Ferroelectric and dielectric properties of Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 thin films grown by the soft chemical method

Polycrystalline Ba0.5Sr0.5(Ti0.80Sn0.20)O-3 (BST:Sn) thin films with a perovskite structure were prepared by the soft chemical method on a platinum-coated silicon substrate from spin-coating technique. The resulting thin films showed a dense structure with uniform grain size distribution. The dielectric constant of the films estimated from C-V curve is around 1134 and can be ascribed to a reduction in the oxygen vacancy concentration. The ferroelectric nature of the film indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed remnant polarization of 14 mu C/cm(2) and coercive field of 74 kV/cm at frequency of 1 MHz. At the same frequency, the leakage current density at 1.0 V is equal to 1.5 x 10(-7) A/cm(2). This work clearly reveals the highly promising potential of BST:Sn for application in memory devices. (c) 2006 Elsevier B.V. All rights reserved.

Influence of thickness on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air was performed at 500 degreesC for 3 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant, dissipation factor and resistance were measured in frequency region from 10 Hz to 10 MHz and the hysteresis loop was obtained. The influence of number of layers on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier B.V. All rights reserved.

Electrical properties of lanthanum doped Bi4Ti3O12 thin films annealed in different atmospheres

Pure-and lanthanun doped Bi4Ti3O12 thin films were deposited on Pt/Ti/SiO2/Si substrate using a polymeric precursor solution. Annealing in static air and oxygen atmosphere was performed at 700 degrees C for 2 h. The obtained films were characterized by X-ray diffraction and atomic force microscopy. The dielectric constant and dissipation factor were measured in the frequency region from 1 kHz to 1 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. Films annealed in static air possess a dielectric constant higher than films annealed in oxygen atmosphere due to differences in the grain size, crystallinity and structural defects. A regularly shaped hystereses loop is observed after annealing in static air. The obtained results suggest that the annealing in oxygen atmosphere can increase the trapped charge and the relaxation phenomenon. (c) 2006 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Influence of oxygen atmosphere on crystallization and properties of LiNbO3 thin films

Thin films of lithium niobate were deposited on the Pt/Ti/SiO2 (111) substrates by spin coating from the polymeric precursor method (Pechini process). Annealing in static air and oxygen atmosphere was performed at 500 degreesC for 3 h. The films obtained were characterized by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The dielectric constant and dissipation factor were measured in frequency region from 10 Hz to 10 MHz. Electrical characterization of the films pointed to ferroelectricity via hysteresis loop. The influence of oxygen atmosphere on crystallization, morphology and properties of LiNbO3 thin films is discussed. (C) 2003 Elsevier Ltd. All rights reserved.

A polaronic stacking fault defect model for CaCu3Ti4O12 material: an approach for the origin of the huge dielectric constant and semiconducting coexistent features

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Nanoscale electromechanical properties of CaCu3Ti4O12 ceramics

Piezoresponse Force Microscopy (PFM) is used to characterize the nanoscale electromechanical properties of centrosymmetric CaCu3Ti4O12 ceramics with giant dielectric constant. Clear PFM contrast both in vertical (out-of-plane) and lateral (in-plane) modes is observed on the ceramic surface with varying magnitude and polarization direction depending on the grain crystalline orientation. Lateral signal changes its sign upon 180 degrees rotation of the sample thus ruling out spurious electrostatic contribution and confirming piezoelectric nature of the effect. Piezoresponse could be locally reversed by suitable electrical bias (local poling) and induced polarization was quite stable showing long-time relaxation (similar to 3 hrs). The electromechanical contrast in unpoled ceramics is attributed to the surface flexoelectric effect (strain gradient induced polarization) while piezoresponse hysteresis and ferroelectric-like behavior are discussed in terms of structural instabilities due to Ti off-center displacements and structural defects in this material. (C) 2011 American Institute of Physics. [doi:10.1063/1.3623767]

Thermal Constant of an Experimental Population of Muscina stabulans (Fallén 1817) (Diptera:Muscidae) in the Laboratory

A study was conducted to investigate the thermal constant in an experimental population of Muscina stabulans (Fallén 1817). A natural population was obtained from a livestock and their F1 generations were maintained at four constant temperatures (16°C, 20°C, 26°C and 31°C). The thermal constant was calculated by the hyperbole method using the base temperature, tb = 4.4°C and the thermal constant K = 35.3 GD. Ricker's geometric regression, considering tb = 7.8°C and K = 28.9 GD was also calculated.

Phenomenology of infrared finite gluon propagator and coupling constant

We report on some recent solutions of the Dyson-Schwinger equations for the infrared behavior of the gluon propagator and coupling constant, discussing their differences and proposing that these different behaviors can be tested through hadronic phenomenology. We discuss which kind of phenomenological tests can be applied to the gluon propagator and coupling constant, how sensitive they are to the infrared region of momenta and what specific solution is preferred by the experimental data.

Two simple techniques for hysteresis power losses measurement

This paper presents two methods to measure magnetic losses in an iron core for didactic applications for undergraduate students. It is based on indirect measurements of magnetic field and induced flux, simplifying the required instrumentation, and thus, making its implementation possible for lab sessions. Moreover, a comparison between two methods is proposed, allowing the students reaching a deeper understanding of the hysteresis phenomena.

