22 resultados para Molecularly-imprinted polymers
Resumo:
In summary, thermoresponsive polyacrylamides with various amounts of different photoswitchable side groups, i. e. azobenzene, salicylideneaniline and fulgimide were successfully prepared. As such, in a first step three different chromophores with an amine functionality were synthesized. The synthesis of the stimuli-responsive materials was based on the RAFT polymerization of activated ester acrylates followed by a polymer analogous reaction with different amines. The procedure has been designed to allow the synthesis of well-defined materials with functional groups. All copolymers prepared in this way showed a LCST in aqueous solution. The LCST was in general decreased by increasing the amount of hydrophobic dye incorporated into the thermoresponsive polymer. However, in the case of the fulgimide, the LCST was hardly affected by the chromophore. For azobenzene containing PNIPAM polymers and analogues, higher LCST values were measured after irradiation of the polymer sample solutions with UV-light (Delta LCSTmax = 7.3°C). A reversible light-induced solubility change within a certain temperature range was possible. In contrast to this, irradiated samples of salicylideneaniline containing thermoresponsive copolymers showed an irreversible increase in the LCST (Delta LCSTmax = 13.0°C). Fulgimide chromophores did not influence the LCST of PNIPAM based copolymers after UV-light exposure.rnSimilar to the thermoresponsive polyacrylamides with azobenzene side groups, poly(oligo(ethylene glycol) methyl ether methacrylate) [P(OEGMA)] polymers with azobenzene end groups showed a LCST shift upon UV-irradiation. These polymers were synthesized by RAFT polymerization using a functional chain transfer agent (CTA). For this, PFP-CTA was used as a RAFT-agent for end group functionalization of (thermoresponsive) polymers. In contrast to the statistically arranged copolymers with azobenzene side groups, P(OEGMA) polymers with terminal azobenzene showed a linear increase of the LCST shifts with increasing amount of chromophore (Delta LCSTmax = 4.3°C). Noteworthy, the chemical nature of the end group exhibited a strong influence on the LCST in the case of short thermoresponsive P(OEGMA) polymers.rnThe investigation on temperature- and lightresponsive polymers was transferred onto block copolymers capable to self-assemble into polymeric micelles. Therefore, PEO-b-PNIPAM block copolymers with azobenzene moieties were synthesized successfully. These polymers showed a “smart” behavior in aqueous solution, as the reversible formation and disruption of the micelles could either be controlled by temperature or using light as a stimulus. The usefulness of these materials was demonstrated by encapsulation of a hydrophobic dye in the core of the micelle. Such materials might have a great potential as a model system for several technical or biological applications.rnFinally, double thermoresponsive block copolymers forming micellar structures in a certain temperature range with functional end groups could successfully be synthesized. These “smart materials” based on POEGMA-b-PNIPMAM have been demonstrated to be very promising for a temperature selective immobilization on a protein surface. This might be a suitable concept for further biological applications.rnConcluding, different thermoresponsive copolymers and block copolymers with lightresponsive moieties arranged along the backbone or located at the chain ends were successfully prepared and investigated. By controlling the nature of functional groups and their respective incorporation ratios, the LCST could be dialed in precisely. Further, the LCST of the polymers could be triggered by light. A light-controlled disruption of micellar structures could be shown for functional block copolymers. The importance of end groups of thermoresponsive polymers was demonstrated by a temperature-controlled protein-polymer binding of a terminal biotin-functionalized double thermoresponsive polymer. The synthetic approaches and the material properties presented here should be promising for further research and applications beyond this dissertation.rn
Resumo:
