Structural and optical properties of GdAlO3:RE3+ (RE = Eu or Tb) prepared by the Pechini method for application as X-ray phosphors

In this work, GdAlO3:RE3+ (RE = Eu or Tb) was successfully prepared by the Pechini method at lower temperatures when compared to others methods as solid-state synthesis and sol-gel process. In accordance to the XRD data, the fully crystalline single-phase GdAlO3 could be obtained at 900 degrees C. The differential thermal analysis (DTA) shows a crystallization peak at 850 degrees C. The samples are composed by monocrystalline particles (50-120 nm) exhibiting the formation of aggregates among them, which indicates the beginning of the sinterization process. This feature indicates a strong tendency to the formation of aggregates, which is a suitable ability for the close-packing of particles, and hence a potential application in X-ray intensifying screens. Luminescence measurements indicate Gd3+ -> RE3+ energy transfer. The Eu3+ emission spectra exhibit all the characteristics D-5(0) -> F-7(j) transitions and the observed profile suggests that RE3+ ions occupy at least one site without center of symmetry. For terbium-doped samples, the D-5(3) -> F-7(j) (blue emission) and D-5(4) -> F-7(j) (green emission) transitions were observed and the ratio between them may depend on the Tb3+ content due to cross-relaxation processes. (C) 2009 Elsevier B.V. All rights reserved.

Correlation between the spectroscopic and structural properties with the occupation of Eu3+ sites in powdered Eu3+-doped LiTaO3 prepared by the Pechini method

In this work we studied the structural and optical properties of lithium tantalate (LiTaO3) powders doped with Eu3+ ions. We have examined the different sites occupied by the rare earth ion through the correlation of the DRX data analyzed with the Rietveld method and some spectroscopic parameters derived from the Eu3+ luminescence. Adirect relation was established between the lattice parameters and the occupation fraction of Eu3+ in each LiTaO3 site. The occupation fraction was set as the relative population of Eu3+ ions for each site obtained by means of the intensity, baricenter, and the spontaneous emission coefficients of the D-5(0)-> F-7(0) transitions. We concluded that the unit cell parameter a presents the same behavior of the Eu3+ occupation fraction in Ta5+ sites as a function of the Eu3+ content in LiTaO3. The same was observed for the variation in Eu3+ occupation fraction in the Li+ site and the unit cell parameter c with the Eu3+ content. (C) 2009 American Institute of Physics. [doi: 10.1063/1.3204967]

Óxido de zinco dopado com gálio preparado pelo método Pechini

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influência do oxalato de amônio na formação do precursor columbita obtido pelo método Pechini

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Analysis of Ca-PZT powder obtained by the Pechini and partial oxalate methods

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Synthesis and sintering of ZrO2-CeO2 powder by use of polymeric precursor based on Pechini process

Nanocrystalline ZrO2-12 mol % CeO2 powders were synthesized using a polymeric precursor method based on the Pechini process. X-ray diffraction (XRD) patterns showed that the method was effective to synthesize tetragonal zirconia single-phase. The mean crystallite size attained ranges from 6 to 15 nm. The BET surface areas were relatively high reaching 97 m(2)/g. Studies by nitrogen adsorption/desorption on powders, dilatometry of the compacts, and transmission electron microscopy (TEM) of the powders, were also developed to verify the particles agglomeration state. Both citric acid : ethylene glycol ratio and calcination temperature affected the powder morphology, which influenced the sinterability and microstructure of the sintered material, as showed by scanning electron microscopy (SEM). (C) 2001 Kluwer Academic Publishers.

Synthesis and characterization of PLZT (9/65/35) by the Pechini method and partial oxalate

ZrTiO4 (ZT), obtained by the Pechini method, was used as precursor for obtaining PLZT (lead lanthanum zirconium titanate). An aqueous solution of oxalic acid was prepared with particles of ZT, Pb(NO3)(2) and La2O3. After the PbC2O4 and La2O3 precipitate on ZT particles, the materials were calcined and X-ray diffraction (XRD) showed the cubic phase of PLZT. This material was sintered, in two steps, and a density of about 8.0 g/cm(3) was obtained. After the second sintering the XRD pattern showed the occurrence of tetragonal and rhombohedral phases. This was caused by a stoichiometric deviation and the material showed a high optical transparency. (C) 1998 Elsevier B.V. B.V. All rights reserved.

Pechini's solution as precursor for Eu(III)-containing ZnO films

The flat-panel-display's (FPD) market and demand for highly efficient and colored luminescent films have been growing quickly. In this work, thin films were obtained from Pechini's solution by dip-coating. The green films were thermally treated at 873 K in order to get ZnO:Eu 1 at% thin film. A Schott(R) glass plate hydrothermally treated was used as substrate. The films have a mosaic shaped feature that was observed by optical microscopy. That feature is a result of substrate thermal treatment. The film deposition decreases the substrate transmittance in the visible range. When the F-7(0) -->L-5(6) (392nm) Eu3+ transition is excited, it is possible to detect emission from D-5(0) --> F-7(J) (J = 1, 2, 3 and 4) transitions. The D-5(0) --> F-7(2) transition is also observed by using ZnO excitation wavelengths indicating energy transfer from ZnO to Eu3+ ion. (C) 2003 Elsevier B.V. (USA). All rights reserved.

