Synthesis and surface modification of semiconductor nanocrystals

The last decade has witnessed an exponential growth of activities in the field of nanoscience and nanotechnology worldwide, driven both by the excitement of understanding new science and by the potential hope for applications and economic impacts. The largest activity in this field up to date has been in the synthesis and characterization of new materials consisting of particles with dimensions in the order of a few nanometers, so-called nanocrystalline materials. [1-8] Semiconductor nanomaterials such as III/V or II/VI compound semiconductors exhibit strong quantum confinement behavior in the size range from 1 to 10 nm. Therefore, preparation of high quality semiconductor nanocrystals has been a challenge for synthetic chemists, leading to the recent rapid progress in delivering a wide variety of semiconducting nanomaterials. Semiconductor nanocrystals, also called quantum dots, possess physical properties distinctly different from those of the bulk material. Typically, in the size range from 1 to 10 nm, when the particle size is changed, the band gap between the valence and the conduction band will change, too. In a simple approximation a particle in a box model has been used to describe the phenomenon[9]: at nanoscale dimensions the degenerate energy states of a semiconductor separate into discrete states and the system behaves like one big molecule. The size-dependent transformation of the energy levels of the particles is called “quantum size-effect”. Quantum confinement of both the electron and hole in all three dimensions leads to an increase in the effective bandgap of the material with decreasing crystallite size. Consequently, both the optical absorption and emission of semiconductor nanaocrystals shift to the blue (higher energies) as the size of the particles gets smaller. This color tuning is well documented for CdSe nanocrystals whose absorption and emission covers almost the whole visible spectral range. As particle sizes become smaller the ratio of surface atoms to those in the interior increases, which has a strong impact on particle properties, too. Prominent examples are the low melting point [8] and size/shape dependent pressure resistance [10] of semiconductor nanocrystals. Given the size dependence of particle properties, chemists and material scientists now have the unique opportunity to change the electronic and chemical properties of a material by simply controlling the particle size. In particular, CdSe nanocrystals have been widely investigated. Mainly due to their size-dependent optoelectronic properties [11, 12] and flexible chemical processibility [13], they have played a distinguished role for a number of seminal studies [11, 12, 14, 15]. Potential technical applications have been discussed, too. [8, 16-27] Improvement of the optoelectronic properties of semiconductor nanocrystals is still a prominent research topic. One of the most important approaches is fabricating composite type-I core-shell structures which exhibit improved properties, making them attractive from both a fundamental and a practical point of view. Overcoating of nanocrystallites with higher band gap inorganic materials has been shown to increase the photoluminescence quantum yields by eliminating surface nonradiative recombination sites. [28] Particles passivated with inorganic shells are more robust than nanocrystals covered by organic ligands only and have greater tolerance to processing conditions necessary for incorporation into solid state structures or for other applications. Some examples of core-shell nanocrystals reported earlier include CdS on CdSe [29], CdSe on CdS, [30], ZnS on CdS, [31] ZnS on CdSe[28, 32], ZnSe on CdSe [33] and CdS/HgS/CdS [34]. The characterization and preparation of a new core-shell structure, CdSe nanocrystals overcoated by different shells (CdS, ZnS), is presented in chapter 4. Type-I core-shell structures as mentioned above greatly improve the photoluminescence quantum yield and chemical and photochemical stability of nanocrystals. The emission wavelengths of type-I core/shell nanocrystals typically only shows a small red-shift when compared to the plain core nanocrystals. [30, 31, 35] In contrast to type-I core-shell nanocrystals, only few studies have been conducted on colloidal type-II core/shell structures [36-38] which are characterized by a staggered alignment of conduction and valence bands giving rise to a broad tunability of absorption and emission wavelengths, as was shown for CdTe/CdSe core-shell nanocrystals. [36] The emission of type-II core/shell nanocrystals mainly originates from the radiative recombination of electron-hole pairs across the core-shell interface leading to a long photoluminescence lifetime. Type-II core/shell nanocrystals are promising with respect to photoconduction or photovoltaic applications as has been discussed in the literature.[39] Novel type-II core-shell structures with ZnTe cores are reported in chapter 5. The recent progress in the shape control of semiconductor nanocrystals opens new fields of applications. For instance, rod shaped CdSe nanocrystals can enhance the photo-electro conversion efficiency of photovoltaic cells, [40, 41] and also allow for polarized emission in light emitting diodes. [42, 43] Shape control of anisotropic nanocrystals can be achieved by the use of surfactants, [44, 45] regular or inverse micelles as regulating agents, [46, 47] electrochemical processes, [48] template-assisted [49, 50] and solution-liquid-solution (SLS) growth mechnism. [51-53] Recently, formation of various CdSe nanocrystal shapes has been reported by the groups of Alivisatos [54] and Peng, [55] respectively. Furthermore, it has been reported by the group of Prasad [56] that noble metal nanoparticles can induce anisotropic growth of CdSe nanocrystals at lower temperatures than typically used in other methods for preparing anisotropic CdSe structures. Although several approaches for anisotropic crystal growth have been reported by now, developing new synthetic methods for the shape control of colloidal semiconductor nanocrystals remains an important goal. Accordingly, we have attempted to utilize a crystal phase control approach for the controllable synthesis of colloidal ZnE/CdSe (E = S, Se, Te) heterostructures in a variety of morphologies. The complex heterostructures obtained are presented in chapter 6. The unique optical properties of nanocrystals make them appealing as in vivo and in vitro fluorophores in a variety of biological and chemical investigations, in which traditional fluorescence labels based on organic molecules fall short of providing long-term stability and simultaneous detection of multiple emission colours [References]. The ability to prepare water soluble nanocrystals with high stability and quantum yield has led to promising applications in cellular labeling, [57, 58] deep-tissue imaging, [59, 60] and assay labeling [61, 62]. Furthermore, appropriately solubilized nanocrystals have been used as donors in fluorescence resonance energy transfer (FRET) couples. [63-65] Despite recent progress, much work still needs to be done to achieve reproducible and robust surface functionalization and develop flexible (bio-) conjugation techniques. Based on multi-shell CdSe nanocrystals, several new solubilization and ligand exchange protocols have been developed which are presented in chapter 7. The organization of this thesis is as follows: A short overview describing synthesis and properties of CdSe nanocrystals is given in chapter 2. Chapter 3 is the experimental part providing some background information about the optical and analytical methods used in this thesis. The following chapters report the results of this work: synthesis and characterization of type-I multi-shell and type-II core/shell nanocrystals are described in chapter 4 and chapter 5, respectively. In chapter 6, a high–yield synthesis of various CdSe architectures by crystal phase control is reported. Experiments about surface modification of nanocrystals are described in chapter 7. At last, a short summary of the results is given in chapter 8.