While polymers with different functional groups along the backbone have intensively been investigated, there is still a challenge in orthogonal functionalization of the end groups. Such well-defined systems are interesting for the preparation of multiblock (co) polymers or polymer networks, for bio-conjugation or as model systems for examining the end group separation of isolated polymer chains. rnHere, Reversible Addition Fragmentation Chain Transfer (RAFT) polymerization was employed as method to investigate improved techniques for an a, w end group functionalization. RAFT produces polymers terminated in an R group and a dithioester-Z group, where R and Z stem from a suitable chain transfer agent (CTA). rnFor alpha end group functionalization, a CTA with an activated pentafluorophenyl (PFP) ester R group was designed and used for the polymerization of various methacrylate monomers, N-isopropylacrylamide and styrene yielding polymers with a PFP ester as a end group. This allowed the introduction of inert propyl amides, of light responsive diazo compounds, of the dyes NBD, Texas Red, or Oregon Green, of the hormone thyroxin and allowed the formation of multiblocks or peptide conjugates. rnFor w end group functionalization, problems of other techniques were overcome through an aminolysis of the dithioester in the presence of a functional methane thiosulfonate (MTS), yielding functional disulfides. These disulfides were stable under ambient conditions and could be cleaved on demand. Using MTS chemistry, terminal methyl disulfides (enabling self-assembly on planar gold surfaces and ligand substitution on gold and semiconductor nanoparticles), butynyl disulfide end groups (allowing the “clicking” of the polymers onto azide functionalized surfaces and the selective removal through reduction), the bio-target biotin, and the fluorescent dye Texas Red were introduced into polymers. rnThe alpha PFP amidation could be performed under mild conditions, without substantial loss of DTE. This way, a step-wise synthesis produced polymers with two functional end groups in very high yields. rnAs examples, polymers with an anchor group for both gold nanoparticles (AuNP) and CdSe / ZnS semi-conductor nanoparticles (QD) and with a fluorescent dye end group were synthesized. They allowed a NP decoration and enabled an energy transfer from QD to dye or from dye to AuNP. Water-soluble polymers were prepared with two different bio-target end groups, each capable of selectively recognizing and binding a certain protein. The immobilization of protein-polymer-protein layers on planar gold surfaces was monitored by surface plasmon resonance.Introducing two different fluorescent dye end groups enabled an energy transfer between the end groups of isolated polymer chains and created the possibility to monitor the behavior of single polymer chains during a chain collapse. rnThe versatility of the synthetic technique is very promising for applications beyond this work.
Resumo:
Zur Untersuchung von Effekten beim Laserheizen von Polymeren wurde ein Temperaturmessaufbau entwickelt. Das Messprinzip basiert auf der Auswertung der thermischen Emission. Der Messaufbau besteht aus einer hochauflösenden Kamera, ausgestattet mit Bildverstärker, sowie Interferenzfiltern um eine spektrale Auflösung zu gewährleisten und einem gepulster NIR-Heizlaser. Die Pulsdauer des Lasers liegt in der Größenordnung von 10 µs, der Strahldurchmesser durch entsprechende Fokussierung in der Größenordnung von 10 µm. Mittels Fit des Planck‘schen Strahlungsgesetzes an die aufgenommene thermische Emission konnten 2D Temperaturgraphen erhalten werden. Eine Ortsauflösung von 1 µm und eine Zeitauflösung von 1 µs konnten realisiert werden. In Kombination mit Finite-Elemente-Simulationen wurde mit diesem Aufbau die Laserablation verschiedener Polymere untersucht. Dabei hat sich gezeigt, dass bei Polymeren mit einem Glasübergang im Temperaturbereich zwischen Raum- und Zerfallstemperatur, photomechanische Ablation stattfand. Die Ablationsschwelle lag für diese Polymere mehrere 10 K über dem Glasübergang, weit unter der Zerfallstemperatur aus thermogravimetrischen Experimenten mit typischen Heizraten von 10 K/min. Bei hohen Laserenergien und damit verbundenen hohen Temperaturen konnte dagegen thermischer Zerfall beobachtet werden. Ein Übergang des Mechanismus von photomechanischer Ablation zu Ablation durch thermischen Zerfall ergab sich bei Temperaturen deutlich über der Zerfallstemperatur des Polymers aus der Thermogravimetrie. Dies wurde bedingt durch die kurzen Reaktionszeiten des Laserexperiments in der Größenordnung der Pulsdauer und steht im Einklang mit dem Gesetz von Arrhenius. Polymere ohne Glasübergang im Heizbereich zeigten dagegen keine photomechanische Ablation, sondern ausschließlich thermischen Zerfall. Die Ablationsschwelle lag auch hier bei höheren Temperaturen, entsprechend dem Gesetz von Arrhenius. Hohe Temperaturen, mehrere 100 K über der Zerfallstemperatur, ergaben sich darüber hinaus bei hohen Laserenergien. Ein drastisches Überhitzen des Polymers, wie in der Literatur beschrieben, konnte nicht beobachtet werden. Experimentelle Befunde deuten vielmehr darauf hin, dass es sich bei dem heißen Material um thermische Zerfallsprodukte, Polymerfragmente, Monomer und Zerfallsprodukte des Monomers handelte bzw. das Temperaturprofil der Zerfallsreaktion selbst visualisiert wurde.
