The role of oxygen vacancies on the microstructure development and on the electrical properties of SnO2-based varistors

Variations on the microstructure development and on the electrical properties of SnO2-based varistors are discussed on the basis of the oxygen vacancies created or annihilated by the presence of different additives. Electron paramagnetic resonance (EPR) analysis of sintered samples evidenced a substantial increase in the paramagnetic oxygen vacancies concentration when Nb2O5 is added to the SnO2 center dot Co3O4 system. on the other hand, the observed diminution in the concentration of such species after the addition of Fe2O3 indicates solid solution formation. The quantification of paramagnetic oxygen vacancies allowed to confirm the proposed substitutions taking place in the lattice during sintering. These findings are supported by scanning electron microscopy, by density measurements and by current density versus electric field curves. The characterization of secondary phases through EDS assisted SEM and TEM is also reported in this work.

How Cr2O3 influences the microstructure and nonohmic features of the SnO2(COx, Mn1-x)O-based varistor system

An investigation was made to discover how the addition of Cr2O3 affects the microstructural heterogeneity and nonohmic features of the SnO2(Co-x, Mn1-x)O-based varistor system, with x varying from 0 to 1. The presence of Cr2O3 was found to strongly increase the nonohmic features when x = 1. However, the nonohmic features of the system decrease when x drops from 1 to 0, a behavior explained by the increase of the junction heterogeneity within the system's microstructure. accompanied by ail excess of precipitates at the triple point in the grain boundary region due to modified MnO sintering. The presence of these precipitates causes the leakage current to increase in response to the creation of ail ineffective barrier. The effect produced by heat-treating these systems in oxygen- and nitrogen-rich atmospheres suggests that, according to mechanisms previously discussed in the literature, Cr2O3 is more susceptible to oxygen, so that increasing the amount of oxygen in the grain boundary region may improve the system's nonohmic properties. (c) 2005 Elsevier Ltd. All rights reserved.

The effect of isostructural seeding on the microstructure and piezoelectric properties of PZT ceramics

Pechini's method was used to prepare lead titanate zirconate with Zr/Ti ratio equal to 53/47. X-ray diffraction data revealed the presence of a rhombohedral phase, rich in zirconium, due to difference in carbonate stabilities, in PZT ceramics calcined at 600 degrees C. Infrared spectroscopy presented COO- bonds in the 1400 cm(-1) region, which disappeared after calcining at 700 degrees C. Seeds with rhombohedral (PZT 57/43) or tetragonal structure (PZT 45/55) were added to the precursor. The microstructure was differentially influenced by the nature of seed particles. Rhombohedral nuclei promoted preferential crystallization of lead zirconate. This heterogeneity directly reflected on values of k(p) and d(33). (C) 1999 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Laser weld: microstructure and corrosion study of Ag-Pd-Au-Cu alloy of the dental application

The laser Welding process was introduced into dentistry by the end of the 1980s, resulting on a great impulse to that area with the development of cheaper and smaller equipment, using simpler technique. This allowed greater use of that process on the confection of prostheses compared to the brazing process since the heat source for that process is a concentrated light beam of high power, which minimizes distortion problems on the prosthetic pieces. Ag-Pd-Au-Cu alloy used on the confection of dental implant prostheses was observed before and after subjection to the laser welding process. The microstructure was analyzed with the. use of optic microscopy and the corrosion resistance was studied by the traditional electrochemical techniques and by electrochemical impedance, under environmental conditions simulating the aggressiveness found in the mouth cavity. A structural change was detected on the weld area, which presented a refined microstructure deriving from the high-speed cooling. The base metal out of the weld area presented a fusion coarse microstructure. The electrochemical essays showed differences on the potentiodynamic polarization behavior in both weld and metal base areas, indicating superior corrosion resistance in the weld area. The impedance spectra were characterized by capacitive distorted components, presenting linear impedance in the low frequencies area. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Effect of denture fabrication and wear on closest speaking space and interocclusal distance during deglutition

