Thermogravimetric and UV-vis spectroscopic studies of chromium redox reactions in rutile pigments

In this study undoped and Cr, Sb or Mo doped TiO(2) were synthesized by polymeric precursor method and characterized by X-ray diffraction, UV-VIS spectroscopy, infrared spectroscopy and thermogravimetry (TG). The TG curves showed a continuous mass loss assigned to the hydroxyl elimination and Cr(6+) reduction. Doped TiO(2) samples showed a higher mass loss assigned to water and gas elimination at lower temperatures. In these doped materials a decrease in the anatase-rutile phase transition temperature was observed. After calcination at 1,000 A degrees C, rutile was obtained as a single phase material without the presence of Cr(6+).

Sequential spectrophotometric determination of chromium(III) and chromium(VI) using flow injection analysis

A flow injection analysis (FIA) procedure for the speciation of Cr(III) and Cr(VI) using the 1,5-diphenylcarbazide (DPC) method is presented. As Cr(III) does not interfere in the Cr(VI) - DPC reaction, both Cr(VI) and total chromium [after the on-line oxidation of Cr(III) by Ce(IV)] are sequentially determined. Cr(III) is obtained by difference. Under the experimental conditions described, the calibration graphs are linear up to 2 μg mh1 of Cr(VI) and 4 μg ml-1 of Cr(III). The detection limits found were 18 ng ml -1 for Cr(VI) and 55 ng ml-1 for Cr(III), at a signal to noise ratio of 3. The common interfering elements in the Cr(VI) - DPC reaction were investigated under dynamic FIA conditions. The FIA method was also compared with the conventional spectrophotometric procedure.

Pore size evolution during sintering of ceramic oxides

This paper reviews the influence of particle size distribution, agglomerates, rearrangement, sintering atmospheres and impurities on the pore evolution of some commonly studied oxides. These factors largely affect sintering mechanisms due to modifications of diffusion coefficients or evaporation-condensation. Very broad particle size distribution leads to grain growth and agglomerates densify first. Rearrangement of particles due to neck asymmetry mainly in the early stage of sintering is responsible for a high rate of densification in the first minutes of sintering by collapse of large pores. Sintering atmospheres play an important role in both densification and pore evolution. The chemical interaction of water molecules with several oxides like MgO, ZnO and SnO2 largely affects surface diffusion. As a consequence, there is an increase in the rates of pore growth and densification for MgO and ZnO and in the rate of pore growth for SnO2. Carbon dioxide does not affect the rate of sintering of MgO but greatly affects both rates of pore growth and densification of ZnO. Oxygen concentration in the atmosphere can especially affect semiconductor oxides but significantly affects the rate of pore growth of SnO2. Impurities like chlorine ions increase the rate of pore growth in MgO due to evaporation of HCl and Mg(OH)Cl, increasing the rate of densification and particle cuboidization. CuO promotes densification in SnO2, and is more effective in dry air. The rate of densification decrease and pore widening are promoted in argon. An inert atmosphere favors SnO2 evaporation due to reduction of CuO. © 1990.

Optical properties of chromium-doped fluoroindate glasses

This work reports on the optical properties of Cr3+ ions in the pseudoternary system InF3-GdF3-GaF3. Linear properties, investigated through absorption and emission spectra, provide information on the crystal field, the frequency, and number of phonons emitted during the absorption to the 4T2 band and the emission to the 4A2 ground state, and the Fano antiresonance line shape in the vicinity of the 4A2→2E transition. A study of the nonlinear refractive index as a function of the wavelength, carried out with the Z-scan technique, provides spectroscopic data about electronic transitions starting from the excited state.

Particle growth during calcination of polycation oxides synthesized by the polymeric precursors method

The particle-growth kinetics of sodium niobate and zirconium titanate powders that were processed by the polymeric precursors method were studied. The growth kinetics that were studied for the particle, in the final stage of crystallization, showed that the growth process occurs in two different stages. For temperatures <800°C, the particle-growth mechanism is associated with surface diffusion, with an activation energy in the range of 40-80 KJ/mol. For temprratures >800°C, particle growth is controlled by densification of the nanometric particle cluster and by a neck-size-controlled particle-growth mechanism. The results suggest that this behavior was typical of the synthesis method, because two different polycation oxides presented the same behavior.

Marginal fit of nickel-chromium copings before and after internal adjustments with duplicated stone dies and disclosing agent.

