Effects of laser-weld joint opening size on fatigue strength of Ti-6Al-4V structures with several diameters

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Flexural strength and hardness of reline and denture base acrylic resins after different exposure times of microwave disinfection

Objectives: To evaluate the effect of microwave disinfection on the flexural strength and Vickers hardness of 4 autopolymerized resins (Kooliner [K], Tokuso Rebase Fast [T], Ufi Gel Hard [U], and New Truliner [N]) and 1 denture base resin (Lucitone 550 [L]). Method and Materials: For each material, 48 specimens (64 x 10 x 3.3 mm) were made and divided into 6 equal groups (n = 8). In the control group, specimens were untreated. Before testing, specimens were immersed in 200 mL of distilled water and submitted to disinfection for 1 of the following irradiation times: 1, 2, 3, 4, or 5 minutes. The irradiation procedure was performed twice. The flexural strength was determined using a testing machine MTS-810 and measurements of Vickers hardness were made on Micromet 2100. The values were submitted to ANOVA and Tukey's test (P = .05). Results: The K material showed a significant increase (P = .0010) in flexural strength following 5 minutes of disinfection compared to control specimens. The flexural strength mean values of materials T, U, and N were not significantly affected (P > .05) by disinfection. Compared to the control group, the K material showed a significant increase in hardness (P < .001) following disinfection for 3, 4, and 5 minutes. For material U, disinfection for 4 and 5 minutes produced specimens with significantly increased hardness values (P < .001) compared to the control group. For material N, disinfection for 5 minutes resulted in significantly higher hardness values (P < .001) than the control group. Conclusion: Regardless of the irradiation time, the flexural strength and hardness of the materials evaluated were not detrimentally affected by microwave disinfection. (Quintessence Int 2008;39:833-840)

Fatigue strength: effect of welding type and joint design executed in Ti-6Al-4V structures

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of water storage on the shear strength and fatigue limit of the reline resin bond to denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

THE EFFECT of DIFFERENT SURFACE TREATMENTS on THE SHEAR BOND STRENGTH of LUTING CEMENTS TO TITANIUM

Statement of problem. Although titanium presents attractive physical and mechanical properties, there is a need for improving the bond at the titanium/luting cement interface for the longevity of metal ceramic restorations.Purpose. The purpose of this study was to evaluate the effect of surface treatments on the shear bond strength (SBS) of resin-modified glass ionomer and resin cements to commercially pure titanium (CP Ti).Material and methods. Two hundred and forty CP Ti cast disks (9.0 x 3.0 mm) were divided into 8 surface treatment groups (n=30): 1) 50 mu m Al2O3 particles; 2) 120 mu m Al2O3 particles; 3) 250 mu m Al2O3 particles; 4) 50 mu m Al2O3 particles + silane (RelyX Ceramic Primer); 5) 120 mu m Al2O3 particles + silane; 6) 250 mu m Al2O3 particles + silane; 7) 30 mu m silica-modified Al2O3 particles (Cojet Sand) + silane; and 8) 120 mu m Al2O3 particles, followed by 110 mu m silica-modified Al2O3 particles (Rocatec). The luting cements 1) RelyX Luting 2; 2) RelyX ARC; or 3) RelyX U100 were applied to the treated CP Ti surfaces (n=10). Shear bond strength (SBS) was tested after thermal cycling (5000 cycles, 5 degrees C to 55 degrees C). Data were analyzed by 2-way analysis of variance (ANOVA) and the Tukey HSD post hoc test (alpha=.05). Failure mode was determined with a stereomicroscope (x20).Results. The surface treatments, cements, and their interaction significantly affected the SBS (P<.001). RelyX Luting 2 and RelyX U100 exhibited similar behavior for all surface treatments. For both cements, only the group abraded with 50 mu m Al2O3 particles had lower SBS than the other groups (P<.05). For RelyX ARC, regardless of silane application, abrasion with 50 mu m Al2O3 particles resulted in significantly lower SBS than abrasion with 120 mu m and 250 mu m particles, which exhibited statistically similar SBS values to each other. Rocatec + silane promoted the highest SBS for RelyX ARC. RelyX U100 presented the highest SBS mean values (P<.001). All groups showed a predominance of adhesive failure mode.Conclusions. The adhesive capability of RelyX Luting 2 and RelyX U100 on the SBS was decisive, while for RelyX ARC, mechanical and chemical factors were more influential. (J Prosthet Dent 2012;108:370-376)

Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fracture strength of flared bovine roots restored with different intraradicular posts

