Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm 2, respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey's test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements. © 2009 Pleiades Publishing, Ltd.

Influence of desensitizing agents on the microshear bond strength of adhesive systems to dentin.

The aim of this study was to evaluate the effect of desensitizing agents on the micro-shear bond strength of adhesive systems to dentin. Forty bovine teeth were divided into 8 groups (n=5): G1--Single Bond (SB); G2--GH.F + SB; G3-- Desensibilize + SB; G4--essensiv + SB; G5 --ingle Bond 2 (SB2); G6--H.E + SB2; G7--esensibilize + SB2; G8--Dessensiv + SB2. In all of the groups, the desensitizing agents were applied after phosphoric acid etching and before the dentin adhesive application. Z250 composite resin tubes were bonded on the treated surface. After 24 hours, the teeth were tested in a universal machine. Data were submitted to ANOVA and Tukey's test (5%). The results showed that the groups where Desensibilize and Dessensiv were applied exhibited smaller bond strength values.

Microhardness of glass ionomer cements indicated for the ART technique according to surface protection treatment and storage time

The aim of this study was to assess the microhardness of 5 glass ionomer cements (GIC) - Vidrion R (V, SS White), Fuji IX (F, GC Corp.), Magic Glass ART (MG, Vigodent), Maxxion R (MR, FGM) and ChemFlex (CF, Dentsply) - in the presence or absence of a surface protection treatment, and after different storage periods. For each GIC, 36 test specimens were made, divided into 3 groups according to the surface protection treatment applied - no protection, varnish or nail varnish. The specimens were stored in distilled water for 24 h, 7 and 30 days and the microhardness tests were performed at these times. The data obtained were submitted to the ANOVA for repeated measures and Tukey tests (α = 5%). The results revealed that the mean microhardness values of the GICs were, in decreasing order, as follows: F > CF = MR > MG > V; that surface protection was significant for MR, at 24 h, without protection (64.2 ± 3.6a), protected with GIC varnish (59.6 ± 3.4b) and protected with nail varnish (62.7 ± 2.8ab); for F, at 7 days, without protection (97.8 ± 3.7ab), protected with varnish (95.9 ± 3.2b) and protected with nail varnish (100.8 ± 3.4a); and at 30 days, for F, without protection (98.8 ± 2.6b), protected with varnish (103.3 ± 4.4a) and protected with nail varnish (101 ± 4.1ab) and, for V, without protection (46 ± 1.3b), protected with varnish (49.6 ± 1.7ab) and protected with nail varnish (51.1 ± 2.6a). The increase in storage time produced an increase in microhardness. It was concluded that the different GICs, surface protection treatments and storage times could alter the microhardness values.

Bone structure, strength and microhardness resulting after hindlimb unloading in rats

Introduction: Bone strength is influenced by a number of different determinants, such as mass, size, geometry and also by the intrinsic material properties of the tissue. Aims: The structure and mechanical properties of the femur were analyzed in aged (14 mo-old) animals submitted to hindlimb unloading (HU) for 21 days. Methods: Twenty Wistar rats were randomly divided into Control and HU groups and the femur was submitted to dual X ray absorptiometry (DXA), DIGORA radiographic density, mechanical compression testing and Knoop microhardness analyse in cortical and cancellous bone. Results: Femurs from HU group presented significantly lower failure load, decreased bone mineral density (BMD)/bone mineral content (BMC) in whole bone; proximal/distal epiphysis and middiaphyseal cortical bone measured by DXA were similar in the two groups; radiographic density from areas in proximal epiphysis was significantly lower in HU group, and microhardness measured at periosteal and endosteal levels were also signifcantly diminished in HU compared with Control group. Conclusion: Disuse induced damage in the trabecular femoral bone architecture with decisive effect on the head and trochanteric fossa, which became weaker. Bone diaphyseal cortical hardness also suffered effect of unloading, probably related to osteocyte/osteoblast activity.

Observation of tags and hybrid layer of a single bottle conventional adhesive system and a self-etching adhesive system, on sound dentin.

This experimental light microscopy study investigated the formation of a hybrid layer and resin tags on sound dentin, after utilization of conventional and self-etching adhesive systems. After restorative procedures, the specimens were decalcified in a formic acid and sodium citrate solution, embedded in paraffin, sectioned at 6-microm thickness and stained by the Brown & Brenn method for analysis and measurement by light microscopy (AXIOPHOT) (400x). The results were statistically analyzed by analysis of variance, at a significance level of 5%. Based on the results, it could be concluded that the conventional adhesive allowed the formation of a thicker hybrid layer than the self-etching adhesive, with similar penetration into the dentinal tubules (resin tags).

