Ferroelectric and dielectric properties of vanadium-doped Ba(Ti0.90Zr0.10)O-3 ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis, characterization, structural refinement and optical absorption behavior of PbWO(4) powders

The present paper describes the synthesis, characterization, structural refinement and optical absorption behavior of lead tungstate (PbWO(4)) powders obtained by the complex polymerization method heat treated at different temperatures for 2h in air atmosphere. PbWO(4) powders were characterized by X-ray diffraction (XRD), Rietveld refinement, Fourier transform Raman (FT-Raman) spectroscopy and ultraviolet visible (UV-vis) absorption spectroscopy measurements. XRD, Rietveld refinement and FT-Raman revealed that PbWO(4) powders are free of secondary phases and crystallizes in a tetragonal structure. The UV-vis absorption spectroscopy measurements suggest the presence of intermediary energy levels into the band gap of structurally disordered powders. (C) 2008 Elsevier B.V. All rights reserved.

Dependence of annealing time on structural and morphological properties of Ca(Zr0.05Ti0.95)O-3 thin films

Ca(Zr0.05Ti0.95)O-3 (CZT) thin films were prepared by the polymeric precursor method by spin-coating process. The films were deposited on Pt(1 1 1)/Ti/SiO2/Si(1 0 0) substrates and annealed at 650 degrees C for 2,4, and 6 It in oxygen atmosphere. Structure and morphology of the CZT thin films were characterized by the X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FT-IR), atomic force microscopy (AFM) and field-emission scanning electron microscopy (FEG-SEM). XRD revealed that the film is free of secondary phases and crystallizes in the orthorhombic structure. The annealing time influences the grain size, lattices parameter and in the film thickness. (c) 2006 Elsevier B.V. All rights reserved.

Study of structural evolution and photoluminescent properties at room temperature of Ca(Zr, Ti)O-3 powders

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

An efficient microwave-assisted hydrothermal synthesis of BaZrO3 microcrystals: growth mechanism and photoluminescence emissions

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

SrMoO4 powders processed in microwave-hydrothermal: Synthesis, characterization and optical properties

In this work, we report on the synthesis of SrMoO4 powders by co-precipitation method and processed in a microwave-hydrothermal at 413 K for 5 h. These powders were analyzed by X-ray diffraction (XRD), Fourier transform Raman (FT-Raman), ultraviolet-visible (UV-vis) absorption spectroscopy and photoluminescence (PL). XRD analyses revealed that the SrMoO4 powders are free of secondary phases and crystallize in a tetragonal structure. FT-Raman investigations showed the presence of Raman-active vibration modes correspondent for this molybdate. UV-vis technique was employed to determine the optical band gap of this material. SrMoO4 powders exhibit an intense PL emission at room temperature with maximum peak at 540 nm (green region) when excited by 488 nm wavelength of an argon ion laser. (C) 2007 Elsevier B.V. All rights reserved.

The role of the Eu3+ ions in structure and photoluminescence properties of SrBi2Nb2O9 powders

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Preparation and characterization of new glassy system As2P2S8-Ga2S3

Glasses having the composition (100 - x)As2P2S8-xGa(2)S(3) with x ranging from 0 to 50% were investigated to determine the compositional effect on properties and local structure. The glass transition temperature (T-g) and the stability parameter against crystallization (T-x - T-g) increased with the addition of Ga2S3. The structure of these glasses was probed by Raman scattering, Fourier transform infrared (FT-IR) and P-31 nuclear magnetic resonance. on the basis of the observed vibrations and the strength of the P-31-P-31 homonuclear magnetic dipolar coupling, two scenarios can be proposed for the structural evolution induced by the addition of Ga2S3. For x <= 20% we may have the formation of GaS4E- groups (E = nonbonding electron), and for x >= 30% we have depolymerization of the As2P2S8 units and the formation of a network of GaPS4 units with each PS4/2 unit (Q(4)) species carrying a single positive formal charge.