Photovoltaics from discotic liquid crystalline HBCs & poly(2,7-carbazole)s

In this study, the use of the discotic liquid crystalline HBCs and conjugated polymers based on 2,7-carbazole were investigated in detail as donor materials in organic bulk-heterojunction solar cells. It has been shown that they perform efficiently in photovoltaic devices in combination with suitable acceptors. The efficiency was found to depend strongly dependent on the morphology of the film. By investigation of a series of donor materials with similar molecular structures based on both discotic molecules and conjugated polymers, a structure-performance relation was established, which is not only instructive for these materials but also serves as a guideline for improved molecular design. For the series of HBCs used in this study, it is found that the device efficiency decreases with increasing length of the alkyl substituents in the HBC. Thus, the derivative with the smallest alkyl mantle, being more crystalline compared to the HBCs with longer alkyl chains, gave the highest EQE of 12%. A large interfacial separation was found in the blend of HBC-C6,2 and PDI, since the crystallization of the acceptor occurred in a solid matrix of HBC. This led to small dispersed organized domains and benefited the charge transport. In contrast, blends of HBC-C10,6/PDI or HBC-C14,10/PDI revealed a rather homogeneous film limiting the percolation pathways due to a mixed phase. For the first time, poly(2,7-carbazole) was incorporated as a donor material in solar cells using PDI as an electron acceptor. The good fit in orbital energy levels and absorption spectra led to high efficiency. This result indicates that conjugated polymers with high band-gap can also be applied as materials to build efficient solar cells if appropriate electron acceptors are chosen. In order to enhance the light absorption ability, new ladder-type polymers based on pentaphenylene and hexaphenylene with one and three nitrogen bridges per repeat unit have been synthesized and characterized. The polymer 2 with three nitrogen bridges showed more red-shifted absorbance and emission and better packing in the solid-state than the analogous polymer 3 with only one nitrogen bridge per monomer unit. An overall efficiency as high as 1.3% under solar light was obtained for the device based on 1 and PDI, compared with 0.7% for the PCz based device. Therefore, the device performance correlates to a large extent with the solar light absorption ability and the lateral distance between conjugated polymer chains. Since the lateral distance is determined by the length and number of attached alkyl side chains, it is possible to assume that these substituents insulate the charge carrier pathways and decrease the device performance. As an additional consequence, the active semiconductor is diluted in the insulating matrix leading to a lower light absorption. This work suggests ways to improve device performance by molecular design, viz. maintaining the HOMO level while bathochromically shifting the absorption by adopting a more rigid ladder-type structure. Also, a high ratio of nitrogen bridges with small alkyl substituents was a desirable feature both in terms of adjusting the absorption and maintaining a low lateral inter-chain separation, which was necessary for obtaining high current and efficiency values.