Effect of accelerated aging on the microhardness and color stability of flexible resins for dentures

Acrylic resins have been widely used due to their acceptable esthetics and desirable characteristics such as easy handling, good thermal conductivity, low permeability to oral fluids and color stability. Flexible resins were introduced on the market as an alternative to the use of conventional acrylic resins in the construction of complete and partial removable dentures. Although these resins present advantages in terms of esthetics and comfort, studies assessing chromatic and microhardness alterations of these materials are still scarce in the related literature. The aim of this study was to evaluate the chromatic and microhardness alterations of two commercial brands of flexible resins in comparison to the conventional resin Triplex when submitted to accelerated aging. The resins were manipulated according to manufacturers' instructions and inserted into a silicone matrix to obtain 21 specimens divided into 3 groups: Triplex, Ppflex and Valplast. Triplex presented the highest microhardness value (p < 0.05) for all the aging periods, which was significantly different from that of the other resins, followed by the values of Valplast and Ppflex. Comparison between the flexible resins (Ppflex and Valplast) revealed a statistically significant difference (p < 0.05) as regards color. The flexible resin Ppflex and the conventional resin Triplex presented no statistically significant difference (p < 0.05) as regards aging. The accelerated aging significantly increased the microhardness values of the resins, with the highest values being observed for Triplex. Valplast presented the greatest chromatic alteration after accelerated aging.

In vitro evaluation of the effect of dietary acids and toothbrushing on human root dentin permeability

OBJECTIVES: The purpose of this in vitro study was to quantify the alterations in human root dentin permeability after exposure to dietary acids and to evaluate the effect of toothbrushing after acid application. METHOD AND MATERIALS: Extracted human third molars had their crowns sectioned above the CEJ, pulp tissue removed, and cervical root dentin exposed using a high-speed bur (approximately 1 mm in depth of substance loss). From each root fragment, one specimen was prepared. A total of 25 specimens were used and distributed randomly into five groups. The specimens were attached to a hydraulic pressure apparatus to evaluate the alterations of root dentin permeability after exposure to different acids. Dentin permeability was measured after the following sequential steps: (1) treatment with EDTA for 3 minutes to obtain the maximum permeability; (2) root planing to create a smear layer; (3) exposure to different acidic substances for 5 minutes (vinegar, cola drink, lemon juice, white wine, and orange juice); and (4) brushing for 3 minutes. RESULTS: All acidic substances increased dentin permeability after root planing. Lemon juice produced higher values for permeability when compared to the other substances (P = .009); moreover, orange juice showed similar results (P < .02) except when compared to vinegar (P = .12). Brushing right after acid exposure significantly reduced dentin permeability except in the vinegar group (P = .07). CONCLUSION: Under the experimental conditions, dietary acids increased root dentin permeability, and immediate brushing reduced permeability levels.

Effects of five carbamide peroxide bleaching gels on composite resin microhardness.

The purpose of this study was to evaluate the effects of five home bleaching products containing 15-16% carbamide peroxide on the microhardness of microhybrid composite resin Z-250 (3M/Espe). A total of 72 specimens were fabricated in cylindrical acrylic matrices (4 x 2 mm), filled with composite resin and photo-activated for 40 seconds. They were divided in 6 study groups (n = 12), according to the bleaching product: Review (SS White), Magic Bleaching (Vigodent), Opalescence (Ultradent), Whiteness Perfect (FGM), Claridex (Biodinâmica), and a control group (not bleached). Specimens were exposed to 1 cc of bleaching gel for 6 hours daily for 2 weeks. The control group specimens were kept in artificial saliva throughout this time. All the specimens were then analyzed in a microhardness tester. Knoop hardness measurements were performed, and the results were submitted to parametric statistical analysis (analysis of variance and Tukey's test). Mean Knoop values and standard deviation were: baseline, 68.52a (4.28); control, 63.42b (7.16); Whiteness Perfect, 57.57c (1.81); Magic Bleaching, 57.22c (3.84); Opalescence, 57.03cd (4.00); Claridex, 53.64de (3.33); Review 51.45e (2.82). Identical letters mean statistical equality according to Tukey's test at the 5% significance level. The products significantly decreased Z-250 (3M/Espe) microhardness.

Cementation of fiber post: influence of the cement insertion techniques on the bond strength of the fiber post-root dentin and the quality of the cement layer.

