Effect of phosphate-bonded investments on titanium reaction layer and crown fit

This study analyzed the reaction layer and measured the marginal crown fit of cast titanium applied to different phosphate-bonded investments, prepared under the following conditions (liquid concentration/casting temperature): Rema Exakt (RE) - 100%/237°C, 75%/287°C, Castorit Super C (CS)-100%/70°C, 75%/141°C and Rematitan Plus (RP)-100%/430°C (special to titanium cast, as the control group). The reaction layer was studied using the Vickers hardness test, and analyzed by two way ANOVA and Tukey's HSD tests (α = 0.05). Digital photographs were taken of the crowns seated on the die, the misfit was measured using an image analysis system and One-way ANOVA, and Tukey's test was applied (α = 0.05). The hardness decreased from the surface (601.17 VHN) to 150 μm (204.03 VHN). The group CS 75%/141°C presented higher hardness than the other groups, revealing higher surface contamination, but there were no differences among the groups at measurements deeper than 150 μm. The castings made with CS - 100%/70°C presented the lowest levels of marginal misfit, followed by RE -100%/237°C. The conventional investments CS (100%) and RE (100%) showed better marginal fit than RP, but the CS (75%) had higher surface contamination.

IMPROVEMENT TO THE MARGINAL COPING FIT of COMMERCIALLY PURE TITANIUM CAST IN PHOSPHATE-BONDED INVESTMENT BY USING A SIMPLE PATTERN COATING TECHNIQUE

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito de um revestimento com processamento rápido para fundição de titânio na camada de reação, porosidade interna, fluidez, rugosidade superficial e adaptação marginal de Copings

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

O efeito da técnica de inclusão para fundição de titânio CP na fluidez, rusogidade, camada de reação e desajuste marginal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A Quality Assessment of Titanium Castings Produced in an Experimental Short-Heating-Cycle Investment

The aim of this study was to evaluate the quality of casting produced in an experimental short-term heating-cycle investment. Thus, reaction layer and castability of titanium casting using an experimental spinel-based investment (VR) with short heating cycle were compared with the commercial short-heating-cycle spinel-based investment Trinell (TR), the silica-phosphate-based investment Rematitan Plus ( RP), and the conventional spinel-based investment Rematitan Ultra (RU). VR has polymeric fibers added to inorganic particles. Reaction layer assessments were carried out using Vickers hardness and elemental analysis using dispersive X-ray microanalysis (EDX). Mesh patterns were used for castability test, and powder characterization was made by scanning electron microscopy (SEM). Hardness evaluation showed no difference among the investments between 100 and 200 mu m. The most important contaminant element for VR, TR, and RU was oxygen. Higher levels of mold filling were found for TR, VR, and RU compared with that obtained with RP. The quality of castings, characterized by means of the assessments of reaction layer and castability, made from the VR was similar to the commercial investments TR and RU but superior to the RP.

The role of sugar cane straw on soil reaction

Conduziram-se dois experimentos em laboratório avaliar o efeito da palha da cana- de-açúcar na acidez do solo. A palha da cana foi adicionada nas doses de 0, 20, 40, e 76 g kg-1 na superfície de um latossolo roxo distrófico acondicionado em colunas de PVC. O solo foi incubado a capacidade de campo durante 0, 7, 14, 45, e 90 dias. Após cada incubação, o solo das colunas foram subdividido e amostrado nas seguintes frações 0-5, 5-10, 10-15, 15-20, e 20-25 cm. Com o aumento da dose da palha da cana verificou-se aumento do pH CaCl2 do solo e decréscimo do alumínio trocável até a camada de 15 cm de solo da coluna de PVC. A contribuição de compostos orgânicos para a destoxificação do Al aumentou com o acréscimo das doses da palha da cana. O crescimento da raiz das plantas trigo usadas como planta indicadora aumentou com o acréscimo das doses da palha de cana. O máximo de crescimento da raiz foi até a camada de 15 cm de solo depois de oito dias para a maior dose de palha da cana-de-açúcar.