Statement of problem. The accuracy of assessing maxillomandibular relationships for trial bases and dentures using phonetic and swallowing methods has not been compared to that observed with definitive prostheses. Thus, there is no evidence to prove whether measurements obtained through such methods remain the same after adaptation to dentures.Purpose. This study investigated changes in the closest speaking space, interocclusal rest space, and interocclusal distance during deglutition in edentulous patients during and after complete denture treatment.Material and methods. Eighteen edentulous subjects participated in this study and measurements were performed after 7 Intervals of time: (1) with occlusion rims and record bases following creation of the maxillomandibular relationship record, (2) with trial dentures, (3) at Insertion of definitive complete dentures, (4) 1 week, (5) 2 weeks, (6) 1 month, and (7) 3 months after insertion. Recordings of interocclusal distances were made with a mandibular kinesiograph. Closest speaking space was measured during the pronunciation of the word 'seis'. The distance between postural rest position and centric occlusion, or interocclusal rest space, was measured using a kinesiograph. Interocclusal distance during deglutition was tested by recording the closest mandibular position recorded during swallowing of 20 mL of water. Data were analyzed using repeated-measure ANOVA, followed by the Student-Newman-Keuls test (alpha=.05).Results. A significant (P <.01)reduction in the mean closest speaking space was found when it was evaluated using occlusion rims and record bases (4.6 mm) compared with other stages (3.0 to 3.4 mm). No significant differences were found in mean interocclusal rest space and interocclusal distance during deglutition among the time periods evaluated.Conclusions. The presence of occlusion rims can influence mandibular position during pronunciation of the /s/ sound. The arrangement of artificial teeth changes the closest speaking space. However, rest position and deglutition were not affected, either during denture fabrication or short-term use.

Fabrication of novel light-emitting devices based on green-phosphor/conductive-polymer composites

We report on light-emitting devices based on a green-phosphor compound (Mn-doped zinc silicate, Zn2SiO4: Mn) dispersed in a conductive polymeric blend (poly-o-methoxyaniline/polyvinylene fluoride, POMA/PVDF-TrFE). The devices exhibited high luminance in the green, good stability and homogeneous brilliance over effective areas up to 5 cm(2). The electroluminescence (EL) spectrum presented essentially the same characteristics as the photoluminescence (PL) and cathodoluminescence spectra, indicating that the light emission originates from decay of the same excited species, regardless of the excitation source. Operating characteristics were analyzed with current density - voltage (J - V) and luminance voltage ( L - V) curves to investigate the nature of the electroluminescence of the active material, which is still not completely understood.

Microstructure and corrosion resistance of inorganic-organic (ZrO2-PMMA) hybrid coating on stainless steel

Zirconia-polymethylmetacrylate hybrids prepared by a sol-gel method were deposited by dip-coating on stainless steel to improve the resistance against wet corrosion. The effect of the concentration of polymethylmetacrylate and the number of coating applications on the microstructure and corrosion performance of coated samples was investigated. The microstructural properties of samples was analyzed by scanning electron and atomic force microscopy, adhesion tests and profilemeter measurements. The electrochemical corrosion was evaluated through potentiodynamic polarization curves at room temperature. Results show that the sample prepared with 17 vol.% of polymethylmethacrylate has a maximum corrosion resistance, smaller roughness, are hermetic and adherent to the substrate. This film increases the life time of the stainless steel by a factor 30. (C) 1999 Elsevier B.V. B.V. All rights reserved.

Electrical properties of YSZ/NiO composites prepared by a liquid mixture technique

We report the preparation and characterization of yttria-stabilized zirconia/nickel oxide composites (YSZ/NiO). This composite is the precursor material of the cermet YSZ/Ni, which is used as solid oxide fuel cell anode material. The performance of the anode is strongly dependent on the microstructural properties of the cermet. Therefore, the control of the microstructure of the YSZ/NiO composite is a key step for the fabrication of high-performance anodes. In this study, the composites were prepared by a modified liquid mixture technique. Scanning electron microscopy analysis evidenced the good dispersion of the phases and that NiO nanoparticles are spread over the YSZ surface. Sintered pellets were studied by X-ray diffraction and impedance spectroscopy. The main results show that the composite is comprised of a well-dispersed mixture of the two phases. The electrical conductivity data show that there is a strong dependence of the transport mechanism on the relative composition of phases. (c) 2005 Elsevier Ltd. All rights reserved.

Microstructure and electric properties of a SnO2 based varistor

High non-linear J x E electrical characteristic (alpha=41) were obtained in the Nb2O5 and Cr2O3 doped CoO highly densified SnO2 ceramics. X-ray diffraction analysis showed that these ceramics are apparently single phase. Electrical properties and microstructure are highly dependent on the Cr2O3 concentration and on the sintering temperature. Excess of Cr2O3 leads to porous ceramics destroying the material's electrical characteristics probably due to precipitation of second phase of CoCr2O4 Dopant segregation and/or solid solution formation at the grain boundaries can be responsible for the formation of the electrical barriers which originate the varistor behaviour. (C) 1998 Elsevier B.V. Limited and Techna S.r.l. All rights reserved.