Retention Characteristics of CBTi144 Thin Films Explained by Means of X-Ray Photoemission Spectroscopy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Estudo do comportamento térmico dos compostos de Ag+ e Pb2+ com o ligante 1,4-bis(3-carbóxi-3-oxo-prop-1-enil)benzeno

Este trabalho reporta o estudo de compostos binários do dicarboxilato 1,4-bis(3-carbóxi-3-oxo-prop-1-enil)benzeno, C6H4(-CH=CH-CO-COO-)2 , com os cátions metálicos Ag+ e Pb2+, obtidos a partir de soluções aquosas do ligante e dos nitratos dos cátions metálicos, em proporções estequiométricas. Para a caracterização e o estudo do processo de decomposição térmica desses compostos foram empregadas Espectrofotometria de Absorção na Região do Infravermelho com Transformada de Fourier (FT-IR), Análise Elementar (C, H), Complexometria com EDTA, Termogravimetria (TG) e Calorimetria Exploratória Diferencial (DSC).

Structural aspects, thermal behavior, and stability of a self-assembled supramolecular polymer derived from flunixin-meglumine supramolecular adducts

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Potenciais delta revisitados via transformada de Fourier

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

RITZ ANALYSIS OF THE FOURIER SPECTRUM OF CH3OH BETWEEN 350 AND 950 CM(-1)

A new ''Ritz'' program has been used for revising and expanding the assignment of the Fourier transform infrared and far-infrared spectrum of CH3OH. This program evaluates the energy levels involved in the assigned transitions by the Rydberg-Ritz combination principle and can tackle such perturbations as Fermi-type resonances or Coriolis interactions. Up to now this program has evaluated the energies of 2768 levels belonging to A-type symmetry and 4133 levels belonging to E-type symmetry of CH3OH. Here we present the assignment of almost 9600 lines between 350 and 950 cm(-1). The Taylor expansion coefficients for evaluating the energies of the levels involved in the transitions are also given. All of the lines presented in this paper correspond to transitions involving torsionally excited levels within the ground vibrational state. (C) 1995 Academic Press, Inc.

Preparation of Pb(Zr,Ti)O-3 thin films by soft chemical route

Lead zirconate titanate, Pb(Zr0.3Ti0.7)O-3 (PZT) thin films were prepared with success by the polymeric precursor method. Differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), Fourier-transform infrared spectroscopy (FT-IR), Micro-Raman spectroscopy and X-ray diffraction (XRD) were used to investigate the formation of the PZT perovskite phase. X-ray diffraction revealed that the film showed good crystallinity and no presence of secondary phases was identified. This indicates that the PZT thin films were crystallized in a single phase. PZT thin films showed a well-developed dense grain structure with uniform distribution, without the presence of rosette structure. The Raman spectra undoubtedly revealed these thin films in the tetragonal phase. For the thin films annealed at the 500-700 degreesC range, the vibration modes of the oxygen sublattice of the PZT perovskite phase were confirmed by FT-IR. The room temperature dielectric constant and dielectric loss of the PZT films, measured at 1 kHz were 646 and 0.090, respectively, for thin film with 365 nm thickness annealed at 700 degreesC for 2 h. A typical P-E hysteresis loop was observed and the measured values of P-s, P-r and E-c were 68 muC/cm(2), 44 muC/cm(2) and 123 kV/cm, respectively. The leakage current density was about 4.8 x 10(-7) A/cm(2) at 1.5 V. (C) 2003 Elsevier Ltd. All rights reserved.

Effects of post-annealing on the dielectric properties of Au/BaTiO3/Pt thin film capacitors

Barium titanate thin films were prepared by the polymeric precursor method and deposited onto Pt/Ti/SiO2/Si substrates. X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FT-IR) and micro-Raman spectroscopy were used to investigate the formation of the BaTiO3 perovskite phase. Afterwards, the films were submitted to post-annealing treatments in oxygen and nitrogen atmospheres at 300 degreesC for 2 h, and had their dielectric properties measured. It was observed that the electric properties of the thin films are very sensitive to the nature of the post-annealing atmosphere. This study demonstrates that post-annealing in an oxygen atmosphere increases the dielectric relaxation phenomenon and that post-annealing in a nitrogen atmosphere produces a slight dielectric relaxation. (C) 2004 Elsevier B.V All rights reserved.