Effect of ion concentration of ionomer in electron injection layer of polymer light-emitting devices

Polymer light-emitting devices (PLEDs) with poly(2-methoxy-5-hexyloxy)-p-phenylenevinylene (OC1OC6-PPV) as the emissive layer were studied with an electron injection layer of ionomers consisting of copolymers of styrene and methylmethacrylate (PS/PMMA) with 3, 6 and 8 mol% degree of sulfonation. The ionomers were able to form very thin films over the emissive layer, with less than 30 nm. Additionally, the presence of ion pairs of ionomer suppresses the tendency toward dewetting of the thin film of ionomer (similar to 10 nm) which can cause malfunction of the device. The effect of the ionomers was investigated as a function of the ion content. The devices performance, characterized by their current density and luminance intensity versus voltage, showed a remarkable increase with the ionomer layer up to 6 mol% of ionic groups, decreasing after that for the 8 mol% ionomer device. The study of the impedance spectroscopy in the frequency range from 0.1 to 10(6) Hz showed that the injection phenomena dominate over the transport in the electroluminescent polymer bulk. (c) 2006 Elsevier B.V. All rights reserved.

Polymer light emitting devices with Langmuir-Blodgett (LB) films: Enhanced performance due to an electron-injecting layer of ionomers

Polymer light-emitting devices (PLEDs) have been produced with Langmuir-Blodgett (LB) films from poly(2-methoxy-5-hexyloxy)-p-phenylenevinylene (OC1OC6-PPV) as the emissive layer and an ionomer of a copolymer of styrene and methylmethacrylate (PS/PMMA) as an electron-injection layer. The main features of such devices are the low operating voltages, obtainable firstly due to the good quality of the ultrathin LB films that allows PLEDs to be produced reproducibly and secondly due to the improved electrical and luminance properties brought by the electron-injection layer. Also demonstrated is the superior performance of an all-LB device compared to another one produced with cast films of the same materials. Published by Elsevier B.V.

Emprego de prótese intra-ocular de resina acrílica. Estudo experimental em ratos

Foram eviscerados os globos oculares esquerdos de 32 ratos, linhagem Wistar, divididos em quatro grupos (A, B, C, D) constituídos, cada um, de cinco testemunhas e três controles. Nos animais-testemunha introduziu-se, dentro da capa córneo-escleral, uma esfera de resina acrílica (metilmetacrilato), previamente confeccionada e esterilizada por autoclavagem, ao passo que nos controles a cavidade eviscerada foi mantida sem prótese. Os ratos dos grupos A, B, C e D foram sacrificados respectivamente aos 7, 15, 30 e 90 dias de pós-operatório, quando os conteúdos orbitários esquerdos foram exenterados e preparados para o exame histopatológico. Observou-se que os animais-testemunha tiveram resposta inflamatória do tipo tecido de granulação ao redor da prótese de cavidade, com edema inflamatório da córnea especialmente nos grupos A e B, quando se iniciou a regressão da inflamação aguda. A cavidade orbitária manteve o tamanho em todos os grupos nos animais-testemunha e houve contração significativa nos animais-controle. Com estas observações, foi possível concluir que a esfera de resina acrílica é uma opção, de baixo custo e fácil confecção, para correção de defeito estético causado pela perda do globo ocular.

Effect of monomer treatment and polymerisation methods on the bond strength of resin teeth to denture base material

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Prótese intra-ocular de resina acrílica em cães e gatos

Foram atendidos no Hospital Veterinário da Faculdade de Medicina Veterinária e Zootecnia da Unesp - Campus de Botucatu, 11 animais (oito cães e três gatos), com alterações oftálmicas unilaterais graves que levaram à perda total da função ocular (protrusão de globo com injúria nervosa e estrutural, perfurações de córnea com perda de conteúdo intra-ocular e endoftalmites, entre outras). Os animais, com idades entre dois meses e 10 anos, foram submetidos à evisceração e posterior inclusão de esfera de resina acrílica (metilmetacrilato) na capa córneo-escleral ou escleral. As esferas foram previamente confeccionadas e esterilizadas por autoclavagem. No pós-operatório foram utilizados antiinflamatórios e antibioticoterapia tópica combinada ou não a sistêmica. O período de observação variou de 2 meses a 3 anos e os aspectos avaliados foram secreção ocular, blefarospasmo, sinais de desconforto e estética. Obtiveram-se resultados satisfatórios em oito casos. Concluiu-se que a resina acrílica pode ser uma alternativa para uso como inclusão em cavidade anoftálmica.

