'ZN IND.7'SB IND. 2'O IND. 12' contendo Ce(III), Pr(III) ou Eu(III): investigação de suas propriedades estruturais e ópticas para potencial aplicação como cintilador

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

MRT letter: Extended depth from focus reconstruction method for stretch zone measurement in 15-5PH steel

The stretch zone width (SZW) data for 15-5PH steel CTOD specimens fractured at -150 degrees C to + 23 degrees C temperature were measured based on focused images and 3D maps obtained by extended depth-of-field reconstruction from light microscopy (LM) image stacks. This LM-based method, with a larger lateral resolution, seems to be as effective for quantitative analysis of SZW as scanning electron microscopy (SEM) or confocal scanning laser microscopy (CSLM), permitting to clearly identify stretch zone boundaries. Despite the worst sharpness of focused images, a robust linear correlation was established to fracture toughness (KC) and SZW data for the 15-5PH steel tested specimens, measured at their center region. The method is an alternative to evaluate the boundaries of stretched zones, at a lower cost of implementation and training, since topographic data from elevation maps can be associated with reconstructed image, which summarizes the original contrast and brightness information. Finally, the extended depth-of-field method is presented here as a valuable tool for failure analysis, as a cheaper alternative to investigate rough surfaces or fracture, compared to scanning electron or confocal light microscopes. Microsc. Res. Tech. 75:11551158, 2012. (C) 2012 Wiley Periodicals, Inc.

Low-level laser on femoral growth plate in rats

OBJETIVO: Determinar a influência do Laser Terapêutico de Baixa Potência sobre a placa de crescimento de ratos. MÉTODOS: Trinta ratos Wistar machos com 40 dias de idade foram divididos em dois grupos, G1 e G2. O grupo G1 foi submetido à irradiação com laser GaAlAs 830 nm, potência de saída de 40 mW, e densidade de energia de 10 J/cm2. A irradiação foi aplicada diariamente por um período máximo de 21 dias. O mesmo procedimento foi realizado no grupo G2, com a probe desativada. Cinco animais em cada grupo foram sacrificados nos dias 7, 14 e 21 e submetidas à análise histomorfométrica. RESULTADOS: em ambos os grupos, o disco fisário esteve radiograficamente visível em todos os momentos nas incidências craniocaudal e médio-lateral. No 21º dia a porcentagem de comprimento longitudinal do fêmur foi maior em G1 que em G2 em relação ao valor basal, e o número de condrócitos da zona hipertrófica foi maior em G1 que em G2. A zona de cartilagem calcificada estava maior em G1 em relação a G2 em todos os momentos de avaliação. A angiogênese foi maior em G1 que em G2 nos 14º e 21º dias. CONCLUSÃO: A terapia com laser terapêutico de baixa potência influenciou negativamente o disco fisário distal do fêmur de ratos.

Effect of GaAlAs Laser Irradiation on the Epiphyseal Cartilage of Rats

Objective: To study the effect of an 830-nm gallium-aluminum-arsenic (GaAlAs) diode laser at two different energy densities (5 and 15 J/cm(2)) on the epiphyseal cartilage of rats by evaluating bone length and the number of chondrocytes and thickness of each zone of the epiphyseal cartilage. Background Data: Few studies have been conducted on the effects of low-level laser therapy on the epiphyseal cartilage at different irradiation doses. Materials and Methods: A total of 30 male Wistar rats with 23 days of age and weighing 90 g on average were randomly divided into 3 groups: control group (CG, no stimulation), G5 group (energy density, 5 J/cm(2)), and G15 group (energy density, 15 J/cm(2)). Laser treatment sessions were administered every other day for a total of 10 sessions. The animals were killed 24 h after the last treatment session. Histological slides of the epiphyseal cartilage were stained with hematoxylin-eosin (HE), photographed with a Zeiss photomicroscope, and subjected to histometric and histological analyses. Statistical analysis was performed using one-way analysis of variance followed by Tukey's post hoc test. All statistical tests were performed at a significance level of 0.05. Results: Histological analysis and x-ray radiographs revealed an increase in thickness of the epiphyseal cartilage and in the number of chondrocytes in the G5 and G15 groups. Conclusion: The 830-nm GaAlAs diode laser, within the parameters used in this study, induced changes in the thickness of the epiphyseal cartilage and increased the number of chondrocytes, but this was not sufficient to induce changes in bone length.

Microestrutura e resistência à corrosão do Ti c.p. soldado a laser utilizando em prótese sobre implantes

Foram realizados estudos para avaliar a microestrutura, a dureza e a resistência à corrosão do titânio comercialmente puro-Ti c.p. soldado por laser e utilizado na confecção de prótese sobre implantes. Verificou-se que na soldagem a laser a microestrutura apresentou três regiões distintas: o cordão de solda, a zona afetada pelo calor - ZAC e o metal base. O Ti c.p. possui microestrutura granular, a microestrutura do cordão de solda é mais refinada e de maior dureza do que o metal base. A ZAC obtida por este processo de soldagem foi relativamente pequena quando comparada com o processo de soldagem por brasagem. Os ensaios eletroquímicos mostraram que a região da solda apresentou menor resistência à corrosão em meio de NaCl 0,15 molL-1 à temperatura ambiente.

