Efeito das dimensões dos corpos de prova na resistência à flexão de compósitos restauradores

The aim of this study was to evaluate the influence of specimen size, in comparison with the ISO Standard, on the three point flexural strength of resin composite restorative materials Filtek Supreme and Filtek Z-250. Forty specimens were fabricated for each material with the following length, width and thickness measurements (n = 10): 1) 20 × 2 × 2 mm (ISO 4049); 2) 10 × 2 × 1 mm; 3) 10 × 1 × 1 mm; 4) 8 × 0.8 × 0.8 mm. The composites were inserted in a single increment into two-piece metal device and light-polymerized. The specimens were dry stored at 37 ± 1 °C and protected from light for 7 days. After this period, flexural strength was measured by three-point flexure test using MTS 810 equipment, with a load cell of 10 kN at a speed of 0.5 mm/min. For the evaluated sizes, the results showed significant variability (p = 0.00) with values when compared with the ISO Standard (116.700 MPa), being statistically higher for the test specimens measuring 10 × 1 × 1 mm (142.530 MPa), similar for those of 10  ×  2  ×  1  mm (115.815 MPa) and lower for those of 8 × 0.8 × 0.8 mm (86.650 MPa). There was statistical equality (p = 0.08) for the studied composites (Filtek Supreme, 125.270 MPa; Filtek Z-250, 108.130 MPa). Specimens measuring 10 × 2 × 1 mm provided flexural strength values equivalent to those obtained in the sizes recommended by the ISO 4049 standard, with lower consumption of material, energy and time.

Planning and clinical strategy in direct composite restorations

Patients are seeking increasingly the expertise of dental surgeons for esthetic dental improvement. The dental surgeons should know the restorative materials and techniques in order to optimize the clinical practice and to obtain satisfactory results. Also the dentist should know the average heights and widths of the anterior teeth to detect the esthetic disharmony and to eliminate it for reproducing the correct dental anatomy. Thus, this study aimed to describe a clinical case report of direct restoration using the palatal barrier technique.

Coroas estéticas anteriores em cerâmica metal-free: relato de caso clínico

Society's change of parameters for health and aesthetics has resulted in an increased demand for dental treatments. Nowadays, ceramics systems have shown a substantial development, becoming more reliable and predictable. Dental ceramics, besides being chemically stable, present excellent optical properties when compared to dental structures, thus assuring a special position in the list of aesthetic restorative materials. OBJECTIVE, CASE REPORT AND CONCLUSION: This article describes a successful clinical procedure involving the anterior teeth aesthetics, which were restored with all-ceramic crowns (IPS e.max® Ivoclar Vivadent).

Fluorescence Level of Composites Assessed by Computer Processing of Digital Images - ScanWhite

The human dentition is naturally translucent, opalescent and fluorescent. Differences between the level of fluorescence of tooth structure and restorative materials may result in distinct metameric properties and consequently perceptible disparate esthetic behavior, which impairs the esthetic result of the restorations, frustrating both patients and staff. In this study, we evaluated the level of fluorescence of different composites (Durafill in tones A2 (Du), Charisma in tones A2 (Ch), Venus in tone A2 (Ve), Opallis enamel and dentin in tones A2 (OPD and OPE), Point 4 in tones A2 (P4), Z100 in tones A2 ( Z1), Z250 in tones A2 (Z2), Te-Econom in tones A2 (TE), Tetric Ceram in tones A2 (TC), Tetric Ceram N in tones A1, A2, A4 (TN1, TN2, TN4), Four seasons enamel and dentin in tones A2 (and 4SD 4SE), Empress Direct enamel and dentin in tones A2 (EDE and EDD) and Brilliant in tones A2 (Br)). Cylindrical specimens were prepared, coded and photographed in a standardized manner with a Canon EOS digital camera (400 ISO, 2.8 aperture and 1/ 30 speed), in a dark environment under the action of UV light (25 W). The images were analyzed with the software ScanWhite©-DMC/Darwin systems. The results showed statistical differences between the groups (p < 0.05), and between these same groups and the average fluorescence of the dentition of young (18 to 25 years) and adults (40 to 45 years) taken as control. It can be concluded that: Composites Z100, Z250 (3M ESPE) and Point 4 (Kerr) do not match with the fluorescence of human dentition and the fluorescence of the materials was found to be affected by their own tone.

