Multilayer adsorption of Cu(II) and Cd(II) over Brazilian Orchid Tree (Pata-de-vaca) and its adsorptive properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

An electroanalytical application of 2-aminothiazole-modified silica gel after adsorption and separation of Hg(II) from heavy metals in aqueous solution

2-Aminothiazole covalently attached to a silica gel surface was prepared in order to obtain an adsorbent for Hg(II) ions having the following characteristics: good sorption capacity, chemical stability under conditions of use, and, especially, high selectivity. The accumulation voltammetry of mercury(II) was investigated at a carbon paste electrode chemically modified with silica gel functionalized with 2-aminothiazole (SIAMT-CPE). The repetitive cyclic voltammogram of mercury(II) solution in the potential range -0.2 to + 0.6 V versus Ag/AgCl (0.02 mol L-1 KNO3; V = 20 mV s(-1)) show two peaks one at about 0.1 V and other at 0.205 V. The anodic wave peak at 0.205 V is well defined and does not change during the cycles and it was therefore further investigated for analytical purposes using differential pulse anodic stripping voltammetry in differents supporting electrolytes. The mercury response was evaluated with respect to pH, electrode composition, preconcentration time, mercury concentration, cleaning solution, possible interferences and other variables. The precision for six determinations (n = 6) of 0.02 and 0.20 mg L-1 Hg(II) was 4.1 and 3.5% (relative standard deviation), respectively. The detection limit was estimated as 0.10 mu g L-1 mercury(II) by means of 3:1 current-to-noise ratio in connection with the optimization of the various parameters involved and using the highest-possible analyser sensitivity. (c) 2006 Elsevier Ltd. All rights reserved.

Kinetics and Adsorption Isotherms of Bisphenol A, Estrone, 17 beta-Estradiol, and 17 alpha-Ethinylestradiol in Tropical Sediment Samples

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nickel adsorption by soils in relation to pH, organic matter, and iron oxides

There is little information on nickel adsorption by Brazilian soils. The objective of this experiment was to determine the effect of pH, organic matter, and iron oxides on nickel adsorption by three soils: a clayey Anionic Rhodic Acrudox, a sandy clay loam Anionic Xanthic Acrudox, and a clayey Rhodic Hapludalf. Soil samples were collected from the 0-0.2 in layer and treated to eliminate organic matter and iron oxides. The nickel adsorption was evaluated in the original samples and in those treated to remove organic matter and to remove both, organic matter and iron oxides, using 2 g soil + 20 mL of 0.01 mol L-1 CaCl2 solution containing 5 mg L-1 Ni, pH varying from 3.5 to 7.5. The nickel adsorption decreased with the elimination of organic matter. For the samples without organic matter and iron oxides, adsorption decreased only in the Anionic Rhodic Acrudox. The pH was the main factor involved in nickel adsorption variation, and for soil samples without organic matter and iron oxides, the maximum adsorption occurred at higher pH values.

Hillslope curvature, clay mineralogy, and phosphorus adsorption in an Alfisol cultivated with sugarcane

As curvaturas do relevo promovem pedoambientes específicos que condicionam os atributos químicos e mineralógicos do solo e podem auxiliar na definição de zonas específicas de manejo. O fósforo (P) é um dos principais elementos limitantes ao desenvolvimento e longevidade do canavial. O teor e a constituição mineralógica da fração argila assumem papel importante na disponibilidade do P, sendo que a gibbsita (Gb), quando presente em altas proporções no solo, pode ser a principal responsável pela sua adsorção e indisponibilidade. Investigaram-se as relações e a variabilidade espacial da adsorção de P e a ocorrência de caulinita (Ct) e gibbsita na fração argila de um Argissolo Vermelho-Amarelo eutrófico originado de rochas areníticas sob diferentes curvaturas do relevo em área sob cultivo de cana-de-açúcar. Duas malhas de 1 ha foram delimitadas numa área côncava e outra área convexa. Foram coletadas 121 amostras em cada área para realização das análises granulométricas, químicas e mineralógicas. A capacidade máxima de adsorção de P foi obtida em seis amostras escolhidas ao acaso em cada área. Os resultados foram submetidos às análises estatísticas descritiva e geoestatística. Os menores valores médios de P disponível encontraram-se na área convexa. Nesta área, a proporção de gibbsita, expressa pelos valores da razão [Gb/(Gb+Ct)] e os valores de capacidade máxima de adsorção de fósforo foram maiores do que na área côncava.

