Effectiveness of surface protection for resin-modified glass-ionomer materials

Objective: the purpose of this study was to evaluate the effectiveness of various surface treatments for resin-modified glass-ionomer restorative materials by determining dye uptake spectrophotometrically. Method and materials: Two hundred twenty-four specimens, 4.1 mm in diameter and 2.0 mm thick, were made of 3 materials: Vitremer, Fuji II LC, and Photac-Fil Aplicap. Specimens were divided into 15 groups. The positive and negative control specimens remained unprotected, while the experimental specimens were protected with Heliobond light-activated bonding resin, Colorama nail varnish, or surface coatings indicated by the manufacturers of the glass-ionomer materials. Finishing Gloss for Vitremer, Fuji Varnish for Fuji II LC, and Ketac Glaze for Photac-Fil. The disks were immersed in 0.05% methylene blue for 24 hours except for the negative control group, which was immersed in deionized water. After 24 hours, the disks were removed, washed, and individually placed in 1 mL of 65% nitric acid for 24 hours. The solutions were centrifuged and the spectrophotometric absorbance was determined at 606 nm. The dye uptake was expressed in micrograms of dye per milliliter, and the results were analyzed with the Kruskal-Wallis test. Results: There were no differences in dye uptake among the 3 resin-modified glass-ionomer restorative materials, however, all of them required surface protection. Conclusion: the best surface protection for the 3 evaluated materials was obtained with Heliobond light-activated bonding resin.

Surface protection of fluoroindate glasses by sol-gel dip-coated SnO2 thin layers

SnO2 coatings were deposited by a sol-gel dip-coating process to shield fluoroindate glasses (40In-F-3:16BaF(2):20SrF(2):20ZnF(2):2NaF:2GaF(3)) against corrosion in aqueous environments. The effect of the number of coating applications and of the withdrawal speed on the thickness, density and roughness of tin oxide films was investigated by X-ray reflectivity. Film thickness increases both with the number of coating applications and the withdrawal speed. The aqueous leaching of uncoated and SnO2-coated fluoroindate glasses was studied by scanning electron microscopy (SEM) and infrared spectroscopy (FTIR), showing that the glass surface was protected against hydrolytic attack. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (α = 5%). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

Structure of SnO2 alcosols and films prepared by sol-gel dip coating

To obtain SnO2 films to be used for surface protection of fluoride glasses, a non-aqueous sol-gel route for the preparation was developed. An ethanolic SnO2 colloidal suspension was prepared by thermohydrolysis of SnCl4 solution at 70 degreesC. By using this procedure, redispersable powders with nanometer sized particles were obtained. Films were obtained by dip coating on glass and mica substrates. The structures of the ethanolic precursor suspension and films were compared to those of similar samples prepared by the classical aqueous sol-gel route. Comparative analyses performed by photon correlation spectroscopy demonstrated that the powders obtained by freeze-drying are fully redispersable either in aqueous or in alcoholic solutions at pH greater than or equal to 8. As prepared sols and redispersed colloidal suspensions have hydrodynamic radius distribution (2-14 nm) with an average size close to 7 nm. The variations in film structures with firing temperature were investigated by small-angle X-ray scattering and X-ray reflectometry. The experimental results show that the films have a two level porous structure composed of agglomerates of primary colloidal particles. The sintering of the primary particles leads to the densification of agglomerates and to the formation of inter-agglomerate spatially correlated pores. The volume fraction of intra-agglomerate pores is reduced from approximate to 50% to approximate to 30% by the precipitation of precursor salts partially hydrolyzed in ethanolic solution. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Avaliação da liberação de íon fluoreto de cimentos ionoméricos antes e após a recarga e com proteção da superfície

