Marginal fit of nickel-chromium copings before and after internal adjustments with duplicated stone dies and disclosing agent.

STATEMENT OF PROBLEM: Despite careful procedures, master stone dies may be damaged during laboratory procedures. The dentist routinely adjusts castings because the marginal fit of casting is not as accurate as on the dies. PURPOSE: This study evaluated the technique of internal adjustment of castings with use of duplicated stone dies and a disclosing agent to improve marginal fit discrepancy. MATERIAL AND METHODS: Thirty-two nickel-chromium copings were fabricated and simulated standard clinical and laboratory procedures with 2 variables: tooth preparation convergence angles of 6 and 18 degrees, with or without internal relief. Master stone dies and their duplicates were selected for coping construction and internal adjustment, respectively. A specimen positioning device was coupled with a Toolmakers microscope to allow reproducibility of measurements. Each coping was evaluated at 8 locations of its marginal perimeter, before and after internal adjustment. RESULTS: Marginal fit discrepancy of copings were significantly reduced with an internal adjustment technique (mean > 52%) for all experimental groups. Tooth preparations with greater convergence and internally relieved castings recorded a better marginal fit. CONCLUSION: The casting internal adjustment technique with use of duplicated stone dies and a disclosing agent substantially reduced marginal fit discrepancy.

Effect of air-powder system on titanium surface on fibroblast adhesion and morphology.

PURPOSE: To evaluate the number and morphology of fibroblasts grown on machined titanium healing abutments treated with an airpowder system. MATERIALS AND METHODS: Twenty-six abutments were assigned to two experimental groups: control (no treatment) and treated (exposed to the Prophy-Jet for 30 seconds). The specimens were incubated for 24 hours with fibroblastic cells in multiwell plates, followed by routine laboratory processing for scanning electron microscope analysis. The specimens were photographed at x 350, and the cell number was counted on an area of approximately 200 um2. RESULTS: No significant differences were found on morphology between the groups (P > 0.05); however, the control group presented a significantly greater amount of cells (71.44 +/- 31.93, mean +/- SD) in comparison with treated group (35.31 +/- 28.14), as indicated by a nonpaired t test (P = 0.001). CONCLUSION: The use of an air-abrasive prophylaxis system on the surface of titanium healing abutments reduced the cells proliferation but did not influence cell morphology.

Histomorphometric evaluation of a threaded, sandblasted, acid-etched implant retrieved from a human lower jaw: A case report

The purpose of this study was to histomorphometrically evaluate the bone-to-implant contact and bone area around a titanium implant retrieved from a human lower jaw. A screw-shaped titanium implant (sandblasted and acid-etched surface) was removed from a 68-year-old male after having been in function for 40 months because of a fracture of the abutment screw. Following the implant removal, an undecalcified section was obtained. The histomorphometric analysis showed a rate of 75.40% of bone-to-implant contact and 89.30% of bone area filling within the limits of the implant threads. The surrounding bone healed in a well-organized pattern and could not be differentiated from the anginal alveolus. The histologic evidence showed a high degree of osseointegration in a threaded, sandblasted, and acid-etched implant retrieved from a human lower jaw after functional loading for 40 months. Copyright © 2005 by Lippincott Williams & Wilkins.

Shear bond strength fatigue limit of rest seats made with dental restoratives

Purpose: This study compared the shear bond strength (SBS) to enamel of rest seats made with a glass-ionomer cement (Fuji IX GP Fast), a resin-modified glass-ionomer cement (Fuji II LC), and a composite resin (Z100 MP) under monotonic and cyclic loading. Materials and Methods: Rest seats were built up onto the lingual surfaces of 80 intact human mandibular incisors. Specimens (n=10) were stored in distilled water at 37°C for 30 days and subjected to shear forces in a universal testing machine (0.5 mm/min) until fracture. The SBS values were calculated (MPa) using the bonding area (9.62 mm2) delimited by adhesive tags. A staircase approach was used to determine the SBS fatigue limit of each material. Specimens were submitted to either 10,000 cycles (5 Hz) or until specimen fracture. A minimum of 15 specimens was tested for each material. Scanning electron microscopy was used to examine the mode of failure. Data were statistically analyzed with one-way ANOVA and Tukey HSD tests (α = 0.05). Results: Z100 MP yielded higher (p < 0.05) SBS (12.25 MPa) than Fuji IX GP Fast (7.21 MPa). No differences were found between Fuji II LC (10.29 MPa) and the other two materials (p > 0.05). Fuji II LC (6.54 MPa) and Z100 MP (6.26 MPa) had a similar SBS limit. Fuji IX GP Fast promoted the lowest (p < 0.05) SBS fatigue limit (2.33 MPa). All samples showed cohesive failure patterns. Conclusion: Fatigue testing can provide a better means of estimating the performance of rest seats made with dental restoratives.

