Hydroxyapatite deposition study through polymeric process on commercially pure Ti surfaces modified by laser beam irradiation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Surface Passivation of Nanoporous TiO2 via Atomic Layer Deposition of ZrO2 for Solid-State Dye-Sensitized Solar Cell Applications

We report here the utilization of atomid layer deposition to passivate surface map states in mosoporous TiO2 nanoparticles for solid state dye sensitized solar cells based on 9,9'-spirobifluorene (spiro-OMeTAD). By depositing ZrO2 films with angstrom-level precision, coating the mesoporous TiO2 produces over a two-fold enhancement in short-circuit current density, as compared to a control device. Impedance spectroscopy measurements provide evidence that the ZrO2 coating reduces recombination lossed at the TiO2/spiro-OMeTAD interface and passivates localized surface states. Low-frequency negative capacitances, frequently observed in nanocomposite solar cells, have been associated with the surface-state mediated charge transfer from TiO2 to the spiro-OMeTAD.

Seeder-fertilizer machine: energetic demand as a function of vegetal covering handling and manure deposition shank depth in no-tillage system

O trabalho teve por objetivo avaliar a demanda energética de uma semeadora-adubadora, em função do tipo e manejo da cultura de cobertura vegetal e da profundidade da haste de deposição de adubo. Foi utilizado um trator Valtra BM100, instrumentado, para tracionar uma semeadora-adubadora de precisão equipada com quatro fileiras de semeadura espaçadas de 0,9 m para cultura de milho. O experimento foi conduzido em parcelas subsubdivididas, na área experimental do Laboratório de Máquinas e Mecanização Agrícola (LAMMA) da UNESP-Jaboticabal, utilizando duas culturas de cobertura (mucuna-preta e crotalária), três manejos dessas coberturas, sendo dois mecânicos (triturador de palhas e rolo-faca) e um químico (pulverização com herbicida), realizados 120 dias após a semeadura das culturas de cobertura e três profundidades da haste de deposição do adubo (0,11; 0,14 e 0,17 m), perfazendo 18 tratamentos, com quatro repetições, totalizando 72 observações. Foram avaliados os parâmetros velocidade de deslocamento, patinagem, força na barra de tração, força de pico, potência na barra de tração, potência de pico e consumo de combustível. Pôde-se concluir que a força na barra de tração foi menor para as profundidades de 0,11 e 0,14 m da haste sulcadora de adubo, o mesmo ocorrendo para força de pico, potência na barra de tração e consumo volumétrico. O consumo específico foi menor na profundidade de 0,17 m da haste sulcadora de adubo. As culturas de cobertura e seus manejos não interferiram no desempenho das máquinas estudadas.

Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Improvement of the dielectric and ferroelectric properties in superlattice structure of Pb(Zr,Ti)O-3 thin films grown by a chemical solution route

Making heterolayered perovskite materials constitutes an approach for the creation of better dielectric and ferroelectric properties. In the experiment reported here, heterolayered PZT40/PZT60 films were grown on Pt/Ti/SiO2/Si (100) by a chemical solution deposition. The dielectric constant of the heterolayered thin film was significantly enhanced compared with that of pure PZT40 and PZT60 thin films. A dielectric constant of 701 at 100 kHz was observed for a stacking periodicity of six layers having a total thickness of 150 nm. The heterolayered film exhibited greater remanent polarization than PZT60 and PZT40 films. The values of remanent polarization were 7.9, 18.5, and 31 muC/cm(2), respectively, for pure PZT60, PZT40, and heterolayered thin films, suggesting that the superior dielectric and ferroelectric properties of the heterolayered thin film resulted from a cooperative interaction between the ferroelectric phases made from alternating tetragonal and rhombohedral phases of PZT, simulating the morphotropic phase boundary of this system. (C) 2004 American Institute of Physics.

Influence of agricultural biomass burning on aerosol size distribution and dry deposition in southeastern Brazil

