Ferroelectric properties of mechanically synthesized nanosized barium titanate

Barium titanate ceramics were prepared through mechanochemical synthesis starting from fresh prepared barium oxide and titanium oxide in rutile form. Mixture of oxides was milled in zirconia oxide jar in the planetary ball-mill during 30, 60, 120 and 240 min. Extended time of milling directed to formation of higher amount of barium titanate perovskite phase. Barium titanate with good crystallinity was formed after 240 min. Sintering without pre-calcinations step was performed at 1330 degrees C for 2 hours with heating rate of 10 degrees C/min. The XRD, DSC, IR and TEM analyses were performed. Electric and ferroelectric properties were studied. Very well defined hysteresis loop was obtained.

a-b axis-oriented lanthanum doped Bi4Ti3O12 thin films grown on a TiO2 buffer layer

a-b axis-oriented, lanthanum doped Bi4Ti3O12 (BLT) thin films with a TiO2 rutile buffer layer deposited on Pt/Ti/SiO2/Si substrates were grown by the soft chemical method. Butterfly dielectric behavior has been achieved and can be ascribed to the ferroelectric domain switching. The remanent polarization and the coercive voltage for the film deposited on TiO2 buffer layer were 22.2 mu C/cm(2) and 1.8 V, respectively. Random-oriented BLT films showed a reduction in switching polarization when compared to the a-b axis-oriented films. Due to the excellent physical properties, these films are a promising candidate for use in lead-free applications in ferroelectric devices. (c) 2006 American Institute of Physics.

Ferroelectric state analysis in grain boundary of Na0.85Li0.15NbO3 ceramic

The electric and dielectric properties of the grain boundary of Na0.85Li0.15NbO3 lead-free ferroelectric-semiconductor perovskite were investigated. The impedance spectroscopy was carried out as a function of a thermal cycle. The sodium lithium niobate was synthesized by a chemical route based on the evaporation method. Dense ceramic, relative density of 97%, was prepared at 1423 K for 2 h in air atmosphere. ac measurements were carried out in the frequency range of 5 Hz-13 MHz and from 673 to 1023 K. Theoretical adjust of the impedance data was performed to deriving the electric parameters of the grain boundary. The electric conductivity follows the Arrhenius law, with activation energy values equal to 1.55 and 1.54 eV for heating and cooling cycle, respectively. The nonferroelectric state of the grain boundary and its correlation with symmetry are discussed in the temperature domain. (C) 2003 American Institute of Physics.

Electronic structure of Pb1-xLaxTiO3 ferroelectric materials from Ti 2p and O 1s soft x-ray absorption spectroscopy

The electronic structure of Pb1-xLaxTiO3 (PLT) compounds for x ranging from 0 to 30 at. % of La is investigated by means of soft x-ray absorption near edge structure (XANES) at the Ti L-3,L-2 and O K edges. The greatest modification in the structure of the Ti 2p XANES spectra of the PLT compounds is observed in the region of the high energy peak of the L-3 edge (e(g) states), which exhibits a splitting in the undoped sample. As the amount of lanthanum increases, this splitting becomes less pronounced. This modification is interpreted as a decrease in the degree of disorder of titanium atoms, which is correlated to the substitution of Pb by La atoms. The structural changes observed at the low energy peaks of the O K-edge XANES spectra of the PLT compounds may be interpreted in terms of hybridization between O 2p, Ti 3d, and Pb 6p orbitals. A decrease in the degree of hybridization observed as Pb atoms are replaced by La atoms may be related to the differences in the ferroelectric properties observed between x=0.0 and x=0.30 compounds. (c) 2006 American Institute of Physics.

