Preparation of Ni-Ti-Mo and Ni-Ti-Mo-Zr Alloys by High-Energy Ball Milling and Subsequent Hot Pressing

This work discusses on the preparation of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr (at-%) alloys by high-energy ball milling and hot pressing, which are potentially attractive for dental and medical applications. The milling process was performed in stainless steel balls (19mm diameter) and vials (225 mL) using a rotary speed of 300rpm and a ball-to-powder weight ratio of 10:1. Hot pressing under vacuum was performed in a BN-coated graphite crucible at 900 degrees C for 1 h using a load of 20 MPa. The milled and hot-pressed materials were characterized by X-ray diffraction, electron scanning microscopy, and electron dispersive spectrometry. Peaks of B2-NiTi and Ni4Ti3 were identified in XRD patterns of Ni-45Ti-5Mo, Ni-40Ti-10Mo and Ni-46Ti-2Mo-2Zr powders milled for 1h. The NiTi compound dissolved small Mo amounts lower than 4 at%, which were measured by EDS analysis. Moreover, it was identified the existence of an unknown Mo-rich phase in microstructures of the hot-pressed Ni-Ti-Mo alloys.

Preparation of Al2TiO5-Al2O3 and Al2TiO5-Al2O3-TiO2 Ceramics by High-Energy Ball Milling and Sintering

The present work reports on the preparation of Al2O3-TiO2 ceramics by high-energy ball milling and sintering, varying the molar fraction in 1:1 and 3:1. The powder mixtures were processed in a planetary Fritsch P-5 ball mill using silicon nitride balls (10 mm diameter) and vials (225 mL), rotary speed of 250 rpm and a ball-to-powder weight ratio of 5:1. Samples were collected into the vial after different milling times. The milled powders were uniaxially compacted and sintered at 1300 and 1500 degrees C for 4h. The milled and sintered materials were characterized by X-ray diffraction and electron scanning microscopy (SEM). Results indicated that the intensity of Al2O3 and TiO2 peaks were reduced for longer milling times, suggesting that nanosized particles can be achieved. The densification of Al2O3-TiO2 ceramics was higher than 98% over the relative density in samples sintered at 1500 degrees C for 4h, which presented the formation of Al2TiO5.

Effect of acid-ethanol treatment followed by ball milling on structural and physicochemical characteristics of cassava starch

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

On Ti-18Si-6B and Ti-7.5Si-22.5B powder alloys prepared by high-energy ball milling and sintering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Use of high energy ball milling on the sintering optimization of alumina ceramics

In this work, the effect of the milling time on the densification of the alumina ceramics with or without 5wt.%Y 2O 3, is evaluated, using high-energy ball milling. The milling was performed with different times of 0, 2, 5 or 10 hours. All powders, milled at different times, were characterized by X-Ray Diffraction presenting a reduction of the crystalline degree and crystallite size as function of the milling time increasing. The powders were compacted by cold uniaxial pressing and sintered at 1550°C-60min. Green density of the compacts presented an increasing as function of the milling time and sintered samples presented evolution on the densification as function of the reduction of the crystallite size of the milled powders. © (2010) Trans Tech Publications.

Effect of ball milling on structural and physicochemical characteristics of cassava and Peruvian carrot starches

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of ball milling on the physicochemical characteristics of Peruvian carrot and cassava starches

Peruvian carrot and cassava starches were ground in a ball mill for 4, 8, 16, and 32 h and their structural and physicochemical characteristics were determined. Results obtained from HPAEC-PAD, GPC, and amylose content indicated a breaking of hydrogen bounds and α-(1 [RIGHTWARDS ARROW] 6) linkages of the starch molecules after treatment. X-ray diffractograms showed that the milling provided a reduction in the crystalline area of the starch granules. Most of the starch granules displayed agglomeration after 4 h of milling, when observed under a scanning electron microscope, and after 16 h a shapeless mass was observed for Peruvian carrot starch. Solubility and water absorption capacity of the starches increased with an increase in the milling time, while RVA profiles showed a progressive reduction of peak, breakdown, and final viscosities, as well as the development of initial viscosity. Gelatinization temperatures and enthalpies were reduced. Prolonged ball milling accelerated the enthalpy relaxation in both starches. These results confirmed a partial gelatinization of the starches, which was 82.6% for Peruvian carrot and 65.4% for cassava starches after 32 h of milling. The Peruvian carrot starch was more affected by the ball milling because of both its lower amylose content and the defects in its crystalline structure

Influence of ball-milled low purity boron powder on the superconductivity of MgB2

MgB2 samples were prepared using as-supplied commercial 96% boron with strong crystalline phase and the same 96% boron (B) after ball milling. The effects of the properties of the starting B powder on the superconductivity were evaluated. We observed that samples using ball-milled 96% B, in comparison with the one made from the as-supplied 96% B, were character- ized by small grain size, broadened full width at half maximum (FWHM), and enhanced magnetic critical current density (J(c)). J(c) reached 2 x 10(3) Acm(-2) at 5 K and 8 T. The improved pinning of these samples seems to be caused by enhanced grain boundary pinning at high field.

