Caracterização microestrutural de junta soldada com arco submerso e análise da propagação de trincas em um tubo de aço API X 70

In this work a study of an API 5L X70 steel, which is used in the manufacture of oil and gas pipelines, has been made. This class of steel show high strength and ductility values, and has been increasingly studied due the growing demand of oil and natural gas, which in consequence, increases the needing of new pipelines to transport them. The material studied has been directly taken from a tube provided by TenarisConfab, and a special attention has been given to the fatigue crack growth rate study, which proved that a crack will grow at different rates according to the tube position where it is growing

Fatigue behavior of PVD coated Ti-6Al-4V alloy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

An investigation of electrolytic surface damages and electroplated crhomium effects on fatigue behavior of high strength steel

Fatigue crack initiation occurs at the surface, although sub surface nucleation has also been reported. Localized imperfections like inclusions close to surface and surface small pits can result in crack sources. Coatings are not always beneficial by fatigue point of view too. Mechanical properties of the covering material can change considerably the fatigue behavior of base metal due to residual surface stresses, to micro cracks or to hydrogen embrittlement. This paper is concerned with analysis of electrolytic etch on the fatigue resistance of a 35NCD16 high strength steel in a mechanical condition of (1760 - 1960) MPa, and analysis of electroplated hard chromium effects on the fatigue resistance in a strength condition of 989 MPa. Hardness impression was used as a reference parameter in case of electrolytic etch. In both cases, experimental data showed that fatigue strength of 35NCD16 steel was considerably reduced. Copyright © 2001 Society of Automotive Engineers, Inc.

Influence of shot peening and hard chromium electroplating on the fatigue strength of 7050-T7451 aluminum alloy

Chromium electrodeposition is a technique for the production of functional coatings on engineering components. These coatings are extensively micro-cracked and present high level of hardness, resistance to corrosion and wear and low coefficient of friction. In this paper the shot peening influence on the fatigue strength of aluminum 7050-T7451 alloy chromium electroplated, was investigated.The shot peening process was carried out to create residual stresses using ceramic and glass shots. A hard chromium electroplated coating of 100 mu m thickness was performed on the base material and the shot peened base material surfaces. S-N curves were obtained in axial and bending fatigue tests and compared with the 7050-T7451 aluminum alloy. In order to study the influence of residual stresses on fatigue life, the behavior of compressive residual stress field was measured by an X-ray tensometry.An increase in the axial fatigue strength of 25% and 50% of ceramic and glass shots, respectively, was observed. The lower performance in fatigue life for ceramic-shot peening may be attributed to higher surface damage, as a consequence of the overpeening intensity performed. However, in bending fatigue the behavior was practically equivalent for both processes. Fracture surface analysis by scanning electron microscopy was used to observe crack origin sites from shot peened and chromium electroplated samples. (C) 2006 Elsevier Ltd. All rights reserved.

Fadiga em compósitos 5HS carbono/epóxi processados via RTM: relação entre cargas axiais no plano e modos de delaminação

Pós-graduação em Engenharia Mecânica - FEG

Influence of anodization on the fatigue strength of 7050-T7451 aluminium alloy

In recent years, with higher demand for improved quality and corrosion resistance, recovered substrates have been extensively used. Consequently residual stresses originated from these coatings reduce the fatigue strength of a component. Due to this negative influence occasioned by corrosion resistance protective coatings, an effective process like shot peening must be considered to improve the fatigue strength. The shot peening treatment pushes the crack sources beneath the surface in most of medium and high cycle cases due to the compressive residual stress field (CRSF) induced. The aim of this study was to evaluate the influence on the fatigue life of anodic films grown on 7050-T7451 aluminium alloy by sulphuric acid anodizing, chromic acid anodizing and hard anodizing. The influence on the rotating and reverse bending fatigue strength of anodic films grown on the aluminium alloy is to degrade the stress life fatigue performance of the base material.A consistent gain in fatigue life in relation to the base material was obtained through the shot peening process in coated specimens, associated to a residual stress field compressive near the surface, useful to avoid fatigue crack nucleation and delay or even stop crack propagation.

Non-linear growth models for bullfrog tadpoles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Oriented growth of Bi3.25La0.75Ti3O12 thin films on RuO2/SiO2/Si substrates by using the polymeric precursor method: Structural, microstructural and electrical properties

c-axis oriented Bi3.25La0.75Ti3O12 (BLT) thin films were grown on a RuO2 top electrode deposited on a (100) SiO2/Si substrate by the polymeric precursor method. X-ray diffraction and atomic force microscope investigations indicate that the films exhibit a dense, well crystallized microstructure having random orientations with a rather smooth surface morphology. The electrical properties of preferred oriented Bi3.25La0.75Ti3O12 (BLT) thin films deposited on RuO2 bottom electrode leaded to a large remnant polarization (P-r ) of 17.2 mu C/cm(2) and (V-c ) of 1.8 V, fatigue free characteristics up to 10(10) switching cycles and a current density of 2.2 mu A/cm(2) at 5 V. We found that the polarization loss is insignificant with nine write/read voltages at a waiting time of 10,000 s. Independently of the applied electric field the retained switchable polarization approached a nearly steady-state value after a retention time of 10 s.

