Thermal behavior of the Cu-10 mass%Al and Cu-10 mass%Al-4 mass%Ag alloys

The thermal behavior of the Cu-10 mass%Al and Cu-10 mass% Al-4 mass%Ag alloys was studied using classical differential thermal analysis (DTA), optical microscopy (OM) and X-ray diffractometry (XRD). The DTA curves were obtained for annealed and quenched samples. The results indicated that the presence of silver introduces new thermal events, associated to the formation of a silver-rich phase, to the shift of the equilibrium concentration to higher A1 contents and to the decomposition of the silver-rich phase in the same temperature range of the beta(1) phase decomposition.

EFFECT OF THE ADDITION OF CR AND NB ON THE MICROSTRUCTURE AND ELECTROCHEMICAL CORROSION OF HEAT-TREATABLE AL-ZN-MG ALLOYS

The effect of the addition of Cr and Nb on the microstructure and the electrochemical corrosion of the weldable, high-strength and stress corrosion cracking (SCC) resistant Al-5%Zn-1.67%Mg-0.23%Cu alloy (H) has been studied. Combined additions of the alloying elements, J (with Nb), L (with Cr) and O (with Cr and Nb) and different heat treatments, ST (cold-rolled), A (annealed), F (quenched), B (quenched and aged) and C (quenched in two steps and aged), to obtain different microstructures and hardness have been performed. To correlate the electrochemical corrosion with the microstructure of the specimens, corrosion potential (E(cor)) measurements in different chloride solutions were performed and optical microscopy, SEM, TEM and EDX were applied. In chloride solutions containing dissolved O-2 or H2O2, the present alloys were polarized up to the pitting attack. It was shown that the E(cor) measurements were very sensitive to the alloy composition and heat treatment, increasing in the order H < J < L < O < Al (for a given heat treatment) and F < A approximate to ST < B < C (for a given alloy). The MgZn2 precipitates of the annealed (A) and cold-rolled (ST) specimens were dissolved in chloride solutions containing oxidizing agents and pitting attack was shown to develop in the cavities where the precipitates were present. In the specimens B and C, the compositions of the precipitate free zones was found to be equal to that of the matrix solid solution and preferential intergranular attack was not evident, this being in agreement with their SCC resistance. The addition of Cr and Nb increased the pitting corrosion resistance. The effects of Cr and Nb were additive, that of Cr being predominant, either, in the E(cor) shift or in the increase in the pitting corrosion resistance.

Shear bond strengths of a ceramic system to alternative metal alloys

Statement of problem. The success of metal-ceramic restorations is influenced by the compatibility between base metal alloys and porcelains. Although porcelain manufacturers recommend their own metal systems as the most compatible for fabricating metal-ceramic prostheses, a number of alloys have been used.Purpose. This study evaluated the shear bond strength between a porcelain system and 4 alternative alloys.Material and methods. Two Ni-Cr alloys: 4 ALL and Wiron 99, and 2 Co-Cr alloys: IPS d.SIGN 20 and Argeloy NP were selected for this study. The porcelain (IPS d.Sign porcelain system) portion of the cylindrical inetal-ceramic specimens was 4 mm thick and 4 mm high; the metal portion was machined to 4 x 4 mm, with a base that was 5 nun thick and 1 mm high. Forty-four specimens were prepared (n=11). Ten specimens from each group were subjected to a shear load oil a universal testing machine using a 1 min/min crosshead speed. One specimen from each group was observed with a scanning electron microscope. Stress at failure (MPa) was determined. The data were analyzed with a 1-way analysis of variance (alpha=.05).Results. The groups, all including IPS d.Sign porcelain, presented the following mean bond strengths (+/-SD) in MPa: 4 ALL, 54.0 +/- 20.0; Wiron, 63.0 +/- 13.5; IPS d.SIGN 20, 71.7 +/- 19.2; Argeloy NP, 55.2 +/- 13.5. No significant differences were found among the shear bond strength values for the metal-ceramic specimens tested.Conclusion. None of the base metal alloys studied demonstrated superior bond strength to the porcelain tested.

The influence of yttrium on a typical SnO2 varistor system: Microstructural and electrical features

The influence of yttrium oxide, Y2O3, on the microstructure development of the SnO(2)center dot Co(3)O(4)center dot Nb2O5 typical varistor system was studied with scanning (SEM) and transmission (TEM) electron microscopies. The different phases present in the studied samples were characterized through XRD, EDS and selected area diffraction patterns (SAD). Particles of Co2SnO4 were observed with TEM in every sample, whereas clusters of the pyrochlore phase T2Sn2O7 were observed with SEM in samples with 0.05, 0.10 and 0.25 mol% of Y2O3. The higher non-linearity (a = 16) was achieved with the addition of 0.05 mol% of Y2O3. The influence of the secondary phases on the electrical properties is also addressed in this work. (c) 2005 Published by Elsevier B.V.