Objective: The aim of this study was to evaluate the fracture strength and failure mode of flared bovine roots restored with different intraradicular posts. Material and Methods: Fifty bovine incisors with similar dimensions were selected and their roots were flared until 1.0 mm of dentin wall remained. Next, the roots were allocated into five groups (n=10): GI-cast metal post-and-core; GII-fiber posts plus accessory fiber posts; GIII-direct anatomic post; GIV-indirect anatomic post and GV-control (specimens without intraradicular post). A polyether impression material was used to simulate the periodontal ligament. After periodontal ligament simulation, the specimens were subjected to a compressive load at a crosshead speed of 0.5 mm/min in a servo-hydraulic testing machine (MTS 810) applied at 135 to the long axis of the tooth until failure. The data (N) were subjected to ANOVA and Tukey's post-hoc test (alpha=0.05). Results: GI and GIV presented higher fracture strength (p<0.05) than GII. GIII presented intermediate values without statistically significant differences (p>0.05) from GI, GII and GIV. Control specimens (GV) produced the lowest fracture strength mean values (p<0.05). Despite obtaining the highest mean value, GI presented 100% of unfavorable failures. GII presented 20% of unfavorable failures. GIII, GIV and GV presented only favorable failures. Conclusions: Although further in vitro and in vivo studies are necessary, the results of this study showed that the use of direct and indirect anatomic posts in flared roots could be an alternative to cast metal post-and-core.

Fracture strength of incisor crowns after intracoronal bleaching with sodium percarbonate

Objectives: To compare the fracture resistance of bovine teeth after intracoronal bleaching with sodium percarbonate (SPC) or sodium perborate (SP) mixed with water or 20% hydrogen peroxide (HP). Materials and methods: Fifty extracted bovine teeth were divided into four experimental groups (G1G4) and one control (n = 10) after endodontic treatment. Following root canal obturation, a glass ionomer barrier was placed at the cementoenamel junction. After that, the pulp chambers were filled with: G1 SP with water; G2 SP with 20% HP; G3 SPC with water; and G4 SPC with 20% HP. No bleaching agent was used in the control group. Coronal access cavities were sealed with glass ionomer and specimens were immersed in artificial saliva. The bleaching agents were replaced after 7 days, and teeth were kept in artificial saliva for an additional 7 days, after which the pastes were removed and the coronal access cavities were restored with glass ionomer. Crowns were subjected to compressive load at a cross head speed of 0.5 mm min-1 applied at 135 degrees to the long axis of the root by an EMIC DL2000 testing machine, until coronal fracture. Data were statistically analysed by anova and Tukey test. Results: No differences in fracture resistance were observed between the experimental groups (P > 0.05). However, all experimental groups presented lower fracture resistance than the control group (P < 0.05). Conclusion: SPC and SP led to equal reduction on fracture resistance of dental crowns, regardless of being mixed with water or 20% HP.

Effect of incorporation of 2-tert-butylaminoethyl methacrylate on flexural strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of surface treatments on the flexural strength of denture base repair

Objective: The purpose of this study was to evaluate the flexural strength of repairs made with autopolymerising acrylic resin after different treatments of joint surfaces.Material and Methods: Fifty rectangular specimens were made with heat-polymerised acrylic resin and 40 were repaired with autopolymerising acrylic resin following joint surface treatments: group 1 (intact specimens), group 2 (chemical treatment: wetting with methyl-methacrylate for 180 s), group 3 (abraded with silicon carbide paper), group 4 (abraded and wetting with methyl-methacrylate for 180 s) and group 5 (without surface treatment). The flexural strength was measured by a three-point bending test using a universal testing machine with a 100 Kgf load cell in the centre of repair at 5 mm/min cross-head speed. All data were analysed using one-way ANOVA and Tukey HSD test for multiple comparisons (p < 0.05).Results: Among repaired specimens, groups 2 and 4 had 66.53 +/- 3.4 and 69.38 +/- 1.8 MPa mean values and were similar. These groups had superior flexural strength than groups 3 and 5 that were similar and had 54.11 +/- 3.4 and 51.24 +/- 2.8 MPa mean values, respectively. Group 1 had a mean value of 108.30 +/- 2.8 MPa being the highest result.Conclusion: It can be concluded that the treatment of the joint surfaces with methyl-methacrylate increases the flexural strength of denture base repairs, although the strength is still lower than that observed for the intact denture base resin. Abrasion with sandpaper was not able to influence the flexural strength of repaired denture bases.

Effect of disinfection by microwave irradiation on the strength of intact and relined denture bases and the water sorption and solubility of denture base and reline materials

This study evaluated the influence of microwave disinfection on the strength of intact and relined denture bases. Water sorption and solubility were also evaluated. A heat-polymerized acrylic resin (Lucitone 550) was used to construct 4-mm-thick (n = 40) and 2-mm-thick (n = 160) denture bases. Denture bases (2mm) were relined with an autopolymerizing resin (Tokuso Rebase Fast, Ufi Gel Hard, Kooliner, or New Truliner). Specimens were divided into four groups (n = 10): without treatment, one or seven cycles of microwave disinfection (650 W for 6 min), and water storage at 37 degrees C for 7 days. Specimens were vertically loaded (5 mm/min) until failure. Disc-shaped specimens (50 min x 0.5 mm) were fabricated (n = 10) to evaluate water sorption and solubility. Data on maximum fracture load (N), deflection (%), and solubility (%) were analyzed by two-way analysis of variance and Student-Newman-Keuls tests (alpha = 0.05). One cycle of microwave disinfection decreased the deflection at fracture and fracture energy of Tokuso Rebase Fast and New Truliner specimens. The strength of denture bases microwaved daily for 7 days was similar to the strength of those immersed in water for 7 days. Microwave disinfection increased the water sorption of all materials and affected the solubility of the reline materials. (C) 2007 Wiley Periodicals, Inc.