Synthese und Charakterisierung von Oxidchalkogeniden und Bronzen für die Nanostrukturierung

Ausgehend von der Entdeckung der reversiblen Strukturierung mittels Rastersondenmethoden im Phasensystem Na2O/V2O5/P2O5 wurden im Rahmen dieser Arbeit zwei Ansatzpunkte verfolgt. Einerseits sollten mittels der Schmelzflußelektrolyse einige bereits existierende niederdimensionale Molybdänbronzen mit bekannten elektronischen Übergängen in ausreichend großen Kristallen gezüchtet werden, um sie auf ihre Strukturierungseigenschaften hin zu untersuchen. Gleichzeitig sollte durch Variation versucht werden, neue, bisher unbekannte Bronzen oder reduzierte Oxide zu synthetisieren und charakterisieren. Der zweite Schwerpunkt dieser Arbeit lag in der Synthese und Charakterisierung von Oxidchalkogeniden, bestehend aus einem Seltenerdmetall und einem 3d-Metall von Titan bis hin zu den mittleren Übergangsmetallen. Diese Verbindungen können durch die Kombination der jeweiligen Eigenschaften der oxidischen und chalkogeniden Teilstrukturen völlig neue elektronische und/oder magnetische Eigenschaften aufweisen. Mögliche auftretende Phasenübergänge sind wiederum für Strukturierungsversuche interessant. Die zu den Oxidchalkogeniden durchgeführten Untersuchungen ergaben im Phasensystem Ln/Ti/S/O (Ln = Lanthanoide) insgesamt sechs Verbindungen. Zwei von ihnen, La8Ti9S24O4 und Nd20Ti11S44O6, besitzen als gemeinsames Strukturelement tetranukleare [Ti4(u4-S)2(u2-O)4]-Cluster, bestehend aus vier miteinander über gemeinsame Flächen kondensierte TiS4O2-Oktaeder. Die Titanpositionen innerhalb der Cluster sind mit Ti+3-Ionen besetzt. Beide Verbindungen weisen in einem Temperaturbereich zwischen 150 K und 250 K eine deutlich ausgeprägte Hysterese der magnetischen Suszeptibilität auf, die sich im Falle von La8Ti9S24O4 auf einen Jahn-Teller-Übergang zurückführen läßt. Daneben konnte erstmals eine Serie oxidisch/sulfidisch gemischter Ruddlesden-Popper-Verbindungen mit Ln2Ti2S2O5 (Ln = Pr, Nd, Sm) synthetisiert und charakterisiert werden. Titan liegt als vierwertiges Ion in aus TiSO5-Oktaedern gebildeten Perowskit-Doppelschichten vor. Die neunfach koordinierten Positionen sind mit den Seltenerdmetallionen gefüllt, die zwölffach koordinierten Lagen sind unbesetzt. Bei dem sechsten erhaltene Titanoxidsulfid, La4TiS6.5O1.5, handelt es sich um einen Halbleiter mit einer Bandlücke von etwa 2 eV. Weiterhin gelang es, die Serie Ln2M3S2O8 (Ln = La, Ce, Pr, Nd, Sm; M = Nb, Ta) zu synthetisieren und in ihren physikalischen Eigenschaften zu charakterisieren. Es handelt sich ausnahmslos um Halbleiter mit Bandlücken zwischen E=0.125 eV für La2Nb3S2O8 und E=0.222 eV für Pr2Ta3S2O8. Die Struktur der Oxidsulfide Ce2Ta3S2O8, Pr2Ta3S2O8, Nd2Nb3S2O8 sowie Sm2Ta3S2O8 weist im Gegensatz zu den anderen Verbindungen eine Fehlordnung eines der beiden kristallographisch unabhängigen Nb- bzw. Ta-Atome auf. Daraus resultiert eine Symmetrieerniedrigung von Pnma zu Pbam. Der Einsatz von Europium führte zu einer neuen Modifikation des bronzoiden Oxids EuTa2O6, in der das Europium als Eu+2 vorliegt, wie 151Eu-Mößbauer-Untersuchungen bestätigten. Vor der Durchführung der Kristallzüchtungen mittels der Schmelzflußelektrolysen mußten die benutzen Öfen und Elektrolysezellen geplant und angefertigt werden. Es konnten dann verschiedene blaue, rote und violette Moybdänbronzen (sowie La2Mo2O7) in Kristallen bis zu 25 mm Länge dargestellt werden. Ferner gelang die erste exakte Einkristalluntersuchung der roten Bronze Rb0.33MoO3. Sie verfügt über die höchste d-Elektronen-Lokalisierungsrate aller bekannten roten Bronzen. Die erhaltenen Bronzen wurden teilweise von der Arbeitsgruppe Fuchs, Physikalisches Institut der Westfälischen Wilhelms-Universität Münster, auf ihre Nanostrukturierbarkeit hin untersucht. Dabei ergaben sich zwei verschiedene Strukturierungsmechanismen. Sind es im Fall der blauen Alkalimetall-Molybdänbronzen ausschließlich Lochstrukturen, die entstehen, handelt es sich bei La2Mo2O7 um Hügelstrukturen. Mittels der Schmelzflußelektrolyse konnte auch das gemischtvalente Alkalimetall-Eisenmolybdat NaFe2(MoO4)3 synthetisiert werden. Daneben gelang die Synthese dreier weiterer Alkalimetall-Eisenmolybdate: Cs2Fe2(MoO4)3, NaFe4(MoO4)5 und CsFe5(MoO4)7. Bis auf Cs2Fe2(MoO4)3, welches in der bekannten Langbeinit-Struktur kristallisiert, handelt es sich bei den übrigen Alkalimetall-Eisenmolybdaten um völlig neuartige Käfigverbindungen, bzw. bei CsFe5(MoO4)7 um eine Tunnelverbindung. Die Kristallstrukturen beinhalten kondensierte FeO6-Oktaeder. Im Fall von NaFe2(MoO4)3 lassen sich [Fe2O10]-Einheiten, für NaFe4(MoO4)5 [Fe2O10]- sowie [Fe3O14]-Einheiten, und für CsFe5(MoO4)7 [Fe4O18]-Baueinheiten beobachten. Die Positionen der Fe+2- und Fe+3-Atome in NaFe4(MoO4)5 wurden mit Hilfe einer 57Fe-Mößbauer-Untersuchung bestimmt.