Electrochemical studies with copper-based alloys: open-circuit potential oscillations in alkaline media

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of subsurface dentin microhardness after Er : yttrium-aluminum-garnet and Nd : yttrium-aluminum-garnet laser irradiation

Background and objectives: To assess the microhardness of dentin subsurface after Er:yttrium-aluminum-garnet (YAG) and Nd:YAG laser irradiation. Study design/materials and methods: Twenty-four bovine incisors, without pulp, were used. The vestibular surface was worn out until the dentin was reached and divided in mesial and distal regions. The samples were divided into two groups: GI-distal, irradiated by Er: YAG laser, and GII-distal, irradiated by Nd: YAG laser. The mesial area was protected so as to not receive the laser irradiation. The measurements were made on Vickers digital microhardmeter. Results: For GI-there was no significant statistical difference, Cl(-4.59 to 0.78), between the values of irradiated (55.61 +/- 4.38) and unirradiated (57.51 +/- 4.00) areas. For GII-the values were higher for the irradiated (62.21 +/- 6.48) compared to the unirradiated (57.82 +/- 5.42) area, CI(1.65 +/- to 7.13). Conclusions: There was an increase of dentin microhardness when the Nd: YAG was used, but the Er: YAG did not cause significant alterations in dentin microhardness. (c) 2007 Laser Institute of America.

Synthesis, characterization and thermal behaviour of solid-state compounds of yttrium and lanthanide benzoates

Solid-state Ln(Bz)(3)center dot H(2)O compounds where Ln stands for trivalent yttrium or lanthanides and Bz is benzoate have been synthesized. Simultaneous thermogravimetry-differential thermal analysis (TG-DTA), X-ray powder diffractometry, infrared spectroscopy and chemical analysis were used to characterize and to study the thermal behaviour of these compounds. The results led to information about the composition, dehydration, thermal stability and thermal decomposition of the isolated compounds.

THE INFLUENCE OF THE ELECTROCHEMICAL TREATMENT ON CU-AL-AG ALLOYS IN DEAERATED 0.5M NAOH

The effect of consecutive cyclic polarization in de-aerated 0.5 M NaOH solutions on the surface microstructure of mechanically polished Cu-Al-Ag alloys of different compositions and heat treatments has been studied using optical microscopy, SEM and EDS. The current peaks of the cyclic polarization curves do not depend on the alloy composition in the composition range studied. The repetitive potential scans between H2 and O2 evolution in alkaline media lead to preferential dissolution of aluminium, the roughness and phase composition of the surface of the alloys changing significantly. The quasistationary I-E curves of the different Cu-Al-Ag alloys studied consist in the superposition of the quasistationary I-E curves of high-purity Cu and Ag, the EDS microanalysis showing that aluminium is not present on the surface of the alloy in these conditions.

Solvothermal method to obtain europium-doped yttrium oxide

Pure yttrium oxide or mixed with europium oxide (3 at%) were treated in supercritical isopropanolic suspension at 500degreesC for 20 It and filling degree of 50%. Products were supercritically dried and characterized by scanning electron microscopy (SEM), X-ray powder diffraction (XRD), infrared spectroscopy (IR) and luminescence spectroscopy (LS). Particle shape is irregular with an equivalent diameter of ca. 5 mum. Cubic crystalline phase is mainly obtained and hydroxide ion in low concentration is detected by IR vibrational spectrum. Europium in this concentration does not extensively change such observed characteristics from the pure yttrium oxide. Luminescence spectra show that the doped product is a mixture of the two oxides added by oxyhydroxide impurities. Nevertheless, this precursor sample, after being heated at 900degreesC during 1 h, has all characteristics, especially luminescent ones, of the P22 commercial phosphor. (C) 2003 Elsevier B.V. (USA). All rights reserved.

Kinetics of eutectoid decomposition in Cu-Al and Cu-Al-Ag alloys

The kinetics of eutectoid decomposition beta(1)' --> gamma(2) + (alpha + gamma(2)) in Cu-12.86 wt% Al and Cu-12.84 wt% Al-1.98 wt% Ag alloys was studied by hardness measurements, using the Johnson-Mehl-Avrami equation. The results indicate that the presence of silver seems to influence the nucleation rate and the activation energy of the reaction.

Thermal studies of solid 4-chlorobenzylidenepyruvates of heavy lanthanides(III) and yttrium(III)

Solid-state compounds of general formula LnL(3).2H(2)O, where Ln is heavier trivalent lanthanides and yttrium, L is 4-chlorobenzylidenepyruvate have been synthetised.On heating these compounds decompose in steps. They lose the hydration water in the first step and the thermal decomposition of the anhydrous compounds occurs with the formation of oxochloride (Eu, Gd); mixture of oxide and oxochloride that decrease with increasing of atomic number of metal (Tb-Tm); or oxide (Yb, Lu, Y) as final residue, up to 900degreesC. The dehydration enthalpies found for terbium, holmium, ytterbium and yttrium compounds were: 34.93, 42.40, 57.39 and 62.24 kJ mol(-1), respectively.