Surface roughness analysis of dental ceramics treated with hydrofl uoric acid and aluminum oxide jet

The aim of this study was to evaluate the surface roughness of 5 indirect restorative materials treated with hydrofluoric acid to 10%, with aluminum oxide jet and a combination of both. The specimens was prepared with 10 mm in diameter and 2 mm thickness, divided into fi ve groups: (1) Ceromer (CeseadII-Kuraray), (2) Leucite crystals ceramics (IPS EmpressIIIvoclarforcasket), (3) glass ceramic with fluorapatite (IPS D. Sign-Ivoclar), (4) lithium disilicate ceramic (IPS Empress II-Ivoclar restorations), (5) ceramics (Cergogold-Degussa). For all groups were performed the controls, and the surfaces with the 3 types of treatment. For testing roughness used the rugosimeter Taylor/Hobson-Precision, model form tracerSV-C525 high sensitivity. After confi rmation of variance analysis with a signifi cance level of 1% (p < 0.01), there was equality between the average roughness of materials from groups 1, 3 and 5, and the group 2 was different from the others. It was also found that the ceramics of the group 5 behaved similar to group 4. However the lowest average roughness was observed in group 2 ceramic. In the evaluation between the types of treatment, the aluminum oxide jet and associations and blasting with hydrofl uoric acid were similar, and different isolated hydrofl uoric acid, and 3 types of treatment signifi cantly higher than the control group. All treatments promoted superfi cial alterations in all tested materials.

Influência da geometria oclusal e material restaurador na carga para fratura e distribuição de tensões em coroas totais

Pós-graduação em Odontologia Restauradora - ICT

Effect of postpolymerization method on the color stability of composite resins submitted to ultraviolet aging

The aim of this research was to evaluate the effect of postpolymerization method on the color stability of resin-based composites. Samples of direct and indirect restorative materials were polymerized with two photo-curing units (Visio photo-curing oven system and LED Elipar Freelight 2). All samples were submitted to an initial chromatic analysis using a spectrometer and submitted to ultraviolet-accelerated artificial aging. The direct material showed less color change than the indirect material, independent of the photo-activation method used. Samples photo cured with the LED system showed less change than those photo cured with the Visio system. The postpolymerization oven did not improve the color stability of direct and indirect resin-based composites.

Comportamento do esmalte de dentes decíduos após desafio desmineralizante em função de materiais restauradores: estudo ao microscópio de luz polarizada

Pós-graduação em Biopatologia Bucal - ICT

Composite resin susceptibility to red wine staining after water sorption

Color stability of restorative materials is essential for longevity of esthetic composite restoration over time. The aim of this investigation was assess the effect of prior water immersion on the color stability of a composite resin to red wine staining. Seventy disccshaped specimens (6mm x 1.5mm) were carried out and randomized in 7 groups (n = 10), according to distilled water immersion time at 0 (control), 24, 48, 72,120,192, and 240 h. Baseline color was measured according to the ciel*a*b* system using a reflection spectrophotometer(uvc2450, shimadzu).After that, the specimens were storage in red wine for 7 days. Color difference (∆e) after aging was calculated based on the color coordinates before(baseline) and after storage period.Data were subjected to onecway anova(alpha=0.05).The different times of immersion in.Water before to the red wine storage showed similar behavior on the color stability, without statistical difference compared to control group, immersed directly in the wine(p=0.7057).The previous water uptake of composite resin evaluated did not decrease the susceptibility to red wine staining.

Emprego de ma teriais rest auradores adesivos direto no ângulo incisal de incisivos centrais fra turados

A case report of a patient who presents as chief complaint presence of stained restorations in the anterior teeth. After analysis and discussion of the clinical therapeutic approaches to be adopted, it was observed the presence of type class IV restorations on teeth 11 and 21, due to an oblique coronal fracture in the past. But the patient was not satisfied with the aesthetic result, then where was planned the realization of the removal of the restorations, for subsequently be used direct restorative materials for the correction of form, function and esthetics. The final result showed that the restorations were able to return the form, function and aesthetic dental, thereby evidencing the proven development of restorative dentistry in the solution of aesthetic problems.

