Preparation and characterization of PVDF/CaCO3 composites

The contribution of new materials, involving composites and blends, has been reaching the most varied fields of science, as much of the scientific as technological point of view. This is due to the man's needs in applications, especially in medicine areas. Thus, this work shows the preparation and characterization of poly(vinylidene fluoride) (PVDF) and calcium carbonate (CaCO3) Composite films in order to analyse the incorporation of CaCO3 in PVDF for future application in bony restoration and bony filling. The films were prepared by casting method, where the PVDF pellet shape was dissolved in dimethylacetamide (DMA) and in a separate container CaCO3/DMA emulsion was also made. Soon afterwards they were mixed in several proportions 100/00, 95/05, 85/15, 70/30 in weight and left to dry in greenhouse. Homogeneous and flexible films were obtained and structurally characterized by attenuated total reflection infrared spectroscopy (FT-IR/ATR), thermal analyses (DSC, TGA), X-ray diffractometry, optical and scanning electron microscopies. The results showed that the material was a composite with good thermal stability until around 400 degrees C, the crystallinity of PVDF was non-polar alpha-phase and the obtained films were porous, being these filled with CaCO3. (c) 2006 Elsevier B.V. All rights reserved.

Thermomechanical characterization of PVDF and P(VDF-TrFE) blends containing corn starch and natural rubber

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tailoring the Structural Properties of PVDF and P(VDF-TrFE) by Using Natural Polymers as Additives

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ultrasonic material characterization using large-aperture PVDF receivers

This work describes the use of a large-aperture PVDF receiver in the measurement of liquid density and composite material elastic constants. The density measurement of several liquids is obtained with accuracy of 0.2% using a conventional NDE emitter transducer and a 70-mm-diameter, 52-mu m P(VDF-TrFE) membrane with gold electrodes. The determination of the elastic constants is based on the phase velocity measurement. Diffraction can lead to errors around 1% in velocity measurement when using alternatively the conventional pair of ultrasonic transducers (1-MHz frequency and 19-mm-diameter) operating in through-transmission mode, separated by a distance of 100 mm. This effect is negligible when using a pair of 10-MHz, 19-mm-diameter transducers. Nevertheless, the dispersion at 10 MHz can result in errors of about 0.5%, when measuring the velocity in composite materials. The use of an 80-mm diameter, 52-mu m-thick PVDF membrane receiver practically eliminates the diffraction effects in phase velocity measurement. The elastic constants of a carbon fiber reinforced polymer were determined and compared with the values obtained by a tensile test. (C) 2009 Elsevier B. V. All rights reserved.

Dielectric behavior of PVDF/POMA blends that have a low doped POMA content

The real (epsilon') and imaginary (epsilon) components of the complex permittivity of blends of PVDF [poly(vinylidene fluoride)] with POMA [poly(o-methoxyaniline)] doped with toluenosulfonic acid (TSA) containing 1, 2.5, and 5 wt % POMA-TSA were determined in the frequency interval between 10(2) and 3 X 10(6) Hz and in the temperature range from -120 up to 120degreesC. It was observed that the values of epsilon' and epsilon had a greater increase with the POMA-TSA content and with a temperature in the region of frequencies below 10 kHz. This effect decreased with frequency and it was attributed to interfacial polarization. This polarization was caused by the blend heterogeneity, formed by conductive POMA-TSA agglomerates dispersed in an insulating matrix of PVDF. The equation of Maxwell-Garnett, modified by Cohen, was used to evaluate the permittivity and conductivity behavior of POMA-TSA in the blends. A strong decrease was observed in POMA-TSA conductivity in the blend, which was bigger the lower the POMA-TSA content in the blend. This decrease could have been caused either by the POMA dedoping during the blend preparation process or by its dispersion into the insulating matrix. (C) 2002 Wiley Periodicals, Inc.

Morphology variation as a function of composition for blends of PVDF and a polyaniline derivative

Blends of poly(vinylidene fluoride), PVDF, and poly(o-methoxyaniline), POMA doped with toluene sulfonic acid, TSA, were prepared by casting at various compositions and studied by scanning electron microscopy, X-ray diffraction and differential scanning calorimetry. The blend composition has a great influence on the morphology obtained. As the concentration of POMA-TSA is increased in the blend an interconnecting fibrillar-like morphology is formed and the spherulites characteristic of pure PVDF are destroyed. The variation of blend morphology is further discussed based on X-ray diffraction and differential scanning calorimetry analysis. (C) 1998 Elsevier B.V. Ltd. All rights reserved.

