Design, manufacturing, and testing of a Nb3Sn coil employing Ti alloy as structural material

We describe the design, manufacturing, and testing results of a Nb3Sn superconducting coil in which TiAIV alloys were used instead of stainless steel to reduce the magnetization contribution caused by the heat treatment for the A-15 Nb-3 Sn phase formation that affects the magnetic field homogeneity. Prior to the coil manufacturing several structural materials were studied and evaluated in terms of their mechanical and magnetic properties in as-worked, welded, and heat-treated conditions. The manufacturing process employed the wind-and-react technique followed by vacuum-pressure impregnation(VPI) at 1 MPa atm. The critical steps of the manufacturing process, besides the heat treatment and impregnation, are the wire splicing and joint manufacturing in which copper posts supported by Si3N4 ceramic were used. The coil was tested with and without a background NbTi coil and the results have shown performance exceeding the design quench current confirming the successful coil construction.

Electrochemical impedance spectroscopy characterization of passive film formed on implant Ti-6Al-7Nb alloy in Hank's solution

The influence of potential on electrochemical behavior of Ti-6Al-7Nb alloy under simulate physiological conditions was investigated by electrochemical impedance spectroscopy (EIS). The experimental results were compared with those obtained by potentiodynamic polarization curves. All measurements were carried out in Hank's aerated solution at 25degreesC, at pH 7.8 and at different potentials (corrosion potential, 0 mV(SCE), 1000 mV(SCE), and 2000 mV(SCE)). The EIS spectra exhibited a two-step or a two-time constant system, suggesting the formation of a two-layer oxide film on the metal surface. The high corrosion resistance, displayed by this alloy in electrochemical polarization tests, is due to the dense inner layer, while its osseointegration ability can be ascribed to the presence of the outer porous layer. (C) 2004 Kluwer Academic Publishers.

Gamma phases in Cu-Al alloys and the influence of a square shaped phase in the electrochemical behavior of a Cu-13.6wt% Al alloy

The electrochemical behavior of Cu-xAl alloys, with 11 wt%less than or equal to x less than or equal to 15wt%, in 0.5 M H2SO4 was studied by means of open-circuit potential decay measurements, quasi-stationary and fast cyclic voltammetry, and electrochemical impedance spectroscopy. Some of the alloys (x less than or equal to 14%), when quenched formed martensitic structures. Alloys with greater than or equal to 13% showed a little square-shaped phase when quenched from temperatures around 800 degrees C. It was observed that in sulfuric medium, these formations were dealuminized differently than the martensitic phase. The values of the rest potentials are more influenced by the heat treatment rather than by the alloy composition. An anodic Tafel slope of ca. 60 mV/decade was observed for all the alloys, independently of the heat treatment. This is explained in terms of a competition between two processes: copper oxidation and copper(I) deproportionation. In the cyclic voltammetric experiments it was observed an anodic current peak, related with copper oxidation with a possible formation of some interfacial species, and a cathodic current peak during the reverse potential scan, associated with the reduction of soluble species and/or of the film. The AC Impedance data were interpreted in terms of electric equivalent circuits.

Thermogravimetry (TG) applied to the study of the reaction of mercury with platinum-rhodium alloy

Thermogravimetry (TG) energy dispersive X-ray microanalysis (EDX), scanning electron microscopy (SEM), mapping surface, X-ray diffraction (XRD), inductively coupled plasma emission spectroscopy and atomic spectroscopy with cold vapor generation have been used to study the reaction of mercury with platinum-rhodium (Pt-Rh) alloy. The results suggest that, the electrodeposited Hg film reacts with Pt-Rh to form intermetallic compounds of different stability, when heated indicated by at least four weight loss steps. Intermetallic compounds as PtHg4 and PtHg2 was characterized by XRD. These intermetallic compound are the main product presents on the surface of the samples after remotion of the bulk mercury via thermal desorption techniques. (C) 2002 Elsevier B.V. B.V. All rights reserved.