Dual path: A concept to improve the esthetic replacement of missing anterior teeth with a removable partial denture

The dual path of insertion concept for removable partial denture (RPD) design may be used in esthetically demanding situations. When compared to conventional RPDs, the main advantage of this design is the minimal use of clasps. This clinical report describes the treatment of a patient with an anterior maxillary edentulous area using a dual path RPD. The diagnostic cast was surveyed to ensure the adequacy of the undercuts on the mesial surfaces of the anterior abutments, where rigid minor connectors were placed. Inverted V-shaped canine cingulum rest seats were prepared to provide resistance to tooth movement during function. The dual path RPD concept allows excellent esthetic results, minimizes tooth preparation, and reduces the tendency toward plaque accumulation in a Kennedy class IV partially edentulous arch. © 2008 by The American College of Prosthodontists.

Accuracy of impression techniques for implants. Part 1 - Influence of transfer copings surface abrasion

Purpose: This study evaluated the influence of surface abrasion of transfer copings to obtain a precise master cast for a partially edentulous restoration with different inclinations. Materials and Methods: Replicas (N = 30) of a metal matrix (control group) containing two implants at 90° and 65° in relation to the benchtop were obtained using a polyether impression material and three impression techniques: square impression copings splint with dental floss and autopolymerizing acrylic resin (TRS), square impression copings abraded with aluminum oxide (TA), and square impression copings abraded with aluminum oxide and adhesive-coated (TAA). The replicas obtained in type V stone were digitalized, and the images were exported to AutoCAD software to perform the readings of possible degree alterations in implant inclinations. The results were submitted to analysis of variance (ANOVA) and Tukey test (α < 0.05). Results: Comparing the techniques with regard to the 90° implant inclination, no statistical difference was observed between the three techniques and the control group. Analyzing the three techniques with regard to the 65° implant inclination, no significant difference was seen between technique TA and the control group. Conclusions: Technique TA presented more accurate master casts than TRS and TAA techniques. The angulated implant (65°) tended to generate more imprecise master casts than implants perpendicular to the surface. © 2008 by The American College of Prosthodontists.

A modified method of immediate occlusal loading using a reinforced framework denture: A case report

The technique presented in this article presents a protocol for treatment that reduces the time required for the fabrication and placement of an implant supported prosthesis. It also offers improved patient comfort at a lower cost when compared to conventional technology.

Influence of implant positioning in extraction sockets on osseointegration: Histomorphometric analyses in dogs

Aim: To evaluate the influence of implant positioning into extraction sockets on osseointegration. Material and methods: Implants were installed immediately into extraction sockets in the mandibles of six Labrador dogs. In the control sites, the implants were positioned in the center of the alveolus, while in the test sites, the implants were positioned 0.8 mm deeper and more lingually. After 4 months of healing, the resorptive patterns of the alveolar crest were evaluated histomorphometrically. Results: All implants were integrated in mineralized bone, mainly composed of mature lamellar bone. The alveolar crest underwent resorption at the control as well as at the test sites. After 4 months of healing, at the buccal aspects of the control and test sites, the location of the implant rough/smooth limit to the alveolar crest was 2±0.9 mm and 0.6±0.9 mm, respectively (P<0.05). At the lingual aspect, the bony crest was located 0.4 mm apically and 0.2 mm coronally to the implant rough/smooth limit at the control and test sites, respectively (NS). Conclusions: From a clinical point of view, implants installed into extraction sockets should be positioned approximately 1 mm deeper than the level of the buccal alveolar crest and in a lingual position in relation to the center of the alveolus in order to reduce or eliminate the exposure above the alveolar crest of the endosseous (rough) portion of the implant. © 2009 John Wiley & Sons A/S.