Synthesis and electrical characterization of CaBi2Nb2O9 thin films deposited on Pt/Ti/SiO2/Si substrates by polymeric precursor method

We report the successful deposition of CaBi2Nb2O9 (CBN) thin films on platinum coated silicon substrates by polymeric precursor method. The CBN thin films exhibited good structural, dielectric and CBN/Pt interface characteristics. The leakage current of the capacitor structure was around 0.15 A cm(-2) at an applied electric field of 30 kV cm(-1). The capacitance-voltage measurements indicated good ferroelectric polarization switching characteristics. The typical measured small signal dielectric constant and the dissipation factor at a frequency of 100 kHz were 90 and 0.053, respectively. The remanent polarization and the drive voltage values were 4.2 C cm(-2) and 1.7 V at an applied voltage of 10 V. No significant fatigue was observed at least up to 10(8) switching cycles. (c) 2005 Elsevier B.V. All rights reserved.

MEASURING HYSTERESIS LOOPS OF FERROELECTRIC POLYMERS USING THE CONSTANT CHARGING CURRENT CORONA TRIODE

A novel method is proposed for measuring the hysteresis loops of ferroelectric polymers. The samples need to have only one electrode and are poled by corona discharge in a constant current corona triode. It is shown how the sample surface potential and the charging current are related to the remanent polarization and coercive field, so that the hysteresis loops can be obtained. An illustrative example is given for samples of beta-PVDF for which the hysteresis cycles were remarkably close to those obtained with the traditional Sawyer-Tower circuit. Values of 80 MV/m and 70 mC/m2 were estimated for the coercive field and remanent polarization, respectively.

Structural and ferroelectric properties of Pb1-xSrxTiO3 thin films

Strontium-modified lead titanate (PST) thin films with composition Pb1-xSrxTiO3 (0.10 < x &LE; 0.60) were grown on Pt/Ti/SiO2/Si substrates using a soft chemical process. The crystallization of the PST thin films was achieved by heat treatment at 600&DEG;C. The structural and microstructural modifications in the films were studied using X-ray diffraction (XRD) and atomic force microscopy, respectively. The XRD study shows that the lattice parameters of polycrystalline PST thin films calculated from X-ray data indicate a decrease in lattice tetragonality with the increase in strontium content in these films. This indicates a gradual change from tetragonal to cubic structure. By atomic force microscopy analysis, the average grain size of the thin films was systematically reduced with the increase in Sr content. The dielectric property of the thin films was found to be strongly dependent on the Sr concentration. With 60 at.% Sr content, a ferroelectric to paraelectric phase transition was observed at room temperature.

Ferroelectric materials with photoluminescent properties

Amorphous LiNbO3 thin films processed by polymeric precursor method exhibited efficient luminescence at room temperature. The films were deposited on silicon substrates and treated at 200degreesC for different times. The photoluminescence emission yield decreases with the increase of the treatment time and disappears for crystalline films. A theoretical-experimental study was performed on amorphous and crystalline materials to understand the influence of the defects on the photoluminescence properties. The theoretical band gap obtained by the difference of energy between the HOMO and LUMO levels is larger for crystalline structure when compared with amorphous material. This result, which is in agreement with experimental band gaps obtained from optical measurements, revealed the emergence of new electronic levels for the amorphous material, which are localized in the wide band gap of the crystalline structure. These new electronic levels may explain the photoluminescence observed at room temperature for LiNbO3 amorphous films.

Preparation of SrBi2Ta2O9 ferroelectric thick films by electrophoretic deposition using aqueous suspensions

SrBi2Ta2O9 ferroelectric thick films were prepared by electrophoretic deposition (EPD). For that, ceramic powders were prepared by chemical method in order to obtain compounds with chemical homogeneity. The polymeric precursor method was used for the synthesis of the SrBi2Ta2O9 powder. The crystallographic structure of the powder was examined by X-ray diffraction, and the surface area was determined by single point BET adsorption. The 0.03 vol% suspension was formed by dispersing the powder in water using two different polymers as dispersants: an ester polyphosphate (C213) and an ammonium polyacrilate (Darvan 821-A). The influence of the different dispersants on the powder surface properties were investigated by zeta potential measurements. The films were deposited on platinum-coated alumina and Pt/Ti/SiO2/Si substrates by electrophoretic deposition using a 4 mA constant current, for 10 min, with two parallel electrodes placed at a separation distance of 3 min in the suspension. Several cycles of deposition-drying of the deposit was carried out until the desired thickness was obtained. After thermal treatment at temperatures ranging from 700 to 1000degreesC, the films were characterized by X-ray diffraction and scanning electron microscopy.

