Production of a low young modulus titanium alloy by powder metallurgy

Titanium alloys have several advantages over ferrous and non-ferrous metallic materials, such as high strengthto-weight ratio and excellent corrosion resistance. A blended elemental titanium powder metallurgy process has been developed to offer low cost commercial products. The process employs hydride-dehydride (HDH) powders as raw material. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy due to its lower modulus of elasticity and high biocompatibility is a promising candidate for aerospace and medical use. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 900 up to 1600 °C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like alpha structure and intergranular beta. A few remaining pores are still found and density above 90% for specimens sintered in temperatures over 1500 °C is reached.

All-Ceramic Crowns Over Single Implant Zircon Abutment. Influence of Young's Modulus on Mechanics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Bacterial cellulose-laponite clay nanocomposites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and characterization of nanocrystalline h-BN films prepared by PECVD method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and mechanical properties of PVDF/PANI blends

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Relaxation and tunnelling of structural units within the LTO phase of La2CuO4

The anelastic relaxation (elastic energy loss and Young modulus) of nearly stoichiometric La2CuO4+delta with LTO structure was measured. Extraordinarily intense effects are present below room temperature in the elastic dynamic susceptibility, indicating relaxational dynamics of a relevant fraction of the lattice. The involved degrees of freedom are identified as rotations of the CuO6 octahedra. Two distinct processes are found at frequencies around 1 kKz: one is observed around 150 K and is characterized by a mean activation energy of 2800 K; the second one occurs below 30 K and is governed by atomic tunnelling. Two explanations are proposed for the faster process: i) formation of fluctuating LTT domains on a scale of few atomic cells; ii) the LTO phase is a dynamical Jahn-Teller phase with all the octahedra tunneling between two LTT-like tilts. In both cases there would be important implications regarding the mechanisms giving rise to charge nanophase separation and strong electron-phonon coupling.

Retention strength of cobalt-chromium vs nickel-chromium titanium vs Cp titanium in a cast framework association of removable partial overdenture

Aim: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). Methods: Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. Results: The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium-titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. Conclusion: This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm. Clinical significance: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.

Influence of the implant diameter with different sizes of hexagon: Analysis by 3-dimensional finite element method

The aim of this study was to evaluate the stress distribution in implants of regular platforms and of wide diameter with different sizes of hexagon by the 3-dimensional finite element method. We used simulated 3-dimensional models with the aid of Solidworks 2006 and Rhinoceros 4.0 software for the design of the implant and abutment and the InVesalius software for the design of the bone. Each model represented a block of bone from the mandibular molar region with an implant 10 mm in length and different diameters. Model A was an implant 3.75 mm/regular hexagon, model B was an implant 5.00 mm/regular hexagon, and model C was an implant 5.00 mm/ expanded hexagon. A load of 200 N was applied in the axial, lateral, and oblique directions. At implant, applying the load (axial, lateral, and oblique), the 3 models presented stress concentration at the threads in the cervical and middle regions, and the stress was higher for model A. At the abutment, models A and B showed a similar stress distribution, concentrated at the cervical and middle third; model C showed the highest stresses. On the cortical bone, the stress was concentrated at the cervical region for the 3 models and was higher for model A. In the trabecular bone, the stresses were less intense and concentrated around the implant body, and were more intense for model A. Among the models of wide diameter (models B and C), model B (implant 5.00 mm/regular hexagon) was more favorable with regard to distribution of stresses. Model A (implant 3.75 mm/regular hexagon) showed the largest areas and the most intense stress, and model B (implant 5.00 mm/regular hexagon) showed a more favorable stress distribution. The highest stresses were observed in the application of lateral load.

Simple green approach to reinforce natural rubber with bacterial cellulose nanofibers

Natural rubber (NR) is a renewable polymer with a wide range of applications, which is constantly tailored, further increasing its utilizations. The tensile strength is one of its most important properties susceptible of being enhanced by the simple incorporation of nanofibers. The preparation and characterization of natural-rubber based nanocomposites reinforced with bacterial cellulose (BC) and bacterial cellulose coated with polystyrene (BCPS), yielded high performance materials. The nanocomposites were prepared by a simple and green process, and characterized by tensile tests, dynamical mechanical analysis (DMA), scanning electron microscopy (SEM), and swelling experiments. The effect of the nanofiber content on morphology, static, and dynamic mechanical properties was also investigated. The results showed an increase in the mechanical properties, such as Young's modulus and tensile strength, even with modest nanofiber loadings. © 2013 American Chemical Society.

Prospects for the use of municipal tree pruning wastes in particleboard production

The purpose of this study was to evaluate the physical and mechanical properties of particleboard made with pruning wastes from Ipê (Tabebuia serratifolia) and Chapéu-de-Sol (Terminalia catappa) trees. Particleboards were prepared with both wood species, using all the material produced by grinding the pruning wastes. The particleboards had dimensions of 45×45 cm, a thickness of approximately 11.5 mm and an average density of 664 kg/m3. A urea-formaldehyde adhesive was used in the proportion of 12% of the dry particle mass. The particleboards were pressed at a temperature of 130 C for 10 mins. The physical and mechanical properties analyzed were density, moisture content, thickness swelling, percentage of lignin and cellulose, modulus of resilience, modulus of elasticity and tensile strength parallel to the grain, accordingly to the standards NBR 14810 and CS 236-66 (1968). The particleboards were considered to be of medium density. The particle size significantly affected the static bending strength and tensile strength parallel to the grain. Ipê presented better results, demonstrating a potential for the production and use of particleboard made from this species. © The Author(s) 2013.

Processamento e caracterização mecânica da liga à base de titânio (Ti-7,5Mo) para confecção de prótese ortopédica

Pós-graduação em Engenharia Mecânica - FEG

Análise da influência dos sistemas de retenção para overdentures implanto-retidas e da espessura e resiliência da fibromucosa na distribuição interna das tensões, através do método de elementos finitos bidimensional

Pós-graduação em Odontologia - FOA

Efeito da colocação de um ponto simples em tendão flexor de coelho em região vascularizada e avascularizada: análise da propriedades mecânicas e histopatológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da qualidade óssea no reparo de defeitos ósseos sob a ação do risedronato e da deficiência estrogênica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Study of elastic properies of Ti3Al intermetallic compound using the ab initio calculation

The elastic properties of a Ti3Al intermetallic compound were studied using full potential (FP LAPW ) with the APW+lo method. The FP-LAPW is among the most accurate band structure calculations currently available and is based on the density functional theory with general gradient approximation for the exchange and correlation potential. This method provides the structural properties of the ground state as bulk modulus, equilibrium lattice parameter, and equilibrium minimum energy, and the elastic properties as shear modulus, young modulus, Zener coefficient (anisotropy), and Poisson coefficient. The calculated elastic properties are coherent with the elastic properties of the material.