Influence of degradation on the electrical conduction process in ZnO and SnO2-based varistors

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Weathering degradation of polyester and polypropylene geotextiles

This paper presents results of physical and mechanical tests in polyester (PET) and polypropilene (PP) nonwoven geotextiles that were exposed to weathering conditions (solar radiation, humidity, wind, rain) after some specific periods of exposure (1, 2, 3 and 4 months). ASTM D5970 and Brazilian standards (NBR) recommendation were followed in this research. Results show variations in tensile properties and in the mass per unit area. Variations in the deformations were more significant in the PP geotextile when compared to the PET geotextile.

Evaluation of geomembrane UV degradation using melt flow index and oxidative induction time tests

Many factors such as the sunlight, intensity of radiation, temperature, and moisture may influence the degradation process of geosynthetics. UV stabilizers are used especially in polyolefin geomembrane to prevent the degradation process. In these geomembranes the service lifetime is initially governed by the consumption of antioxidants. Tests like MFI and OIT are a alternative to detect the oxidative degradation in polyolefins. This article evaluates HDPE geomembrane degradation after UV exposure through the results of MFI and OIT tests. Two kinds of geomembranes were evaluated: a black and smooth (0.8, 1.0, 1.5, 2.5 mm) and a white and textured (1.0 mm). MFI test showed some levels of superficial degradation (crosslink) in HDPE geomembrane.

Degradation of [D-Leu]-Microcystin-LR by solar heterogeneous photocatalysis (TiO2)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

A comparative study of the non-isothermal degradation of natural rubber from Mangabeira (Hancornia speciosa Gomes) and Seringueira (Hevea brasiliensis)

Due to the increasing search for alternative sources of natural rubber (NR) whose properties are similar to Hevea brasiliesis, several sources have been studied in the past few years. Among them, Mangabeira (Hancornia speciosa Gomes), which is native to Amazon rainforest and other regions of Brazil, has a potential as another viable rubber source. As a continuation of a series of comparative studies between Hancornia and Hevea (clone RRIM 600) these two species by our research team, their thermal behavior was analyzed by thermogravimetry (TG) using Flynn-Wall-Ozawa's approach in order to obtain kinetic parameters (reaction order, pre-exponential factor and activation energy) of the decomposition process. Results indicated that the thermal behavior of NR from Hancornia was comparable to Hevea with some differences observed as follows: reaction order for Hancornia was higher than for Hevea at the beginning of degradation and very close for temperatures over 350 A degrees C; activation energy and pre-exponential factor had the same trend, i.e., increased with increasing degree of conversion remaining almost constant between 20 and 70% and then increasing for higher degrees, although Hevea was slightly more thermally stable than Hancornia. These major influences in the degradation process in the early stage are attributed to differences in non-rubber constituents present in these two species.

Effects of cyclosporin, phenytoin, and nifedipine on the synthesis and degradation of gingival collagen in tufted capuchin monkeys (Cebus apella): Histochemical and MMP-1 and -2 and collagen I gene expression analyses

Background: The purpose of this experimental study was to evaluate the collagen fiber distribution histologically after phenytoin, cyclosporin, or nifedipine therapy and to correlate it with collagen I and matrix metalloproteinase (MMP)-1 and -2 gene expression levels.Methods: Gingival samples from the canine area were obtained from 12 male monkeys (Cebus apella). The mesial part of each sample was assessed by reverse transcription-polymerase chain reaction, whereas the distal part was processed histologically for picrosirius red and hematoxylin and eosin stainings, as well as for collagen IV immunostaining. One week after the first biopsy, the animals were assigned to three groups that received daily oral dosages of cyclosporin, phenytoin, or nifedipine for 120 days. Additional gingival samples were obtained on days 52 and 120 of treatment from two animals from each group on the opposite sides from the first biopsies.Results: Picrosirius red staining showed a predominance of mature collagen fibers in the control group. Conversely, there was an enlargement of areas occupied by immature collagen fibers in all groups at days 52 and 120, which was not uniform over each section. There was a general trend to lower levels of MMP-1 gene expression on day 52 and increased levels on day 120. Phenytoin led to increased levels of MMP-2 and collagen I gene expression on day 120, whereas the opposite was observed in the nifedipine group.Conclusion: Cyclosporin, phenytoin, and nifedipine led to phased and drug-related gene expression patterns, resulting in impaired collagen metabolism, despite the lack of prominent clinical signs.