Resumo:
In this thesis, anodic aluminum oxide (AAO) membranes, which provide well-aligned uniform mesoscopic pores with adjustable pore parameters, were fabricated and successfully utilized as templates for the fabrication of functional organic nanowires, nanorods and the respective well-ordered arrays. The template-assisted patterning technique was successfully applied for the realization of different objectives:rnHigh-density and well-ordered arrays of hole-conducting nanorods composed of cross-linked triphenylamine (TPA) and tetraphenylbenzidine (TPD) derivatives on conductive substrates like ITO/glass have been successfully fabricated. By applying a freeze-drying technique to remove the aqueous medium after the wet-chemical etching of the template, aggregation and collapsing of the rods was prevented and macroscopic areas of perfectly freestanding nanorods were feasible. Based on the hole-conducting nanorod arrays and their subsequent embedding into an electron-conducting polymer matrix via spin-coating, a novel routine concept for the fabrication of well-ordered all-organic bulk heterojunction for organic photovoltaic applications was successfully demonstrated. The increased donor/acceptor interface of the fabricated devices resulted in a remarkable increase of the photoluminescence quenching compared to a planar bilayer morphology. Further, the fundamental working principle of the templating approach for the solution-based all-organic photovoltaic device was demonstrated for the first time.rnFurthermore, in order to broaden the applicability of patterned surfaces, which are feasible via the template-based patterning of functional materials, AAO with hierarchically branched pores were fabricated and utilized as templates. By pursuing the common templating process hierarchically polymeric replicas, which show remarkable similarities with interesting biostructures, like the surface of the lotus leaf and the feet of a gecko, were successfully prepared.rnIn contrast to the direct infiltration of organic functional materials, a novel route for the fabrication of functional nanowires via post-modification of reactive nanowires was established. Therefore, reactive nanowires based on cross-linked pentafluorophenylesters were fabricated by utilizing AAO templates. The post-modification with fluorescent dyes was demonstrated. Furthermore, reactive wires were converted into well-dispersed poly(N-isopropylacrylamide) (PNIPAM) hydrogels, which exhibit a thermal-responsive reversible phase transition. The reversible thermal-responsible swelling of the PNIPAM nanowires exhibited a more than 50 % extended length than in the collapsed PNIPAM state. rnLast but not least, the shape-anisotropic pores of AAO were utilized to uniformly align the mesogens of a nematic liquid crystalline elastomer. Liquid crystalline nanowires with a narrow size distribution and uniform orientation of the liquid crystalline material were fabricated. It was shown that during the transition from the nematic to the isotropic phase the rod’s length shortened by roughly 40 percent. As such these liquid crystalline elastomeric nanowires may find application, as wire-shaped nanoactuators in various fields of research, like lab-on-chip systems, micro fluidics and biomimetics.rn
Resumo:
Die vorliegende Arbeit befasst sich mit der Synthese und Charakterisierung von Polymeren mit redox-funktionalen Phenothiazin-Seitenketten. Phenothiazin und seine Derivate sind kleine Redoxeinheiten, deren reversibles Redoxverhalten mit electrochromen Eigenschaften verbunden ist. Das besondere an Phenothiazine ist die Bildung von stabilen Radikalkationen im oxidierten Zustand. Daher können Phenothiazine als bistabile Moleküle agieren und zwischen zwei stabilen Redoxzuständen wechseln. Dieser Schaltprozess geht gleichzeitig mit einer Farbveränderung an her.rnrnIm Rahmen dieser Arbeit wird die Synthese neuartiger Phenothiazin-Polymere mittels radikalischer Polymerisation beschrieben. Phenothiazin-Derivate wurden kovalent an aliphatischen und aromatischen Polymerketten gebunden. Dies erfolgte über zwei unterschiedlichen synthetischen Routen. Die erste Route beinhaltet den Einsatz von Vinyl-Monomeren mit Phenothiazin Funktionalität zur direkten Polymerisation. Die zweite Route verwendet Amin modifizierte Phenothiazin-Derivate zur Funktionalisierung von Polymeren mit Aktivester-Seitenketten in einer polymeranalogen Reaktion. rnrnPolymere mit redox-funktionalen