EFFECT of GAMMA IRRADIATION on CAPROLACTAM MIGRATION FROM MULTILAYER POLYAMIDE 6 FILMS INTO WATER FOOD SIMULANT and VALIDATION of THE METHOD

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Identification and migration of degradation compounds from irradiation of multilayer polyamide 6 films for meat foodstuffs and cheese

The aim of this work was to identify the degradation compounds produced during irradiation of multilayer polyamide 6 (PA-6) films and to study their migration into water and 95% ethanol food simulant. After irradiation of multilayer PA-6 films at 3, 7 and 12 kGy, degradation compounds were extracted using solid-phase microextraction, for which the time and temperature of extraction and stirring were optimized, and identified by gas chromatography-mass spectrometry. Caprolactam, 2-cyclopentylcyclopentanone and aldehydes, among other compounds, were identified in the headspace of the films. Polydimethylsiloxane was considered the best fiber for extraction. The optimum conditions of time, temperature and stirring to extract the compounds were 20 min, 80 degrees C and 225 rpm. For validation purposes, the compounds were quantified in water and 95% ethanol and the results showed high sensitivity, good precision and accuracy. Migration of compounds from irradiated and non-irradiated multilayer PA-6 films into water and 95% ethanol food simulants was carried out at 40 degrees C for 10 days. The method was efficient for the quantification of decaldehyde, 2-cyclopentylcyclopentanone and caprolactam that migrated from multilayer PA-6 films into food simulants.

Effect of Gamma Irradiation on Caprolactam Migration from Multi layer Polyamide 6 Films into Food Simulants: Development and Validation of a Gas Chromatographic Method

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Carbon nanotubes/polyamide 6.6 nanostructured composites crystallization kinetic study

Compared with the traditional composites, the incorporation of carbon nanotubes into polymeric matrices can generate materials with superior properties, especially thermal, electrical and tribological properties. The aim of this study was to study the polyamide 6.6/carbon nanotubes (PA 6.6/CNT) nanostructured composites crystallization kinetics. The solution mixing technique was used to obtain the nanostructured composites studied in this work. PA 6.6 films were produced with amounts of 0.1, 0.5, and 1.0 wt% (weight/weight) CNT. X-ray diffraction analyses were performed in order to determine the crystallographic properties of nanostructured composite. The nanostructured composites crystallization kinetic study was performed using the differential scanning calorimetry under isothermal and nonisothermal (dynamic) conditions. The results have shown addition of CNTs in the PA 6.6 reduces the Avrami exponent, affecting the crystallization process of the composite. © The Author(s) 2012.

Nonoxidative thermal degradation kinetic of polyamide 6,6 reinforced with carbon nanotubes

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of gamma irradiation on caprolactam migration from multilayer polyamide 6 films into food simulants: development and validation of a gas chromatographic method

A GC method to determine caprolactam in water, 15 ethanol, and olive oil food simulants was developed and validated. Linear ranges varied from 0.96 to 642.82 g/mL for water, 0.64 to 800.32 g/mL for 15 ethanol, and 1.06 to 1062.34 g/g for olive oil, with correlation coefficients higher than 0.999. Method precision studies showed RSD values lower than 5.45, while method accuracy studies showed recovery from 72 to 111 for all simulants. The effect of gamma irradiation on caprolactam migration from multilayer polyamide 6 (PA-6) films intended for cheese into water, 15 ethanol, olive oil, and 3 acetic acid simulants was also studied. For migration assay, non-irradiated and irradiated (12 kGy) films were placed in contact with the simulant and exposed at 40C for 10 days. The validated method was used to quantify caprolactam migration from multilayer PA-6 films into the simulants, which ranged from 1.03 to 7.59 mg/kg for non-irradiated films, and from 4.82 to 11.32 mg/kg for irradiated films. Irradiation caused almost no changes in caprolactam levels, with the exception of olive oil, which showed an increase in the caprolactam level. All multilayer PA-6 films were in accordance with the requirements of the legislation for caprolactam migration.

