Bacterial and chemical leaching of chalcopyrite concentrates as affected by the redox potential and ferric/ferrous iron ratio at 22 degrees C

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of Na-chloride on the bioleaching of a chalcopyrite concentrate in shake flasks and stirred tank bioreactors

Oxidative dissolution of chalcopyrite at ambient temperatures is generally slow and subject to passivation, posing a major challenge for developing bioleaching applications for this recalcitrant mineral. Chloride is known to enhance the chemical leaching of chalcopyrite, but much of this effect has been demonstrated at elevated temperatures. This study was undertaken to test whether 100-200 mM Na-chloride enhances the chemical and bacterial leaching of chalcopyrite in shake flasks and stirred tank bioreactor conditions at mesophilic temperatures. Acidithiobacillus ferrooxidans, Acidithiobacillus thiooxidans and abiotic controls were employed for the leaching experiments. Addition of Na-chloride to the bioleaching suspension inhibited the formation of secondary phases from chalcopyrite and decreased the Fe(III) precipitation. Neither elemental S nor secondary Cu-sulfides were detected in solid residues by X-ray diffraction. Chalcopyrite leaching was enhanced when the solution contained bacteria, ferrous iron and Na-chloride under low redox potential (< 450 mV) conditions. Scanning electron micrographs and energy-dispersive analysis of X-rays revealed the presence of precipitates that were identified as brushite and jarosites in solid residues. Minor amounts of gypsum may also have been present. Electrochemical analysis of solid residues was in concurrence of the differential effects between chemical controls, chloride ions, and bacteria. Electrochemical impedance spectroscopy was used to characterize interfacial changes on chalcopyrite surface caused by different bioleaching conditions. In abiotic controls, the impedance signal stabilized after 28 days, indicating the lack of changes on mineral surface thereafter, but with more resistive behavior than chalcopyrite itself. For bioleached samples, the signal suggested some capacitive response with time owing to the formation of less conductive precipitates. At Bode-phase angle plots (middle frequency), a new time constant was observed that was associated with the formation of jarosite, possibly also with minor amount or elemental S, although this intermediate could not be verified by XRD. Real impedance vs. frequency plots indicated that the bioleaching continued to modify the chalcopyrite/solution interface even after 42 days. © 2013 The Authors.

The mechanism of 234U 238U activity ratio enhancement in karstic limestone groundwater

Experimental etch/leach of Carboniferous Limestone gravels on a laboratory time-scale has demonstrated that 234U 238U activity ratios (AR's) greater than the radiochemical equilibrium value may be generated on short time-scales. The molar U/Ca and Mg/Ca ratios show that both U and Mg are leached preferentially relative to Ca whereas the molar U/Mg ratio is only slightly greater than that of the rock matrix. The generation of enhanced AR's is attributed to a two-stage process in which the limestone surface is dissolved by zero-order etch and silicate minerals so released are subjected to first-order chemical leach of U and Mg. The implications of these results for the production of enhanced AR's in Carboniferous Limestone groundwater are discussed. It is suggested that chemical leaching or exchange of U between groundwater and its particulate load or at the aquifer fluid-solid interface is an important mechanism controlling AR changes as groundwater migrates beyond a redox boundary. AR's for dissolved U in groundwater are more probably related to chemical equilibria than to groundwater age. © 1993.

Chemical properties of soils treated with biological sludge from gelatin industry

O impacto dos resíduos orgânicos agroindustriais no ambiente pode ser reduzido com o seu uso agrícola. do ponto de vista da fertilidade do solo, o que se deseja com a aplicação dos resíduos é aumentar o teor de matéria orgânica e fornecer nutrientes para as plantas. Neste trabalho, objetivou-se avaliar o efeito do lodo biológico de indústria de gelatina em atributos químicos de dois Argissolos Vermelho-Amarelos (PVA-arenoso e PVA-textura média) e de um Latossolo Vermelho (LV-argiloso). O experimento foi conduzido por 120 dias em laboratório, em delineamento inteiramente casualizado e esquema fatorial combinando os três solos e seis doses de lodo (0, 100, 200, 300, 400 e 500 m³ ha-1), com três repetições. A aplicação de até 500 m³ ha-1 de lodo diminui a acidez do solo e aumenta a CTC efetiva e a disponibilidade de N, Ca, Mg e P, sem ultrapassar o limite de tolerância para Na. O aumento do teor de bases, maior do que o da CTC efetiva, indica que a maior parte dos cátions adicionados pelo lodo permanece em solução e pode ser perdida por lixiviação.

