Evaluation of dental restorations: a comparative study between clinical and digital photographic assessments

The aim of this study was to compare the efficacy of a direct clinical evaluation method with an indirect digital photographic method in assessing the quality of dental restorations. Seven parameters (color, occlusal marginal adaptation, anatomy form, roughness, occlusal marginal stain, luster, and secondary caries) were assessed in 89 Class I and Class II restorations from 36 adults using the modified US Public Health Service/Ryge criteria. Standardized photographs of the same restorations were digitally processed by Adobe Photoshop software, separated into the following four groups and assessed by two calibrated examiners: Group A: The original photograph displayed at 100%, without modifications (IMG100); Group B: Formed by images enlarged at 150% (IMG150); Group C: Formed by digital photographs displayed at 100% (mIMG100), with digital modifications (levels adjustment, shadow and highlight correction, color balance, unsharp Mask); and Group D: Formed by enlarged photographs displayed at 150% with modifications (mIMG150), with the same adjustments made to Group C. Photographs were assessed on a calibrated screen (Macbook) by two calibrated clinicians, and the results were statistically analyzed using Wilcoxon tests (SSPS 11.5) at 95% CI. Results: The photographic method produced higher reliability levels than the direct clinical method in all parameters. The evaluation of digital images is more consistent with clinical assessment when restorations present some moderate defect (Bravo) and less consistent when restorations are clinically classified as either satisfactory (Alpha) or in cases of severe defects (Charlie). Conclusion: The digital photographic method is a useful tool for assessing the quality of dental restorations, providing information that goes unnoticed with the visual-tactile clinical examination method. Additionally, when analyzing restorations using the Ryge modified criteria, the digital photographic method reveals a significant increase of defects compared to those clinically observed with the naked eye. Photography by itself, without the need for enlargement or correction, provides more information than clinical examination and can lead to unnecessary overtreatment.

Clinical/photographic evaluation of a single application of two sealants after eleven years

The clinical behavior of Concise and Prisma Shield sealants for pit and fissure was analyzed by clinical/photographic evaluation. A hematoxylin-based staining solution was applied to the occlusal surface 7 days, 18 months, 36 months, and 11 years after the occlusal sealing, thus allowing the sealant material on the surface to be checked. At each analysis time, each occlusal surface was photographed, and the photographs corresponding to each time were submitted to clinical/photographic evaluation. Although the sealant materials showed marginal alterations over time, they did not require reapplication because the region composed of the pit and fissure remained covered.

Analysis of residual stress and hardness in regions of pre-manufactured and manual bends in fixation plates for maxillary advancement

The aim of this study was to analyze, through Vickers hardness test and photoelasticity analysis, pre-bent areas, manually bent areas, and areas without bends of 10-mm advancement pre-bent titanium plates (Leibinger system). The work was divided into three groups: group I-region without bend, group II-region of 90° manual bend, and group III-region of 90° pre-fabricated bends. All the materials were evaluated through hardness analysis by the Vickers hardness test, stress analysis by residual images obtained in a polariscope, and photoelastic analysis by reflection during the manual bending. The data obtained from the hardness tests were statistically analyzed using ANOVA and Tukey's tests at a significance level of 5 %. The pre-bent plate (group III) showed hardness means statistically significantly higher (P < 0.05) than those of the other groups (I-region without bends, II-90° manually bent region). Through the study of photoelastic reflection, it was possible to identify that the stress gradually increased, reaching a pink color (1.81 δ / λ), as the bending was performed. A general analysis of the results showed that the bent plate region of pre-bent titanium presented the best results.