Influence of aged Ti-15V-3Cr-3Sn-3Al alloy microstructure on chemical and electrochemical behavior in the Kroll reagent for metallographic etching

The chemical and electrochemical behaviour of the Ti-1 5V-3Cr-3Sn-3Al alloy in Kroll reagent has been studied after ageing at 350-600degreesC, to optimise metallographic etching. Etching tests and polarisation curves showed that samples aged at higher temperatures have been more susceptible to corrosion. It has been attributed to the formation of intra- and intergranular alpha-phase precipitates during ageing.

Influence of spraying parameters on the electrochemical behaviour of HVOF thermally sprayed stainless steel coatings in 3.4% NaCl

Stainless steel coatings obtained by High Velocity Oxygen Fuel (HVOF) were characterized using optical (OM) and scanning electron microscopy (SEM), electron probe micro-analysis, X-ray diffraction (XRD), open-circuit potential (E-OC) measurements, electrochemical impedance spectroscopy (EIS) and polarisation tests. Differences among coated steels were mainly related with the gun-substrate distance parameter (310 nm for samples A and B and 260 min for C and D). The open-circuit potential values measured for all the samples after 18 h of immersion in aerated and unstirred 3.4% NaCl solution were: - 0.334, - 0.360, - 0.379 and - 0.412 V vs. Ag/AgCl,KClsat. for samples A to D, respectively. For EIS measurements, Nyquist plots showed higher capacitive semi-circle for samples sprayed at longer distance, indicating higher corrosion resistance in NaCl solution. (c) 2005 Elsevier B.V. All rights reserved.

Effects of thickness coating on the electrochemical behaviour of thermal spray Cr3C2-NiCr coatings

Thermally sprayed HVOF coatings are increasingly being used in industrial applications where high wear and corrosion resistance are needed [1,2]. In this paper, electrochemical ac and de experiments were used in order to obtain the corrosion resistance of coated steel with different numbers of Cr3C2-NiCr layers. This work has been performed in order to determine the role of coating thickness in the corrosion behaviour of a steel protected with cermet thermally sprayed coatings. It is known that a thicker layer protects better against corrosion when a metallic coating is evaluated. But cermet coatings, such as Cr3C2-NiCr, contain higher levels of porosity and residual stresses than metallic coatings, which really could influence the corrosion resistance of the deposited layer. Electrochemical measurements, such as Open-Circuit Potential (E-Osubset of), Polarisation Resistance (RP) and Cyclic Voltammetry (CV), were performed in an aerated 3.4 NaCI media (%wt.). Electrochemical Impedance Measurements (EIS) were also done in order to obtain a mechanism that explains the corrosion process. Structural Characterisation was carried out by means of Optical and Scanning Electron Microscopes (OM, SEM) with an Energy Dispersive Spectrometry analyser (EDS). Results show that the corrosion resistance of the complete system is mainly influenced by the substrate behaviour. The application of a higher number of deposited layers did not substantially increase their anticorrosive properties. Stress generation during the spraying deposition process plays an important role in the behaviour of the coated steel against corrosion phenomena. (C) 2002 Elsevier B.V. B.V All rights reserved.

Strain behavior of lanthanum modified BiFeO3 thin films prepared via soft chemical method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of thermal treatments in the corrosion behaviour of HVOF Cr 3C2-NiCr coatings

Thermal spray coatings as Cr3C2-NiCr obtained by high velocity oxy-fuel spraying (HVOF) are mainly applied due to their behaviour against aggressive erosive-abrasive and corrosive atmospheres and their thermal stability at high temperatures [1]. In order to increase the corrosion protection that it offers to the substrate trying to close the interconnected pores, it is possible to apply a thermal treatment with the gun during the spraying of the coating. This treatment could be applied in different ways. One of these ways consists of spraying only a few layers of coating followed by thermal treatment and finally the spray of the rest of layers. This thermal treatment on spraying is studied related to the corrosion properties of the system. The study comprises the electrochemical characterisation of the system by open circuit potential (OC), polarisation resistance (Rp), cyclic voltammetry (CV) and impedance spectroscopy measurements (EIS). Optical and scanning electron microscopy characterisation (OM and SEM) of the top and cross-section of the system has been used in order to justify the electrochemical results.

Um estudo sobre a corrosão aquosa de ligas de alumínio 7xxx submetidas a diferentes tratamentos térmicos

This job aim has been to study the aqueous corrosion of the 7xxx heattreatable aluminium alloys, used in the aeronautical industry. The 7010, 7050 and 7475 alloys, have been supplied in the T7 condition and submitted to the annealed and aging thermal treatments of in order to study their behaviours front to corrosion in 5% NaCl pH 6,0, air-saturated and deaerated solutions. The electrochemical study has been accomplished through potential measures in open circuit, potentiodynamic polarisation curves and electrochemical impedance spectroscopy (EIS). The aged alloy resulted to be the most resistant to corrosion and annealed the less resistant ones. In spite of it they have different chemical compositions, in each mean, the alloy with the same thermal treatment has behaved in a similar way. In aerated solution, the process is controlled by oxygen diffusion and in oxygen absence for dissolution through a film. Hardness and mass loss measures, after corrosion test, have supported this research.

