Influence of oxygen flow on crystallization and morphology of PLZT thin films

PLZT thin films were prepared by a dip coating process using Pechini's method, also known as polymeric precursor method. The PLZT solution was obtained from a mixture of the individual cation solutions and the process to prepare each solution is based on metallic citrate polymerization. The viscosity of the PLZT solution was adjusted at 40 cP while the ionic concentration was adjusted at 0.1 M. PLZT solutions were deposited on silicon (100) and platinum coated silicon (100) substrates with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with a heating rate of 1 degreesC/min up to 300 degreesC and 5 degreesC/min up to 650 degreesC in order to obtain homogeneous and cracks free films. The influence of oxygen flow on crystallization and morphology of PLZT (9/65/35) thin film is discussed. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Influence of thickness on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air was performed at 500 degreesC for 3 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz and the hysteresis loop was obtained. The influence of number of layers on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier B.V. All rights reserved.

Synthesis and characterization of antimony tartrate for ceramic precursors

Synthesis and characterization of antimony tartrate used as a precursor of ceramic powders obtained by Pechini's method were carried out. Antimony tartrate was chosen as a substitute for the antimony citrate commonly used in this chemical processing, because of difficulties in preparing the citrate. FTIR and TGA/DTA analysis showed that antimony tartrate, H-2[Sb-2(C4H2O6)(2)]. forms a polymeric structure. The procedure described indicates that the antimony chelate obtained is adequate for Pechini's method.

The influence of thermal treatment on the preparation of PNM and PMN-PT thin films

Ferroelectric thin films belong to a class of materials with great technological importance in optic fibers, micro-electromechanical systems, and microprocessors and computers memories.The (1-x)PbMg1/3Nb2/3O3(x)PbTiO3 (PMN-PT) thin films, with x=0, 0.1, 0.35 and 0.5, were prepared by Pechini's process and deposited by spin-coating on Si(100), Pt/Ti/SiO2/Si(100) and quartz substrates. The goal of the present paper is to verify the thermal treatment influence on the perovskite phase formation, which is desirable for these applications. The phase formation was analyzed by X-ray diffraction. The film's surface was characterized by atomic force microscopy to analyze the roughness and the homogeneity. The results of this study indicate that the optimum conditions for obtaining the perovskite phase using a Pt/Ti/SiO2/Si(100) substrate, were drying each deposited layer at 140 degreesC (heating plate), and a final thermal treatment at 600 degreesC for 3 h in a closed system with a lead-rich atmosphere. (C) 2003 Elsevier B.V. All rights reserved.

Influence of viscosity and ionic concentration on morphology of PLZT thin films

PLZT thin films were prepared by a dip-coating process using Pechini's method. The PLZT solution was obtained from the mixture of the cation solutions. The viscosity of the solution was adjusted in the range of 20-40 cP, while the ionic concentration was adjusted in the range of 0.1 and 0.2 M. PLZT solutions were deposited on Si (1 0 0) substrate with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with heating rate of 1 degreesC/min up to 300 and 5 degreesC/ min up to 650 degreesC in order to obtain homogeneous and crack free films. The influence of viscosity and ionic concentration on crystallization and morphology of PLZT (9/65/35) thin film will be discussed. (C) 2001 Elsevier B.V. B.V. All rights reserved.

The effect of preparation method and Sb content on SnO2-CuO sintering

The sintering behavior of SnO2-CuO system has been investigated for two preparation methods and as a function of antimony concentration. A chemical preparation (Pechini's method) resulted in powders with smaller particle sizes than for a conventional oxide mixture. This led to smaller grain sizes in Pechini's method ceramics. The microstructures were heterogeneous in both systems, showing grain coarsening. The densification was aided by liquid phase formation, due to copper, in both systems, but the temperature of maximum shrinkage rate was larger for the Pechini's method ceramic because copper had to diffuse to the grain surface. Independently of the preparation method, antimony did not aid densification, and increasing its concentration led to a higher densification temperature and lower shrinkage rate. (C) 2003 Kluwer Academic Publishers.

Influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500 degreesC for 3 h. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant and dissipation factor were measured in frequency region from 10 Hz to 10 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier Ltd. All rights reserved.

Al3+ environments in nanostructured ZnAl2O4 and their effects on the luminescence properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural and Spectroscopic Studies of Pr3+-Doped GdAlO3

In this work, GdAlO3:Pr3+ was successfully prepared by the Pechini method at lower temperatures when compared to others methods such as solid-state synthesis and sol-gel process. In accordance to the XRD data, the fully crystalline single-phase GdAlO3 could be obtained at 900 degrees C. Luminescence measurements indicate Gd -> Pr3+ energy transfer. In the emission spectra, the P-3(0) ->(3) H-4 (blue emission) and D-1(2) ->(3) H-4 (red emission) transitions of Pr3+ ions can be observed and the ratio between their intensities depends on the Pr3+ content due to the cross-relaxation phenomenon.

Effect of heat treatment on the generation of structural defects in LaTaO4 ceramics and their correlation with photoluminescent properties

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparação de LiNbO3 e LiNbO3:Eu3+ pelo método dos precursores poliméricos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito da adição simultânea de sementes e dopantes na microestrutura e propriedade dielétrica da cerâmica 0,93 PZN - 0,07 BT

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Desenvolvimento de sensores para gás à base de SnO2 nanoestruturado: influência da microestrutura no desempenho do sensor

Pós nanométricos SnO2.Nb2O5 foram estudados para o desenvolvimento de sensores de etanol. Estes pós foram preparados pelo método Pechini, caracterizados quanto à sua morfologia por difração de raios X, determinação de área superficial específica por BET e Microscopia Eletrônica de Transmissão e foram submetidos a testes de sensibilidade ao vapor de etanol. Foi estabelecida uma correlação entre a microestrutura do material, os efeitos do dopante e a resposta do sensor.

Filmes finos de Titanato de Chumbo e Lantânio - PLT: influência do pH

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sinterização e caracterização de segunda fase em sistemas SnO2-ZnO

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)