STATEMENT OF PROBLEM: Despite careful procedures, master stone dies may be damaged during laboratory procedures. The dentist routinely adjusts castings because the marginal fit of casting is not as accurate as on the dies. PURPOSE: This study evaluated the technique of internal adjustment of castings with use of duplicated stone dies and a disclosing agent to improve marginal fit discrepancy. MATERIAL AND METHODS: Thirty-two nickel-chromium copings were fabricated and simulated standard clinical and laboratory procedures with 2 variables: tooth preparation convergence angles of 6 and 18 degrees, with or without internal relief. Master stone dies and their duplicates were selected for coping construction and internal adjustment, respectively. A specimen positioning device was coupled with a Toolmakers microscope to allow reproducibility of measurements. Each coping was evaluated at 8 locations of its marginal perimeter, before and after internal adjustment. RESULTS: Marginal fit discrepancy of copings were significantly reduced with an internal adjustment technique (mean > 52%) for all experimental groups. Tooth preparations with greater convergence and internally relieved castings recorded a better marginal fit. CONCLUSION: The casting internal adjustment technique with use of duplicated stone dies and a disclosing agent substantially reduced marginal fit discrepancy.

Chromium-containing silica materials

Chromium-containing silica samples were obtained from soluble sodium silicate solutions in the presence of different chromium nitrate concentrations. Precipitation was carried out in ethanolic media. Gel precipitate was dried by liophylization and samples measured by transmission electron microscopy (TEM), X-ray energy-dispersive spectrometer, X-ray mapping, X-ray photoemission spectroscopy (XPS), and particle size analysis. Spherical chromium containing silica particles with 3.5% and 4.8% (at.%) of chromium were obtained. Particle size analysis results showed that with increased addition of chromium in sodium silicate solutions produces agglomerates whose sizes range from 1 to 0.2 μm. Chromium mapping and XPS results show that chromium oxide is preferentially segregated on particle surfaces. Chromium oxide was detected on particle surface with a binding energy of 576.77 ± 0.05 eV as obtained from XPS analysis. During the hydrolysis and condensation processes chromium oxide precipitates on the silica surface and it affects the silica chain size. © 2000 Elsevier Science B.V. All rights reserved.

Effects of tungsten carbide thermal spray coating by HP/HVOF and hard chromium electroplating on AISI 4340 high strength steel

In cases of decorative and functional applications, chromium results in protection against wear and corrosion combined with chemical resistance and good lubricity. However, pressure to identify alternatives or to improve conventional chromium electroplating mechanical characteristics has increased in recent years, related to the reduction in the fatigue strength of the base material and to environmental requirements. The high efficiency and fluoride-free hard chromium electroplating is an improvement to the conventional process, considering chemical and physical final properties. One of the most interesting, environmentally safer and cleaner alternatives for the replacement of hard chrome plating is tungsten carbide thermal spray coating, applied by the high velocity oxy-fuel (HVOF) process. The aim of this study was to analyse the effects of the tungsten carbide thermal spray coating applied by the HP/HVOF process and of the high efficiency and fluoride-free hard chromium electroplating (in the present paper called 'accelerated'), in comparison to the conventional hard chromium electroplating on the AISI 4340 high strength steel behaviour in fatigue, corrosion, and abrasive wear tests. The results showed that the coatings were damaging to the AISI 4340 steel behaviour when submitted to fatigue testing, with the tungsten carbide thermal spray coatings showing the better performance. Experimental data from abrasive wear tests were conclusive, indicating better results from the WC coating. Regarding corrosion by salt spray test, both coatings were completely corroded after 72 h exposure. Scanning electron microscopy technique (SEM) and optical microscopy were used to observe crack origin sites, thickness and adhesion in all the coatings and microcrack density in hard chromium electroplatings, to aid in the results analysis. © 2001 Elsevier Science B.V. All rights reserved.

Spectroscopic studies of SnO2 doped with Cr, Co or Nb

SnO2 ceramics doped with different amounts of Co, Cr or Nb were investigated using visible and infrared spectroscopy at room temperature. Based on the observed d-d transitions the valence states of incorporated dopants were determined. Values of the optical band-gap were calculated in all samples. The infrared spectra of the samples displayed variations in the position, relative intensity and width of the bands, which were attributed to the presence of dopants.