The aim of this study was to assess the influence of resin cement insertion methods on the bond strength of a fiber post to root dentin and quality of the cement layer. Forty bovine single-roots (length =16 mm) were randomly allocated into four groups, according to the cement insertion methods (N.=10): Gr1- Lentulo drill #40, Gr2- Centrix syringe, Gr3- Explorer #5, Gr4- fiber post. The root canals were prepared at 12 mm, using preparation bur # 3 of a cylinder quartz-FRC post (Aesthet post-plus, Bisco). The fiber posts were cemented using a multi-step etch-and-rinse adhesive system (All Bond 2®, Bisco) and a dual-cured resin cement (Duolink, Bisco). Each root was cut into seven samples: four samples of 1.8 mm thickness for push-out testing, and three with 0.5 mm for cement layer quality analyzing. One-way ANOVA was used for the push-out test values and the One-Way Kruskal-Wallis (P<0.05) and Dunn (10%) tests for the cement layer analyzes. ANOVA showed that the cement layer quality was affected by the cement insertion methods (P=0.0044): Gr1 (3.8 ± 1.3a), Gr2 (3.2 ± 1.3a), Gr3 (5.2 ± 1.5a,b) and Gr4 (5.2 ± 1.5b) (Dunn test), whereas the bond strength (MPa) was not affected by cement insertion methods: G1 (4.2 ± 1.3), G2 (3.2 ± 1.8), G3 (4.5 ± 0.9), G4 (3.1 ± 1.3). The fiber posts should be cemented with the assistance of the lentulo drill or centrix syringe to promote the best cement layer results.

Effect of an acid diet allied to sonic toothbrushing on root dentin permeability: An in vitro study

This study quantified alterations in root dentin permeability after exposure to different acid beverages. Twenty-five third molars were sectioned below the cementoenamel junction, the root segment was collected, and the pulp tissue was removed. The root segments were connected to a hydraulic pressure apparatus to measure the permeability of root dentin after the following sequential steps, with 5 specimens in each: 1) phosphoric acid etching for 30 s (maximum permeability), 2) root planning to create new smear layer, 3) exposure to different acid substances for 5 min (orange, cola drink, vinegar, white wine, lemon juice), 4) toothbrushing with sonic toothbrush for 3 min, 5) toothbrushing with sonic toothbrush plus dentifrice for 3 min. Considering step I as 100%, the data were converted into percentage and each specimen was its own control. Data were analyzed statistically by Kruskal-Wallis and Dunn's post test at 5% significance level. All acidic substances increased dentin permeability significantly after scraping (p<0.05). Toothbrushing after exposure to acid substances decreased dentin permeability and the association with dentifrice accentuated the decrease (p<0.05), except for the specimens treated with cola drink. Thus, it may be concluded that all tested acid fruit juices increased dentin permeability, and toothbrushing with or without dentifrice can decrease root dentin permeability after dentin exposure to acid diet.

The effect of carbamide peroxide bleaching agents on the microhardness of dental ceramics.

This study examined the effect of 10% and 16% carbamide peroxide bleaching agents on the surface microhardness of micro-particulate feldspathic ceramics (VM7 and VM13, Vita Zahnfabrik). Forty specimens (8-mm diameter, 2-mm thickness) were divided into four groups (n=10): GI-VM7 + 10% Whiteness, G2-VM7 + 16% Whiteness, G3-VM13 + 10% and G4-VM13 + 16% Whiteness. The home-use bleaching agents were applied for 8 hours on 15 days, and the specimens were stored in distilled water at 37 degrees C. The Vickers hardness number (HV) was determined for each specimen. Data were analyzed by the Wilcoxon and Mann-Whitney tests (p < 0.05). The microhardness values before exposure were: g1-433 (57); g2-486 (22); g3-509 (28); g4-518 (24), and after exposure: G1-349 (32); G2-496 (95); G3-519 (38); G4-502 (81). G2 exhibited a higher and significant difference than GI in VM7 groups, and the effect of bleaching concentration was shown to be significant by the Mann-Whitney test. And for VM13, both the Wilcoxon and Mann-Whitney tests showed no significant differences. When using 10% carbamide peroxide, the microhardness of VM7 ceramic was affected, and there were no effect on the microhardness between VM7 and VM13 ceramics when 16% carbamide peroxide was used.

Evaluation of the dentin-pulp complex after cavity preparation with ultrasonic diamond tip

The aim of this paper was to compare the dentin-pulp complex response to cavity preparation in human teeth using ultrasonic chemical vapor deposition (CVD) diamond tip and high-speed diamond bur. Class V buccal cavities were randomly prepared in 40 premolars from 14 patients aged 11 to 15 years. The cutting time was recorded and the cavities had the axial walls protected with gutta-percha and were filled with glass ionomer cement. The teeth were extracted at intervals of 0, 5, 10 and 20 days, and were decalcified, sectioned and stained by Hematoxylin & Eosin, Masson's Trichrome and Brown & Brenn techniques. The inflammatory response and cell disorganization were blindly evaluated by two examiners. The remaining dentin thickness (RDT) was measured by a linear scale using computer software. Statistical analysis by one-way ANOVA showed no statistically significant difference (P≤0.05) among the cavities prepared with either type of instrument, with mean RDT of 1132.50 mm. Cutting time and the pulp-dentin complex responses were analyzed statistically by Kruskal-Wallis and Dunn tests (P≤0.05). The ultrasonic CVD diamond tip took 5 times longer to prepare the cavities and there were no typical inflammatory pulp responses in cavities prepared with either type of cutting instrument, only mild to moderate cell disorganization was present. Even taking longer to cut the dental substrate, the ultrasonic CVD diamond tip produced similar pulp response compared to the conventional high-speed diamond bur.