A new route to obtain PVDF/PANI conducting blends

Electrically conductive poly(vinylidene fluoride)(PVDF) - polyaniline blends of different composition were synthesized by chemical polymerization of aniline in a mixture of PVDF and dimethylformamide (DMF) and studied by electrical conductivity measurement, UV-Vis-NIR and FTIR spectroscopy. The samples were obtained as flexible films by pressing the powder at 180 degrees C for 5 min. The electrical conductivity showed a great dependence on the syntheses parameters. The higher value of the electrical conductivity was obtained for the oxidant/aniline molar ratio equal to 1 and p-toluenesulfonic acid-TSA/aniline ratio between 3 and 6. UV-Vis-NIR and FTIR spectra of the blend are similar to the doped PANI, indicating that the PANI is responsible for the high electrical conductivity of the blend. The electrical conductivity of blend proved to be stable as a function of temperature decreasing about one order at temperature of 100 degrees C. The route used to obtain the polymer blend showed to be a suitable alternative in order to obtain PVDF/PANI-TSA blends with high electrical conductivity. (c) 2006 Elsevier Ltd. All rights reserved.

Adhesion strength characterization of PVDF/HA coating on cp Ti surface modified by laser beam irradiation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural modifications in stretch-induced crystallization in PVDF films as measured by small-angle X-ray scattering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of PVDF/HAP composites for medical applications

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Thermal and mechanical properties of PVDF/PANI blends

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Composites PVDF-TrFE/BT used as bioactive membranes for enhancing bone regeneration

In this paper a piezoelectric composite membranes were developed for charge generator to promoter bone regeneration on defects sites. Is known that the osteogenesis process is induced by interactions between biological mechanisms and electrical phenomena. The membranes were prepared by mixing Barium Titanate (BT) powders and PVDF-TrFE (PVDF:TrFE = 60:40 mol%) on dimethylformamide medium. This precursor solution was dried and crystallized at 100degreesC for 12 hours. Composites membranes were obtained by following methods: solvent casting (SC), spincoating (SP), solvent extraction by water addition (WS) and hot pressing (HP).The microstructural analysis performed by SEM showed connectivity type 3-0 and 3-1 with high homogeneity for samples of ceramic volume fraction major than 0.50. Powder agglomerates within the polymer matrix was evidenced were observed for composites with the BT volume fraction major than 40%. The composite of ceramic fraction of 0.55 presented the best values of remanent polarization (similar to33 muC/cm(2)), but the flexibility of these composites with the larger ceramic fraction was significantly affected.For in vivo evaluation PVDF-TrFE/BT 90/10 membranes with 3cm larger were longitudinally implanted under tibiae of male rabbit. After 21 days the animals were sacrificed. By histological analyses were observed neo formed bone with a high mitotic activity. In the interface bone-membrane was evidenced a pronounced callus formation. These results encourage further applications of these membranes in bone-repair process.

Effect of low contents of a polyaniline derivative on the crystallization and electrical properties of blends with PVDF

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The investigation of alpha -> beta phase transition in poly(vinylidene fluoride) (PVDF)

The phase transition from the non-polar a-phase to the polar beta-phase of poly(vinylidene fluoride) (PVDF) has been investigated using micro-Raman spectroscopy, which is advantageous for being a non-destructive technique. Films of alpha-PVDF were subjected to stretching under controlled rates and at 80 degrees C, the transition to beta-PVDF being monitored by the decrease in the Raman band at 794 cm(-1) characteristic of the a-phase, with the concomitant increase in the 839 cm(-1) band characteristic of the beta-phase. Poling with negative corona discharge was found to affect the alpha-PVDF morphology improving the Raman bands related to this crystalline phase. This effect is minimized for films stretched to higher ratios. Significantly, corona-induced effects could not be observed with the other experimental techniques, viz. X-ray diffraction and infrared spectroscopy.

Fabrication and testing of a poly(vinylidene fluoride) (PVDF) microvalve for gas flow control

A microactuator made from poly(vinylidene fluoride) (PVDF), a piezoelectric polymer, was fabricated to control the gas flow rate through a glass micronozzle. The actuator was formed by gluing together two PVDF sheets with opposite polarization directions. The sheets were covered with thin conducting films on one side, that were then used as electrodes to apply an electric field to move the valve. The actuator has a rectangular shape, 3 mm x 6 mm. The device was incorporated with a micronozzle fabricated by a powder blasting technique. Upon applying a DC voltage across the actuator electrodes, one sheet expands while the other contracts, generating an opening motion. A voltage of +300 V DC was used to open the device by moving the actuator 30 mu m, and a voltage of -200 V DC was used to close the device by moving the actuator 20 mu m lower than the relaxed position. Flow measurements were performed in a low-pressure vacuum system, maintaining the microvalve inlet pressure constant at 266 Pa. Tests carried out with the actuator in the open position and with a pressure ratio (inlet pressure divided by outlet pressure) of 0.5, indicated a flow rate of 0.36 sccm. In the closed position, and with a pressure ratio of 0.2, a flow rate of 0.32 sccm was measured.