Sol-gel synthesis of titania-alumina catalyst supports

Titanium oxide is a good candidate as new support for hydrotreating (HDT) catalysts, but has the inconvenience of presenting small surface area and poor thermal stability. To overcome these handicaps TiO2-Al2O3 mixed oxides were proposed as catalyst support. Here, the results concerning the preparation, characterization and testing of molybdenum catalyst supported on titania-alumina are presented. The support was prepared by sol-gel route using titanium and aluminum isopropoxides, chelated with acetylacetone (acac) to promote similar hydrolysis ratio for both the alcoxides. The effect of nominal complexing ratios [acac]/[Ti] and of sol aging temperature on the structural features of nanometric particles was analyzed by quasi-elastic light scattering (QELS) and N-2 adsorption isotherm measurements. These characterizations have shown that the addition of acac and the increase of aging temperature favor the full dispersion of primary nanoparticles in mother acid solution. The dried powder presents a monomodal distribution of slit-shaped micropores, formed by irregular packing of platelet primary particles, surface area superior to 200 m(2) g(-1) and mean pore size of about 1 nm. These characteristics of porous texture are preserved after firing at 673 K. The diffraction patterns of sample fired above 973 K show only the presence of anatase crystalline phase. The crystalline structure of the support remained unaltered after molybdenum adsorption, but the surface area and the micropore volume were drastically reduced. (C) 2002 Published by Elsevier B.V. B.V.

Influence of strains and defects on ferroelectric and dielectric properties of thin-film barium-strontium titanates

Pristine, W and Mn 1% doped Ba(0.6)Sr(0.4)TiO(3) epitaxial thin films grown on the LaAlO(3) substrate were deposited by pulsed laser deposition (PLD). Dielectric and ferroelectric properties were determined by the capacitance measurements and X-ray diffraction was used to determine both residual elastic strains and defect-related inhomogeneous strains-by analyzing diffraction line shifts and line broadening, respectively. We found that both elastic and inhomogeneous strains are affected by doping. This strain correlates with the change in Curie-Weiss temperature and can qualitatively explain changes in dielectric loss. To explain the experimental findings, we model the dielectric and ferroelectric properties of interest in the framework of the Landau-Ginzburg-Devonshire thermodynamic theory. As expected, an, elastic-strain contribution due to the epilayer-substrate misfit has an important influence on the free-energy. However, additional terms that correspond to the defect-related inhomogeneous strain had to be introduced to fully explain the measurements.

Bactericidal stainless steel

Coatings are largely used in industries. However the development of new materials with improved properties still feeds a continuous need for performance, cost or endurance, the coatings are obtained by a hybrid material, organic-inorganic, and this polymer is applied on metallic, ceramic and glassy surfaces. The material generated in-situ on the desired surface has a nanometric structure. Results in abrasion loss (according ASTM standards) showed that the coatings improve the abrasion resistance of stainless steel by 30%, and also, diminish oxidization and surface rugosity.

Local Er(III) environment in luminescent titanosilicates prepared from microporous precursors

The local environment of Er3+ ions in microporous titanosilicate ETS-10 and in synthetic narsarsukite and glassy materials obtained by calcination of ETS-10 has been investigated by EXAFS, Raman and photoluminescence spectroscopies. Er L-III-edge EXAFS studies of Er3+-doped ETS-10 support the view that the exchanged Er3+ ions reside close to the (negatively charged) TiO6 octahedra. In ETS-10, Er3+ is partially bonded to framework oxygen atoms and hydration water molecules. The Er...Ti distance (3.3 Angstrom) is similar to the Na...Ti distances (3.15-3.20 Angstrom) reported previously for Na-ETS-10. Although the exact location of the ErO6 units within the host structure of Er3+-doped synthetic narsarsukite is still an open question, it is most likely that Er3+ substitutes Ti4+ rather than Na+ ions. EXAFS spectroscopy indicates that no significant clustering of erbium atoms occurs in the titanosilicate samples studied. Evidence for the insertion of Er3+ ions in the framework of narsarsukite has been obtained by Raman spectroscopy. This is indicated by the increasing full-width at half-maximum (FWHM) of the 775 cm(-1) peak and the increasing intensity of the anatase peaks as the erbium content increases. In addition, as the narsarsukite Er3+ content increases a band at ca. 515 cm(-1) firstly broadens and subsequently a new peak appears at ca. 507 cm(-1).Er3+-doped narsarsukite exhibits a characteristic local vibrational frequency, (h) over bar omega ca. 330 cm(-1), with an electron-phonon coupling, g ca. 0.2, which constitutes additional evidence for framework Er3+ insertion. The number of lines in the infrared emission spectrum of synthetic narsarsukite indicates the presence of two optically-active erbium centres with very similar local environments and an average I-4(13/2) lifetime of 7.8 +/- 0.2 ms.

Single-exposure, photorefractive holographic surface contouring with multiwavelength diode lasers

We studied the use of multiwavelength diode lasers for surface profilometry through holographic recording in sillenite Bi(12)TiO(20) crystals. When such lasers are used, the holographic image from single-exposure recordings appears covered with interference fringes providing information on the surface relief of the object. By taking advantage of the narrow interference fringes due to the multiwavelength emission of the laser, we obtained interferograms by holographic recording with two reference beams, which improves the surface analysis by visual inspection and enhances the profilometry sensitivity. (c) 2005 Optical Society of America.

