The effect of EU3+ ion doping concentration in Gd2O3 fine spherical particles

This work reports on the preparation of Gd2O3, cubic system, with spherical particles, narrow size distribution, whether or not doped with 1-5 at.% of Eu3+ and the influence of Eu3+ concentration on optical and morphological properties. Average diameter and size distribution particle analyses were performed for all samples from SEM results. Doped samples were also investigated by luminescence spectroscopy and emission kinetic measurements. All oxide samples present a particle average diameter distribution range from 110 to 150 nm and a decrease of particle average diameter with the presence of Eu3+. The particle size decrease is almost the same for all samples with different doping ion concentration. Therefore, the presence of doping ion may be inhibiting particle growth after the nucleation process. From spectroscopic studies, the doping ion distribution in the surface of oxide samples can be considered homogeneous because concentration quenching is not observed, as well as a significant difference among the calculated lifetime for each sample. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Influence of Zn2+ co-doping ion on Eu3+-O2- associate luminescence in Sr2SiO4

This work reports on the study about the luminescence behavior of Eu3+-O2- associates in Sr2SiO4 doped with Eu3+, or simultaneously doped with Eu3+ and Zn2+ ions, where the Zn2+ doping ion acts as a charge compensating agent. Both Sr2SiO4:Eu3+ and Sr2SiO4:Eu3+,Zn2+ emission spectra show two types D-5(0)-->F-7(0) type transitions, one type related to Eu3+ in the Sr2+ Site, at 577 and 580 nm and the other one related to Eu3+-O2- associates, at 574 nm. Excitation spectra present two CT bands at 275 and 324 nm related to each emission center, respectively. Comparing the relative intensities between the emission spectra, the 0-->0 transition at 574 nm assigned to Eu3+-O2- associates in the Sr2SiO4:Eu3+ emission spectrum is much more intense than the same transition in the Sr2SiO4:Eu3+,Zn2+ emission spectrum. Moreover, in the Sr2SiO4:Eu3+ excitation spectrum, the intensity ratio between the CT band related to the Eu3+-O2- emission center and Eu3+ F-7-->L-5(6) transition is also larger than in the Sr2SiO4:Eu3+,Zn2+ one. Therefore, the presence of Zn2+ species provides an extra charge compensating mechanism, which decreases the formation of Eu3+-O2- associates. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Study of Ti-modified columbite route and the effect of lithium doping in 0.9PMN-0.1PT ceramics

The influence of lithium on the structural characteristics of PMN-PT ceramic was studied. The synthesis of PMN-PT powders using this precursor leads to the formation of high amount of perovskite phase. The insertion of Li(+) ions in B-site affects the microstructure because the rise in mass transport changes the mechanical characteristics of sintered ceramic. Higher values of K(m) and T(m) were gotten when lithium is inserted into perovskite phase. Secondary phase was found when lithium content increase beyond 1 mol%, besides the occurrence of transgranular fractures in sintered ceramic. Also, the additive acts increasing the relaxor behavior.

Magnetic doping in Zn7-xMxSb2O12 spinels (M = Ni and Co)

In this article we present a concise report on our studies on the magnetic behavior and structural arrangements of the inverse spinel Zn7-xMxSb2O12 system (M = Ni, Co). Studies on the temperature dependence of the magnetization (M) of several samples in this system showed the occurrence of a spin-glass-like state in temperatures around 10 K. The capability of this system to hold magnetic ions in either octahedral and/or tetrahedral positions is responsible for the occurrence of competing ferromagnetic and antiferromagnetic interactions. This condition is likely to cause the appearance of the observed spin-glass-like behavior. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Rural-urban migration in D-dimensional lattices

The rural-urban migration phenomenon is analyzed by using an agent-based computational model. Agents are placed on lattices which dimensions varying from d = 2 up to d = 7. The localization of the agents in the lattice defines that their social neighborhood (rural or urban) is not related to their spatial distribution. The effect of the dimension of lattice is studied by analyzing the variation of the main parameters that characterizes the migratory process. The dynamics displays strong effects even for around one million of sites, in higher dimensions (d = 6, 7).

SUPERSYMMETRIC CONSTRUCTION OF W-ALGEBRAS FROM SUPER TODA AND WZNW THEORIES

A systematic construction of super W algebras in terms of the WZNW model based on a super Lie algebra is presented. These are shown to be the symmetry structure of the super Toda models, which can be obtained from the WZNW theory by Hamiltonian reduction. A classification, according to the conformal spin defined by an improved energy momentum tensor, is discussed in general terms for all super Lie algebras whose simple roots are fermionic. A detailed discussion employing the Dirac bracket structure and an explicit construction of W algebras for the cases of OSP(1, 2), OSP(2, 2), OSP(3, 2) and D(2, 1\ alpha) are given. The N = 1 and N = 2 superconformal algebras are discussed in the pertinent cases.