Phenothiazin-Seitenketten sind aufgrund ihrer Elektron-Donor-Eigenschaften geeignete Kandidaten für die Verwendung als Kathodenmaterialien. Zur Überprüfung ihrer Eignung wurden Phenothiazin-Polymere als Elektrodenmaterialien in Lithium-Batteriezellen eingesetzt. Die verwendeten Polymere wiesen gute Kapazitätswerte von circa 50-90 Ah/kg sowie schnelle Aufladezeiten in der Batteriezelle auf. Besonders die Aufladezeiten sind 5-10 mal höher als konventionelle Lithium-Batterien. Im Hinblick auf Anzahl der Lade- und Entladezyklen, erzielten die Polymere gute Werte in den Langzeit-Stabilitätstests. Insgesamt überstehen die Polymere 500 Ladezyklen mit geringen Veränderungen der Anfangswerte bezüglich Ladezeiten und -kapazitäten. Die Langzeit-Stabilität hängt unmittelbar mit der Radikalstabilität zusammen. Eine Stabilisierung der Radikalkationen gelang durch die Verlängerung der Seitenkette am Stickstoffatom des Phenothiazins und der Polymerhauptkette. Eine derartige Alkyl-Substitution erhöht die Radikalstabilität durch verstärkte Wechselwirkung mit dem aromatischen Ring und verbessert somit die Batterieleistung hinsichtlich der Stabilität gegenüber Lade- und Entladezyklen. rnrnDes Weiteren wurde die praktische Anwendung von bistabilen Phenothiazin-Polymeren als Speichermedium für hohe Datendichten untersucht. Dazu wurden dünne Filme des Polymers auf leitfähigen Substraten elektrochemisch oxidiert. Die elektrochemische Oxidation erfolgte mittels Rasterkraftmikroskopie in Kombination mit leitfähigen Mikroskopspitzen. Mittels dieser Technik gelang es, die Oberfläche des Polymers im nanoskaligen Bereich zu oxidieren und somit die lokale Leitfähigkeit zu verändern. Damit konnten unterschiedlich große Muster lithographisch beschrieben und aufgrund der Veränderung ihrer Leitfähigkeit detektiert werden. Der Schreibprozess führte nur zu einer Veränderung der lokalen Leitfähigkeit ohne die topographische Beschaffenheit des Polymerfilms zu beeinflussen. Außerdem erwiesen sich die Muster als besonders stabil sowohl mechanisch als auch über die Zeit.rnrnZum Schluss wurden neue Synthesestrategien entwickelt um mechanisch stabile als auch redox-funktionale Oberflächen zu produzieren. Mit Hilfe der oberflächen-initiierten Atomtransfer-Radikalpolymerisation wurden gepfropfte Polymerbürsten mit redox-funktionalen Phenothiazin-Seitenketten hergestellt und mittels Röntgenmethoden und Rasterkraftmikroskopie analysiert. Eine der Synthesestrategien geht von gepfropften Aktivesterbürsten aus, die anschließend in einem nachfolgenden Schritt mit redox-funktionalen Gruppen modifiziert werden können. Diese Vorgehensweise ist besonders vielversprechend und erlaubt es unterschiedliche funktionelle Gruppen an den Aktivesterbürsten zu verankern. Damit können durch Verwendung von vernetzenden Gruppen neben den Redoxeigenschaften, die mechanische Stabilität solcher Polymerfilme optimiert werden. rn rn
Resumo:
Different concepts for the synthesis of sulfur-containing polymers as well as their adsorption onto gold surfaces were studied. The present work is divided into three parts. The main part focuses on the synthesis of poly(1,2-alkylene sulfides) (“polysulfides”) with complex architectures on the basis of polyether-based macroinitiators by the anionic ring-opening polymerization of ethylene sulfide and propylene sulfide. This synthetic tool kit allowed the synthesis of star-shaped, brush-like, comb-like and pom-pom-like polysulfides, the latter two with an additional poly(ethylene glycol) chain. Additionally, the number of polysulfide arms as well as the monomer composition could be varied over a wide range to obtain copolymers with multiple thioether functionalities.rnThe second section deals with the synthesis of a novel lipoic acid-based initiator for ring-opening polymerizations for lactones and epoxides. A straightforward approach was selected to accomplish the ability to obtain tailored polymers with a common used disulfide-anchoring group, without the drawbacks of post-polymerization functionalization. rnIn the third part, a new class of block-copolymers consisting of polysulfides and polyesters were investigated. For the first time this approach enabled the use of hydroxyl-terminated poly(propylene sulfide) as macroinitiator for the synthesis of a second block.rnThe adsorption efficiency of those different polymer classes onto gold nanoparticles as well as gold rnsupports was studied via different methods.rn