New compositions of fluoroindate glasses with higher chemical resistance

In this paper, glasses in the systems In-Ba-Mg and In-Ba-Zn-Sr-Mg were water leachead at 80ºC showing surface degradation after 72 hours of leaching. The extent of such degradation is determined by the solubility and the concentration of the elemental fluorides that constitute the glasses. The formation of a layer of crystallized phases on the surface of the samples was observed. Small weight losses were registered and the absence of water on the glass matrix after the attack suggested that the use of MgF2 in the systems studied can lead to better results against moisture corrosion when compared to other fluoride glasses such as the fluorozirconates.

Biological leaching of Mn, Al, Zn, Cu and Ti in an anaerobic sewage sludge effectuated by Thiobacillus ferrooxidans and its effect on metal partitioning

The chemical fractionation and bioleaching of Mn, At, Zn, Cu and Ti in municipal sewage sludge were investigated using Thiobacillus ferrooxidans as leaching microorganism. As a result of the bacterial activity, ORP increase and pH reduction were observed. Metal solubilization was accomplished only in experimental systems supplemented with energy source (Fe(II)). The solubilization efficiency approached similar to80% for Mn and Zn, 24% for Cu, 10% for At and 0.2% for Ti. The chemical fractionation of Mn, At, Zn, Cu and Ti was investigated using a five-step sequential extraction procedure employing KNO3. KF, Na4P2O7, EDTA and HNO3. The results show that the bioleaching process affected the partitioning of Mn and Zn, increasing its percentage of elution in the KNO3 fraction while reducing it in the KF, Na4P2O7 and EDTA fractions. No significant effect was detected on the partitioning of Cu and Al. However, quantitatively the metals Mn, Zn, Cu and At were extracted with higher efficiency after the bacterial activity. Titanium was unaffected by the bioleaching process in both qualitative and quantitative aspects. (C) 2002 Elsevier B.V. Ltd. All rights reserved.

Leaching of nitrate and ammonium from cover crop straws as affected by rainfall

Nitrogen (N) mineralization dynamics in no-till systems is affected, among other factors, by N amount and quality in the mulch and by climatic conditions. Leaching of NO3-N and NH4-N from six plant species used as soil cover crops in tropical environments were evaluated when the straw was submitted to rainfall after chemical desiccation. Millet (Pennisetum glaucum), guinea sorghum (Sorghum vulgare), black oat (Avena strigosa), triticale (Triticum secale), Indian hemp (Crotalaria juncea), and brachiaria (Brachiaria decumbens) were grown in a greenhouse, in Botucatu-SP, Brazil. Forty-five days after emergence, the plants were cut at the root collar, oven-dried, and submitted to simulated rainfalls of 4.4, 8.7, 17.04, 34.9, and 69.8 mm, considering an amount of straw equivalent to 8 t ha(-1) of dry matter. The amounts of N-NO3- extracted from the straw by rainwater were very small. However, accumulated rainfall around 70 mm caused ammonium leaching ranging from 2.5 to 9.5kg ha(-1), depending on the species. Plant residues of triticale and black oat (grasses) and Indian hemp (legume) showed high N leaching intensity with the first rains after chemical desiccation. The amount of N leached from straw was highly correlated with N tissue content.

Leaching of Ni and Cu from mine wastes (tailings and slags) using acid solutions and A. ferrooxidans

The objective of this work is to evaluate the acidic and biological leaching of tailings containing Ni/Cu from a flotation and smelting plant. Acidithiobacillus ferrooxidans, strain LR, was used for bioleaching at pH 1.8 and chemical controls were run parallel to that. The acidic leaching was done within 48 hours at pH 0.5 and 1.0. In the slag inoculated flasks the redox potential was high (600 mV), thus indicating oxidative bacterial activity, however, the obtained results after 15 days showed only around 13% Ni and 8% Cu extractions, which were not different to those of the controls. For the flotation tailings bioleaching extractions were approximately 45% for Ni and 16% for Cu while differing figures were obtained for the chemical controls. These were 30% and 12% respectively. Here we could observe that the presence of bacterial activity led to a higher solubility of Ni. Acid leaching of slag showed higher nickel and copper extractions: 56% and 24% respectively at pH 0.5 and 21% and 11% at pH 1.0. However, the acid consumption was 320 and 150 Kg/ton of slag, respectively, both much higher than in bacterial assays. These results indicated that Ni and Cu solubilization from the slag is acid dependent no matter the redox potential or ferric iron concentration of the leaching solution. For flotation tailings, acid treatment showed extractions of 23% for Ni and 16% for copper at pH 0.5 and 22% and 28%, respectively at pH 1.0. The acid consumption was also higher: 220 and 120 Kg/ton, at pH 0.5 and 1.0, respectively. Based on own findings we could observe that acid leaching is found to be more effective for slag, though the acid consumption is much higher, while for the flotation tailings, bacterial leaching seems to be the best alternative. © (2009) Trans Tech Publications.

Chemical changes in an oxisol treated with pyroligneous acid