Artrodese do carpo em gatos associada à hidroxiapatita

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evolution of rheological properties and local structure during gelation of siloxane-polymethylmethacrylate hybrid materials

Hybrid siloxane-polymethylmethacrylate (PMMA) nanocomposites with covalent bonds between the inorganic (siloxane) and organic (polymer) phases were prepared by the sot gel process through hydrolysis and polycondensation of 3-(trimethoxysilyl)propylmethacrylate (TMSM) and polymerization of methylmethacrylate (MMA) using benzoyl peroxide (BPO) as initiator. The effect of MMA, BPO and water contents on the viscoelastic behaviour of these materials was analysed during gelation by dynamic rheological measurements. The changes in storage (G') and loss moduli (G), complex viscosity (eta*) and phase angle (6) were measured as a function of the reaction time showing the viscous character of the sot in the initial step of gelation and its progressive transformation to an elastic gel. This study was complemented by Si-29 and C-13 solid-state nuclear magnetic resonance (NMR/MAS) measurements of dried gel. The analysis of the experimental results shows that linear chains are formed in the initial step of the gelation followed by a growth of branched structures and formation of a three-dimensional network. Near the gel point this hybrid material demonstrates the typical scaling behaviour expected from percolation theory.

Small-angle X-ray and nuclear-magnetic resonance study of siloxane-PMMA hybrids prepared by the sol-gel process

Transparent siloxane-polymethylmethacrylate (PMMA) hybrids were synthesized by the sol-gel process through hydrolysis of methacryloxyproyltrimethoxysilane (TMSM), tetramethoxysilane (TMOS) and polymerization of methylmethacrylate (MMA) using benzol peroxide (BPO) as catalyst. These composites have a good chemical stability due to the presence of covalent bonds between the inorganic (siloxane) and organic (PMMA) phases. The effects of siloxane content, pH of the initial sol and BPO content on the structure of the dried gels were analyzed by small-angle X-ray scattering (SAXS). SAXS results revealed the presence of an interference (or correlation) peak at medium q-range for all compositions, suggesting that siloxane groups located at the ends of PMMA chains form isolated clusters that are spatially correlated. The average intercluster distance - estimated from the q-value corresponding to the maximum in SAXS spectra - decreases for samples prepared with increasing amount of TMSM-TMOS. This effect was assigned to the expected increase in the number density of siloxane groups for progressively higher siloxane content. The increase of BPO content promotes a more efficient polymerization of MMA monomers but has no noticeable effect on the average intercluster distance. High pH favors polycondensation reactions between silicon species of both TMOS and TMSM silicon alcoxides, leading to a structure in which all siloxane clusters are bonded to PMMA chains. This effect was confirmed by Si-29 nuclear-magnetic resonance (NMR) measurements.

Effect of Surface Treatments on the Bond Strength between Composite Resin and Acrylic Resin Denture Teeth

Purpose: This investigation studied the effects of 3 surface treatments on the shear bond strength of a light-activated composite resin bonded to acrylic resin denture teeth. Materials and Methods: The occlusal surfaces of 30 acrylic resin denture teeth were ground flat with up to 400-grit silicon carbide paper. Three different surface treatments were evaluated: (1) the flat ground surfaces were primed with methyl methacrylate (MMA) monomer for 180 seconds; (2) light-cured adhesive resin was applied and light polymerized according to the manufacturer's instructions; and (3) treatment 1 followed by treatment 2. The composite resin was packed on the prepared surfaces using a split mold. The interface between tooth and composite was loaded at a cross-head speed of 0.5 mm/min until failure. Results: Analysis of variance indicated significant differences between the surface treatments. Results of mean comparisons using Tukey's test showed that significantly higher shear bond strengths were developed by bonding composite resin to the surfaces that were previously treated with MMA and then with the bonding agent when compared to the other treatments. Conclusion: Combined surface treatment of MMA monomer followed by application of light-cured adhesive resin provided the highest shear bond strength between composite resin and acrylic resin denture teeth.

Prototipagem como forma alternativa para realização de cranioplastia com metilmetacrilato: Nota técnica

The prototyping is a method for reconstruction of human body segments by computer software. It has been used in neurosurgery for cranial reproduction in patients allowing the programming of surgical procedures and the production of prosthesis to reconstruct bone failures in the skull. We present two cases of cranioplasty performed with the use of acrylic prosthesis constructed by prototyping. After 10 months of follow-up, they donot present signs of infection and show good aesthetic result. The advantages pointed at the literature for this method (reduction of surgical time, easy technical handle, and good aesthetic result) were confirmed.