Study of the dielectric and ferroelectric properties of chemically processed BaxSr1-xTiO3 thin films

Polycrystalline BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films with a perovskite structure were prepared by the polymeric precursor method on a platinum-coated silicon substrate. High-quality thin films with uniform composition and thickness were successfully produced by dip-coating and spin-coating techniques. The resulting thin films prepared by dip and spin-coating showed a well-developed dense polycrystalline structure with uniform grain size distribution. The metal-BST-metal structure of the thin films displays good dielectric and ferroelectric properties. The ferroelectric nature to BaxSr1-xTiO3 (x = 0.8) thin film, indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed 2P(r) = 5.0 muC/cm(2) and E-c = 20 kV/cm. The capacitance-frequency curve reveals that the dielectric constant may reach a value of up to 794 at 1 kHz. on the other hand, the BaxSr1-xTiO3 (x = 0.4) thin films had paraelectric nature and dielectric constant and the dissipation factor at a frequency of 100 kHz were 680 and 0.01, respectively, for film annealed at 700 degreesC. In addition, an examination of the film's I-V curve at room temperature revealed the presence of two conduction regions in the BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films, showing ohmic-like behavior at low voltage and a Schottky-emission or Poole-Frenkel mechanism at high voltage. (C) 2001 Elsevier B.V. B.V. All rights reserved.

High Verdet constant Ga : S : La : O chalcogenide glasses for magneto-optical devices

The magneto-optical rotation at room temperature was measured for three Ga:S:La:O chalcogenide glasses at several laser lines in the visible. The first sample was a binary system constituted by 70 mol % Ga2S3 and 30 mol % La2O3, whereas in the second and third ones the lanthanum oxide was partially substituted by lanthanum sulfide, keeping the amount of gallium sulfide fixed. A pulsed magnetic field between 50 and 80 kG was used for the Faraday rotation measurements. The Verdet constant for one of the ternary samples was found to be as high as 0.205 min G(-1) cm(-1) at 543 nm, indicating that these chalcogenide glasses are very promising for magneto-optical applications. The data for each sample were fitted using the expected analytical expression for the magneto-optical dispersion. Measurements of the refractive index of the glasses at 632.8 nm are also reported. Data on the magneto-optical properties of two high Verdet constant, heavy-metal oxide diamagnetic glasses are also included for comparison. (C) 1999 Society of Photo-Optical Instrumentation Engineers. [S0091-3286(99)00102-6].

Niobium doped Bi4Ti3O12 ceramics obtained by the polymeric precursor method

Pure and niobium doped bismuth titanate ceramics (Bi4Ti3-xNbxO12 (BTN)), with x ranging from 0 to 0.4 were prepared by the polymeric precursor method. X-ray diffraction showed no secondary phases. Increasing niobium content leads to more resistive ceramics. The shape and size of the grains are strongly influenced by the niobiurn added to the system. The dielectric constant is not influenced by the niobium addition while hysteresis loops are significantly narrowed. (c) 2006 Elsevier B.V All rights reserved.

Determination of the U-238 spontaneous fission decay constant without neutron irradiation

We have developed a methodology for measuring the decay constant of the spontaneous fission of U-238, lambda(f), using nuclear particle track detectors where thermal neutron irradiation is unnecessary. This methodology is based on the fact that the radiation damage caused by spontaneous fission of trans-uranium elements bearing a mass number close to 238 are similar to U-238 spontaneous-fission ones. Loading a thick source of uranium (thickness greater than the fission fragment range) with a small amount of a suitable trans-uranium element (for instance, Pu-242, which presents a spontaneous fission half-life of 6.75(.)10(10) y), it is possible to determine the observation efficiency of a particle-track detector for fission fragments. Procedures concerning our thick source manufacture and uniformity tests of the trans-uranium distribution are also presented. These results make it possible for the exposure of thick uranium sources (without trans-uranium element) to lead to a lambda(f) value.

High dielectric constant of SrTiO3 thin films prepared by chemical process

SrTiO3 thin films were prepared by the polymeric precursor method and deposited by spin-coating onto Pt/Ti/SiO2/Si(100) substrates. The spin-coated films heat treated at 700 degrees C were crack-free, dense, and homogeneous. Microstructural and morphological evaluations were followed by grazing incident X-ray, scanning electron microscopy and atomic force microscopy. Dielectric studies indicated a dielectric constant of about 475, which is higher than that of ceramic SrTiO3, and a factor dissipation of about 0.050 at 100 kHz. SrTiO3 thin films were found to have paraelectric properties with C-V characteristics. (C) 2000 Kluwer Academic Publishers.

STUDY OF POLING BEHAVIOR OF BIAXIALLY STRETCHED POLY(VINYLIDENE FLUORIDE) FILMS USING THE CONSTANT-CURRENT CORONA TRIODE

This article reports systematic results of corona poling measurements obtained on biaxially stretched polyvinylidene fluoride films charged in dry air. Charging was performed using the constant current corona triode. The dependence of the poling process on the sample thickness, charging current, and successive charging processes was investigated. Phase transitions from alpha to delta and to beta phases were observed when virgin samples were corona charged. The thermal pulse technique showed that the polarization profiles during charging can be made consistently almost uniform and that the ferroelectric reorientation can be associated with the rising plateau region displayed on potential buildup curves. (C) 1995 American Institute of Physics.