads to the deposition of the droplet, which can evaporate. The resulting microstructure is investigated in dependence of the processes parameters, i.e. the approach and the retraction speed of the substrate and the delay between them, and in dependence of the intrinsic material properties, i.e. the molar mass and the type of the polymer/solvent system. The principal equivalence with the microstructuring by the ink-jet technique was demonstrated. For a high approach and retraction speed of 9 mm/s and no delay between them, a concave microtopology was observed. In agreement with the literature, this can be explained by a flow of solvent and the dissolved polymer to the rim of the pinned droplet, where polymer is accumulated. This effect is analogue to the well-known formation of ring-like stains after the evaporation of coffee drops (coffee-stain effect). With decreasing retraction speed down to 10 µm/s the resulting surface topology changes from concave to convex. This can be explained with the increasing dissolution of polymer into the solvent drop prior to the evaporation. If the polymer concentration is high enough, gelation occurs instead of a flow to the rim and the shape of the convex droplet is received. With increasing delay time from below 0 ms to 1s the depth of the concave microwells decreases from 4.6 µm to 3.2 µm. However, a convex surface topology could not be obtained, since for longer delay times the polymer sticks to the tip of the syringe. Thus, by changing the delay time a fine-tuning of the concave structure is accomplished, while by changing the retraction speed a principal change of the microtopolgy can be achieved. We attribute this to an additional flow inside the liquid bridge, which enhanced polymer dissolution. Even if the pendant drop is evaporating about 30 µm above the polymer surface without any contact (non-contact mode), concave structures were observed. Rim heights as high as 33 µm could be generated for exposure times of 20 min. The concave structure exclusively lay above the flat polymer surface outside the structure even after drying. This shows that toluene is taken up permanently. The increasing rim height, rh, with increasing exposure time to the solvent vapor obeys a diffusion law of rh = rh0  tn, with n in the range of 0.46 ~ 0.65. This hints at a non-Fickian swelling process. A detailed analysis showed that the rim height of the concave structure is modulated, unlike for the drop deposition. This is due to the local stress relaxation, which was initiated by the increasing toluene concentration in the extruded polymer surface. By altering the intrinsic material parameters i.e. the polymer molar mass and the polymer/solvent combination, several types of microstructures could be formed. With increasing molar mass from 20.9 kDa to 1.44 MDa the resulting microstructure changed from convex, to a structure with a dimple in the center, to concave, to finally an irregular structure. This observation can be explained if one assumes that the microstructuring is dominated by two opposing effects, a decreasing solubility with increasing polymer molar mass, but an increasing surface tension gradient leading to instabilities of Marangoni-type. Thus, a polymer with a low molar mass close or below the entanglement limit is subject to a high dissolution rate, which leads to fast gelation compared to the evaporation rate. This way a coffee-rim like effect is eliminated early and a convex structure results. For high molar masses the low dissolution rate and the low polymer diffusion might lead to increased surface tension gradients and a typical local pile-up of polymer is found. For intermediate polymer masses around 200 kDa, the dissolution and evaporation rate are comparable and the typical concave microtopology is found. This interpretation was supported by a quantitative estimation of the diffusion coefficient and the evaporation rate. For a different polymer/solvent system, polyethylmethacrylate (PEMA)/ethylacetate (EA), exclusively concave structures were found. Following the statements above this can be interpreted with a lower dissolution rate. At low molar masses the concentration of PEMA in EA most likely never reaches the gelation point. Thus, a concave instead of a convex structure occurs. At the end of this section, the optically properties of such microstructures for a potential application as microlenses are studied with laser scanning confocal microscopy. In the third part, the droplet was confined into a glass microcapillary to avoid evaporation. Since here, due to an increased area to volume ratio, the surface properties of the liquid and the solid walls became important, the influence of the surface hydrophilicity of the wall on the interfacial tension between two immiscible liquid slugs was investigated. For this a novel method for measuring the interfacial tension between the two liquids within the capillary was developed. This technique was demonstrated by measuring the interfacial tensions between slugs of pure water and standard solvents. For toluene, n-hexane and chloroform 36.2, 50.9 and 34.2 mN/m were measured at 20°C, which is in a good agreement with data from the literature. For a slug of hexane in contact with a slug of pure water containing ethanol in a concentration range between 0 and 70 (v/v %), a difference of up to 6 mN/m was found, when compared to commercial ring tensiometry. This discrepancy is still under debate.

Evaporation of sessile microdrops studied with microcantilevers

The aim of this work is to investigate the evaporation dynamics of water microdrops deposited on atomic force microscope cantilevers, which were employed as sensitive stress, mass and temperature sensors with high time resolution. The technique has some advantages with respect to video-microscope imaging and ultra-precision weighting with electronic microbalances or quartz crystal microbalances, since it allows to measure more drop parameters simultaneously for smaller drop sizes. On hydrophobic surfaces a single measurement with a silicon cantilever provides data for the drop mass, contact angle and radius until very close to complete evaporation. On hydrophilic surfaces, it is as well possible to measure drop mass and inclination of the cantilever. The technique further allows to detect differences between water microdrops evaporating from clean hydrophilic and hydrophobic surfaces. On hydrophilic surfaces the cantilever inclination is negative at the end of the evaporation process. Negative inclination mostly occurs when drops are pinned. This effect can not be detected with any of the other well-established methods. The evidence arises that on the hydrophilic surface a thin water film forms, while this is not the case for the hydrophobic surface. Metal coated cantilevers can be used as thermometers, and allow to precisely measure the temperature of an evaporating microdrop. This can be relevant for further applications of cantilevers as calorimetric sensors for chemical reactions taking place in drops on their surface. The applicability of Young’s equation was verified for microdrops. It was shown that Young’s equation can not be applied to microscopic drops due to their fast evaporation. A study on evaporation of microdrops in saturated vapor atmosphere was performed to estimate evaporation times and compare them with a theory developed, which relates the initial drop volume with the overall evaporation time.

