Thermal decomposition and rehydration of strontium oxalate: morphological evolution

Undoped and Eu3+ doped monohydrate strontium oxalate samples were precipitated under ultrasound and conventional stirring and were heated at different temperatures. All samples were characterized by X-ray powder diffraction (XDR), infrared spectra (IR) and scanning electron microscopy (SEM). Monohydrate, dehydrate oxalates and carbonate particles are ellipsoids indicating a topotatic process. Particle size decrease is observed when ultrasound stirring and europium. doping are used and rehydration of strontium oxalate results in uniform hexagonal particle shape. An oxide and carbonate mixture is obtained from oxalates treated at 1050 degreesC and its suspension in water undergoes incomplete hydrolysis. The products from this incomplete hydrolysis present dendrite shape particles only when the former is precipitated under ultrasound stirring. In this process, surface energy is important for particle dispersion and ultrasound supplies activation energy to oxalate precursor. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Polymeric precursor method to the synthesis of XWO(4) (X = Ca and Sr) thin films-Structural, microstructural and spectroscopic investigations

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microstructural and optical characterization of CaWO4 and SrWO4 thin films prepared by a chemical solution method

Stoichiometric CaWO4 and SrWO4 thin films were synthesized using a chemical solution processing, the so-called polymeric precursor method. In this soft chemical method, soluble precursors such as strontium carbonate, calcium carbonate and tungstic acid, as starting materials, were mixed in an aqueous solution. The thin films were deposited on glass substrates by means of the spinning technique. The surface morphology and crystal structure of the thin films were investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). Nucleation stages and surface morphology evolution of the thin films on glass substrates were studied by atomic force microscopy. The films nucleate at 300 degreesC, after the coalescence of small nuclei into larger grains yielding a homogeneous dense surface. XRD characterization of these films showed that the CaWO4 and SrWO4 phases crystallize at 400 degreesC from an inorganic amorphous phase. No intermediate crystalline phase was identified. The optical properties were also studied. It was found that CaWO4 and SrWO4 thin films have an optical band gap, E-gap=5.27 and 5.78 eV, respectively, of a direct transition nature. The excellent microstructural quality and chemical homogeneity confirmed that this soft solution processing provides an inexpensive and environmentally friendly route for the preparation of CaWO4 and SrWO4 thin films. (C) 2003 Elsevier B.V. All rights reserved.

Crystallographic, dielectric and optical properties of SrBi2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (PvTi/SiO2/Si), n-type (100)-oriented and p-type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P-r values of 6.24 muC/cm(2) and 31.5 kV/cm for the film annealed at 800 degreesC. The film deposited onto fused silica and treated at 700 degreesC presented around 80 % of transmittance.

Influence of Cu(II) in the SrSnO3 crystallization

Perovskite type oxides have been intensively studied due to their interesting optical, electrical, and catalytic properties. Among perovskites the alkaline earth stannates stand out, being strontium stannates (SrSnO3) the most important material in ceramic technology among them due to their wide application as dielectric component. SrSnO3 has also been applied as stable capacitor and humidity sensor. In the present work, SrSnO3:Cu was synthesized by polymeric precursor method and heat treated at 700, 800, and 900 A degrees C for 4 h. After that, the material was characterized by thermal analysis (TG/DTA), X-ray diffraction (XRD), infrared spectroscopy, and UV-vis spectroscopy. Results indicated three thermal decomposition steps and confirmed the presence of strontium carbonate and Cu2+ reduction to Cu+ at higher dopant amounts. XRD patterns indicated that the perovskite crystallization started at 700 A degrees C with strontiatite (SrCO3) and cassiterite (SnO2) as intermediate phases, disappearing at higher temperatures. The amount of secondary phase was reduced with the increase in the Cu concentration.

Microstructure and phase evolution of SrTiO3 thin films on Si prepared by the use of polymeric precursors

The use of polymeric precursors was employed in preparing SrTiO3 thin films by dip coating using Si (111) as substrate. Crack free films were obtained after sintering at temperatures ranging from 550 to 1000°C. The microstructure, characterized by SEM, shows the development of dense polycrystalline films with smooth surface and mean grain size of 52 nm, for films sintered at 1000°C. Grazing incident angle XRD characterization of these films shows that the SrTiO3 phase crystallizes from an inorganic amorphous matrix. No intermediate crystalline phase was identified.

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

Propriedades ferroelétricas, microestruturais e ópticas dos materiais cerâmicos Ba0,5 Sr0,5 (Ti1-ySny) O3

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparação de filmes finos ferroelétricos de SrBi2'('TA IND.1-x''NB IND.x)ÍND.2 'O IND.9' puro e dopado com tungstênio, obtidos pelo método dos precursores poliméricos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento de materiais catalisadores heterogêneos a base de estrôncio (Sr) e zircônio (Zr) para transesterificação de óleos e gorduras - síntese, caracterização e performance reacional

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Utilização sistêmica de estrôncio não radioativo como potencializador da osseointegração de implantes: avaliação biomeânica, microtomográfica e histomorfométrica em ratos

Pós-graduação em Odontologia - FOAR

Compressive strength and setting time of MTA and portland cement associated with different radiopacifying agents

The aim of this study was to evaluate the compressive strength and setting time of MTA and Portland cement (PC) associated with bismuth oxide (BO), zirconium oxide (ZO), calcium tungstate (CT), and strontium carbonate (SC). Methods. For the compressive strength test, specimens were evaluated in an EMIC DL 2000 apparatus at 0.5 mm/min speed. For evaluation of setting time, each material was analyzed using Gilmore-type needles. The statistical analysis was performed with ANOVA and the Tukey tests, at 5% significance. Results. After 24 hours, the highest values were found for PC and PC + ZO. At 21 days, PC + BO showed the lowest compressive strength among all the groups. The initial setting time was greater for PC. The final setting time was greater for PC and PC + CT, and MTA had the lowest among the evaluated materials (< 0.05). Conclusion. The results showed that all radiopacifying agents tested may potentially be used in association with PC to replace BO.

Strontium zirconate heterogeneous catalyst for biodiesel production: Synthesis, characterization and catalytic activity evaluation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Barium strontium titanate powder obtained by polymeric precursor method

Pure barium strontium titanate powder, with Ba/Sr ratio of 80/20 was prepared by the polymeric precursor method (also called Pechini process). The powder was obtained after a calcination at 800 degreesC for 8 h and characterized by XRD, IR, BET and SEM. The requirements to avoid barium carbonate as a secondary phase are presented and discussed in detail. (C) 2003 Elsevier B.V. All rights reserved.

Influence of synthesis conditions on carbonate entrapment in perovskite SrSnO(3)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)