Toxic and genotoxic effects of trivalent and hexavalent chromium - A review

During the last years, the emission of heavy metals to the environment has increased, causing a severe negative impact to the ecosystems and seriously compromising human health due to their mutagenic potential. Tri- (III) and hexavalent (VI) chromium (Cr) constitute the oxidative states of the metal chromium that are active in living organisms. These two oxidation states of the chromium differ with regards to their cellular effects, mainly due to the different abilities they possess in relation to easy of transport through biological membranes. Cr VI is transported into the cell through transference channels of endogenous anions that are isostructural and isoelectronical to Cr VI, such as SO 4 -2 and HPO 4 -2. On the other hand, Cr III is unable to diffuse through the cell membrane. Its existence inside the cells is generally due to the reduction of Cr VI, the endocytosis, or the absortion by the cells via phagocytosis. Cr III acts directly on the DNA molecule, while Cr VI reacts little with this molecule. In the ecosystem, however, Cr VI is more dangerous since this is the form that presents greater reactivity with biological membranes, crossing them and being easily incorporated into the cell. In the cell it is biotransformed to Cr III, a potentially mutagenic molecule. In vivo and in vitro studies have shown that organisms exposed to Cr VI present greater induction to a variety of damages to the DNA molecule. Among the damages induced by Cr, changes in the structure of the DNA molecule have been reported, with breaks of the major chain and base oxidation. In the organisms, these alterations generate chromosomal aberrations, micronucleus formation, sister chromatid exchanges, and errors in DNA synthesis.

Magnetic properties of spinel-type oxides NiMn2-xMexO4

New materials, based on the well-known spinel compound NiMn 2O4, have been synthesized and characterized from the magnetic point of view. The manganese cation was partially substituted in the general formula NiMn2-xMexO4, by nonmagnetic and magnetic elements, such as Me = Ga, Zn, Ni and Cr (0 × 1). Prior to the determination of their magnetic properties, the non-substituted spinel NiMn2O4 was carefully characterized and studied as a function of the oxygen stoichiometry, based on the influence of the annealing atmosphere and quenching rate. The ferrimagnetic character was observed in all samples, with a paramagnetic-to-ferromagnetic transition temperature T c stabilized at 110 K, and well defined long-range antiferromagnetic interactions at lower temperatures, which depend on the applied field and the substitute concentration. © 2006 Sociedad Chilena de Química.

Evaluation of the genotoxic potential due to the action of an effluent contaminated with chromium, by the comet assay in CHO-K1 cultures

The comet assay technique has been considered to be more efficient in the biomonitoring of aquatic environments that the micronucleus and sister chromatid exchange techniques. The comet assay has been used to determine breaks in the DNA strands of organisms exposed to pollutants with a genotoxic potential. The comet technique was applied to CHO-K1 cells in order to evaluate the genotoxic potential of the waters of the Sapucaizinho River (Municipality of Patrocínio Paulista, State of São Paulo, Brazil), which receive tannery effluents and therefore are contaminated with chromium. The results indicated high genotoxicity of the waters collected at sites located downstream from the emission of tannery effluents, where the concentration of chromium was found to be high.

Anelastic spectroscopy in superconducting oxides

Since the discovery of the high Tc superconductors, several works have been made about the different properties of these materials. Anelastic spectroscopy experiments are sensitive tools to the study of defects in solids and phase transitions. By this technique, we can distinguish the different types of atomic jumps that happen to different temperatures. The intensity of the peaks in the anelastic spectrum and the step in the torsional modulus are related with the concentration of the relaxing entities, and the position of the peaks is determined by its mobility. In this paper, the study on Bi and Sm based superconducting oxides was made by anelastic relaxation measurements using a torsion pendulum. The samples were submitted to successive thermal treatments in high vacuum, in the temperature range between 100 K and 650 K, heating rate about 1 K/min. For Bi based superconducting oxides the results shown two peaks, that were associated to interstitial oxygen mobility and to orthorhombic to monoclinic phase transition. For Sm based superconducting oxides the results shown a relaxation peak that was attributed to the jumps of the oxygen atoms in the inter-chains O1 and 05 of the lattice.

Screen-printed carbon electrode modified with poly-L-histidine applied to voltammetric determination of chromium (VI)

The present work reports the use of a screen-printed carbon electrode (SPCE) modified by poly-L-histidine film to determine chromium (VI). Stable films can be formed by direct addition of PH solution 1 % (w/v) on the electrode surface, followed by heating at 80°C during 5 min. Calibration curves can be constructed for Cr(VI) from 1.0 × 10-5 mol L-1 to 7.0 × 10-5 mol L-1 Cr (VI) in acetate buffer pH 4 using a preconcentration step of 60s at open circuit potential. A relative standard deviation of 3.2% was for five determination of 4.0 × 10 -5 mol L-1 Cr (VI). The method was successful applied to determination of Cr(VI) in wastewater samples from a leather dyeing industry. copyright The Electrochemical Society.