Bond strength of adhesive restorations to Er : YAG laser-treated dentin

Background and Objective: evaluate the adhesion of adhesive restorations with and without a base of resin-modified glass-ionomer cement (RMGIC) to dentin irradiated with Er:YAG laser.Study Design/Materials and Methods: Twenty-four human molar teeth were divided into 6 groups (n=4): G1) 37% Phosphoric acid (PA) + Adhesive system (Ad) + Composite resin (CR); G2) RMGIC + CR; G3) Laser (60mJ-5Hz-20s) + PA + Ad + CR; G4) Laser (60 mJ-5 Hz-20 s) + RMGIC + CR; G5) Laser (100mJ-5Hz-20s) + PA + Ad + CR; G6) Laser (100mJ-5Hz-20s) + RMGIC + CR. Teeth were prepared, restored and cut into specimens, according to the treatment proposed and to methodology for microtensile test. Data were submitted to ANOVA and Tukey statistical tests (alpha=5%).Results:. The mean values for adhesion (MPa) and standard deviation (+/- SD) were: G1) 26.30(+/- 4.50), G2) 5.34(+/- 2.87), G3) 21.16(+/- 6.01), G4) 5.22(+/- 1.52), G5) 22.23(+/- 4.98), G6) 5.25(+/- 3.08).Conclusion: the use of Er:YAG laser did not influence on the restorations adhesion.

Influence of Er,Cr: YSGG laser on bond strength of self-adhesive resin cement

The purpose of this study was to investigate the bond strength of fiber post previously laser treated root canals. Forty single-rooted bovine teeth were endodontically treated, randomly and equally divided into two main groups according to the type of pretreatment: G1: 2.5% NaOCl (control group); and G2: Er,Cr:YSGG laser. Each group was further subdivided into 2 groups based on the category of adhesive systems/ luting materials used: a: an etch-and-rinse resin cement (Single Bond/RelyX ARC; 3M ESPE), and b: a self-adhesive resin cement (Rely X Unicem; 3M ESPE). Three 1.5 mm thick slabs were obtained per root and the push-out test was performed at a crosshead speed of 0.5 mm/min until post dislodgement occurred. Data were analyzed by ANOVA and post-hoc Tukey's test at a pre-set alpha of 0.05. Analysis of variance showed no statistically significant difference (p > 0.05) among the groups G1a (25.44 ± 2.35) and G1b (23.62 ± 3.48), G2a (11.77 ± 2.67) and G2b (9.93 ± 3.37). Fractures were observed at the interface between the dentin and the resin in all groups. The Er,Cr:YSGG laser irradiation did not influence on the bond strength of the resin cements and the etch-and-rinse resin cement had better results on bond strength than self-adhesive resin cement.

Microtensile bond strength of different adhesive systems in dentin irradiated with Er : YAG laser

The objective this study was to evaluate in vitro the bond strength of two etch-and-rise and one self-etching adhesive system after dentin irradiation with Er:YAG (erbium: yttrium aluminum garnet) laser using microtensile test. The results revealed that the groups treated with laser Er:YAG presented less tensile bond strength, independently to the adhesive system used. The prompt L-pop adhesive presented less microtensile bond strength compared to the other adhesives evaluated. There was no difference between single bond and excite groups. The adhesive failures were predominant in all the experimental groups. The Er:YAG laser influenced negatively bond strength values of adhesive systems tested in dental substrate.

Bond strength of different endodontic sealers to dentin: push-out test

Objective: The aim of this in vitro study was to evaluate the bond strength of different root canal sealers to dentin. Material and Methods: Forty extracted single-rooted human teeth were examined and the coronal and middle thirds of the canals were prepared with a 1.50 mm post drill (FibreKor Post System, Pentron). The teeth were allocated in two experimental groups, irrigated with 2.5% NaOCl+17% EDTA or saline solution (control group) and instrumented using Race rotary files (FKG) to a size #40 at the working length. Then, the groups were divided into four subgroups and filled with Epiphany sealer (Group 1), EndoREZ (Group 2), AH26 (Group 3) and Grossman's Sealer (Group 4). After 2 weeks of storage in 100% humidity at 37 degrees C, all teeth were sectioned transversally into 2-mm-thick discs. Push-out tests were performed at a cross-head speed of 1 mm/min using a universal testing machine. The maximum load at failure was recorded and expressed in MPa. Results: Means (+/- SD) in root canals irrigated with 2.5% NaOCl and 17% EDTA were: G1 (21.6 +/- 6.0), G2 (15.2 +/- 3.7), G3 (14.6 +/- 4.5) and G4 (11.7 +/- 4.1). Two-way ANOVA and Tukey's test showed the highest bond strength for the Epiphany's group (p < 0.01) when compared to the other tested sealers. Saline solution decreased the values of bond-strength (p < 0.05) for all sealers. Conclusion: Epiphany sealer presented higher bond strength values to dentin in both irrigating protocols, and the use of 2.5% NaOCl and 17% EDTA increased the bond strength values for all sealers.