Objective: To evaluate fluoride ion release from two anhydrous glass ionomer cements (GICs) and two resin-modified GICs (RMGICs) before and after recharge with 2% neutral sodium fluoride for 4 min and after surface protection of the Maxxion R GIC with an adhesive system, a cavity varnish and a colorless nail polish. Method: A stainless steel 2x6 mm matrix was used for fabricating 5 specimens of each material, which were immersed in 5 mL of deionized water, renewed every 24 h. Measurements with a potentiometer were performed on days 1, 2, 9 and 17, in the 1st and 2nd phases, and the specimens were buffered with a TISAB III solution. In the 2nd phase, the specimens were subjected to recharge and immersed again in 5 mL of deionized water. In the 3rd phase, the GIC surfaces were protected and readings were made at 5 min, 24 h, 48 h and 72 h. Tukey's post-hoc and Student's t tests were used for statistical analyses (p<0.05). Results: There was statistically significant difference in the comparison between the 1st and 2nd phases for all materials, except at day 2 for Vidrion R and VitroFil LC. In the 3rd phase, it was observed that for all materials, comparison of the first 5 min with the other times revealed statistically significant differences among the means of fluoride ion release. In the comparison with the other times, both the varnish and the colorless nail polish presented statistically significant difference between 24 and 48 h as well as between 24 and 72 h. Conclusion: The anhydrous GICs were more effective in fluoride ion release and recharge compared with the RMGICs. Maxxion R presented a homogeneous and statistically significant behavior in both phases. All materials for surface protection were efficient and the colorless nail polish had the best behavior.

Microdureza de cimentos de ionômeros de vidro indicados para a técnica do ART, variando-se a proteção superficial e o tempo de armazenamento

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

XPS study on water corrosion of fluorzirconate glasses and their protection by a layer of surface modified tin dioxide nanoparticles

The surface corrosion process associated with the hydrolysis of fluorozirconate glass, Z-BLAN (53ZrF(4), 20BaF(2), 20NaF, 4LaF(2), 3AlF(3)), and the corrosion protection efficiency of a nanocrystalline transparent SnO2 layer were investigated by X-ray photoelectron spectroscopy. The tin oxide film was deposited by the sol-gel dip-coating process in the presence of Tiron(R) as particle surface modifier agent. The chemical bonding structure and composition of the surface region of coated and non-coated ZBLAN were studied before water contact and after different immersion periods (5-30 min). In contrast to the effects occurring for non-coated glass, where the surface undergoes a rapid selective dissolution of the most soluble species inducing the formation of a new surface phase consisting of stable zirconium oxyfluoride, barium fluoride and lanthanum fluoride species, the results for the SnO2-coated glass showed that the hydrolytic attack induces a filling of the film nanopores by dissolved glass material and the formation of tin oxylluoride and zirconium oxyfluoride species. This process results in a modified film, which acts as a hermetic diffusion barrier protecting efficiently the glass surface. (C) 2006 Elsevier B.V. All rights reserved.

Corrosion protection of fluorzirconate glasses coated by a layer of surface modified tin oxide nanoparticles

The protection efficiency against water corrosion of fluorozirconate glass, ZBLAN, dip-coated by nanocrystalline tin oxide film containing the organic molecule Tiron® was investigated by X-ray photoelectron spectroscopy (XPS) and atomic force microscopy (AFM). The chemical bonding structure of the surface region and morphology were studied before and after two water exposure periods of 5 and 30 min. The results of the analysis for the as-grown sample revealed a SnO1.6 phase containing carbon and sulfur, related to Tiron®, and traces of elements related to ZBLAN (Zr, F, Ba). This fact and the clear evidence of the presence of tin oxifluoride specie (SnOxF y) indicates a diffusion of the glass components into the porous coating. After water exposure, the increase of the oxygen concentration accompanied by a strong increase of Zr, F, Ba and Na content is interpreted as filling of the nanopores of the film by glass compounds. The formation of a compact protective layer is supported by the morphological changes observed by AFM. © 2005 Elsevier B.V. All rights reserved.

Antitumor effects in vitro and in vivo and mechanisms of protection against melanoma B16F10-Nex2 cells by fastuosain, a cysteine proteinase from Bromelia fastuosa

