Influence of storage times on bond strength of resin cements to root canal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

A comparison of microhardness of indirect composite restorative materials

The purpose of this study was to compare the microhardness of four indirect composite resins. Forty cylindrical samples were prepared according to the manufacturer s recommendations using a Teflon mold. Ten specimens were produced from each tested material, constituting four groups (n=10) as follows: G1 - Artglass; G2 - Sinfony; G3 - Solidex; G4 - Targis. Microhardness was determined by the Vickers indentation technique with a load of 300g for 10 seconds. Four indentations were made on each sample, determining the mean microhardness values for each specimen. Descriptive statistics data for the experimental conditions were: G1 - Artglass (mean ±standard deviation: 55.26 ± 1.15HVN; median: 52.6); G2 - Sinfony (31.22 ± 0.65HVN; 31.30); G3 - Solidex (52.25 ± 1.55HVN; 52.60); G4 - Targis (72.14 ± 2.82HVN; 73.30). An exploratory data analysis was performed to determine the most appropriate statistical test through: (I) Levene's for homogeneity of variances; (II) ANOVA on ranks (Kruskal-Wallis); (III) Dunn's multiple comparison test (0.05). Targis presented the highest microhardness values while Sinfony presented the lowest. Artglass and Solidex were found as intermediate materials. These results indicate that distinct mechanical properties may be observed at specific materials. The composition of each material as well as variations on polymerization methods are possibly responsibles for the difference found in microhardness. Therefore, indirect composite resin materials that guarantee both good esthetics and adequate mechanical properties may be considered as substitutes of natural teeth.

Composite resin susceptibility to red wine staining after water sorption

Color stability of restorative materials is essential for longevity of esthetic composite restoration over time. The aim of this investigation was assess the effect of prior water immersion on the color stability of a composite resin to red wine staining. Seventy disccshaped specimens (6mm x 1.5mm) were carried out and randomized in 7 groups (n = 10), according to distilled water immersion time at 0 (control), 24, 48, 72,120,192, and 240 h. Baseline color was measured according to the ciel*a*b* system using a reflection spectrophotometer(uvc2450, shimadzu).After that, the specimens were storage in red wine for 7 days. Color difference (∆e) after aging was calculated based on the color coordinates before(baseline) and after storage period.Data were subjected to onecway anova(alpha=0.05).The different times of immersion in.Water before to the red wine storage showed similar behavior on the color stability, without statistical difference compared to control group, immersed directly in the wine(p=0.7057).The previous water uptake of composite resin evaluated did not decrease the susceptibility to red wine staining.