Efeito do nitrato e nitrito na corrosão das ligas de alumínio 2024 e 7050 em soluções de NaCl

The 2024-T3 and 7050-T7 aluminium alloys electrochemical behavior has been studied in NaCl 5% neutral solutions and 0,1M concentration containing NO 3 - or NO 2 -. The current job supports corrosion research on aluminium alloys used in aeronautic industry. Open circuit potential, polarisation curves and electrochemical impedance spectroscopy techniques have been used. In chloride solutions, alloys corrosion takes place through a pitting mechanism. Added anions to aerated solutions do not possess inhibition effect. In deaerated solutions, nitrite has diminished anodic dissolution rate, probably by incorporating this anion in the oxide and/or hydroxide film.

Corrosion and tribocorrosion behaviour of Al-Si-Cu-Mg alloy and its composites reinforced with B4C particles in 0.05M NaCl solution

The corrosion behaviour of metal matrix composites (MMCs) is strictly linked with the presence of heterogeneities such as reinforcement phase, microcrevices, porosity, secondary phase precipitates, and interaction products. Most of the literature related to corrosion behaviour of aluminium matrix composites (AMCs) is focused on SiC reinforced AMCs. On the other hand, there is very limited information available in the literature related to the tribocorrosion behaviour of AMCs. Therefore, the present work aims to investigate corrosion and tribocorrosion behaviour of Al-Si-Cu-Mg alloy matrix composites reinforced with B4C particulates. Corrosion behaviour of 15 and 19% (vol) B4C reinforced Al-Si-Cu-Mg matrix composites and the base alloy was investigated in 0.05M NaCl solution by performing immersion tests and potentiodynamic polarisation tests. Tribocorrosion behaviour of Al-Si-Cu-Mg alloy and its composites were also investigated in 0.05M NaCl solution. The tests were carried out against alumina ball using a reciprocating ball-on-plate tribometer. Electrochemical measurements were performed before, during, and after the sliding tests together with the recording of the tangential force. Results suggest that particle addition did not affect significantly the tendency of corrosion of Al-Si-Cu-Mg alloy without mechanical interactions. During the tribocorrosion tests, the counter material was found to slide mainly on the B4C particles, which protected the matrix alloy from severe wear damage. Furthermore, the wear debris were accumulated on the worn surfaces and entrapped between the reinforcing particles. Therefore, the tendency of corrosion and the corrosion rate decreased in Al-Si-Cu-Mg matrix B4C reinforced composites during the sliding in 0.05M NaCl solution. © 2013 Elsevier B.V.

Electrochemical studies of copper, copper-aluminium and copper-aluminium-silver alloys: Impedance results in 0.5M NaCl

The electrochemical behaviour of Cu, Cu-Al and Cu-Al-Ag alloys in aqueous solutions of NaCl (0.5 M, pH = 3.00) was studied by means of voltammetric methods and electrochemical impedance spectroscopy. The surfaces were examined by SEM and EDX analysis. Cu-Al-Ag alloy shows a potentiodynamic behaviour similar to that of the pure copper electrode while the Cu-Al alloy presents some minor differences. In the active dissolution region the electrodes suffer pitting corrosion and in the other potential regions there are the formation of a passivant film with composition depending on the potential. The impedance responses of the electrodes are discussed. An electrodissolution mechanism is proposed and the effect of the alloying elements upon the impedance response and polarisation curves is explained. The main effects are due to the production of copper and silver chlorides and aluminium oxides/ hydroxides at the corroding interface. The addition of Al or (Al + Ag) increases the corrosion resistance of pure copper. © 1995.

Corrosion behaviour of aluminium syntactic functionally graded composites

Syntactic Functionally Graded Metal Matrix Composites (SFGMMC) are a type of composites reinforced by microballoons exhibiting a graded reinforcement distribution. These materials constitute a promising new generation of lightweight structural materials for aerospace, marine and shielding/insulation applications. In this work, A356 alloy reinforced with silica-alumina microballoons (SiO2-Al2O3) was processed by casting techniques. The influence of the microballoon distribution gradient on the corrosion behaviour of the composite was investigated by potentiodynamic polarisation and Electrochemical Impedance Spectroscopy (EIS). Composite surfaces were analysed before and after testing by Optical Microscopy (OM) and Scanning Electron Microscopy (SEM) to determine the influence of microstructural changes.