Luminescence and ESR properties of Brazilian feldspars

The IRSL and TL responses of three different feldspar crystals have been analysed. TL measurements were taken in the ultraviolet UV (290-370 nm) and the visible VIS (340-610 nm) regions of the spectrum. For the UV region and for a natural sample, peaks were observed at 283, 287 and 310 degrees C for grey, white and pink crystals, respectively. For samples irradiated after prior preheating, it was noted that TL peaks occurred at about 200 degrees C for all the samples; irradiation with high doses above 500 Gy induced the formation of one additional peak at 170 degrees C. The VIS region results were similar to those for the UV. ESR experiments have been developed to verify the influence of radiation and heat treatments on the centres and preliminary results showed great variation in the intensities of [TiO(4)](-), Al-O(-)-Al and Fe(3+) centres. (c) 2006 Elsevier Ltd. All rights reserved.

Thermal behavior of the Ti(IV), Zr(IV) and Pb(II) complexes with 5-nitro-8-hydroxyquinoline

Ti(IV), Zr(IV) and Pb(II) complexes with 5-nitro-8-hydroxyquinoline (5-NQ) were obtained by precipitation in acetone/ammonium solution medium. The compounds TiO(C9H5N2O3)(2).0.5H(2)O, ZrO(C9H5N2O3)(2)2H(2)O and Pb(C9H5N2O3)(2) were characterized by Elemental Analysis, X-ray Diffratometry and Infrared Absorption Spectrometry and their thermal behavior followed by TG/DTA. This present study intends to show the variations in the thermal behavior of the compounds and in the composition and/or structure of final oxide residues, in different atmospheres and heating rates.

Anisotropic growth of oxide nanocrystals: Insights into the rutile TiO2 phase

In this work, we report the synthesis of titanium oxide nanocrystals, especially the rutile TiO2 phase with nanorod morphology, by a method based on peroxotitanium complex decomposition. The results indicate that the anisotropic morphology reported for rutile TiO2 nanocrystals is related to the oriented attachment process. Despite the predominance of rutile nanocrystals at longer treatment times, the nanocrystals were obtained also in the anatase type, according to the degradation time adopted. XANES results evidenced the absence of structural correlation between the peroxytitanium complex and phase evolution, and the coexistence of the two phases strongly suggests a correlation of the oriented attachment mechanism and the rutile phase stabilization.

Surface modification of Ti dental implants by Nd: YVO4 laser irradiation

Surface modifications have been applied in endosteal bone devices in order to improve the osseointegration through direct contact between neoformed bone and the implant without an intervening soft tissue layer. Surface characteristics of titanium implants have been modified by addictive methods, such as metallic titanium, titanium oxide and hydroxyapatite powder plasma spray, as well as by subtractive methods, such as acid etching, acid etching associated with sandblasting by either AlO2 or TiO2, and recently by laser ablation. Surface modification for dental and medical implants can be obtained by using laser irradiation technique where its parameters like repetition rate, pulse energy, scanning speed and fluency must be taken into accounting to the appropriate surface topography. Surfaces of commercially pure Ti (cpTi) were modified by laser Nd:YVO4 in nine different parameters configurations, all under normal atmosphere. The samples were characterized by SEM and XRD refined by Rietveld method. The crystalline phases alpha Ti, beta Ti, Ti6O, Ti3O and TiO were formed by the melting and fast cooling processes during irradiation. The resulting phases on the irradiated surface were correlated with the laser beam parameters: the aim of the present work was to control titanium oxides formations in order to improve implants osseointegration by using a laser irradiation technique which is of great importance to biomaterial devices due to being a clean and reproducible process. (c) 2007 Elsevier B.V. All rights reserved.

Barium titanate screen-printed thick films

Barium titanate (BT) thick films were prepared from mechanically activated powders based on BaCO(3) and TiO(2). After homogenization and milling in a high-energy vibro mill, the powders were calcined at 700 degreesC for 2 h by slow heating and cooling rates. A thick film paste was prepared by mixing BT fine powders with small amount of low temperature sintering aid and organic binder. The thick films were screen-printed on alumina substrates electroded with Ag-Pd. The BT films were sintered at 850 degreesC for 1 h. The thickness was 25-75 mum depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate were investigated by SEM Results of dielectric property measurements are also reported. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Designing Gaussian basis sets to the theoretical study of the piezoelectric effect of perovskite (BaTiO3)

Gaussian basis sets (24s14p, 30s19p14d, and 33s21p14d for O (P-3), Ti (S-5), and Ba (S-1) atoms, respectively), are designed with the strategy of the Generator Coordinate Hartree-Fock method. The basis sets are then contracted to [6s4p], [10s5p4d], and [16s9p5d] to O, Ti, and Ba atoms, respectively, and used in calculations of total and orbital energies of (TiO+2)-Ti-1 and (BaO)-Ba-1 fragments for quality evaluation in molecular studies. For O atom, the [6s4p] basis set is enriched with d polarization function and used along with the [10s5p4d] and [16s9p5d] basis sets for the theoretical study of the piezoelectric effect of perovskite (BaTiO3). The results of this work evidence that the piezoelectric properties in BaTiO3 can be caused by electrostatic interactions. (C) 2003 Elsevier B.V. All rights reserved.

The influence of temperature on the color of TiO2:Cr pigments

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Influence of structural disorder on the photoluminescence emission of PZT powders

Intense and broad visible photoluminescent (PL) band was observed at room temperature in disordered Pb(Zr(0.53)Ti(0.47))O(3) powders. Structural order-disorder was evaluated by different methods. XANES results pointed to the presence of different coordination modes of disordered Ti powders, and in the ordered sample the local structure around titanium atoms is characteristic of the structurally ordered PZT with only TiO(6) units. Only samples containing simultaneous structural order and disorder in their network present the intense visible PL emission at room temperature.

Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Ceramic raw materials from the State of Maranhao, Brazil. Part 1: chemical and mineralogical characterization and technological properties of clays from Sao Luis, Rosario, Pinheiro and Mirinzal

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)