Photoinduced effects in As-S-P glasses

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Photoinduced effect in Ga-Ge-S based thin films

Glassy films of Ga10Ge25S65 with 4 mu m thickness were deposited on quartz substrates by electron beam evaporation. Photoexpansion (PE) (photoinduced increase in volume) and photobleaching (PB) (blue shift of the bandgap) effects have been examined. The exposed areas have been analyzed using perfilometer and an expansion of 1.7 mu m (Delta V/V approximate to 30%) is observed for composition Ga10Ge25S65 exposed during 180 min and 3 mW/cm(2) power density. The optical absorption edge measured for the film Ge25Ga10S65 above and below the bandgap show that the blue shift of the gap by below bandgap photon illumination is considerable higher (Delta E-g = 440 meV) than Delta E-g induced by above bandgap illumination (Delta E-g = 190 meV). The distribution of the refraction index profile showed a negative change of the refraction index in the irradiated samples (Delta n = -0.6). The morphology was examined using a scanning electron microscopy (SEM). The chemical compositions measured using an energy dispersive analyzer (EDX) indicate an increase of the oxygen atoms into the irradiated area. Using a Lloyd's mirror setup for continuous wave holography it was possible to record holographic gratings using the photoinduced effects that occur in them. Diffraction efficiency up to 25% was achieved for the recorded gratings and atomic force microscopy images are presented. (c) 2005 Elsevier B.V. All rights reserved.

Raman spectroscopy analysis of structural photoinduced changes in GeS2 + Ga2O3 thin films

Photoexpansion and photobleaching effects have been observed in amorphous GeS2 + Ga2O3 (GGSO) thin films, when their surfaces were exposed to UV light. The photoinduced changes on the surface of the samples are indications that the structure has been changed as a result of photoexcitation. In this paper, micro-Raman, energy dispersive X-ray analysis (EDX) and backscattering electrons (BSE) microscopy were the techniques used to identify the origin of these effects. Raman spectra revealed that these phenomena are a consequence of the Ge-S bonds' breakdown and the formation of new Ge-O bonds, with an increase of the modes associated with Ge-O-Ge bonds and mixed oxysulphide tetrahedral units (S-Ge-O). The chemical composition measured by EDX and BSE microscopy images indicated that the irradiated area is oxygen rich. So, the present paper provides fundamental insights into the influence of the oxygen within the glass matrix on the considered photoinduced effects. (C) 2010 Elsevier B.V. All rights reserved.

Photoexpansion and photobleaching effects in oxysulfide thin films of the GeS2+Ga2O3 system

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Ga incorporation on photoinduced phenomena in Ge-S based glasses

To study the influence of Ga addition on photoinduced effect, GaGeS glasses with constant atomic ratio S/Ge = 2.6 have been prepared. Using Raman spectroscopy, we have reported the effect of Ga on the structural behavior of these glasses. An increase of the glass transition temperature T(g), the linear refractive index and the density have been observed with increasing gallium content. The photoinduced phenomena have been examined through the influence of time exposure and power density, when exposed to above light bandgap (3.53 eV). The correlation between photoinduced phenomena and Ga content in such glasses are shown hereby. (C) 2009 Elsevier B.V. All rights reserved.

Refractive index changes in photochromic SbPO4-WO3 glass by exposure to band-gap radiation

We report photoinduced photo-darkening in SbPO4-WO3 glass by exposure to 532 nm light with a power density of 143 mW/cm(2). The time of exposure was varied between 0 and 256 min following which visible photo-darkening, peaking at 850 nm was observed. Spectrophotometer measurement of absorption was performed for both treated and untreated regions of the sample. Time exposure to below band-gap light results in a single exponent Gaussian absorption function over an exceptionally wide range of wavelengths (500 nm-1600 nm), with a 1/e width of 647.5 nm. Kramers-Kronig transform of the change in the absorption indicates a negative local change in the refractive index. The dispersed refractive index change at 1550 nm, Delta n, is calculated to be similar to -5 x 10(-8). The peak absorption increases with time of exposure and the photo-darkening remains irreversible at room temperature. Crown Copyright (C) 2010 Published by Elsevier B.V. All rights reserved.

Glasses in the SbPO4-WO3 system

Glasses in the binary system (100 - x)SbPO4-xWO3 (20 <= x <= 60, x in mol%) have been prepared and characterized. Differential thermal analysis (DTA) shows that the glass transition temperature, T-g increases from 412 degrees C, for samples containing 20 mol% of WO3 to 481 degrees C observed for glass containing 60 mol%. Sample containing 40 mol% in WO3 were observed to be the most stable against devitrification. The structural organization of the glasses has been studied by using Fourier transform infra-red (FTIR), Raman, P-31 Magic angle spinning (MAS) and spin echo nuclear magnetic resonance (NMR) spectroscopies. Results suggest two distinct networks comprising the glass structure, one with high SbPO4 content and the other characteristic of the highest WO3 content samples. The glasses present photochromic properties. Colour changes are observed for samples after exposure to ultraviolet or visible laser light. XANES, at L-1 absorption edge of tungsten, suggests partial reduction from W6+ to W5+ species during the laser irradiation. The photochromic effects and the colour changes, promoted by laser excitation, are reversible and easily removed by heat for during 1 h at 150 degrees C. Subsequent 'write/erase' cycles can be done without degradation of the glasses. (C) 2007 Elsevier B.V. All rights reserved.

Photoinduced orientation in natural rubber

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Photoinduced hole-transfer in semiconducting polymer/low-bandgap cyanine dye blends: evidence for unit charge separation quantum yield

Power-conversion efficiencies of organic heterojunction solar cells can be increased by using semiconducting donor-acceptor materials with complementary absorption spectra extending to the near-infrared region. Here, we used continuous wave fluorescence and absorption, as well as nanosecond transient absorption spectroscopy to study the initial charge transfer step for blends of a donor poly(p-phenylenevinylene) derivative and low-band gap cyanine dyes serving as electron acceptors. Electron transfer is the dominant relaxation process after photoexcitation of the donor. Hole transfer after cyanine photoexcitation occurs with an efficiency close to unity up to dye concentrations of similar to 30 wt%. Cyanines present an efficient self-quenching mechanism of their fluorescence, and for higher dye loadings in the blend, or pure cyanine films, this process effectively reduces the hole transfer. Comparison between dye emission in an inert polystyrene matrix and the donor matrix allowed us to separate the influence of self-quenching and charge transfer mechanisms. Favorable photovoltaic bilayer performance, including high open-circuit voltages of similar to 1 V confirmed the results from optical experiments. The characteristics of solar cells using different dyes also highlighted the need for balanced adjustment of the energy levels and their offsets at the heterojunction when using low-bandgap materials, and accentuated important effects of interface interactions and solid-state packing on charge generation and transport.

Raman investigation of structural photoinduced irreversible changes of Ga10Ge25S65 chalcogenide glasses

The influence of time exposure, when exposed to above band gap light (3,52 eV) and annealing, on Ga10Ge25S65 glasses has been studied through their effects on the structure and optical properties. To evaluate the photostructural change infrared and Raman spectra for bulk Ga10Ge25S65 glasses have been measured before and after exposure. The Raman spectra are interpreted in terms of models in which the Ge atoms are fourfold coordinated and the S atoms are two fold coordinated. The observed changes in the spectral region of (S-S) stretching vibration (470-490 cm (-1)) is a direct evidence for the occurrence of important structural changes in local bonding configuration caused by optical irradiation. It is shown that the dominant photostrucural changes are chain formation tendency of the chalcogenide atoms under the laser irradiation rather than rings.