SURFACE EFFECTS IN THE HYDROGEN EVOLUTION REACTION ON NI-ZN ALLOY ELECTRODES IN ALKALINE-SOLUTIONS

Hydrogen evolution reaction was studied on Ni-Zn (25% of Ni before leaching) in 1 M NaOH at 25 degrees C. These electrodes were characterized by very low Tafel slopes of 67 mV dec(-1). Other techniques used included potential and current pulse, potential relaxation in an open circuit, and ac impedance spectroscopy. Analysis of the experimental results led to the conclusion that hydrogen adsorption in the surface layers was responsible for the observed behavior. Influence of the oxidation of the electrode surface and the addition of poisons, thiourea and cyanides, were also studied. These processes inhibit the hydrogen absorption and restore ''normal'' Tafel slopes. Kinetic parameters of the hydrogen evolution reaction were determined.

Raman phonon modes of zinc blende InxGa1-xN alloy epitaxial layers

Transverse-optical (TO) and longitudinal-optical (LO) phonons of zinc blende InxGa1-xN (0 less than or equal to x less than or equal to 0.31) layers are observed through first-order micro-Raman scattering experiments. The samples are grown by molecular-beam epitaxy on GaAs (001) substrates, and x-ray diffraction measurements are performed to determine the epilayer alloy composition. Both the TO and LO phonons exhibit a one-mode-type behavior, and their frequencies display a linear dependence on the composition. The Raman data reported here are used to predict the A(1) (TO) and E-1 (TO) phonon frequencies of the hexagonal InxGa1-xN alloy. (C) 1999 American Institute of Physics. [S0003-6951(99)01234-6].

Thermal behavior of the Cu-22.55 at.%Al alloy with small Ag additions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Modification of surface properties of Ti-16Si-4B powder alloy by plasma immersion ion implantation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The characterisation of the protective film formed by benzotriazole on the 90/10 copper-nickel alloy surface in H2SO4 media

The nature of the protective film formed by benzotriazole (BTAH) on the surface of the 90/10 CuNi alloy in deaerated 0.5 mol L-1 H2SO4 solution containing Fe(III) ions as oxidant was investigated by weight-loss, calorimetric measurements, and by surface-enhanced Raman spectroscopy (SERS). The SERS measurements show that the protective film is composed by the [Cu(I)BTA](n), polymeric complex and that the BTAH molecules are also adsorbed on the electrode surface. A modification of the BET isotherm for adsorption of gases ill solids is proposed to describe the experimental results obtained from weight-loss experiments that suggest an adsorption in multilayers. Electrochemical studies of copper and nickel in 0.5 mol L-1 H2SO4 in presence and absence of BTAH have also been made as an aid to interpret the results. The calculated adsorption free energy of the cuprous benzotriazolate on the surface of the alloy is in accordance with the value for pure copper. (C) 2007 Elsevier Ltd. All rights reserved.

Influence of Ag addition on the thermal behavior of the Cu-11 mass% Al alloy

In this work the influence of Ag additions on the thermal behavior of the Cu-11 mass% Al alloy was studied using differential scanning calorimetry, in situ X-ray diffractometry and scanning electron microscopy. The results indicated that changes in the heating rate shift the peak attributed to alpha phase formation to higher temperatures, evidencing the diffusive character of this reaction. The activation energy value for the alpha phase formation reaction, obtained from a non-isotherm kinetic model, is close to that corresponding to Cu atoms self diffusion, thus confirming that this reaction is dominated by Cu atoms diffusion through the martensite matrix.

(alpha + gamma(1)) Complex phase formation in the Cu-10 mass% Al-6mass% Ag alloy

In this work the (alpha + gamma(1)) complex phase formation reaction in the Cu-10mass% Al-6mass% Ag alloy was studied using Differential Scanning Calorimetry (DSC), Differential Thermodilatometry (DTD), X-ray diffractometry (XRD), Optical (OM) and Scanning Electron Microscopies (SEM). The results indicated the presence of two different processes, related to a change in the Ag diffusion route from the alpha matrix to the (alpha + gamma(1)) complex phase.