Effects of different treatments on purity of silica from soluble sodium silicate

Noncrystalline silica was obtained with low iron, sodium, and nitrate ions concentrations from soluble sodium silicate (water glass) and nitric acid solution. Extractions with nitric acid solution and/or deionized water and/or dialysis were carried out to eliminate soluble metal ions. Products were dried in a microwave oven and characterized by chemical analysis, XRD, and IR. Dialysis seems to be the best treatment for the elimination of sodium and nitrate ions. Silica purified by nitric acid and water extractions followed by dialysis yields the purest silica sample.

Field-dependent conductivity at low electric fields in pressed pellets of doped poly (3-methylthiophene): evidence of charge-density wave depinning

Field-dependent conductivity at low electric fields was observed from low to room temperature in pressed pellets of doped poly(3-methylthiophene). The room temperature data showed good agreement with Bardeen's theory of charge-density wave depinning and the values of the parameters obtained are consistent with a strong electron-phonon interaction as expected for quasi-one dimensional systems. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Spectroscopic and thermal characterization in poly(p-phenylene vinylene)/sol-gel silica sample

The absorption and luminescence spectra for the poly(p-phenylene vinylene)/sol-gel silica with different thermal treatments were measured. A considerable increase in the luminescence was observed for the polymer introduced into SiO2 matrix with thermal treatment at 120 degreesC. The thermal diffusivity of these samples was measured using the thermal lens technique, and the obtained value 3.3 x 10(-5) cm(2)/s (sample treated at 37 degreesC) is practically independent of the thermal treatment (37-150 degreesC). (C) 2003 Elsevier B.V. All rights reserved.

Macrobenthic intertidal communities from wave to tide dominated beach environments. A case study in two Brazilian beaches

Modification showed by intertidal macrofaunal communities between two nearby sites that change from a wave to a tide dominated beach environment, was analyzed on the present study. At each site, eleven intertidal sampling stations were distributed along a transect, from the drift line to the spring low tide water level. Four macrofaunal samples one meter long-shore spaced were collected at, each station with an iron core of 0.05 m(2) surface area, taken to a depth of 20 cm. Major,differences on sediments between sites were the offshore decrease of mean particle size diameter and increase of kurtosis and water content at the tide dominated site. KIDS ordination showed major similarities between the lowest stations of this site, that represents the dissipative low tide-terrace portion of the beach. Two lower station of the wave dominated site presented similarities with this group. The other stations of the tide-dominated site, that represents the reflective high tide beach portion, grouped distant from the former. (canonical Correspondence Analysis (CCA) showed a similar spatial distribution of stations, suggesting the importance of environmental factors on the explanation of species distribution patterns. Sediment water content and water table depth, with the highest inertia value, seems to be the principal physical factor. Increase on water content affects the macrofaunal distribution by the expansion of typical infralitoral species, as was the case of Bathyporeiapus ruffoi, on the dissipative low tide terrace beach portion. A disrupted distribution with the lost of a gradate zonation along a physical gradient is one of the major modification presented by macrobenthic communities on the transition from a wave to a tide dominated beach environment.

Silica-PEG hybrid ormolytes: structure and properties

The effect of lithium salt doping on the structure and ionic conduction properties of silica-polyethyleneglycol composites is reported. These materials, so called ormolytes (organically modified electrolytes), were obtained by the sol-gel process. They have chemical stability due to the covalent bonds between the inorganic (silica) and organic (polymer) phase. The structure of these hybrid materials was investigated by small-angle X-ray scattering (SAXS) as a function of lithium concentration [O]/[Li] (O being the oxygens of the ether type). The spectra have a well-defined peak attributed to the existence of a liquid-like spatial correlation of silica clusters. The ionic conductivity was studied by AC impedance spectroscopy and is maximum for [O]/[Li] = 15. This result is consistent with SAXS and thermo-mechanical analysis measurements and is due to the formation of cross-linking between the polymer chains for the larger lithium concentrations. These materials are solid, transparent, flexible and have an ionic conductivity up to 10(-4) S/cm. (C) 1999 Elsevier B.V. B.V. All rights reserved.

GREEN-FUNCTION FOR A SPIN-1/2 PARTICLE IN AN EXTERNAL PLANE-WAVE ELECTROMAGNETIC-FIELD

The Green function for a spin-1/2 charged particle in the presence of an external plane wave electromagnetic field is calculated by algebraic techniques in terms of the free-particle Green function.