Boron adsorption in lowland soils from Parana State, Brazil

Boron adsorption by soil is the main phenomenon that affects its availability to plants. This, the present study investigated the effect of liming on B adsorption by lowland soils of Parana State, and to correlate these values with the physical and chemical properties of the soils. Surface samples of three lowland soils [Gleissolo Haplico (GX), Plintossolo Haplico (FX) and Cambissolo Haplico (CX)], with different origin material and physicochemical properties were used. Samples with or without liming application were incubated during 60 days. Boron adsorption was accomplished by shaking 4.0g soil samples, for 24 h, with 20 mL of 0.01 mol L-1 CaCl2 solution containing different concentrations of B (0, 1, 2, 4, 8 and 16 mg L-1). Sorption was fitted to non-linear form of the Langmuir adsorption isotherm. The adsorption isotherms indicated that the B adsorption increased with its increasing concentration in the equilibrium solution. Maximum adsorption capacity of B ranged from 3.0 to 13.9 mg kg(-1) (without liming) and 14.7 to 35.7 mg kg(-1) (with liming). Liming increased the amount of adsorbed B in Gleissolo Haplico and Plintossolo Haplico soils, although the bonding energy has decreased. The amount of adsorbed B by Cambissolo Haplico soil was not affected by liming application. The most important soil properties affecting the B adsorption in lowland soils were pH, clay content, exchangeable aluminum and iron oxide contents.

Effects of gamma-irradiation on caprolactam level from multilayer PA-6 films for food packaging: Development and validation of a gas chromatographic method

A gas chromatographic method to determine caprolactam in multilayer PA-6 films used for meat foodstuffs and cheese was developed and validated. A wide linear range (0.8-400 mu g/ml), RSD <= 4.1% and recovery higher than 90.0% were obtained for the chromatographic system, while precision and accuracy of the method showed RSD <= 3.8%, recovery from 95.5-100.0% and LOQ of 32 mu g/g. Irradiated (3, 7 and 12 kGy) and non-irradiated commercial films were analyzed. Most of them increased caprolactam levels with the increase of irradiation doses. (C) 2008 Elsevier Ltd. All rights reserved.

EFFECT of GAMMA IRRADIATION on CAPROLACTAM MIGRATION FROM MULTILAYER POLYAMIDE 6 FILMS INTO WATER FOOD SIMULANT and VALIDATION of THE METHOD

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Identification and migration of degradation compounds from irradiation of multilayer polyamide 6 films for meat foodstuffs and cheese

The aim of this work was to identify the degradation compounds produced during irradiation of multilayer polyamide 6 (PA-6) films and to study their migration into water and 95% ethanol food simulant. After irradiation of multilayer PA-6 films at 3, 7 and 12 kGy, degradation compounds were extracted using solid-phase microextraction, for which the time and temperature of extraction and stirring were optimized, and identified by gas chromatography-mass spectrometry. Caprolactam, 2-cyclopentylcyclopentanone and aldehydes, among other compounds, were identified in the headspace of the films. Polydimethylsiloxane was considered the best fiber for extraction. The optimum conditions of time, temperature and stirring to extract the compounds were 20 min, 80 degrees C and 225 rpm. For validation purposes, the compounds were quantified in water and 95% ethanol and the results showed high sensitivity, good precision and accuracy. Migration of compounds from irradiated and non-irradiated multilayer PA-6 films into water and 95% ethanol food simulants was carried out at 40 degrees C for 10 days. The method was efficient for the quantification of decaldehyde, 2-cyclopentylcyclopentanone and caprolactam that migrated from multilayer PA-6 films into food simulants.

Adsorption and detection of DNA dendrimers at carbon electrodes

Dendritic nucleic acids are highly branched and ordered molecular structures, possessing numerous single-stranded oligonucleotide arms, which hold great promise for enhancing the sensitivity of DNA biosensors. This article evaluates the interfacial behavior and redox activity of nucleic acid dendrimers at carbon paste electrodes, in comparison to DNA. Factors influencing the adsorption behavior, including the adsorption potential and time, solution conditions, or dendrimer concentration, are explored. The strong adsorption at the anodically pretreated carbon surface is exploited for an effective preconcentration step prior to the chronopotentiometric measurement of the surface species. Coupled with the numerous guanine oxidation sites, such stripping protocol offers remarkably low detection limits (e.g., 3 pM or 2.4 femtomole of the I-layer dendrimer following a 15 min accumulation). The new observations bear important implications upon future biosensing applications of nucleic dendrimers.

Adsorption of Cu(II) and Co(II) complexes on a silica gel surface chemically modified with 2-mercaptoimidazole

The isotherms of adsorption of MeX2 (Me = Cu2+, Co2+; X = Cl-, Br-, ClO4-) by silica gel chemically modified with 2-mercaptoimidazole (SiMI) were studied in acetone and ethanol solutions, at 25 degrees C. Covalently attached 2-mercaptoimidazole molecule to silica gel surface adsorbs MeX2 from solvent by forming a surface complex. The metal is bonded to the surface through the nitrogen atom of attached 2-mercaptoimidazole. At low loading, the electronic and ESR spectral parameters indicated that the Cu2+ complexes are in a distorted-tetragonal symmetry field. The d-d electronic transition spectra showed that for Cu(ClO4)(2) complex, the peak of absorption did not change for any degree of metal loading and for Cl- and Br- complexes, the peak maxima shifted to higher energy with lower metal loading. The CoX2(X = Cl-, Br-, ClO4-) analogues possess a distorted-tetrahedral field.