In the present work, the antitumor effect of fastuosain, a cysteine proteinase from Bromelia fastuosa, was investigated. In the intravenous model of lung colonization in C57Bl/6 mice, fastuosain and bromelain injected intraperitoneally were protective, and very few nodules of B16F10-Nex2 melanoma cells were detected. Tumor cells treated with fastuosain showed reduced expression of CD44 and decreased invasion through Matrigel, lost their cytoplasmic extensions and substrate adherence, and became round and detached, forming strongly bound cell clusters in suspension. Peritoneal cells recruited and activated by fastuosain treatment ( mainly monocytic cells and lymphocytes) migrated to the lung, where pulmonary melanoma metastases grew. Adoptive transference of peritoneal cells recruited by fastuosain had no protective effect against lung metastases in recipient mice. Treatment of green fluorescent protein - chimeric animals with fastuosain did not change the number of cells that migrated to the lung, compared to PBS-injected control mice, but the number of positive major histocompatibility complex class II cells increased with fastuosain treatment. Murine antibodies against fastuosain, bromelain, and cathepsins B and L cross-reacted in ELISA and recognized surface and cytoplasmic components expressed on B16F10-Nex2 cells. Anti-fastuosain antibodies were cytotoxic/lytic to B16F10-Nex2 cells. Antitumor effects of fastuosain involve mainly the direct effect of the enzyme and elicitation of protective antibodies.

XPS study of the corrosion protection of fluorozirconate glasses dip-coated with SnO2 transparent thin films

Tin oxide nanoparticles prepared by an aqueous sol-gel method were deposited by dip-coating on fluorozirconate glass, ZBLAN (53%ZrF4-20%BaF2-4%LaF3-3%AlF3-20%NaF) to improve its resistance against wet corrosion. The aqueous leaching of uncoated and SnO2-coated fluorozirconate glass was studied by X-ray photoemission spectroscopy (XPS) and it was shown that even an ultra thin tin dioxide film provides good protection of the glass surface against the bulk propagation of the hydrolytic attack.

Corrosion protection of stainless steel by polysiloxane hybrid coatings prepared using the sol-gel process

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of the fluorination of DLC film on the corrosion protection of aluminum alloy (AA 5052)

It is presented a study conducted on the physical and electrochemical properties of fluorinated a-C:H films deposited onto a commercial aluminum alloy (AA 5052). The coatings were deposited from mixtures of 91% of acetylene and 9% of argon by plasma immersion ion implantation and deposition technique, PIIID. Total gas pressure was 44 Pa and deposition time (t(dep)) was varied from 300 to 1200 s. The depositing plasmas were generated by the application of radiofrequency power (13.56 MHz, 100W) to the upper electrode and high voltage negative pulses (2400 V. 300 Hz) to the sample holder. Fluorine was incorporated in a post-deposition plasma treatment (13.56 MHz, 70W, 13 Pa) generated from sulfur hexafluoride atmosphere. Chemical structure and composition of the films were investigated using infrared reflectance/absorbance spectroscopy and X-ray photoelectron spectroscopy. The corrosion resistance of the layers was determined by electrochemical impedance spectroscopy (EIS) in a 3.5% NaCl solution, at room temperature. Films presented good adhesion to the substrates and are classified as hydrogenated amorphous carbon (a-C:H) with oxygen traces. Fluorine was detected in all the samples after the post-deposition treatment being its proportion independent on the deposition time. Film thickness presented different tendencies with t(dep), revealing the variation of the deposition rate as a function of the deposition time. Such fluorinated a-C:H films improved the corrosion resistance of the aluminum surface. In a general way the corrosion resistance was higher for films prepared with lower deposition times. The variation of sample temperature with t(dep) was found to be decisive for the concentration of defects in the films and, consequently, for the performance of the samples in electrochemical tests. Results are interpreted in terms of the energy delivered to the growing layer by ionic bombardment. (C) 2010 Elsevier B.V. All rights reserved.

Ceramic coating for refractories protection against carbon oxidation, Part 1: Protection mechanisms

For retarding carbon oxidation in refractories during the preheating of metallurgical furnaces, a ceramic coating, made mainly of sodium phosphosilicate and clay was developed. The coating presents high adherence to the substrate with no swelling. The coating was characterized by thermal analysis, X-ray diffraction at room temperature (XRD) and at high temperature (HTXRD), X-ray fluorescence and scanning electronic microscopy (SEM). The glass transition temperature is reached at 800 °C and only glassy phase is observed above this temperature. Thus the mechanism of protection seems to be the formation of a glassy phase on the surface of the refractory, and the coating tends to be more efficient at temperatures higher than 800 °C.

Scanning electron microscope analysis of internal adaptation of materials used for pulp protection under composite resin restorations

Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.