In vitro reduction of Streptococcus mutans biofilm on silver nanoparticle-modified resin composite

Introduction: Currently, new methods to reduce biofilm formation on biomaterials are very studied, for example the use of silver nanoparticles, which were bactericidal. However, there are few studies investigating the benefits of these particles in dental restorative materials. Objective: This study aimed to compare in vitro the Streptococcus mutans biofilm formation on conventional light-cured composite resin with that on experimental light-cured composite resin, modified with silver nanoparticles. Material and methods: Discs were produced with either conventional resin (control group) and resin modified with different concentrations of silver nanoparticles, 0.1%, 0.3% and 0.6 % wt. (groups 1, 2 and 3, respectively). The samples were incubated in bacterial suspension (S. mutans) enriched with 20% sucrose to promote biofilm growth on the surfaces. Incubation times were 1, 4 and 7 days. After each period, adherent biofilms were disaggregated by ultrasound. Then, the numbers of viable cells recovered from the biofilms were counted through the serial dilution method. A morphological analysis of biofilm was also performed by Scanning Electron Microscopy. The data were subjected to Anova and Tukey’s test (α = 0.05). Results: The number of viable cells was statistically lower in groups 2 and 3 than in group 1 and control group, after the three incubation periods, without statistical difference between groups 2 and 3. The number of viable cells was statistically lower in group 1 than in control group, after 4 and 7 days of incubation. Conclusion: Resins modified with silver presented reduction of S. mutans biofilm on their surfaces, according to the conditions of this study.

Alkali activated materials based on fluid catalytic cracking catalyst residue (FCC): Influence of SiO2/Na2O and H 2O/FCC ratio on mechanical strength and microstructure

Reuse of industrial and agricultural wastes as supplementary cementitious materials (SCMs) in concrete and mortar productions contribute to sustainable development. In this context, fluid catalytic cracking catalyst residue (spent FCC), a byproduct from the petroleum industry and petrol refineries, have been studied as SCM in blended Portland cement in the last years. Nevertheless, another environmental friendly alternative has been conducted in order to produce alternative binders with low CO2 emissions. The use of aluminosilicate materials in the production of alkali-activated materials (AAMs) is an ongoing research topic which can present low CO2 emissions associated. Hence, this paper studies some variables that can influence the production of AAM based on spent FCC. Specifically, the influence of SiO 2/Na2O molar ratio and the H2O/spent FCC mass ratio on the mechanical strength and microstructure are assessed. Some instrumental techniques, such as SEM, XRD, pH and electrical conductivity measurements, and MIP are performed in order to assess the microstructure of formed alkali-activated binder. Alkali activated mortars with compressive strength up to 80 MPa can be formed after curing for 3 days at 65°C. The research demonstrates the potential of spent FCC to produce alkali-activated cements and the importance of SiO2/Na2O molar ratio and the H2O/spent FCC mass ratio in optimising properties and microstructure. © 2013 Elsevier Ltd. All rights reserved.

Use of slag/sugar cane bagasse ash (SCBA) blends in the production of alkali-activated materials

Blast furnace slag (BFS)/sugar cane bagasse ash (SCBA) blends were assessed for the production of alkali-activated pastes and mortars. SCBA was collected from a lagoon in which wastes from a sugar cane industry were poured. After previous dry and grinding processes, SCBA was chemically characterized: it had a large percentage of organic matter (ca. 25%). Solutions of sodium hydroxide and sodium silicate were used as activating reagents. Different BFS/SCBA mixtures were studied, replacing part of the BFS by SCBA from 0 to 40% by weight. The mechanical strength of mortar was measured, obtaining values about 60 MPa of compressive strength for BFS/SCBA systems after 270 days of curing at 20 °C. Also, microstructural properties were assessed by means of SEM, TGA, XRD, pH, electrical conductivity, FTIR spectroscopy and MIP. Results showed a good stability of matrices developed by means of alkali-activation. It was demonstrated that sugar cane bagasse ash is an interesting source for preparing alkali-activated binders. © 2013 by the authors; licensee MDPI, Basel, Switzerland.