Preparation of films from aluminum acetylacetonate by plasma sputtering

Aluminum acetylacetonate has been reported as a precursor for the deposition of alumina films using different approaches. In this work, alumina-containing films were prepared by plasma sputtering this compound, spread directly on the powered lowermost electrode of a reactor, while grounding the substrates mounted on the topmost electrode. Radiofrequency power (13.56 MHz) was used to excite the plasma from argon atmosphere at a working pressure of 11 Pa. The effect of the plasma excitation power on the properties of the resulting films was studied. Film thickness and hardness were measured by profilometry and nanoindentation, respectively. The molecular structure and chemical composition of the layers were analyzed by Fourier transform infrared spectroscopy and energy dispersive spectroscopy. Surface micrographs, obtained by scanning electron microscopy, allowed the determination of the sample morphology. Grazing incidence X-ray diffraction was employed to determine the structure of the films. Amorphous organic layers were deposited with thicknesses of up to 7 μm and hardness of around 1.0 GPa. The films were composed by aluminum, carbon, oxygen and hydrogen, their proportions being strongly dependent on the power used to excite the plasma. A uniform surface was obtained for low-power depositions, but particulates and cracks appeared in the high-power prepared materials. The presence of different proportions of aluminum oxide in the coatings is ascribed to the different activations promoted in the metalorganic molecule once in the plasma phase. Copyright © 2013 John Wiley & Sons, Ltd. Copyright © 2013 John Wiley & Sons, Ltd.

Properties of films obtained from biopolymers of different origins for skin lesions therapy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Biodegradation of films of low density polyethylene (LDPE), poly(hydroxibutyrate-co-valerate) (PHBV), and LDPE/PHBV (70/30) blend with Paecilomyces variotii

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Agora é Lula: enquadramentos do governo do PT pelo Jornal Nacional

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Televisão analógica e televisão digital: o futuro do telejornalismo

This study proposes to present the process of implementation of Digital TV, the available resources found in the Japanese standard employed in the country and the form in which news programs will adapt to the new technology. Following the presentation of the technological tools, the current state of Brazilian television is discussed, focusing on two nationally broadcast programs, Jornal da Band on Bandeirantes channel and Jornal da Record on Record channel. As a case study, three editions of each show are evaluated with an individual and comparative analysis. Following the analyses, perspectives on the future of television journalism in the digital TV age are given. Additionally, the possibilities for interaction between the TV viewer and the channel and the forms of interaction that may exist within particular programs are discussed, thus allowing for active participation from the part of the viewer. The newly developed functions of journalists in the digital age are also broken down in the research. In order to gain a full understanding of the phases of this process of technological convergence and how programs will adapt to these tools, interviews with professionals who work in the production of televised news programs are conducted in the study

Influence of pH of Colloidal Suspension on the Electrical Conductivity of SnO2 thin Films Deposited Via Sol-Gel-Dip-Coating

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effect of pH of colloidal suspension on crystallization and activation energy of deep levels in SnO2 thin films obtained via sol-gel

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Improvement of fatigue resistance on La modified BiFeO(3) thin films

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

The influence of soil and landfill leachate microorganisms in the degradation of PVC/PCL films cast from DMF

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The use of Langmuir-Blodgett films of a perylene derivative and polypyrrole in the detection of trace levels of Cu2+ ions

Langmuir films of a tetracarboxylic perylene derivative and polypyrrole display condensed surface pressure isotherms that are shifted when Cu2+ ions are added to the ultrapure water subphase. These films were transferred onto interdigitated gold electrodes leading to Y-type Langmuir-Blodgett (LB) films. The electrodes modified with 5-layer LB films were immersed into a flask with ultrapure water and water containing Cu2+ ions at concentrations ranging from mM to muM. Impedance measurements indicated a distinct electrical response for the two types of films. Although the materials chosen have no specificity for ionic metals, they can be combined for detecting trace levels of Cu2+, which may be exploited in water quality monitoring. (C) 2004 Elsevier B.V. All rights reserved.