Laserlike emission from silica inverse opals infiltrated with rhodamine 6G

Monodisperse latex spheres were obtained by a surfactant free styrene polymerization method and used to obtain colloidal crystals by controlled centrifugation settling. Silica inverse opals were then prepared by using the colloidal crystals as templates and TEOS/ethanol solution. The inverse opals were infiltrated with Rhodamine 6G and laserlike emission was observed at 590 nm under 532 nm pump wavelength. The data show line narrowing of the dye fluorescence and a laser threshold of similar to 0.1 mJ/pulse. Local-field effects and light scattering due to structural defects are the main mechanisms contributing to generation of the laser-action observed. (c) 2005 Elsevier B.V. All rights reserved.

Ultrastructural and immunocytochemical evaluation of the effects of extracorporeal shock wave treatment in the hind limbs of horses with experimentally induced suspensory ligament desmitis

Objective-To evaluate the effects of extracorporeal shock wave therapy (ESWT) on affected ligaments in the hind limbs of horses with experimentally induced suspensory ligament desmitis by use of ultrasonographic, ultrastructural, and immunocytochemical techniques.Animals-10 horses.Procedure-Suspensory ligament desmitis was induced in both hind limbs of each horse by use of 2 collagenase injections (administered 2 weeks apart) in each suspensory ligament. Two weeks after the second injection, the right hind limb of each horse was treated with ESWT (3 treatments at 3-week intervals)- the left hind limb was not treated (control limb). Periodically during the study, the healing process was monitored ultrasonographically and the proportions of ligaments affected with lesions were assessed. Four weeks after the last ESWT treatment, biopsy specimens were collected from all ligaments for ultrastructural evaluation and immunocytochemical analysis of transforming growth factor beta-1.Results-The difference in the proportion of the lesion-affected ligament between ESWT-treated and control limbs was significant (P < 0.05) from 3 weeks after the second ESWT treatment to the end of the study. Compared with control ligaments, ESWT-treated ligaments had more small, newly formed collagen fibrils and greater expression of transforming growth factor beta-1 4 weeks after the last ESWT treatment was administered.Conclusions and Clinical Relevance-Results have indicated that ESWT appears to facilitate the healing process in horses with experimentally induced hind limb suspensory ligament desmitis.

Adsorption of chromium(VI) by titanium(IV) oxide coated on a silica gel surface

Titanium(IV) oxide, coated on the surface of silica gel (surface area, 308 m2 g-1; amount of Ti(IV) per gram of modified silica gel, 1.8 x 10(-3) mol), was used to adsorb CrO4(2-) ions from acidic solutions. The exchange capacity increased at lower pH values and was affected to some extent by the acid used. The material was used to preconcentrate Cr(VI) from 0.5 ppm solutions of chromate very efficiently and virtually 100% recovery was achieved in every instance.

A NOVEL SYNTHETIC ROUTE FOR SUPPORTING RUTHENIUM COMPLEXES ON FUNCTIONALIZED SILICA-GEL

The immobilization of the ruthenium moiety Ru(NH3)4SO3 by reaction of trans-[Ru(NH3)4SO2(H2O)]2+ with silica gel functionalized with 3-(1-imidazolyl)propyl groups is reported. A 60% surface coverage was obtained in the proportion of the resulting material [=Si(CH2)3imN-Ru(NH3)4SO3]. The anchored Ru(II) complex was characterized and its reactivity investigated. Derivatives of CO, pyrazine, and isonicotinamide have been prepared and characterized by electronic and vibrational spectroscopies, as well as by chemical means. The [=Si(CH2)3imN-Ru(NH3)4SO4]Cl, obtained through oxidation of the corresponding ruthenium(II) sulfite species, has been characterized and the aquo and the oxalate derivative have been synthesized.

SILICA MORPHOLOGY CHARACTERIZED BY SEM - THE EFFECTS OF THE SOLVENT TREATMENT AND THE DRYING PROCESS

Scanning electron microscopy (SEM) was used to investigated the effects of volatile solvents (such as water, propanone, ethanol, methanol or ethyl ether), treatment and drying processes, microwave ovens, drying ovens, and vacuum desiccators or freeze driers, on silica morphology. Silica gel was obtained from diluted sodium silicate (1:5 w/w SiO2:H2O). The results showed that the drying process based on freeze drying is more efficient for structural conservation of the precipitate. Treatment with volatile solvents does not change the shape of the aggregates, but has an important role in the determination of aggregate surface roughness.