Influence of the concentration of Sb2O3 and the viscosity of the precursor solution on the electrical and optical properties of SnO2 thin films produced by the Pechini method

SnO2:Sb multi-layer coatings were prepared by the Pechini method. An investigation was made of the influence of the concentration of Sb2O3 and the viscosity of the precursor solution on the electrical and optical properties of SnO2 thin films. The use of a multi-layer system as an alternative form of increasing the packing and. thus. decreasing porosity proved to be efficient, decreasing the system's resistivity without altering its optical properties. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Europium(III)-containing zinc oxide from Pechini method

ZnO:Eu3+ (0.1 and 3 at%) with average particle size of 500 nm were prepared by the Pechini method. Photoluminescence spectroscopy evidences that there is no energy transfer between ZnO and Eu3+ ion. The emission spectrum at 77 K shows that Eu3+ ions occupy at least three different sites in ZnO:Eu 3 at% sample. The experimental intensity parameter Omega(2) indicates that Eu3+ ions in the sample doped with 3 at% occupy sites where 4-configurational levels can better mix with opposite-parity states than those in the sample doped with 0.1 at%. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Seeding of PMN powders made by the Pechini method

The partial oxalate method, with the columbite route, associated with the Pechini method, was used to obtain a very fine ceramic powder at low temperature. Using this route it was possible to obtain a very reactive powder and to synthesize a lead magnesium niobate (PMN) powder with up to 100% of perovskite phase at a lower temperatures than the PbO melting point. The influence of the BaTiO3 and PbTiO3 seeds in the phase formation, along with time and temperature during the PMN calcination, was also investigated. The amount of 2% of BaTiO3 seeds promoted PMN powder formation with 100% of perovskite phase and a very narrow particle size distribution. (C) 2001 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Influence of TiO2 and AI(2)O(3) on the electrical and microstructural properties of SnO2 ceramics obtained by the Pechini method

Tin oxide has wakened up great scientific and technological interest for its potential use in varistors production and as gas sensor. In order to improve the microstructural and electrical properties in SnO2 varistor ceramics, the influence of differents dopants used, like TiO2 and Al2O3, is under research. The effect of TiO2 and Al2O3 on the properties of Sn-Co-Nb varistor systems obtained by the Pechini method has been investigated in this work. Characterization of synthesized raw material was performed by X-Ray Diffraction (XRD) and Scanning Electronic Microscopy (SEM). The microstructural and electrical characterization of sintered samples show that the TiO2 favors the grain growth and the Al2O3 contributes to the decrease it, effect that is manifested in the Sn-Co-Nb varistor systems. Breakdown field increase up to 6300V/cm with increasing Al2O3 content and non-linear coefficients with alpha=22 were obtained.

Estudio de PMN cerámico dopado con KNbO3 y LiNbO 3 sintetizado por Pechini

PMN belongs to a special class of materials named relaxor ferroelectrics. It has high volumetric efficiency due to its high dielectric constant, which makes it in a perfect material for application in multilayer capacitors. When prepared the columbite route its preparation has many advantages. In this work, the preparations of columbite and PMN were done by Pechini and Partial Oxalate methods, respectively. The effects of the KNbO3 and LiNbO3 dopants added in various concentrations. The idea is founded on the correlations that they have with BaTiO3 y PbTiO3, respectively. The whole process was supervised by TG/DTA, XRD, SEM and determination of the specific surface area of the powders. LiNbO3 carries out the pre-sinterization of the particles, observed by a reduction in the surface area. There are not particle grow, but occur its lengthening. However, for KNbO3 these particle growth, but the agglomerates are softer. The effect produced by the doping during the synthesis of the PMN powder is different from the one produced in the columbite precursor. Pure precursor shows an average particle size of 0,2μm, but the addition of 5,0mol% of dopants carries out the formation of agglomerates close to 4μm. LiNbO 3 addition carries out spherical particles and pre-sinterization, while KNbO3 addition does not change the particles shape.

Influence of oxygen atmosphere on LiNbO3 thin films prepared by Pechini process

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500°C for 3 hours. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz. Electrical characterizations of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films is discussed.

Respuesta eléctrica de películas gruesas del sistema SnO2-TiO2, conformadas con polvos cerámicos obtenidos a través del método pechini

Tin oxide is the compound more used in the gas sensor production, mainly to reduce gases like CO and H2. Their electrical properties are strongly dependent of its surface. For this is of great importance to synthesize nanoscale tin oxide particles to use they later in the films conformation. The synthesis of SnO2-TiO2 nanoparticles by polymeric precursor method is reported in this work. The particles were characterized by DTA/TG, FT-IR, XRD and SEM. Also, the electrical response of thick films measured under oxygen and carbon monoxide atmospheres is was analyzed.