Influence of milling time on mechanically assisted synthesis of Pb0.91Ca0.1TiO3 powders

Pb0.91Ca0.1TiO3 powders (PCT) were prepared by mechanochemical synthesis from high-energy ball milling process. The influence of milling time on the phase formation, crystal structure, specific surface area, density and powder morphology was observed. We adopted the Rietveld refinement technique to investigate the crystal structure of the PCT powders. Scanning electron microscopy (SEM) analysis revealed that PCT powders milled for 5 h showed a wide distribution of particle agglomerates while milled for 35 h showed a decrease in agglomerates size. Further prolongation of milling time resulted in the agglomerates growth. (C) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Bulk and high-energy ball-milled Gd5Si2Ge2: Comparative study of magnetic and magnetocaloric properties

High-energy ball milling was employed to produce small particles of Gd5Si2Ge2. Magnetic and magnetocaloric properties of the ball-milled and bulk Gd5Si2Ge2 samples were investigated through the magnetization measurements. When compared to the bulk material, a significant decrease in saturation magnetization and magnetocaloric effect (-Delta S-max = 4 vs. 20 J/kgK for Delta H = 0-5 T) is observed even after the relatively short ball milling time of 4 h which produced particles with an average size of ca. 0.5 mu m. The ball-milled samples appear to loose a first-order structural transition, present in bulk Gd5Si2Ge2, and display a superparamagnetic behaviour below the corresponding Curie temperatures. (C) 2010 Elsevier Masson SAS. All rights reserved.

Efficiency evaluation of ZrB2 incorporation in the MgB 2 matrix phase using high-energy milling

The present study suggests the use of high energy ball milling to mix (to dope) the phase MgB2 with the AlB2 crystalline structure compound, ZrB2, with the same C32 hexagonal structure than MgB 2, in different concentrations, enabling the maintenance of the crystalline phase structures practically unaffected and the efficient mixture with the dopant. The high energy ball milling was performed with different ball-to-powder ratios. The analysis of the transformation and formation of phases was accomplished by X-ray diffractometry (XRD), using the Rietveld method, and scanning electron microscopy. As the high energy ball milling reduced the crystallinity of the milled compounds, also reducing the size of the particles, the XRD analysis were influenced, and they could be used as comparative and control method of the milling. Aiming the recovery of crystallinity, homogenization and final phase formation, heat treatments were performed, enabling that crystalline phases, changed during milling, could be obtained again in the final product. © (2010) Trans Tech Publications.

High-yield direct synthesis of Mg 2FeH 6 from the elements by reactive milling

Magnesium complex hydrides as Mg 2FeH 6 are interesting phases for hydrogen storage in the solid state, mainly due to its high gravimetric and volumetric densities of H2. However, the synthesis of this hydride is not trivial because the intermetallic phase Mg2Fe does not exist and Mg and Fe are virtually immiscible under equilibrium conditions. In this study, we have systematically studied the influence of the most important processing parameters in reactive milling under hydrogen (RM) for Mg 2FeH 6 synthesis: milling time, ball-to-powder weight ratio (BPR), hydrogen pressure and type of mill. Low cost 2Mg-Fe mixtures were used as raw materials. An important control of the Mg 2FeH 6 direct synthesis by RM was attained. In optimized combinations of the processing parameters, very high proportions of the complex hydride could be obtained. © (2011) Trans Tech Publications.

Structural characterization and Curie temperature determination of a sodium strontium niobate ferroelectric nanostructured powder

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Análise cristalográfica da solução sólida com estrutura tipo Tungstênio Bronze de niobato de potássio e estrôncio dopado com ferro

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

On the Phase Transformation in Mechanically Alloyed Ni-Nb and Ni-Ta and Ni-Nb-Ta Powders

This paper reports on the phase transformation during the preparation of Ni-25Nb, Ni-25Ta, Ni-20Nb-5Ta and Ni-15Nb-10Ta (at-%) powders by high-energy ball milling from elemental powders. The milling process was performed in a planetary ball milling using stainless steel balls and vials, rotary speed of 300rpm, and a ball-to-powder of 10:1. To minimize contamination and spontaneous ignition the powders were handled under argon atmosphere in a glove box. The milled powders were characterized by means of X-ray diffraction techniques. Results indicated that the Ni atoms were preferentially dissolved into the Nb (and/or Ta) lattice at the initial milling times, which contributed to change the relative intensity on the diffraction peaks. After the dissolution of Nb (and/or Ta) into the Ni lattice, the Ni peaks were moved to the direction of lower diffraction angles in Ni-25Nb, Ni-25Ta, Ni-20Nb-5Ta, Ni-15Nb-10Ta powders, indicating that the mechanical alloying was achieved.