Fractografia quantitativa de superfícies obtidas em ensaios de propagação de trincas por fadiga em aço inoxidável 15 –5PH

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito da fadiga cíclica na resistência, crescimento subcrítico de trincas e tempo de vida de cerâmicas a base de alumina infiltradas por vidro

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do comportamento em fadiga de uma chapa de aço microligado, grau API 5L X70

In engineering, for correct designing the structural components required for cyclical stresses, it is necessary to determine a limit of resistance to fatigue, which is the maximum amplitude of the applied tension under which the fatigue failure does not occurs after a certain number cycles. The marine environment is hostile, not only by the high pressure, corrosion, but also by low temperatures. Petrol Production units, composed of the risers (pipelines connecting the oil well to the ship), are dimensioned to remain installed for periods of 20 up to 30 years, and must therefore be prepared to support various efforts, such as tidal, wind currents and everything that is related. This paper focuses on a study on the fatigue behavior of microalloyed steel, API 5L Grade X70, used to transport oil and gas by pipelines. For analysis, we obtained the curves S-N (stress vs. number of cycles) using laboratory data collected from cylindrical longitudinal and transverse specimens used in axial fatigue test in accordance with ASTM E466. The tensile tests and microhardness were performed to characterize the mechanical properties of the samples, and it was found that the values meet the specifications of the standard API 5L. To characterize microstructurally the material, it was also made a metallographic analysis of the steel under study, and the origin of the fatigue crack was investigated with the support of a scanning electron microscope (SEM).

Estudo do comportamento em fadiga das ligas AA6005, AA6063 e AA6351

Aluminum alloys have shown great potential for the automotive industry, especially aluminum alloys 6xxx series. This category has good mechanical strength and excellent corrosion resistance, important for the areas of construction and transport. The automotive industry has always shown great interest in the study of fatigue behavior, because structural components are subjected to cyclic and vibration loads, generating cracks and fracturing. The mechanical response depends on the material properties, applications, surface condition and microstructure. In this work was study the fatigue behavior of high cycle of machined bodies (not polished) and the effect of roughness on the fatigue life for three aluminum alloys of 6xxx series: AA6005, AA6351 and AA606, all in the T6 condition . S / N curves were made from fatigue tests in rotating bending (R = -1). The influence of roughness was studied by measuring the roughness of each specimen. Was compare the fatigue behavior of polished specimen and not polished specimens. The fractured surfaces of samples were observed by MEV, and it was observed that most of nucleation sites for fatigue crack is initiated below the surface

Influência de defeitos e diferentes processos de fabricação nas propriedades mecânicas finais de cerâmicas

Os materiais cerâmicos são atualmente cada vez utilizados como opção na engenharia mundial. Por se tratar de materiais com alta resistência mecânica, possuem muitas aplicações em diversas áreas, como por exemplo a de mancais, a automotiva (sensores, isoladores, catalisadores, pistões, válvulas, revestimentos), a de implantes biocompatíveis (dentário, substituição óssea, válvulas cardíacas), a de produtos sujeitos ao desgaste (guias), a de refratários (revestimento de equipamento bélico, componentes de fornos), a eletrônica, e outras. Nos processos de fabricação da cerâmica há uma gama de fatores que contribuem para as características do produto final. Devido a isso, muitos pesquisadores têm trabalhado no estudo da influência de determinados defeitos e técnicas de produção de cerâmicas nas características do produto final. Este trabalho tem como objetivo fazer uma revisão bibliográfica de recentes artigos que analisam a influência de fatores como velocidade de queima, surgimento de trincas, porosidade, fases cristalinas, e tamanho de partículas, nas propriedades mecânicas finais das cerâmicas. Pode-se concluir que é possível aperfeiçoar o processo de fabricação da cerâmica a fim de promover as melhores propriedades mecânicas possíveis, conhecendo-se fatores prejudiciais e métodos adequados para se obter o melhor produto final.

A Cellular Automaton Approach to Spatial Electric Load Forecasting

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Morphology characterization of layer-by-layer films from PAH/MA-co-DR13: the role of film thickness

We report on the use of dynamic scale theory and fractal analyses in the Study of distinct growth stages of layer-by-layer (LBL) films of poly(allylamine hydrochloride) (PAH) and a side-chain-substituted azobenzene copolymer (Ma-co-DR13). The LBL films were adsorbed oil glass substrates and characterized with atomic force microscopy with the Ma-co-DR13 at the top layer. The ganular morphology exhibited by the films allowed the observation of the growth process inside and outside the grains. The growth outside the grains was found to follow the Kardar-Parisi-Zhang model, with fractal dimensions of ca. 2.6. One could expect that inside the grains the morphology would be close to a Euclidian surface with fractal dimension of ca. 2 for any growth stage. The latter, however, was observed only for thicker films containing more than 10 bilayers. For thinner films the morphology was well described by a self-affine fractal. Such dependence of the growth behavior with the film thickness is associated with a more complete coverage of adsorption sites in thicker films due to diffusion of polymer molecules. (c) 2004 Elsevier B.V. All rights reserved.