Compressive strength of dental composites photo-activated with different light tips

The aim of this study was to evaluate the compressive strength of microhybrid (Filtek™ Z250) and nanofilled (Filtek™ Supreme XT) composite resins photo-activated with two different light guide tips, fiber optic and polymer, coupled with one LED. The power density was 653 mW cm -2 when using the fiber optic light tip and 596 mW cm-2 with the polymer. After storage in distilled water at 37 ± 2 °C for seven days, the samples were subjected to mechanical testing of compressive strength in an EMIC universal mechanical testing machine with a load cell of 5 kN and speed of 0.5 mm min-1. The statistical analysis was performed using ANOVA with a confidence interval of 95% and Tamhane's test. The results showed that the mean values of compressive strength were not influenced by the different light tips (p > 0.05). However, a statistical difference was observed (p < 0.001) between the microhybrid composite resin photo-activated with the fiber optic light tip and the nanofilled composite resin. Based on these results, it can be concluded that microhybrid composite resin photo-activated with the fiber optic light tip showed better results than nanofilled, regardless of the tip used, and the type of the light tip did not influence the compressive strength of either composite. Thus, the presented results suggest that both the fiber optic and polymer light guide tips provide adequate compressive strength to be used to make restorations. However, the fiber optic light tip associated with microhybrid composite resin may be an interesting option for restorations mainly in posterior teeth. © 2013 Astro Ltd.

Avaliação da profundidade de polimerização de uma resina composta, pela técnica trans-dental, utilizando-se três diferentes fontes de luz: halógena, laser de argônio e leds

Pós-graduação em Ciências Odontológicas - FOAR

Avaliação de um aparelho de luz halógena e um dispositivo Leds na técnica de fotoativação trans-dental: estudo da profundidade de polimerização pelos testes de dureza e espectroscopia de fluorescência

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito da aplicação de sistemas adesivos autocondicionantes associados ao laser Nd:YAG na prevenção do desgaste erosivo/abrasivo do esmalte dental

Pós-graduação em Odontologia Restauradora - ICT

Effect of delayed start of light-curing on microtensile bond strengths of two adhesives bonded to dentin

The aim of the present study was to evaluate the microtensile bond strength to dentin (ATBS) of two total-etching adhesives applied with delays of 1-30 s for curing. Fifty extracted molar teeth were used. Occlusal enamel was sectioned to expose flat dentin surface, which was further polished with 600-grit paper for smear layer standardization. The specimens were divided into two groups, G1: Single Bond total-etching adhesive (SB), and G2: Prime & Bond NT total-etching adhesive (PB). Each group was further divided into 5 subgroups according to the delayed light-cure initiation after the adhesive systems application (n=5): Subgroup 1s - 1 s; Subgroup 5s -5 s; Subgroup 10s - 10 s; Subgroup 20s - 20 s; Subgroup 30s - 30 s. Composite resin cones 5 mm height and 10 mm in diameter were fabricated. Specimens were stored in distilled water at 37 degrees C for 24 h and sectioned to obtain 1 x 1 mm(2) transversal specimens. Specimens were thermocycled and mu TBS was measured. Data were submitted to two-way ANOVA (AdhesiveXDelay time) and Tukey's test. The level of significance was set at 5%. The results in mean MPa(+/- SD) for interaction between adhesive and delay time were: PB/1s - 23.82 +/- 2.54a; SB/5s - 19.52 +/- 2.67b; PB/5s - 18.56 +/- 3.06bc; SB/1s - 15.49 +/- 2.69cd; SB/20s - 16.33 +/- 2.55d; SB/10s - 13.88 +/- 1.67d; PB/10s - 11.04 +/- 1.28e; PB/30s - 10.89 +/- 1.31e; PB/20s - 10.24 +/- 2.33e; SB/30s - 9.19 +/- 1.91e. It was concluded that light-cure initiation timing of total-etching adhesives interferes negatively with mu TBS to dentin. (C) 2014 Elsevier Ltd. All rights reserved.

Effect of light-curing on the antibacterial activity of dentin bonding agents

Aim: This study evaluated the effect of light-activation on the antibacterial activity of dentin bonding systems. Methods: Inocula of Streptococcus mutans and Lactobacillus casei cultures were spread on the surface of BHI agar and the materials were applied and subjected or not to light-activation. Zones of bacterial growth inhibition around the discs were measured. Results: Excite, Single Bond and the bond of Clearfil SE Bond (SE) and Clearfil Protect Bond (CP) did not show any antibacterial activity. The strongest inhibitory activity was observed for the primers of CP and Prompt (PR) against S. mutans and the primers of SE and PB against L. casei. Conclusion: Light-activation significantly reduced or suppressed the antibacterial activity of the initially active uncured dentin bonding systems

Influence of light curing units and fluoride mouthrinse on morphological surface and color stability of a nanofilled composite resin