Epitaxial growth of LiNbO3 thin films in a microwave oven

Oriented LiNbO3 thin films were prepared using a polymeric precursor solution deposited on (0001) sapphire substrate by spin coating and crystallized in a microwave oven. Crystallization of the films was carried out in a domestic microwave oven. The influence of this type of heat treatment on the film orientation was analyzed by X-ray diffraction and electron channeling patterns, which revealed epitaxial growth of films crystallized at 550 and 650 degreesC for 10 min. A microstructural study indicated that the films treated at temperatures below 600 degreesC were homogeneous and dense, and the optical properties confirmed the good quality of these films. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Grazing incidence X-ray diffraction and atomic force microscopy analysis of BaBi2Ta2O9 thin films

Thin films of BaBi2Ta2O9 (BBT) composition were prepared through the metal organic decomposition method. The crystallinity, phase formation, crystallite size and morphology of the thin films were measured as a function of the type of substrate, stoichiometry of solution and process variables such as thickness and temperature. The thin films were investigated by grazing incidence X-ray diffractometry and atomic force microscopy (AFM) techniques. For the sample without excess of bismuth, diffraction peaks other than that of the BBT phase were observed. A well crystallized BBT single phase was observed for films prepared from a solution with 10% excess of bismuth, deposited on Si/Pt substrate, with a thickness up to 150 nm and sintered at temperatures of 700 degreesC. The thin BBT phase films heat-treated at 600 degreesC presented a diffraction pattern characteristic of samples with lower degree of crystallinity whereas for the thin films heat-treated at 800 degreesC, we observed the presence of other phases than the BBT. For the thin film deposited on the Sin+ substrate, we observe that the peaks corresponding to the BBT phase are broader than that observed on the samples deposited on the Pt and Si/Pt substrates. No variation of average crystallite size was observed as the excess of Bi increased from 10 to 20%. AFM images for the samples showed that the increasing the amount of bismuth promotes grain growth. The average surface roughness measured was in the range of 16-22 nm showing that the bismuth amount had no or little effect on the roughness of films. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Structural electrical and optical properties of undoped and indium doped ZnO thin films prepared by the pyrosol process at different temperatures

The influence of the substrate temperature on the structural features and opto-electrical properties of undoped and indium-doped ZnO thin films deposited by pyrosol process was investigated. The addition of indium induces a drastic decrease (by a factor approximate to 10(10) for samples deposited at 300 degreesC) in the electrical resistivity of films, the lowest electrical resistivity (6 mOmega-cm) being observed for the film deposited at 450 degreesC. Films are highly transparent (>80%) in the Vis-NIR ranges, and the optical band gap exhibits a blue shift (from 3.29 to 3.33 eV) for the In-doped films deposited at increasing temperature. Preferential orientation of the ZnO crystallites with the c-axis perpendicular to the substrate surface and an anisotropic morphology of the nanoporous structure was observed for films growth at 300 and 350 degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Nanostructure and properties of ZnO films produced by the pyrosol process

Indium doped ZnO films were deposited by the pyrosol process on glass substrates at different temperatures from solutions containing In/Zn molar ratios up to 10%. The nanostructure of the films was investigated using grazing-incidence small angle X-ray scattering (GISAXS). The mass density was determined by X-ray reflectivity and the composition by X-ray photoelectron spectroscopy. The GISAXS measurements revealed an anisotropic pattern for films deposited at 573 and 623 K and a isotropic one for those deposited at higher temperatures. The anisotropic patterns indicate the presence of elongated nanopores with their long axes perpendicular to the film surface. In contrast, the isotropic nature of GISAXS patterns of films grown at high temperatures (673 and 723 K) suggests the presence of spherical voids. The pore size distribution function determined from the isotropic patterns indicates a multimodal size distribution. on the other hand, the measured mass density of the doped films with isotropic nanotexture is higher than that of the anisotropic films while the electric resistivity is significantly lower. This is in agreement with the detected strong reduction of the void density and specific surface area at approximately constant pore size.

Effect of thermal treatment temperature on the crystallinity and morphology of LiTaO3 thin films prepared from polymeric precursor method

Lithium tantalate thin films (LiTaO3) with (50:50) stoichiometry were prepared by spin coating method using a polymeric organic solution. The films were deposited on silicon (100) substrates with 4 layers. The substrates were previously cleaned and then the solution of lithium tantalate was deposited by adjusting the speed at 5000 rpm. The thin films deposited were thermally treated from 350 to 600degreesC for 3 hours in order to study the influence of the thermal treatment temperature on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction (XRD) results showed that the films are polycrystalline and secondary phases free. The thickness of films was observed by scanning electron microscopy (SEM). The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by thermal treatment.