Zeta potential and doping in polyaniline dispersions

Polyaniline (PAni) has been classified as an intractable polymer, particularly in its conducting form, the emeraldine salt (ES). Therefore one can consider the mixture of water and PAni as a suspension. The conducting form of PAni can be obtained by a doping process known as acid doping, in which a strong acid turns PAni from its insulating form, the emeraldine base (EB), into the conducting form, the emeraldine salt. With the objective of establishing a correlation between the doping level and the zeta potential of polyaniline dispersions, polyaniline + HCl aqueous suspensions were prepared. Positive zeta potential values for the various suspensions of PAni showed that it acquired positive charges after the doping process. It was also observed an increase in zeta potential values as HCl concentration increased, which could be correlated to UV-visible spectra of PAni suspensions.

The effect of Nb doping on ferroelectric properties of PZT thin films prepared from polymeric precursors

Pure and Nb doped PbZr0.4Ti0.603 thin films was prepared by the polymeric precursor method and deposited by spin coating on Pt/Ti/SiO2/Si (100) substrates and annealed at 700 degreesC. The films are oriented in (1 1 0) and (1 0 0) direction. The electric properties of PZT thin films show strong dependence of the crystallographic orientation. The P-E hysteresis loops for the thin film with composition PbZr0.39Ti0.6Nb0.103 showed good saturation, with values for coercive field (E-c) equal to 60 KV cm(-1) and for remanent polarization (P-r) equal to 20 muC cm(-2). The measured dielectric constant (epsilon) is 1084 for this film. These results show good potential for application in FERAM. (C) 2004 Elsevier B.V. All rights reserved.

Improvement of the corrosion resistance of polysiloxane hybrid coatings by cerium doping

Polysiloxane hybrid films were deposited on stainless steel by dip-coating using a sol prepared by hydrolytic co-polycondensation of tetraethoxysilane (TEOS) and 3-methacryloxy propyltrimethoxysilane (MPTS), followed by radical polymerization of methacrylic moieties. The TEOS/MPTS ratio was chosen equal to 2 and the Ce/Si ratio varied between 0.01 and 0.1. The effects of cerium concentration and valence (Ce(III) and Ce (IV)) on the structural features of polysiloxane films were studied by X-ray photoelectron spectroscopy (XPS) and (29)Si nuclear magnetic resonance (NMR). The corrosion protection of stainless steel by the hybrid coatings was investigated by XPS, electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization curves, after immersion in saline and acid solutions. The NMR results have shown for Ce(IV) doped films a high degree of polycondensation of up to 89%. Electrochemical analysis has evidenced that hybrid films with the lowest Ce concentration act as an efficient diffusion barrier by increasing the corrosion resistance and reducing the current densities up to 3 orders of magnitude compared to bare stainless steel. The analysis of structural effects induced by Ce(III) and Ce(IV) species, performed by XPS, indicates that the improved corrosion protection of Ce(IV) doped films might be mainly related to the enhanced polymerization of siloxane groups. (C) 2010 Elsevier B.V. All rights reserved.

Heritability Estimate and Genetic Correlations of Reproductive Features in Nellore Bulls, Offspring of Super Precocious, Precocious and Normal Cows Under Extensive Farming Conditions

The present work aimed to estimate heritability and genetic correlations of reproductive features of Nellore bulls, offspring of mothers classified as superprecocious (M1), precocious (M2) and normal (M3). Twenty one thousand hundred and eighty-six animals with average age of 21.29 months were used, evaluated through the breeding soundness evaluation from 1999 to 2008. The breeding soundness features included physical semen evaluation (progressive sperm motility and sperm vigour), semen morphology (major, minor and total sperm defects), scrotal circumference (SC), testicular volume (TV) and SC at 18 months of age (SC18). The components of variance, heritability and genetic correlations for and between the features were estimated simultaneously by restricted maximum likelihood, with the use of the vce software system vs 6. The heritability estimates were high for SC18, SC and TV (0.43, 0.63 and 0.54; 0.45, 0.45 and 0.44; 0.42, 0.45 and 0.41, respectively for the categories of mothers M1, M2 and M3) and low for physical and morphological semen aspects. The genetic correlations between SC18 and SC were high, as well as between these variables with TV. High and positive genetic correlations were recorded among SC18, SC and TV with the physical aspects of the semen, although no favourable association was verified with the morphological aspects, for the three categories of mothers. It can be concluded that the mothers sexual precocity did not affect the heritability of their offspring reproduction features.

Influence of doping on the preferential growth of alpha-MoO3

MoO3 is a lamellar material with applications in different areas, as solid lubricants, catalysis, solar cells, etc. In the present work, MoO3 powders, synthesized by the polymeric precursor method, were doped with nickel or cobalt. The powder precursors were characterized by TG/DTA. After calcination between 500 and 700 degrees C, the samples were characterized by X-ray diffraction, infrared and Raman spectroscopy and scanning electron microscopy. beta-MoO3 was obtained after calcination at low temperatures. With the temperature increase, alpha-MoO3 is observed, with a preferential growth of the (0 2k 0) planes, when the material is doped and calcined at 700 degrees C. Doping with nickel increases five times the preferential growth. As a consequence, plate-like particles are observed. (c) 2007 Elsevier B.V. All rights reserved.

The dielectric suppress and the control of semiconductor non-Ohmic feature of CaCu3Ti4O12 by means of tin doping

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Band edge states of the < n >=0 gap of Fibonacci photonic lattices

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Anderson localization and Brewster anomalies in photonic disordered quasiperiodic lattices

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)