Effect of unilateral misfit on preload of retention screws of implant-supported prostheses submitted to mechanical cycling

Purpose: The aim of this study was to evaluate the effect of different levels of unilateral angular misfit on preload maintenance of retention screws of single implant-supported prostheses submitted to mechanical cycling. Materials and methods: Premachined UCLA abutments were cast with cobalt-chromium alloy to obtain 48 crowns divided into four groups (n=12). The crowns presented no misfit in Group A (control group) and unilateral misfits of 50μm, 100μm and 200μm in the groups B, C and D, respectively. The crowns were attached to external hexagon implants with a titanium retention screw with torque of 30N/cm. Oblique loading of 130N at 2Hz was applied on each replica, totalizing 5×104 and 1×106cycles. Detorque values were measured initially and after each cycling period. Data were evaluated by analysis of variance and Tukey's HSD test (p<0.05). Results: All groups presented reduced initial detorque values (p< 0.05) in comparison to the insertion torque (30. ± 0.5. N/cm) and Group A (25.18. N/cm) exhibited the lowest reduction. After mechanical cycling, all groups presented detorque values from 19.5. N/cm to 22.38. N/cm and the mechanical cycling did not statistically influence the detorque values regardless the misfit level of the replicas. Conclusion: The unilateral misfit influenced the preload maintenance only before mechanical cycling. The mechanical cycling did not influence the torque reduction. © 2010 Japan Prosthodontic Society.

Photoelastic comparison of single tooth implant-abutment-bone of platform switching vs conventional implant designs

Objectives: The maintenance and stability of peri-implantar soft tissue seem to be related to the crestal bone around the implant platform and different implant designs connections might affect this phenomenon. The aim of this study was to evaluate by photoelastic analysis the stress distribution in the cervical and apical site of implant-abutment interface of conventional implant joints (external hex, internal hex and cone morse) and compare to the novel platform switching design. Materials and methods: It was fabricated photoelastic models using five different implant-abutment connection, one set of external hex (Alvim Ti, Neodent, Curitiba, Brazil), one set of internal hex (Full Osseotite, Biomet 3i, Florida, USA), one cone morse set (Alvim CM, Neodent, Curitiba, Brazil), and two sets of internal hex plus platform switching concept (Alvim II Plus, Neodent, Curitiba, Brazil) (Certain Prevail, Biomet 3i, Florida, USA). These models were submitted to two compressive loads, axial from 20 kgf (load I) and another (load II), inclined 45° from 10 kgf. During the qualitative analysis, digital pictures were taken from a polariscope, for each load situation. For the quantitative analyses in both situations of load, the medium, minimum and maximum in MPa values of shear strain were determined in the cervical and apical site. The Kruskal-Wallis test was used to compare the results between the different systems and between cervical and apical site were compared using Mann-Whitney U test. Results: The results from qualitative analysis showed less concentration of strain in the cervical area to the internal hex plus platform switching (Certain Prevail), in both situation of load. The same results were get in the quantitative analysis, showing less stress concentrations around the implant Certain Prevail with internal hex plus the novel design (17.9 MPa to load I and 29.5 MPa to load II), however, without statistical significant difference between the systems. Conclusion: The minor stress concentration strongly suggest the use of platform switching design as a manner to prevent bone loss around the implant-abutment platform. Clinical Significance: From the result of this study its possible to make clinical decision for implant system which provides implant components with platform switching characteristics.

Effect of axial loads on implant-supported partial fixed prostheses by strain gauge analysis

Objectives: The present study used strain gauge analysis to perform an in vitro evaluation of the effect of axial loading on 3 elements of implant-supported partial fixed prostheses, varying the type of prosthetic cylinder and the loading points. Material and methods: Three internal hexagon implants were linearly embedded in a polyurethane block. Microunit abutments were connected to the implants applying a torque of 20 Ncm, and prefabricated Co-Cr cylinders and plastic prosthetic cylinders were screwed onto the abutments, which received standard patterns cast in Co-Cr alloy (n = 5). Four strain gauges (SG) were bonded onto the surface of the block tangentially to the implants, SG 01 mesially to implant 1, SG 02 and SG 03 mesially and distally to implant 2, respectively, and SG 04 distally to implant 3. Each metallic structure was screwed onto the abutments with a 10 Ncm torque and an axial load of 30 kg was applied at five predetermined points (A, B, C, D, E). The data obtained from the strain gauge analyses were analyzed statistically by RM ANOVA and Tukey's test, with a level of significance of p<0.05. Results: There was a significant difference for the loading point (p=0.0001), with point B generating the smallest microdeformation (239.49 με) and point D the highest (442.77 με). No significant difference was found for the cylinder type (p=0.748). Conclusions: It was concluded that the type of cylinder did not affect in the magnitude of microdeformation, but the axial loading location influenced this magnitude.