Effect of the association of nystatin with a tissue conditioner on its ultimate tensile strength

Purpose: This study evaluated the ultimate tensile strength of a tissue conditioner without nystatin incorporation (GI - control group) and the same tissue conditioner modified by the addition of nystatin in two concentrations: GII - 500,000 International Units (U) and GIII - 1,000,000 U, in which each milligram of the medicament corresponded to 6079 U. Materials and Methods: Dumbbell-shaped specimens (N = 7) with a central cross-sectional area of 33 × 6 × 3 mm were produced for the three experimental groups. After polymerization following manufacturer's instructions, specimens were immersed in distilled water at 37°C for either 24 hours or 7 days and then tested in tension in the MTS 810 at 40 mm/minute. Data were analyzed by two-way ANOVA followed by Tukey's test, at 95% level of confidence. Results: The means (force-grams (gf) ± standard deviation) of the ultimate tensile strength were: GI - 634.29 ± 122.80; GII - 561.92 ± 133.56; and GIII - 547.30 ± 73.47 for 24-hour storage, and GI - 536.68 ± 54.71; GII - 467.50 ± 143.51; and GIII - 500.62 ± 159.76 for 7-day storage. There were no statistically significant differences among the three experimental groups (p > 0.05). The ultimate tensile strength means of all experimental groups after 7 days were significantly lower than those observed after 24 hours (p = 0.04). Conclusions: The results of this study suggest that the addition of nystatin into the tissue conditioner investigated in concentrations below 1,000,000 U did not affect its ultimate tensile strength. Copyright © 2006 by The American College of Prosthodontists.

Bond strength of acrylic teeth to denture base resin after various surface conditioning methods before and after thermocycling

This study aimed to evaluate the durability of adhesion between acrylic teeth and denture base acrylic resin. The base surfaces of 24 acrylic teeth were flatted and submitted to 4 surface treatment methods: SM1 (control): No SM; SM2: application of a methyl methacrylate-based bonding agent (Vitacol); SM3: air abrasion with 30-μm silicone oxide plus silane; SM4: SM3 plus SM2. A heat-polymerized acrylic resin was applied to the teeth. Thereafter, bar specimens were produced for the microtensile test at dry and thermocyled conditions (60 days water storage followed by 12,000 cycles). The results showed that bond strength was significantly affected by the SM (P < .0001) (SM4 = SM2 > SM3 > SM1) and storage regimens (P < .0001) (dry > thermocycled). The methyl methacrylate-based adhesive showed the highest bond strength.

Dental students' familiarity with the medical management of dental patients at Brazilian dental schools

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ressonância paramagnética eletrônica (RPE) aplicada em semicondutores orgânicos

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo de propriedades da resina acrílica termoativada por energia de micro-ondas frente às variações nos procedimentos de inclusão

On heat cured acrylic resins by microwaves energy the action of electromagnetic waves on methylmethacrylate promote the polymerization process. However, part of this energy is absorbed by the gypsum present in the flask and the function of this gypsum is to maintain the characteristics of specimen, nevertheless is unknown in the literature as the amount of water present in this gypsum affects the characteristics of acrylic resin. The proposal of this study was verified if dried gypsum influenced in some properties of the acrylic resins thermally activated by microwaves: presence of porosity, microhardness, roughness, flexural strength and dimensional change. Two different types of acrylic resin for complete denture were utilized: Lucitone 550 e Vipi-Wave and groups were formed: Lucitone 550, polymerization by microwave energy without gypsum treatment; Lucitone 550, polymerization by microwave energy with pretreatment gypsum; Vipi-Wave by microwave energy without gypsum treatment; Vipi Wave, polymerization by microwave energy with pretreatment gypsum; Lucitone 550 control group polymerization in hot water bath. For both situations were performed analysis of microhardness and porosity three different metallic shaped specimens were formed with followed dimensions: 2,0x2,0x2,0cm (8cm3); 2,0x2,0x1,0 (4cm3) e 2,0x2,0x0,5 (2cm3). Standardized wax specimens was used to prepare groups (n=9) and included in glass fiber flasks. The gypsum dry was made by microwave oven cycle (10min and 600W) and then the flasks were maintained in dry oven during two hours. Polymerizations of specimens were made and then polished. Wax patterns #7 obtained from the metal were embedded in plastic flask and following the processes of pressing and polymerization of the resin according to established groups. To evaluate the flexural strength, specimens 65mm x 10mm x 3.0mm from metallic patterns in bar format were made. ...