Structural and electrochemical properties of LiCoO2 prepared by combustion synthesis

LiCoO2 powders were prepared by combustion synthesis, using metallic nitrates as the oxidant and metal sources and urea as fuel. A small amount of the LiCoO2 phase was obtained directly from the combustion reaction, however, a heat treatment was necessary for the phase crystallization. The heat treatment was performed at the temperature range from 400 up to 700 degreesC for 12 h. The powders were characterized by X-ray diffraction (XRD), X ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and specific surface area values were obtained by BET isotherms. Composite electrodes were prepared using a mixture of LiCoO2, carbon black and poly(vinylidene fluoride) (PVDF) in the 85:10:5% w/w ratio. The electrochemical behavior of these composites was evaluated in ethylene carbonate/dimethylcarbonate solution, using lithium perchlorate as supporting electrolyte. Cyclic voltammograms showed one reversible redox process at 4.0/3.85 V and one irreversible redox process at 3.3 V for the LiCoO2 obtained after a post-heat treatment at 400 and 500 degreesC.Raman spectroscopy showed the possible presence of LiCoO2 with cubic structure for the material obtained at 400 and 500 degreesC. This result is in agreement with X-ray data with structural refinement for the LiCoO2 powders obtained at different temperatures using the Rietveld method. Data from this method showed the coexistence of cubic LiCoO2 (spinel) and rhombohedral (layered) structures when LiCoO2 was obtained at lower temperatures (400 and 500 degreesC). The single rhombohedral structure for LiCoO2 was obtained after post-heat treatment at 600 degreesC. The maximum energy capacity in the first discharge was 136 mA g(-1) for the composite electrode based on LiCoO2 obtained after heat treatment at 700 degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Anelastic characterization and superconducting properties of RuSr2GdCu2O8+delta

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evidence for the monoclinic-tetragonal phase coexistence in Pb(Zr(0.53)Ti(0.47))O(3) thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of Different Solvent Ratios (Water/Ethylene Glycol) on the Growth Process of CaMoO4 Crystals and Their Optical Properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of thermal treatment under oxygen atmosphere on the superconducting properties of RuSr2GdCu2O8

The discovery of the spatial uniform coexistence of superconductivity and ferromagnetism in rutheno-cuprates, RuSr2GdCu2O8 (Ru-1212), has spurred an extraordinary development in the study of the competition between magnetism and superconductivity. However, several points of their preparation process and characterization that determine their superconductive behavior are still obscure. The improvement of sample preparation conditions involves some thermal treatments in inert atmosphere. The first treatment results in the immediate formation of Sr2GdRuO 6. Using the CuO composition as a precursor, we produced Ru-1212. To turn it metallic and superconductor, besides the previous treatment, a final sinterization is carried out in oxygen flow for several days. Three Ru-1212 samples were produced by varying the last sinterization time (two, four, and six days under oxygen flow). Through measurements of x-ray diffraction, scanning electron microscopy, differential thermal analysis, magnetic susceptibility and mechanical spectroscopy, it was studied the influence of the treatments under oxygen atmosphere on the structural and superconducting properties of the material.

Anelastic characterization and superconducting properties of RuSr2GdCu2O8+δ

Since the discovery of the high Tc superconductors, many researches have been carried out on the different properties of these materials, especially on the transition temperature into the superconducting state. The rutheno-cuprates belong to a new class of composites, which were synthesized for the first time by Bauernfeind in 1995. Bernhard and collaborators discovered, in 1999, the coexistence of the ferromagnetism and the superconductivity in this phase, which is known as antagonistic phenomenon in the electromagnetism due to spin-charge interactions established in these states. However, the physical nature of the superconducting and magnetic states is still very obscure. The non-stoichiometric (interstitial) oxygen is considered as a possible cause for the non-uniformity of the sample properties. In this paper, results of mechanical spectroscopy in Ru-1212 samples are presented showing complex anelastic spectra, which were attributed to the mobility of the interstitial oxygen atoms in the Ru-1212 lattice.

Thickness dependence of structure and piezoelectric properties at nanoscale of polycrystalline PZT thin films

Lead zirconate titanate Pb(Zr 0.50Ti 0.50)O 3 (PZT) thin films were deposited by a polymeric chemical method on Pt(111)/Ti/SiO2/Si substrates to understand the mechanisms of phase transformations and the effect of film thickness on the structure, dielectric and piezoelectric properties in these films. PZT films pyrolyzed at temperatures higher than 350 °C present a coexistence of pyrochlore and perovskite phases, while only perovskite phase grows in films pyrolyzed at temperatures lower than 300 °C. For pyrochlore-free PZT thin films, a small (100) orientation tendency near the film-substrate interface was observed. Finally, we demonstrate the existence of a self-polarization effect in the studied PZT thin films. Results suggest that Schottky barriers and/or mechanical coupling near the filmsubstrate interface are not primarily responsible for the observed self-polarization effect in our films. © 2012 IEEE.

Thickness dependence of structure and piezoelectric properties at nanoscale of polycrystalline lead zirconate titanate thin films

Lead zirconate titanate Pb(Zr0.50Ti0.50)O3 (PZT) thin films were deposited by a polymeric chemical method on Pt(111)/Ti/SiO2/Si substrates to understand the mechanisms of phase transformations and the effect of film thickness on the structure, dielectric, and piezoelectric properties in these films. PZT films pyrolyzed at temperatures higher than 350 °C present a coexistence of pyrochlore and perovskite phases, while only perovskite phase grows in films pyrolyzed at temperatures lower than 300 °C. For pyrochlore-free PZT thin films, a small (100)-orientation tendency near the film-substrate interface was observed. Finally, we demonstrate the existence of a self-polarization effect in the studied PZT thin films. The increase of self-polarization with the film thickness increasing from 200 nm to 710 nm suggests that Schottky barriers and/or mechanical coupling near the film-substrate interface are not primarily responsible for the observed self-polarization effect in our films. © 2013 AIP Publishing LLC.

Physical properties of self-polarized PZT thin films at compositions around the morphotropic phase boundary

The physical properties of self-polarized PbZr1-xTixO3 thin films with no preferential orientation in a range of compositions 0.46 <= x <= 0.50 were investigated. Structural analysis revealed the coexistence of monoclinic-tetragonal and monoclinic-rhombohedral phases at compositions 0.46 <= x <= 0.49, where the monoclinic phase was in the majority and both the tetragonal and the rhombohedral phases in the minority. The dielectric permittivity (epsilon'= 447) reached its maximum at around composition x = 0.48. Asymmetries in the macroscopic and local hysteresis loops confirmed the existence of the self-polarization effect in the studied films.