Preparation, characterization, and CuX2 and CoX2 (X = Cl-, Br-, ClO4-) adsorption behavior of a polyhedral oligomer silsesquioxane functionalized with an organic base

In this paper we report on the synthesis, characterization, and adsorption properties of the first 3-amino-1,2,4-triazole-modified porous silsesquioxane (ATPS). The isotherms of adsorption of MX2 (M = Cu(II), Co(II); X = Cl-, Br-, ClO4-) by ATPS were studied in ethanol and aqueous solutions at 298 K. The results showed that there is a good fit between the experimental data and the Langmuir isotherm. The adsorption capacity in both solvents followed the sequence Cu(II) >> Co(II). The lowest adsorption for Co(II) should be related to the largest hydration volume, which obstructs the adsorption capacity of the surface, and consequently causes a decrease in the number of cations adsorbed. For the salts with different anions the sequence was MCl2 > MBr2 > M(ClO4)2 in both solvents. The low affinity for M(ClO4)(2) toward the solid phase is a consequence of the poorer coordination ability of the ClO4-. Adsorptions from ethanol solutions were higher than those from aqueous solutions due to the higher polarity of water, which can more strongly solvate the solute and the basic sites on the surface. The following adsorption capacities (in mmol g(-1)) were determined: 0.24 (aq) and 0.84 (eth) for CuCl2, 0.09 (aq) and 0.16 (eth) for CuBr2, and 0.08 (aq) and 0.11 (eth) for Cu(ClO4)(2); 0.02 (aq) and 0.07 (eth) for CoCl2, 0.02 (aq) and 0.06 (eth) for CoBr2, and 0.01 (aq) and 0.05 (eth) for Co(ClO4)(2). (c) 2007 Elsevier B.V. All rights reserved.

Thermolysis of octa (hydridodimethylsiloxyl) octasilsesquioxane in pyridine media and subsequent toluidine blue O adsorption

This work describes the synthesis of octa (hydridodimethylsiloxyl) octasilsesquioxane, (Q(8)M(8)(H)) and its thermolysis in pyridine media. The new compound called CPy was characterized by FTIR, NMR-MAS, XRD, MEV spectroscopies and TGA analyses. These results indicate that silsesquioxanes cages (octanion) are maintained after thermal treatment. A cleavage of vertex siloxy groups yielding a nanocomposite with polymeric nature is proposed. Its structure and morphology allows the adsorption/inclusion of electrochemical mediator, toluidine blue O. The square wave voltammetry analysis of resulting composite (CPyTBO) exhibits two redox couple with a formal potential (E-0') 0.1 V and 0.26 V to I and II redox couples respectively, (Britton-Robinson (BR) buffer pH 3, v = 10 Hz versus SCE) ascribed to a monomer and dimmer of the toluidine blue species. This paper opens the use of spherosiloxane derived materials a's host for small molecules in the electrochemical field. (C) 2004 Elsevier B.V. All rights reserved.

Adsorption of CuX2 (X = Cl-, Br-, and ClO4-) on a silica gel surface chemically modified with thiazolidine-2-thione from acetone and ethanol solutions

The isotherms of adsorption of CuX2 (X = Cl-, Br, ClO4-,) by silica gel chemically modified with thiazolidine-2-thione were studied in acetone (ac) and ethanol (eth) solutions at 25 degrees C. The following equilibrium constants (in 1 mol(-1)) were determined: a) CuCl2, 1.9 x 10(3) (ac), 1.6 x 10(3) (eth); b) CuBr2, 1.7 x 10(3) (ac), 1.2 x 10(3) (eth); c) Cu(ClO4)(2), 1.1 x 10(3) (ac), 1.0 x 10(3) (eth). The electron spin resonance spectra of the surface complexes indicate a tetragonal distorted structure in the case of lower degrees of metal loading on the chemically modified surface. The d-d electronic transition spectra show that for the ClO4- complex, the peak of absorption did not change for any degree of metal loading, and for Cl- and Br complexes, the peak maxima shift to higher energy with lower metal loading.

Adsorption of copper(II) and cobalt(II) complexes on a silica gel surface chemically modified with 3-amino-1,2,4-triazole

The isotherms of adsorption of MX2 (M = Cu2+, Co2+; X = Cl-, Br-, ClO4) by silica gel chemically modified with 3-amino-1,2,4-triazole (SiATR) were studied in acetone and ethanol solutions, at 25 degrees C. The 3-amino-1,2,4-triazole molecule, covalently bound to the silica gel surface, adsorbs MX2 from solvent by forming a surface complex. At low loading, the electronic and electron spin resonance spectral parameters indicated that the Cu2+ complexes have distorted tetragonal symmetry. The CoX2 (X = Cl-, Br-) analogues exhibit a distorted-tetrahedral geometry, whilstthe (SiATR)mCo)ClO4)(2) complex has a tetragonally distorted octahedral geometry, with four equatorial nitrogen atoms around the cobalt. (C) 1998 Elsevier B.V. B.V. All rights reserved.