Investigação da Interface Metal-Porcelana da Liga Ni-Cr-Mo Soldada a LASER

The interface formed between the metal and the porcelain of a LASER welded Ni-Cr-Mo alloy was studied. The characterization was carried out through optical microscopy, scanning electron microscopy, X-ray dispersive spectroscopy-EDS and mechanical testing by three-point flexion test-TPE in the region LASER welded with and without the porcelain. The porcelain adhesion with the alloy alone is possible after the oxidation of the metallic surface and subsequent application of an adhesive called opaco. The applied porcelain, on the base metal and fusion zone presented some distinct behaviors. After the TPF test the base metal presented fractures while that in the fusion zone was completely gone. One noticed that the region submitted to the LASER welding showed less porcelain adhesion than the region of the base metal due to the microestructural refinement of the fusion zone. These results can be evidenced by the EDS of the studied regions. The TPF had demonstrated that the Ni-Cr-Mo alloy submitted to the LASER welding, undergone significant alterations in its mechanical properties after the application of the porcelain.

Caracterização mecânica e microestrutural de juntas de alumínio 6013 T4 soldados a laser

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo do comportamento mecânico e microestrutural de um aço maraging após soldagem a laser e tratamentos térmicos

Pós-graduação em Engenharia Mecânica - FEG

Aplicação do processo laser CO2 de soldagem em aço ARBL na fabricação de rotores para máquinas elétricas

Pós-graduação em Engenharia Mecânica - FEG

Application of pulsed Nd:YAG laser in thin foil microwelding

Experimental investigations were carried out using a Nd:YAG laser operating in pulsed mode for welding a lap joint between thin foil and thick sheet. The pulse energy was varied from 1.5 to 3.0 J at increments of 0.25 J with a 4 ms pulse duration. The base material used for this study was AISI 316L foils with 100 mu m thickness and sheet with 3.0 mm thickness. The welds were analysed by optical and electronic microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to join thin foil and thick sheet with good quality. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. The process appeared to be very sensitive to the gap between couples. Large voids delimited by the molten zone boundary were observed in joints welded with high pulse energy.

Effects of laser beam energy on the pulsed Nd:YAG laser welding of thin sheet corrosion resistant materials

The aim of this study was to value the possibility to join, for pulsed Nd:YAG laser welding, thin foils lap joints for sealing components in corrosive environment. Experimental investigations were carried out using a pulsed neodymium: yttrium aluminum garnet laser weld to examine the influence of the pulse energy in the characteristics of the weld fillet. The pulse energy was varied from 1.0 to 2.5 J at increments of 0.25 J with a 4 ms pulse duration. The base materials used for this study were AISI 316L stainless steel and Ni-based alloys foils with 100 mu m thickness. The welds were analyzed by electronic and optical microscopy, tensile shear tests and micro hardness. The results indicate that pulse energy control is of considerable importance to thin foil weld quality because it can generate good mechanical properties and reduce discontinuities in weld joints. The ultimate tensile strength of the welded joints increased at first and then decreased as the pulse energy increased. In all the specimens, fracture occurred in the top foil heat-affected zone next to the fusion line. The microhardness was almost uniform across the parent metal, HAZ and weld metal. A slight increase in the fusion zone and heat-affected zone compared to those measured in the base metal was observed. This is related to the microstructural refinement in the fusion zone, induced by rapid cooling of the laser welding. The process appeared to be very sensitive to the gap between couples.

Heat Treatment and Yb-Fiber Laser Welding of a Maraging Steel

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Pré tratamento dentinário influência do condicionamento ácido, irradiação laser e hipermineralização na resistência ao cisalhamento de sistema adesivo multi uso

The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose of the present study, therefore, was to investigate the effects of three dentin treatments: laser irradiation, acid etching and hypermineralization, in the shear bond strength of the SMP Plus bonding system. Sixty bovine incisors were extracted and randomly selected immediatly alter the animal's death. They were kept frozen (-18°C) for no longer than 14 days. After buccal dentinal surface had been exposed, X-Rays were taken to control the dentin thickness. The specimens were separated into two groups: (1) Control, kept in distilled water at 4ºC; (2) Mineralized, kept in hypermineralized solution at 4°C for 14 days. Each group was divided into three sub-groups according to the type of dentin treatment used: group F - followed the manufacturer instructions (acid-etching + primer + bond), group AL (acid-etching + primer + bond + laser) and group LA (laser + (laser + acid-etching + primer + bond). A composite resin standard cylinder (Z100-3M) was bond to the dentinal surface and the shear bond strength performed on a Universal lnstron machine 4301, with 500 Kg load and at 0,5mm/min. speed. The analysis of variance (ANOVA) determined that the treatments influenced the shear bond strength values (p<0,05) with the following average shearing load at failure: AL (9,96 MPa), F (7,28MPa) e LA (4,87 MPa). The interaction between the two factors analyzed Group (control and mineralized) and treatment (F, AL, LA) also influenced the shear bond strength (p<0,05). The highest values were obtained...

Caracterização mecânica e microestrutural de juntas soldadas a laser em aços maraging com posterior tratamento térmico e termoquímico de superfície a plasma

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)