NMR study of ion-conducting organic-inorganic nanocomposites poly(ethylene glycol) - Silica - LiClO4

Hybrid organic-inorganic ionic conductors, also called ormolytes, were obtained by dissolution of LiClO4 into silica/poly(ethylene glycol) matrices. Solid-state nuclear magnetic resonance (NMR) was used to probe the inorganic phase structure (Si-29) and the effects of the temperature and composition on the dynamic behavior of the ionic species (Li-7) and the polymer chains (H-1 and C-13). The NMR results between -100 and +90 degrees C show a strong correlation with ionic conductivity and differential scanning calorimetry experiments. The results also demonstrate that the cation mobility is assisted by segmental motion of the polymer, which is in agreement with the results previously reported for pure poly(ethylene oxide), PEG, electrolytes.

Sol-gel Er-doped SiO(2)-HfO(2) planar waveguides: A viable system for 1.5 mu m application

70SiO(2)-30HfO(2) planar waveguides, doped with Er(3+) concentrations ranging from 0.3 to 1 mol %, were prepared by sol-gel route, using dip-coating deposition on silica glass substrates. The waveguides show high densification degree, effective intermingling of the two components of the film, and uniform surface morphology. Propagation losses of about 1 dB/cm were measured at 632.8 nm. When pumped with 987 or 514.5 nm continuous-wave laser light, the waveguides show the (4)I(13/2)-->(4)I(15/2) emission band with a bandwidth of 48 nm. The spectral features are found independent both on erbium content and excitation wavelength. The (4)I(13/2) level decay curves presented a single-exponential profile, with a lifetime between 2.9 and 5.0 ms, depending on the erbium concentration. (C) 2002 American Institute of Physics.

Characterization and catalytic activity of 2,6-dichlorophenyl substituted iron(III) porphyrin supported on silica gel and imidazole propyl gel

In this work we have made use of the study of the interaction between Fe(TDCPP)(+) and the axial ligands OH- and imidazole in order to help characterize the heterogenized catalysts Fe(TDCPP)SG and Fe(TDCPP)IPG through UV-VIS and EPR spectroscopies and thus, better understand their different catalytic activity in the oxidation of cyclohexane by PhIO. We have found out that in Fe(TDCPP)SG (containing 1.2 X 10(-6) mol Fe(TDCPP)(+)/g of support), the FeP bis-coordinates to silica gel through Fe-O coordination and it is high-spin (FeP)-P-III species. In Fe(TDCPP)IPG 1 (containing 1.1 X 10(-6) mol Fe(TDCPP)(+) and 2.2 X 10(-4) mol imidazole/g of support), the FeP is bis-ligated to imidazole propyl gel through Fe-imidazole coordination and using NO as a paramagnetic probe, we present evidence that Fe(TDCPP)(+) is present as a mixture of low-spin (FeP)-P-III and (FeP)-P-II species. This catalyst led to a relative low yield of cyclohexanol (25%) because the bis-coordination of the (FeP)-P-III to the support partially blocks the reaction between Fe(TDCPP)(+) and PhIO, thus leading to the formation of only a small amount of the active species Fe-IV(OP+, while the (FeP)-P-II species do not react with the oxygen donor. Increasing the amount of Fe(TDCPP)(+) and decreasing the amount of imidazole in the support led to the obtention of high-spin (FeP)-P-III EPR signals in the spectra of Fe(TDCPP)IPG 5 (containing 4.4 X 10(-6) mol Fe(TDCPP)(+) and 2.2 X 10(-5) mol imidazole/g of IPG), together with low-spin (FeP)-P-III species. This latter catalyst led to better cyclohexanol yields (67%) than Fe(TDCPP)IPG 1. Fe(TDCPP)IPG 5 was further used in a study of the optimization of its catalytic activity and in recycling experiments in the optimized conditions. Recycling oxidation reactions of Fe(TDCPP)IPG 5 led to a total turnover number of 201 and total cyclohexanol yield of 201%, which could not be attained with Fe(TDCPP)Cl in homogeneous solution (turnover = 96) due to the difficulty in recovering and reusing it.

Infrared-to-visible CW frequency upconversion in erbium activated silica-hafnia waveguides prepared by sol-gel route

70SiO(2)-30HfO(2) mol% planar waveguides, doped with Er3+ with concentrations ranging from 0.3 to 2 mol% were prepared by sol-gel route, using dip-coating deposition on vitreous-SiO2 substrates. Infrared-to-visible upconversion emission, upon excitation at 980 nm, has been observed for all the samples. The upconversion results in green, red and blue emissions. The investigation of the upconversion dynamic as a function of the Er3+ concentration and excitation power, show that processes such as excited state absorption and energy transfer upconversion are effective. (C) 2003 Elsevier B.V. All rights reserved.