The size distributed composition of ambient aerosols is used to explore seasonal differences in particle chemistry and to show that dry deposition fluxes of soluble species, including important plant nutrients, increase during periods of biomass (sugar cane trash) burning in São Paulo State, Brazil. Measurements were made at a single site centrally located in the State's sugar cane growing region but away from the immediate vicinity of burns, so that the air sampled was representative of the regional background. Calculation of ion equivalent balances showed that during burning periods smaller particles (Aitken and accumulation modes) were more acidic, containing higher concentrations of SO(4)(2-), oxalate, NO(3)(-), HCOO(-), CH(3)COO(-), and Cl(-), but insufficient NH(4)(+) and K(+) to achieve neutrality. Larger particles showed an anion deficit due to the presence of unmeasured ions and comprised resuspended dusts modified by accumulation of nitrate, chloride, and organic anions. Increases of resuspended particles during the burning season were attributed to release of earlier deposits from the surfaces of burning vegetation as well as increased vehicle movement on unsurfaced roads. During winter months the relative contribution of combined emissions from road transport and industry diminished due to increased emissions from biomass combustion and other activities specifically associated with the harvest period. Positive increments in annual particulate dry deposition fluxes due to higher fluxes during the sugar cane harvest were 44.3% (NH(4)(+)), 42.1 % (K(+)), 31.8% (Mg(2+)), 30.4% (HCOO(-)), 12.8% (Cl(-)), 6.6% (CH(3)COO(-)), 5.2% (Ca(2+)), 3.8% (SO(4)(2-)), and 2.3% (NO(3)(-)). Na(+) and oxalate fluxes were seasonally invariant. Annual aerosol dry deposition fluxes (kg ha(-1)) were 0.5 (Na(+)), 0.25 (NH(4)(+)), 0.39 (K(+)), 0.51 (Mg(2+)), 3.19 (Ca(2+)), 1.34 (Cl(-)), 4.47 (NO(3)(-)), 3.59 (SO(4)(2-)), 0.58 (oxalate), 0.71 (HCOO(-)), and 1.38 (CH(3)COO(-)). Contributions of this mechanism to combined aerosol dry deposition and precipitation scavenging (inorganic species, excluding gaseous dry deposition) were 31% (Na(+)), 8% (NH(4)(+)), 26% (K(+)), 63% (Mg(2+)), 66% (Ca(2+)), 32% (Cl(-)), 33% (NO(3)(-)), and 36% (SO(4)(2-)).

SrBi2Ta2O9 ferroelectric thick films prepared by electrophoretic deposition using aqueous suspension

SrBi2Ta2O9 ferroelectric thick films were prepared by electrophoretic deposition (EPD). For that, ceramic powders were prepared by chemical method in order to obtain compounds with chemical homogeneity. The polymeric precursor method was used for the synthesis of the SrBi2Ta2O9 powder. The crystallographic structure of the powder was examined by X-ray diffraction, and the surface area was determined by single point BET adsorption. The 0.03 vol.% suspension was formed by dispersing the powder in water using two different polymers as dispersants: an ester polyphosphate (C213) and an ammonium polyacrilate (Darvan 821-A). It was investigated the influence of the different dispersants in the surface properties of the powder by zeta potential measurements. The films were deposited on platinum-coated alumina and Pt/Ti/SiO2/Si substrates by a 4 mA constant current, for 10 min, using two parallel electrodes placed at a separation distance of 3 min in the suspension. Several cycles of deposition-drying of the deposit were carried out until reaching the desired thickness. After thermal treatment at temperatures ranging from 700 to 1000 degreesC, the films were characterized by X-ray diffraction and scanning electron microscopy for the microstructure observation. (C) 2003 Elsevier Ltd. All rights reserved.

Study of electrical, chemical and structural characteristics of superconductor thin film obtained by polymeric precursors method

Superconductor films of the BSCCO system have been grown by dip coating technique with good success. The chemical method allows us to grow high temperature superconductor thin films to get better control of stoichiometry, large areas and is cheaper than other methods. There is a great technological interest in growth oriented superconductor films due anisotropic characteristics of superconductor materials of high critical temperature, specifically the cuprates, as we know that the orientation may increase the electrical transport properties. Based on this, the polymeric precursor method has been used to obtain thin films of the BSCCO system. In this work we have applied that method together with the deposition technique known as dip coating to obtain Bi-based superconductor thin films, specifically, Bi1.6Pb0.4Sr2.0C2.0Cu3.0Ox+8, also known as 2223 phase with a critical temperature around 110 K. The films with multilayers have been grown on crystalline substrates of LaAlO3 and orientated (100) after being heat treated around 790 degrees C - 820 degrees C in lapse time of 1 hour in a controlled atmosphere. XRD measurements have shown the presence of a crystalline phase 2212 with a critical temperature around 85 K with (001) orientation, as well as a small fraction of 2223 phase. SEM has shown a low uniformity and some cracks that maybe related to the applied heat treatment. WDS has also been used to study the films composition. Different heat treatments have been used with the aim to increase the percentage of 2223 phase. Measurements of resistivity confirmed the presence of at least two crystalline phases, 2212 and 2223, with T-c around 85 K and 110 K, respectively.

Precipitation chemistry and wet deposition in Kruger National Park, South Africa

The chemical composition, as well as the sources contributing to rainwater chemistry have been determined at Skukuza, in the Kruger National Park, South Africa. Major inorganic and organic ions were determined in 93 rainwater samples collected using an automated wet-only sampler from July 1999 to June 2002. The results indicate that the rain is acidic and the averaged precipitation pH was 4.72. This acidity results from a mixture of mineral acids (82%, of which 50% is H2SO4) and organic acids (18%). Most of the H2SO4 component can be attributed to the emissions of sulphur dioxide from the industrial region on the Highveld. The wet deposition of S and N is 5.9 kgS.ha(-1).yr(-1) and 2.8 kgN.ha(-1).yr(-1), respectively. The N deposition was mainly in the form of NH4+. Terrigenous, sea salt component, nitrogenous and anthropogenic pollutants have been identified as potential sources of chemical components in rainwater. The results are compared to observations from other African regions.