Dielectric properties and microstructure of SrTiO3/BaTiO3 multilayer thin films prepared by a chemical route

Multilayer thin films with perovskite structures were produced by the polymeric precursor method. SrTiO3/BaTiO3 (STO/BTO) multilayers were deposited on Pt(111)/Ti/SiO2/Si(100) substrates by the spin-coating technique and heated in air at 700 degreesC. The microstructure and crystalline phase of the multilayered thin films were examined by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), resolution-high transmission electron microscopy (HRTEM), atomic force microscopy (AFM) and X-ray diffraction. The SrTiO3/BaTiO3 multilayer thin films consisted of grainy structures with an approximate grain size of 60 nm. The multilayered thin films showed a very clear interface between the components. The SrTiO3/BaTiO3 multilayer thin films revealed dielectric constants of approximately 527 and loss tangents of 0.03 at 100 kHz. The dielectric constant calculated for this multilayer film system is the value of the sum of each individual component of the film, i.e. The total value of the sum of each SrTiO3 (STO) and BaTiO3 (BTO) layer. The multilayer SrTiO3/BaTiO3 obtained by the polymeric precursor method, also showed a ferroelectric behavior with a remanent polarization of 2.5 muC/cm(2) and a coercive field of 30 kV/cm. The multilayer films displayed good fatigue characteristics under bipolar stressing after application of 10(10) switching cycles. (C) 2001 Published by Elsevier B.V. B.V. All rights reserved.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Dielectric and fatigue properties of Pb(Zr0.53Ti0.47)O-3 thin films prepared from oxide precursors method

Fatigue is an important problem to be considered if a ferroelectric film is used for non-volatile memory devices. In this phenomena, the remanent polarization and coercive field properties degrades in cycles which increase in hysteresis loops. The reasons have been attributed to different mechanisms such as a large voltage applied on ferroelectric film in every reading process in Ferroelectric Random Access Memory (FeRAM) or memories for digital storage in computer, grain size effects and others. The aim of this work is to investigate the influence of the crystallization kinetics on dielectric and ferroelectric properties of the Pb(Zr0.53Ti0.47)O-3 thin films prepared by an alternative chemical method. Films were crystallized in air on Pt/Ti/SiO2/Si substrates at 700 degrees C for 1 hour, in conventional thermal annealing (CTA), and at 700 degrees C for 1 min and 700 degrees C 5 min, using a rapid thermal annealing (RTA) process. Final films were crack free and presented an average of 750 nm in thickness. Dielectric properties were studied in the frequency range of 100 Hz - 1 MHz. All films showed a dielectric dispersion at low frequency. Ferroelectric properties were measured from hysteresis loops at 10 kHz. The obtained remanent polarization (P-r) and coercive field (E-c) were 3.7 mu C/cm(2) and 71.9 kV/cm respectively for film crystallized by CTA while in films crystallized by RTA these parameters were essentially the same. In the fatigue process, the P, value decreased to 14% from the initial value after 1.3 x 10(9) switching cycles, for film by CTA, while for film crystallized by RTA for 5 min, P, decreased to 47% from initial value after 1.7 x 10(9) switching cycles.

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.

Structure, microstructure, ferroelectric/electromechanical properties and retention characteristics of [Bi1-x Nb (x) ]FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermistor behaviour and electric conduction analysis of Ni-doped niobate ferroelectric: the role of multiple beta parameters