A new intraoral device to facilitate preparation of the guide plane for removable dental prostheses

The design of the ParalAB device facilitates transfer of the path of insertion from the diagnostic cast to the mouth quickly and efficiently.

Effect of microthread presence and restoration design (screw versus cemented) in dental implant reliability and failure modes

Objectives: This study evaluated the reliability and failure modes of implants with a microthreaded or smooth design at the crestal region, restored with screwed or cemented crowns. The postulated null hypothesis was that the presence of microthreads in the implant cervical region would not result in different reliability and strength to failure than smooth design, regardless of fixation method, when subjected to step-stress accelerated life-testing (SSALT) in water. Materials and methods: Eighty four dental implants (3.3 × 10 mm) were divided into four groups (n = 21) according to implant macrogeometric design at the crestal region and crown fixation method: Microthreads Screwed (MS); Smooth Screwed (SS); Microthreads Cemented (MC), and Smooth Cemented (SC). The abutments were torqued to the implants and standardized maxillary central incisor metallic crowns were cemented (MC, SC) or screwed (MS, SS) and subjected to SSALT in water. The probability of failure versus cycles (90% two-sided confidence intervals) was calculated and plotted using a power law relationship for damage accumulation. Reliability for a mission of 50,000 cycles at 150 N (90% 2-sided confidence intervals) was calculated. Differences between final failure loads during fatigue for each group were assessed by Kruskal-Wallis along with Benferroni's post hoc tests. Polarized-light and scanning electron microscopes were used for failure analyses. Results: The Beta (β) value (confidence interval range) derived from use level probability Weibull calculation of 1.30 (0.76-2.22), 1.17 (0.70-1.96), 1.12 (0.71-1.76), and 0.52 (0.30-0.89) for groups MC, SC, MS, and SS respectively, indicated that fatigue was an accelerating factor for all groups, except for SS. The calculated reliability was higher for SC (99%) compared to MC (87%). No difference was observed between screwed restorations (MS - 29%, SS - 43%). Failure involved abutment screw fracture for all groups. The cemented groups (MC, SC) presented more abutment and implant fractures. Significantly higher load to fracture values were observed for SC and MC relative to MS and SS (P < 0.001). Conclusion: Since reliability and strength to failure was higher for SC than for MC, our postulated null hypothesis was rejected. © 2012 John Wiley & Sons A/S.

Reliability and failure modes of internal conical dental implant connections

Objective: Biological and mechanical implant-abutment connection complications and failures are still present in clinical practice, frequently compromising oral function. The purpose of this study was to evaluate the reliability and failure modes of anterior single-unit restorations in internal conical interface (ICI) implants using step-stress accelerated life testing (SSALT). Materials and methods: Forty-two ICI implants were distributed in two groups (n = 21 each): group AT-OsseoSpeed™ TX (Astra Tech, Waltham, MA, USA); group SV-Duocon System Line, Morse Taper (Signo Vinces Ltda., Campo Largo, PR, Brazil). The corresponding abutments were screwed to the implants and standardized maxillary central incisor metal crowns were cemented and subjected to SSALT in water. Use-level probability Weibull curves and reliability for a mission of 50,000 cycles at 200 N were calculated. Differences between groups were assessed by Kruskal-Wallis along with Bonferroni's post-hoc tests. Polarized-light and scanning electron microscopes were used for failure analyses. Results: The Beta (β) value derived from use level probability Weibull calculation was 1.62 (1.01-2.58) for group AT and 2.56 (1.76-3.74) for group SV, indicating that fatigue was an accelerating factor for failure of both groups. The reliability for group AT was 0.95 and for group SV was 0.88. Kruskal-Wallis along with Bonferroni's post-hoc tests showed no significant difference between the groups tested (P > 0.27). In all specimens of both groups, the chief failure mode was abutment fracture at the conical joint region and screw fracture at neck's region. Conclusions: Reliability was not different between investigated ICI connections supporting maxillary incisor crowns. Failure modes were similar. © 2012 John Wiley & Sons A/S.