Effect of addition of pigments and opacifier on the hardness, absorption, solubility and surface degradation of facial silicone after artificial ageing

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of acid etching time on the degradation of resin-dentin bonds in primary teeth

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Cytotoxicity of monomers, plasticizer and degradation by-products released from dental hard chairside reline resins

Objectives. The aim of this study was to evaluate the cytotoxic effect of the monomers isobutyl methacrylate (IBMA) and 1,6-hexanediol dimethacrylate (1,6-HDMA), the plasticizer di-n-butyl phthalate (DBP), and the degradation by-products methacrylic acid (MA) and benzoic acid (BA) on L929 cells. Based on previous investigations on the release of these compounds from hard chairside reline resins, a range of concentrations (mu mol/L) were selected for the cytotoxicity tests (IBMA, 5.491406.57; 1,6-HDMA, 1.2239.32; DBP, 1.12143.8; MA, 9.07581; BA, 3.19409).Methods. Cytotoxic effects were assessed using MTT and 3H-thymidine assays after the cells had been exposed to the test compounds at the given concentrations for 24h. Cytotoxicity was rated based on cell viability relative to controls (cells exposed to medium without test substances).Results. DNA synthesis activity was inhibited by all compounds. Mitochondrial dehydrogenase activity decreased in cells treated with monomers, plasticizer and MA by-product, whereas no cytotoxic effect was observed on contact with BA at the majority of concentrations tested. The ranges of suppression for 3H-thymidine assay were: IBMA, 2595%; 1,6-HDMA, 9598%; DBP, 4098%; MA, 9799%; BA, 5471%. For MTT assay, the ranges of suppression were: IBMA, 096%; 1,6-HDMA, 2689%; DBP, 1780%; MA, 5266%; BA, 027%. The 3H-thymidine assay was more sensitive than the MTT assay.Significance. This study evaluated the cytotoxicity of a wide range of concentrations of monomers (IBMA and 1,6-HDMA), plasticizer (DBP) and degradation by-products (MA and BA), including those expected to be released from hard chairside reline resins. The differences observed in the cytotoxicity of these compounds, along with other properties, may assist the dental practitioners in the selection of reline materials with improved service life performance and low risk of adverse reactions in patients who wear relined dentures.

Leachability of degradation products from hard chairside reline resins in artificial saliva: effect of water-bath post-polymerization treatment

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Microscopic evidence supports the hypothesis of high cellulose degradation capacity by the symbiotic fungus of leaf-cutting ants

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Giardia duodenalis: protein substrates degradation by trophozoite proteases

The present investigation was undertaken to identify and characterize trophozoite proteases of five axenic strains of Giardia duodenalis isolated in Brazil and the reference strain Portland 1 isolated in the United States. Trophozoite cell lysates of each strain were analysed for the pattern of proteins and for proteolytic activity. Samples were tested in SDS-polyacrylamide gel electrophoresis for the protein profiles, and the detection of proteases in cell lysates was performed using substrate gel electrophoresis [gelatin, collagen, bovine serum albumin (BSA) and haemoglobin] and azocasein assays. Indeed, synthetic inhibitors were included in the assays to characterize the protease classes. Differences on the hydrolysis patterns of protein substrates were observed in relation to the substrate composition as much as the Giardia trophozoite strain. The substrate-containing gels revealed hydrolysis bands with molecular masses ranging from > 97 to 20-15 kDa, and most zones were common to the five strains. However, some pronounced differences could be detected in the BTU-11 pattern. Azocasein was also degraded; however, depending on the lysate assayed, the degree of substrate degradation was variable. It was observed that inhibitory effects are substrate-dependent since the activity was predominantly due to cysteine proteases against gelatin, collagen, BSA and azocasein substrates and due to serine against haemoglobin. The presence of aspartic protease and aminopeptidase activity in the lysates was also indicated.

Synthesis and characterization of TiO2 chemically modified by Pd(II) 2-aminothiazole complex for the photocatalytic degradation of phenol

An investigation was made into the photocatalytic activity of in situ synthesized TiO2 chemically modified by Pd(II) 2-aminothiazole complex for phenol degradation at different pH values. At longer reaction times, the bare titania presented far poorer pbotoactivity than the modified catalysts in the entire range of pH studied. The catalyst complexed with Pd(II) was more efficient than the metal-free Pd, irrespective of pH and reaction time, suggesting that metal plays an important role. A cooperative mechanism is proposed, involving the possible photoactivation of both TiO2 and sensitizer. (C) 2007 Elsevier B.V. All rights reserved.

Biodegradation of blend films in soil and soil with chorume. I. PVC/PCL

Blends of synthetic and biodegradable polymers can be important in attaining material plastic degradation in the environment. Biodegradation using soil and chorume (liquid waste from landfill) microorganisms is a promising area these days. This paper intends to study the PVC/PCL blend degradation in soil using aerobic biodegradation (Bartha respirometer). The morphology and structural changes of the blends were studied by FTIR, scanning electron microscopy, differential scanning calorimetry and contact angle measurements. Blend films prepared by the casting of dichloroethane solutions were buried in a Bartha respirometer containing soil and soil plus chorume and kept there for 120 days. During this time CO2 evolution was measured from time to time. The results showed that PCL films degrade faster than PVC/PCL and PVC films.