Catechol biosensing using a nanostructured layer-by-layer film containing Cl-catechol 1,2-dioxygenase

dThe detection of aromatic compounds from pesticides and industrial wastewater has become of great interest, since these compounds withstand chemical oxidation and biological degradation, accumulating in the environment. In this work, a highly sensitive biosensor for detecting catechol was obtained with the immobilization of Cl-catechol 1,2-dioxygenase (CCD) in nanostructured films. CCD layers were alternated with poly(amidoamine) generation 4 (PAMAM G4) dendrimer using the electrostatic layer-by-layer (LbL) technique. Circular dichroism (CD) measurements indicated that the immobilized CCD preserved the same conformation as in solution. The thickness of the very first CCD layers in the LbL films was estimated at ca. 3.6 nm, as revealed by surface plasmon resonance (SPR). PAMAM/CCD 10-bilayer films were employed in detecting diluted catechol solutions using either an optical or electrical approach. Due to the mild immobilization conditions employed, especially regarding the pH and ionic strength of the dipping solutions, CCD remained active in the films for periods longer than 3 weeks. The optical detection comprised absorption experiments in which the formation of cis-cis muconic acid, resulting from the reaction between CCD and catechol, was monitored by measuring the absorbance at 260 nm after film immersion in catechol solutions. The electrical detection was carried out using LbL films deposited onto gold-interdigitated electrodes immersed in aqueous solutions at different catechol concentrations. Using impedance spectroscopy in a broad frequency range (1Hz-1kHz), we could detect catechol in solutions at concentrations as low as 10(-10) M. (c) 2005 Elsevier B.V. All rights reserved.

Exploiting Cascade Reactions in Bienzyme Layer-by-Layer Films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reaction of rat connective tissue to implanted dentin tubes filled with mineral trioxide aggregate or calcium hydroxide

This study was conducted to observe the rat subcutaneous connective tissue reaction to the implanted dentin tubes filled with calcium hydroxide or mineral trioxide aggregate. The animals were sacrificed after 7 and 30 days, and the specimens were prepared for morphological study. Some undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for calcium. The results were similar for both studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. It is possible that the mechanism of action of both materials has some similarity. Copyright © 1999 by The American Association of Endodontists.

Reaction of rat connective tissue to implanted dentin tube filled with mineral trioxide aggregate, Portland cement or calcium hydroxide.

The subject of this study was to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes filled with mineral trioxide aggregate, Portland cement or calcium hydroxide. The animals were sacrificed after 7 or 30 days and the undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for mineralized tissues. The results were similar for the studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. The mechanism of action of the studied materials has some similarity.

Reaction of rat connective tissue to implanted dentin tubes filled with a white mineral trioxide aggregate.

The purpose of this paper was to study the reaction of rat subcutaneous connective tissue to the implantation of dentin tubes filled with white mineral trioxide aggregate (MTA), a material that will be marketed. The tubes were implanted into rat subcutaneous tissue and the animals were sacrificed after 7 and 30 days. The undecalcified pieces were prepared for histological analysis with polarized light and von Kossa technique for mineralized tissues. Granulations birefringent to polarized light and an irregular structure like a bridge were observed next to the material; both were von Kossa positive. Also, in the dentin wall tubules a layer of birefringent granulations was observed. The results were similar to those reported for gray MTA, indicating that the mechanisms of action of the white and gray MTA are similar.

A comparison of mycolic acid analysis for nontuberculous mycobacteria identification by thin-layer chromatography and molecular methods

The development of fast, inexpensive, and reliable tests to identify nontuberculous mycobacteria (NTM) is needed. Studies have indicated that the conventional identification procedures, including biochemical assays, are imprecise. This study evaluated a proposed alternative identification method in which 83 NTM isolates, previously identified by conventional biochemical testing and in-house M. avium IS1245-PCR amplification, were submitted to the following tests: thin-layer chromatography (TLC) of mycolic acids and PCR-restriction enzyme analysis of hsp65 (PRA). High-performance liquid chromatography (HPLC) analysis of mycolic acids and Southern blot analysis for M. avium IS1245 were performed on the strains that evidenced discrepancies on either of the above tests. Sixty-eight out of 83 (82%) isolates were concordantly identified by the presence of IS1245 and PRA and by TLC mycolic acid analysis. Discrepant results were found between the phenotypic and molecular tests in 12/83 (14.4%) isolates. Most of these strains were isolated from non-sterile body sites and were most probably colonizing in the host tissue. While TLC patterns suggested the presence of polymycobacterial infection in 3/83 (3.6%) cultures, this was the case in only one HPLC-tested culture and in none of those tested by PRA. The results of this study indicated that, as a phenotypic identification procedure, TLC mycolic acid determination could be considered a relatively simple and cost-effective method for routine screening of NTM isolates in mycobacteriology laboratory practice with a potential for use in developing countries. Further positive evidence was that this method demonstrated general agreement on MAC and M. simiae identification, including in the mixed cultures that predominated in the isolates of the disseminated infections in the AIDS patients under study. In view of the fact that the same treatment regimen is recommended for infections caused by these two species, TLC mycolic acid analysis may be a useful identification tool wherever molecular methods are unaffordable.

Correlation between structural and catalytic properties of copper supported on porous alumina for the ethanol dehydrogenation reaction

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)