Composite resin is a dental material susceptible to color change over time which limits the longevity of restorations made with this material. The influence of light curing units and different fluoride mouthrinses on superficial morphology and color stability of a nanofilled composite resin was evaluated. Specimens (N = 150) were prepared and polished. The experimental groups were divided according to the type of light source (halogen and LED) and immersion media (artificial saliva, 0.05% sodium fluoride solution-manipulated, Fluordent Reach, Oral B, Fluorgard). Specimens remained in artificial saliva for 24-h baseline. For 60 days, they were immersed in solutions for 1 min. Color readout was taken at baseline and after 60 days of immersion. Surface morphology was analyzed by Scanning Electron Microscopy (SEM) after 60 days of immersion. Color change data were submitted to two-way Analysis of Variance and Tukey tests (α = 0.05). Surface morphology was qualitatively analyzed. The factor light source presented no significant variability (P = 0.281), the immersion media, significant variability (P < 0.001) and interaction between factors, no significant variability (P = 0.050). According to SEM observations, no difference was noted in the surface of the specimens polymerized by different light sources, irrespective of the immersion medium. It was concluded that the light source did not influence the color stability of composite, irrespective of the immersion media, and among the fluoride solutions analyzed, Fluorgard was the one that promoted the greatest color change, however, this was not clinically perceptible. The immersion media did not influence the morphology of the studied resin. Microsc. Res. Tech. 77:941–946, 2014. © 2014 Wiley Periodicals, Inc.

Isolation of Pseudomonas aeruginosa strains from dental office environments and units in Barretos, state of São Paulo, Brazil, and analysis of their susceptibility to antimicrobial drugs

Uma ampla variedade de patógenos oportunistas tem sido detectadas nos tubos de alimentação de água dos equipos odontológicos, particularmente no biofilme formado na superfície do tubo. Entre os patógenos oportunistas encontrados nos tubos de água, Pseudomonas aeruginosa é reconhecida como uma das principais causadoras de infecções nosocomiais. Foram coletadas 160 amostras de água e 200 amostras de fomites em quarenta clinicas odontológicas na cidade de Barretos, São Paulo, Brasil, durante o período de Janeiro a Julho de 2005. Setenta e seis cepas de P. aeruginosa, isoladas a partir dos fomites (5 cepas) e das amostras de água (71 cepas), foram analisadas quanto à susceptibilidade à seis drogas antimicrobianas freqüentemente utilizadas para o tratamento de infecções provocadas por P. aeruginosa. As principais suscetibilidades observadas foram para a ciprofloxacina, seguida pelo meropenem. A necessidade de um mecanismo efetivo para reduzir a contaminação bacteriana dentro dos tubos de alimentação de água dos equipos odontológicos foi enfatizada, e o risco da exposição ocupacional e infecção cruzada na prática odontológica, em especial quando causada por patógenos oportunistas como a P. aeruginosa foi realçado.

Genetic relatedness of commensal strains of Candida albicans carried in the oral cavity of patients' dental prosthesis users in Brazil

The aim of this study is to describe the degree of yeast-colonization in diabetic and hemodialysed-users of dental prostheses. Individuals (306) were examined using an oral rinse technique in order to evaluate the incidence of yeast-carriage, and genotype of C. albicans. Yeasts were isolated from 68.4% (91/133) individual's dental prostheses users. Dental prostheses were found to be a significant factor for the yeast colonization (P < 0.05). Overall, the intensity of carriage was higher in diabetic patients as compared with health and hemodialysed individuals (P < 0.05). The isolation rates were: C. albicans (51.7%), C. parapsilosis (20.9%), C. tropicalis (14.3%), C. glabrata (6.6%), C. krusei (3.3%), C. rugosa (1.1%), and Pichia (Pichia ohmeri, 2.2%). Ready-To-Go RAPD Analysis Beads were used and primer OPJ 6 distinguished the C. albicans isolates found in prostheses users. All the isolates were grouped into 11 RAPD profiles in four main clusters and, the average S (AB) for the entire collection of 47 C. albicans isolates were 0.779 +/- 0.178. Over 85% of isolates had a similarity level higher than or equal to 0.8 reinforcing the idea that the use of dental prostheses, independently of the host's clinical condition, probably provides the necessary conditions for these strains to gain a growth-specific advantage over others.

Surface dental enamel lead levels and antisocial behavior in Brazilian adolescents

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Recovery of silver residues from dental amalgam

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Finite-Element Analysis of Stress on Dental Implant Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Wear resistance of experimental titanium alloys for dental applications

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Glass transition and degree of conversion of a light-cured orthodontic composite

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Infrared spectroscopy: a tool for determination of the degree of conversion in dental composites

Infrared spectroscopy is one of the most widely used techniques for measurement of conversion degree in dental composites. However, to obtain good quality spectra and quantitative analysis from spectral data, appropriate expertise and knowledge of the technique are mandatory. This paper presents important details to use infrared spectroscopy for determination of the conversion degree.