Influence of seed particle frequency on the phase formation and on the microstructure of 0.88 PZN-0.07 BT-0.05 PT ceramic

The Pechini method as well as the simultaneous addition of seeds particles and dopant solutions of BaTiO3 (BT) and PbTiO3 (PT) were used to prepare the perovskite phase 0.88 PZN-0.07 BT-0.05 PT. To study the influence of seed particle frequency on the synthesis of the PZN ceramic, two ranges of seed particle size were used: the range from 30 to 100 nm, termed small seed particles (frequency of 10(15) particles/cm(3)); and the range from 100 to 900 nm, termed large seed particles (frequency of 10(13) particles/cm(3)). The crystalline nuclei size influenced the calcining process, the sintering process and the microstructure. Samples prepared with lower seed frequency displayed more amount of pyroclore phase, need higher temperatures for sintering and showed a more heterogeneous microstructure with poor dielectric properties. (C) 2000 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Influence of temperature on the microstructure and electrical properties of BBT thin films

The BBT films were prepared by a spin-coating process from the polymeric precursor method (Pechini process). In order to study the influence of the temperature on the BBT microstructure and electrical properties, the films were deposited on platinum coated silicon substrates and annealed from 700degreesC to 800degreesC for 2 hours in oxygen atmosphere. The crystallinity of the films was examined by X-ray diffraction while the surface morphology was analysed by atomic force microscope. The dielectric properties and dissipation factor of BaBi2Ta2O9 films at 1 MHz were observed. The polarization-electric field hysteresis loops revealed the ferroelectric characteristics of BaBi2Ta2O9 thin films.

Development of Ti-Mo alloys for biomedical applications: Microstructure and electrochemical characterization

Ti-Mo alloys from 4 to 20 Mo wt.% were arc-melted. Their compositions and surfaces were analyzed by EDX, XRF and SEM. The Mo mapping shows a homogeneous distribution for all alloys. The XRD analysis showed that the crystal structure of the alloys is sensitive to the Mo concentration; a mixture of the hexagonal alpha' and orthorhombic alpha '' phases was observed for the Ti-4Mo alloy, and the alpha '' phase is observed almost exclusively when the concentration of Mo added to the Ti reaches 6%. A significant retention of the beta phase is observed for the alloy containing 10% Mo, while at higher Mo concentrations (15% and 20%), retention of phase beta is only verified. Preliminary electrochemical studies have indicated a valve-metal behavior and good corrosion resistance in aerated Ringer solution for all alloys. (c) 2006 Published by Elsevier B.V.

Changes of microstructure in alpha AgZn during post-deformation annealing after cold-rolling

The annealing processes of deformation-induced defects after cold-rolling to about 30 and 60% thickness reduction were investigated for Ag-21, 23, 28 at% Zn by means of residual electrical resistivity, microhardness, light microscopy and transmission electron microscopy (TEM) Three annealing stages have been detected and consistently interpreted as annealing-out of mainly point defects and their agglomerates (stage I), formation of dislocation cells and recrystallized strain-free grains (stage II) and grain growth (stage III). Further, it is tried to determine the evolution of defect production (point defects and dislocations) during rolling deformation from measured changes of electrical resistivity and microhardness. Copyright (C) 1996 Acta Metallurgica Inc.

Fabrication of phytic acid sensor based on mixed phytase-lipid Langmuir-Blodgett films

This paper reports the surface activity of phytase at the air-water interface, its interaction with lipid monolayers, and the construction of a new phytic acid biosensor on the basis of the Langmuir-Blodgett (LB) technique. Phytase was inserted in the subphase solution of dipalmitoylphosphatidylglycerol (DPPG) Langmuir monolayers, and its incorporation to the air-water interface was monitored with surface pressure measurements. Phytase was able to incorporate into DPPG monolayers even at high surface pressures, ca. 30 mN/m, under controlled ionic strength, pH, and temperature. Mixed Langmuir monolayers of phytase and DPPG were characterized by surface pressure-area and surface potential-area isotherms, and the presence of the enzyme provided an expansion in the monolayers ( when compared to the pure lipid at the interface). The enzyme incorporation also led to significant changes in the equilibrium surface compressibility (in-plane elasticity), especially in liquid-expanded and liquid-condensed regions. The dynamic surface elasticity for phytase-containing interfaces was investigated using harmonic oscillation and axisymmetric drop shape analysis. The insertion of the enzyme at DPPG monolayers caused an increase in the dynamic surface elasticity at 30 mN m(-1), indicating a strong interaction between the enzyme and lipid molecules at a high-surface packing. Langmuir-Blodgett (LB) films containing 35 layers of mixed phytase-DPPG were characterized by ultraviolet-visible and fluorescence spectroscopy and crystal quartz microbalance nanogravimetry. The ability in detecting phytic acid was studied with voltammetric measurements.