Effects of gamma-irradiation on caprolactam level from multilayer PA-6 films for food packaging: Development and validation of a gas chromatographic method

A gas chromatographic method to determine caprolactam in multilayer PA-6 films used for meat foodstuffs and cheese was developed and validated. A wide linear range (0.8-400 mu g/ml), RSD <= 4.1% and recovery higher than 90.0% were obtained for the chromatographic system, while precision and accuracy of the method showed RSD <= 3.8%, recovery from 95.5-100.0% and LOQ of 32 mu g/g. Irradiated (3, 7 and 12 kGy) and non-irradiated commercial films were analyzed. Most of them increased caprolactam levels with the increase of irradiation doses. (C) 2008 Elsevier Ltd. All rights reserved.

Migração de ε-caprolactama de embalagens contendo poliamida 6 para simulante ácido acético 3% e validação do método analítico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Evaluation by Free Vibration Method of Moisture Absorption Effects in Polyamide/Carbon Fiber Laminates

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reciclagem química por hidrólise da poliamida 6,6 reforçada com fibra de vidro após ciclos de reciclagem mecânica

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Evaluation of Different Conditions of Contact for Caprolactam Migration from Multilayer Polyamide Films into Food Simulants

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação dos efeitos ambientais nas propriedades do compósito de poliamida 6,6/fibras de carbono

This graduation work done study of polyamide 6.6/composite carbon fibres, since its processing, characterization of the main properties. Besides the influence of temperature, UV radiation, salt spray and moisture on the mechanical and viscoelastic behavior. To achieve this goal, the first composite was processed from the heat compression molding using known variables of the process and using the empirical method to find the best value for other parameters. The method processing molding was chosen because it common in composites processing in order to evaluate the influence of crystallinity of the properties that influence the mechanical and viscoelastic behavior laminates. From the obtained laminate specimens were evaluated in weathering, such as: in hygrothermal chamber, UV, salt spray and thermal shock. In another step, the effect produced by these constraints were evaluated by optical microscopy, ultrasound, dynamic mechanical analysis and vibration tests. This project was conducted at the Department of Technology and Materials of UNESP in Guaratingueta, where all the equipment and techniques for the implementation of this project met available. After the tests proved the applicability of the composite polyamide 6.6/carbon fibers in aeronautical applications with resistance the main climatic influences

Influência da incorporação de nanofibras de poliamida 6 com e sem nanotubos de carbono como reforço de prótese parcial fixa adesiva

The aim of this study was to evaluate the behavior of reinforced composites with polyamide 6 fibers aligned (6000 rpm) and alignment (120 rpm) with or without CNT using the flexural strength test. After preparation of nanofibers aligned nylon 6 (6000 rpm) and alignment (120 rpm) with and without incorporation of nanotube carbon by the method of electrospinning, were performed one control group (n = 10) and 4 experimental groups (n = 40) G1: Control (just resin Charisma - Heraeus Kulzer) ;G2 Resin + N6 aligned (6000 rpm) + CNT; G3:Resin + N6 alignment (120 rpm) + CNT; G4: Resin + aligned ( 6000 rpm) N6. G5: Resin + N6 alignment (120 rpm). The fibers were cut to the dimensions of 0,3 x 15 mm and were applied an adhesive at the surface (Single Bond 2) for 5 min and cured. In the matrix, was added resin in the proximal box (Charisma A2, Heraeus Kulzer) and cured for 40 s. (power 1100 mW / cm²). A first layer of resin and on the resin was deposited. The resin layers specimens were light irradiated with three overlapping exposures delivered. For each resin layer were light irradiated for 40 sec. The samples were tested with a cross-speed of 1 mm / min, and a 50 Kgf at Universal testing machine (EMIC mod.DL2000). The Dunnet test showed that only the nanotube group was significantly different from the control group. The ANOVA two-way indicates that the nanotube factor was statistically significant (p < 0.05) and there is no interaction between factors and orientation nanotube. The presence of nanotube showed lower fracture resistance values for aligned and unaligned groups. The results of this study showed that the orientation of the fibers does not influence the strength of composite resins and the incorporation of nylon nanofibers with carbon nanotubes decreased the fracture resistance values. The presence of the fibers has not been able to improve the strength of the material in any of the...

Desenvolvimento e validação de método analítico para determinação de caprolactama em simulantes de alimentos: estudo de migração e efeito da irradiação

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)