Preparation, microstructural and electrical characterization of SrTiO3 thin films prepared by chemical route

Polycrystalline SrTiO3 thin films having a cubic perovskite structure were prepared at different temperatures by the polymeric precursor method on platinum-coated silicon substrate. Crystalline films with uniform composition and thickness were prepared by spin-coating and the post-deposition heat treatment was carried out at different temperatures. The film showed good structural, dielectric, and insulating properties, Scanning electron microscopy (SEM) micrographs showed no occurrence of interdiffusion between the bottom electrode (platinum) and the film during post-annealing, indicating a stable interface between the SrTiO3 and the bottom electrode. The dielectric constant and dissipation factor at a frequency of 100 kHz were 250 and 0.01, respectively, for a 360 nm thick film annealed at 600 degreesC. The capacitance versus applied voltage characteristics showed that the capacitance was almost independent of the applied voltage. The I-V characteristics were ohmic in low fields and a Schottky emission and/or Poole-Frenkel emission were postulated in high fields. Room temperature leakage current density was found to be in the order of 10(-7) A/cm(2) for a 360 nm thick film in an applied electric field of about 100 kV/cm. The charge storage density of 36 fC/mum(2) was obtained in an applied electric field of about 100 kV/cm. (C) 2001 Published by Elsevier B.V. Ltd. All rights reserved.

Preparation of SrBi2Ta2O9 ferroelectric thick films by electrophoretic deposition using aqueous suspensions

SrBi2Ta2O9 ferroelectric thick films were prepared by electrophoretic deposition (EPD). For that, ceramic powders were prepared by chemical method in order to obtain compounds with chemical homogeneity. The polymeric precursor method was used for the synthesis of the SrBi2Ta2O9 powder. The crystallographic structure of the powder was examined by X-ray diffraction, and the surface area was determined by single point BET adsorption. The 0.03 vol% suspension was formed by dispersing the powder in water using two different polymers as dispersants: an ester polyphosphate (C213) and an ammonium polyacrilate (Darvan 821-A). The influence of the different dispersants on the powder surface properties were investigated by zeta potential measurements. The films were deposited on platinum-coated alumina and Pt/Ti/SiO2/Si substrates by electrophoretic deposition using a 4 mA constant current, for 10 min, with two parallel electrodes placed at a separation distance of 3 min in the suspension. Several cycles of deposition-drying of the deposit was carried out until the desired thickness was obtained. After thermal treatment at temperatures ranging from 700 to 1000degreesC, the films were characterized by X-ray diffraction and scanning electron microscopy.

Developments in hot-filament metal oxide deposition (HFMOD)

Hot-filament metal oxide deposition (HFMOD) is a variant of conventional hot-filament chemical vapor deposition (HFCVD) recently developed in our laboratory and successfully used to obtain high-quality, uniform films of MOx WOx and VOx. The method employs the controlled oxidation of a filament of a transition metal heated to 1000 degrees C or more in a rarefied oxygen atmosphere (typically, of about 1 Pa). Metal oxide vapor formed on the surface of the filament is transported a few centimetres to deposit on a suitable substrate. Key system parameters include the choice of filament material and diameter, the applied current and the partial pressures of oxygen in the chamber. Relatively high film deposition rates, such as 31 nm min(-1) for MoOx, are obtained. The film stoichiometry depends on the exact deposition conditions. MoOx films, for example, present a mixture of MoO2 and MoO3 phases, as revealed by XPS. As determined by Li+ intercalation using an electrochemical cell, these films also show a colouration efficiency of 19.5 cm(2) C-1 at a wavelength of 700 nm. MOx and WOx films are promising in applications involving electrochromism and characteristics of their colouring/bleaching cycles are presented. The chemical composition and structure of VOx films examined using IRRAS (infrared reflection-absorption spectroscopy), RBS (Rutherford backscattering spectrometry) and XPS (X-ray photoelectron spectrometry) are also presented. (c) 2007 Elsevier B.V. All rights reserved.

Influence of Intensive Agriculture on Dry Deposition of Aerosol Nutrients

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Plasma-deposition of Ag-containing polyethyleneoxide-like coatings

Ag-containing polyethyleneoxide (FEO)-like thin films have been deposited in Radio Frequency Glow Discharges fed with vapors of diethyleneglycol-dimethyl-ether and argon. Proper experimental conditions have been utilized in order to fragment the monomer in the glow and, at the same time, sputter Ag from the silver RF cathode of the reactor, in a way that polyethyleneoxide(PEO)-like coatings with embedded Ag clusters have been deposited at the ground electrode. The composition of the coatings has been investigated by means of different techniques; the plasma process has been investigated by means of Actinometric Optical Emission Spectroscopy. A correlation has been found between the amount of silver embedded in the coatings and that sputtered in the discharge, monitored by actinometry, that could eventually be utilized to control in situ the deposition process.