Adhesion between fiber post and root dentin: evaluation of post surface conditioning for bond strength improvement.

The aim of this paper was to evaluate two surface conditioning methods associated with the application of adhesive on the post surface for improving the bond to resin cement. Sixty single-rooted bovine teeth were sectioned at 16 mm in length, prepared (9 mm depth), embedded in a PVC cylinder using acrylic resin, and allocated into 3 groups (N.=20) according to post surface treatment: cleaning with ethanol (control group); etching with hydrogen peroxide; etching with hydrofluoric acid. Ten posts for each group were silanized and other 10 posts were silanized and received an adhesive agent. The posts were cemented with self-adhesive resin cement (RelyX U100 resin cement). All teeth were sectioned perpendicularly to the long axis (2 mm thickness per slice), submitted to push out bond strength testing and the type of failure was recorded. The obtained data were submitted to two-way ANOVA and Turkey's test, with the level of significance set at 5%. Neither the hydrofluoric acid or hydrogen peroxide post surface treatment, nor the adhesive application, had an influence on bond strength values. The main type of failure was adhesive between cement and dentin. Etching and the application of an adhesive on the post surface did not presented a significant influence on the bond strength results for the fiber post resin cement-root dentin assembly. The cement appears to adhere very well to the fiber post surface rather than the dentin surface.

Micromechanics of dentin/adhesive interface in function of dentin depth: 3d finite element analysis

Objectives: The aim of this study was to analyze the stress distribution on dentin/adhesive interface (d/a) through a 3-D finite element analysis (FEA) varying the number and diameter of the dentin tubules orifice according to dentin depth, keeping hybrid layer (HL) thickness and TAǴs length constant. Materials and Methods: 3 models were built through the SolidWorks software: SD - specimen simulating superficial dentin (41 x 41 x 82 μm), with a 3 μm thick HL, a 17 μm length Tag, and 8 tubules with a 0.9 μm diameter restored with composite resin. MD - similar to M1 with 12 tubules with a 1.2 μm diameter, simulating medium dentin. DD - similar to M1 with 16 tubules with a 2.5 μm diameter, simulating deep dentin. Other two models were built in order to keep the diameter constant in 2.5 μm: MS - similar to SD with 8 tubules; and MM - similar to MD with 12 tubules. The boundary condition was applied to the base surface of each specimen. Tensile load (0.03N) was performed on the composite resin top surface. Stress field (maximum principal stress in tension - σMAX) was performed using Ansys Wokbench 10.0. Results: The peak of σMAX (MPa) were similar between SD (110) and MD (106), and higher for DD (134). The stress distribution pathway was similar for all models, starting from peritubular dentin to adhesive layer, intertubular dentin and hybrid layer. The peak of σMAX (MPa) for those structures was, respectively: 134 (DD), 56.9 (SD), 45.5 (DD), and 36.7 (MD). Conclusions: The number of dentin tubules had no influence in the σMAX at the dentin/adhesive interface. Peritubular and intertubular dentin showed higher stress with the bigger dentin tubules orifice condition. The σMAX in the hybrid layer and adhesive layer were going down from superficial dentin to deeper dentin. In a failure scenario, the hybrid layer in contact with peritubular dentin and adhesive layer is the first region for breaking the adhesion. © 2011 Nova Science Publishers, Inc.

Morphological alterations on human radicular dentin after exposure to different fruit juice drinks

Purpose: This in vitro study aimed to evaluate the effect of different fruit juice drinks available in the Brazilian market on smear layer removal and dentinal tubules opening, as well as to verify the effect of toothbrushing subsequently to the juices exposure. Methods: Dentin specimens were prepared and randomly distributed into the control group (distilled water) and twelve types of fruit juice drinks (cashew, orange, mandarin, apple, passion fruit, guava, strawberry, grape, mango, pear, peach, pineapple). The following treatments were applied: immersion or immersion + brushing. After preparation for SEM, photomicrographs were assessed using an index of smear layer removal. Results: No significant differences regarding smear layer removal and dentinal tubules exposure could be observed between the groups after both treatments (Kruskal-Wallis, post-hoc paired comparisons, P>0.05). The control solution and the fruit juice drinks were not able to remove smear layer and to open dentinal tubules. Significant difference between the applied treatments was detected only for the mango juice group (Mann-Whitney, P<0.05). Conclusion: Under the experimental conditions, the different fruit juice drinks did not promote significant alterations on human radicular dentin morphology regardless of the subsequent application of brushing procedures. Copyright: © 2011 Zandim et al.