Hypersonic phonon propagation in mesoscopic systems by Brillouin spectroscopy

Phononic crystals, capable to block or direct the propagation of elastic/acoustic waves, have attracted increasing interdisciplinary interest across condensed matter physics and materials science. As of today, no generalized full description of elastic wave propagation in phononic structures is available, mainly due to the large number of variables determining the band diagram. Therefore, this thesis aims for a deeper understanding of the fundamental concepts governing wave propagation in mesoscopic structures by investigation of appropriate model systems. The phononic dispersion relation at hypersonic frequencies is directly investigated by the non-destructive technique of high-resolution spontaneous Brillouin light scattering (BLS) combined with computational methods. Due to the vector nature of the elastic wave propagation, we first studied the hypersonic band structure of hybrid superlattices. These 1D phononic crystals composed of alternating layers of hard and soft materials feature large Bragg gaps. BLS spectra are sensitive probes of the moduli, photo-elastic constants and structural parameters of the constituent components. Engineering of the band structure can be realized by introduction of defects. Here, cavity layers are employed to launch additional modes that modify the dispersion of the undisturbed superlattice, with extraordinary implications to the band gap region. Density of states calculations in conjunction with the associated deformation allow for unambiguous identication of surface and cavity modes, as well as their interaction with adjacent defects. Next, the role of local resonances in phononic systems is explored in 3D structures based on colloidal particles. In turbid media BLS records the particle vibration spectrum comprising resonant modes due to the spatial confinement of elastic energy. Here, the frequency and lineshapes of the particle eigenmodes are discussed as function of increased interaction and departure from spherical symmetry. The latter is realized by uniaxial stretching of polystyrene spheres, that can be aligned in an alternating electric field. The resulting spheroidal crystals clearly exhibit anisotropic phononic properties. Establishing reliable predictions of acoustic wave propagation, necessary to advance, e.g., optomechanics and phononic devices is the ultimate aim of this thesis.