Helix-coil-transition in solid polypeptides

Abstract Poly(L-glutamic acid) (PLGA) was synthesized by living anionic ring-opening polymerization of the NCA monomer, which was obtained by reacting diphosgene with an amino acid derivative. The chemical structures and thermal properties were characterized by 1H-NMR, 13C-NMR, TGA and DSC. XRD powder patterns found to be amorphous for all polymers obtained. The molecular weights could be determined under severe limitations due to low solubility and high aggregation tendency. The secondary structure of the PLGA films was analyzed in the solid state by IR spectroscopy; the order was determined mainly by XRD. Uniform bulk films (1-5 µm) were produced by drop-casting of PLGA solutions in TFA on silica. The XRD film analysis indicated the absence of a long range order or an orientation even if a helical microstructure was confirmed by IR spectroscopy. The coil solvent TFA delivered constantly a helical or a β-sheet structure in the solid state depending on the water content of the solvent which was observed for the first time to exhibit a high influence on the crystallization process for PLGA. Temperature dependent in-situ IR measurements were examined to analyze if a helix-coil transition occurs, but there could be no solvent system determined, which resulted in a disordered coil structure in the solid state. General parameters like solvent systems, evaporation conditions, concentration, substrates etc. were analyzed. New crystallizations were obtained on silica prepared by drop-casting of solutions of PLGA in DMF, DMA, TMU, NMP, and pyridine/water mixtures, respectively. PSCBC in DMF, CDCl3/TFA-d, and PSBC in CDCl3/TFA-d exhibited the same crystalline diffraction patterns like PLGA. The long range order in the X-ray diffraction pattern is proven by extremely sharp crystalline signals, which are not changing the shape or the position of the peak by increasing the temperature up to 160°C. The substrate seems to play a decisive role because the crystalline structures were not obtainable on glass. The crystal structure consists probably of two different layered structures based on the intensity ratios of the two series of crystalline signals in the X-ray diffraction patterns. The source of the layered structure remains unclear and needs further studies to investigate the spatial arrangement of the chains in more detail. The secondary structure was still not changing upon heating even if a highly crystalline diffraction pattern occurs. Concluding that even the newly investigated crystallization did not show a helix-coil transition in the solid state by annealing, the phenomenon known in solution has to be claimed as unachievable in the solid state based on the results of this work. A remaining open question represents the observation that the same crystalline pattern can be reproducibly prepared with exhibiting two different ordered secondary structures (helix and β-sheet). After the investigation that the evaporation time cannot be decisive for the crystal growth, the choice of a strong hydrogen bonding interrupting solvent is most probably the key to support and induce the crystallization process.

Time-of-flight two-photon photoemission spectromicroscopy with femtosecond laser radiation

Time-of-flight photoemission spectromicroscopy was used to measure and compare the two-photon photoemission (2PPE) spectra of Cu and Ag nanoparticles with linear dimensions ranging between 40 nm and several 100 nm, with those of the corresponding homogeneous surfaces. 2PPE was induced employing femtosecond laser radiation from a frequency-doubled Ti:sapphire laser in the spectral range between 375 nm and 425 nm with a pulse width of 200 fs and a repetition rate of 80 MHz. The use of a pulsed radiation source allowed us to use a high-resolution photoemission electron microscope as imaging time-of-flight spectrometer, and thus to obtain spectroscopic information about the laterally resolved electron signal. Ag nanoparticle films have been deposited on Si(111) by electron-beam evaporation, a technique leading to hemispherically-shaped Ag clusters. Isolated Cu nanoparticles have been generated by prolonged heating of a polycrystalline Cu sample. If compared to the spectra of the corresponding homogeneous surfaces, the Cu and Ag nanoparticle spectra are characterized by a strongly enhanced total 2PPE yield (enhancement factor up to 70), by a shift (about 0.1 eV) of the Fermi level onset towards lower final state energies, by a reduction of the work function (typically by 0.2 eV) and by a much steeper increase of the 2PPE yield towards lower final state energies. The shift of the Fermi level onset in the nanoparticle spectra has been explained by a positive unit charge (localized photohole) residing on the particle during the time-scale relevant for the 2PPE process (few femtoseconds). The total 2PPE yield enhancement and the different overall shape of the spectra have been explained by considering that the laser frequency was close to the localized surface plasmon resonance of the Cu and Ag nanoparticles. The synchronous oscillations induced by the laser in the metal electrons enhance the near-zone (NZ) field, defined as the linear superposition of the laser field and the field produced in the vicinity of the particles by the forced charge oscillations. From the present measurements it is clear that the NZ field behavior is responsible for the 2PPE enhancement and affects the 2PPE spatial and energy distribution and its dynamics. In particular, its strong spatial dependence allows indirect transitions through real intermediate states to take place in the metal clusters. Such transitions are forbidden by momentum conservation arguments and are thus experimentally much less probable on homogeneous surfaces. Further, we investigated specially tailored moon-shaped small metal nanostructures, whose NZ field was theoretically predicted, and compared the calculation with the laterally resolved 2PPE signal. We could show that the 2PPE signal gives a clear fingerprint of the theoretically predicted spatial dependence of the NZ field. This potential of our method is highly attractive in the novel field of plasmonics.