Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments

The purpose of this study was to evaluate the effect of heat treatments on the Vickers hardness of commercially pure titanium and Ti-6Al-4V cast alloys. Six-millimeter-diameter cylindrical specimens were cast in a Rematitan System. Commercially pure titanium and Ti-6Al-4V alloy specimens were randomly assigned to 3 groups (n=10) that received the following heat treatments: control (no heat treatment); treatment 1 (T1): heating at 750°C for 2 h; and treatment 2 (T2): annealing at 955°C for 1 h and aging at 620°C for 2 h. After heat treatments, the specimens were embedded in acrylic resin and their surface was ground and polished and hardness was measured. Vickers hardness means (VHN) and standard deviations were analyzed statistically by Kruskal-Wallis test at 5% significance level. For commercially pure titanium, Vickers hardness means of group T2 (259.90 VHN) was significantly higher than those of the other groups (control - 200.26 VHN and T1 - 202.23 VHN), which presented similar hardness means to each other (p>0.05). For Ti-6Al-4V alloy, statistically significant differences were observed among the three groups: T2 (369.08 VHN), T1 (351.94 VHN) and control (340.51 VHN) (p<0.05). The results demonstrated different hardness of CP Ti and Ti-6Al-4V when different heat treatments were used. For CP Ti, VHN means of T2 group was remarkably higher than those of control and T1 group, which showed similar VHN means to each other. For Ti-6Al-4V alloy, however, VHN means recorded for each group may be presented as follows: T2>T1>control.

Spatial distribution and shell utilization in three sympatric hermit crabs at non-consolidated sublittoral of estuarine-bay complex in São Vicente, São Paulo, Brazil

The objective of the present study was to characterize the spatial distribution and shell utilization of three hermit crab species in the estuarine-bay complex of São Vicente, São Paulo State, Brazil. Monthly samples were done throughout two years, in the non-consolidated sub-littoral at the estuarine-bay complex. The environmental factors, such as temperature, salinity and depth, were measured every month. The three hermit crab species, Clibanarius vittatus, Loxopagurus loxochelis and Isocheles sawayai, were captured utilizing shells from six gastropods species; 92.7% of the hermit crabs utilized Stramonita haemastoma. The results suggest a strong correlation between hermit crabs spatial distribution and salinity, which was considered the main environmental factor limiting their distribution in the estuary. I. sawayai was the only species present in all transects sampled; C. vittatus was captured only in regions with low salinity and L. loxochelis occurred only in high salinity waters.

A unique intraorbital osseous structure in the large fruit-eating bat (Artibeus lituratus)

Objective: To describe the normal bony orbital structure of the large fruit-eating bat (Artibeus lituratus) with emphasis on a unique intraorbital bony structure previously not described in the literature. Procedures: The bony anatomy of the orbital cavity was studied on dissected skulls of large fruit-eating bats. The anatomic description of a unique intraorbital spine was made while studying the bony orbit of macerated skulls. Additional observations were made on dissected formalin-fixed whole heads. Both procedures were performed under a stereo dissecting microscope, using ×2-4-magnification. A histologic analysis of soft tissues surrounding this cylindrical bony structure was performed using cross and longitudinal oblique sections from decalcified whole heads, which had been fixed in formalin. Additionally, biometric measurements and a histomorphometric analysis were performed. Results and conclusions: An intraorbital cylindrical osseous structure measuring 3.96 ± 0.68 mm in length and 155.62 ± 14.03 μm in diameter was observed in the large fruit-eating bat (A. lituratus), creating a unique orbital structural design among mammals. We suggest the name optic spine of the alisphenoid bone. The anatomic, biometric and histologic characterization of this element might contribute to a further understanding of the dynamics of bat vision and the sort of factors that influenced evolution of the visual system of microbats. The authors hope that the documentation of this distinctive anatomic feature will also expand the debate about the phylogenetic analysis of the relationship among bat species in the near future. © 2007 American College of Veterinary Ophthalmologists.

Morfo-anatomia do eixo vegetativo aéreo de Achyrocline alata (Kunth) DC. (Asteraceae)

Achyrocline alata occurs in a dense and low vegetation in Mato Grosso do Sul State, Brazil and it has been studied under physical-chemical and yield aspects, being scarce anatomical data. The present work has as objective the study of the aerial vegetative axis. Stem is cylindrical and hairy, having five wings, which are arisen from their leaves. The blade shows the presence of uniseriate epidermis, which is covered by the cuticle of variable thickness; and non-glandular and glandular trichomes. The non-glandular trichomes are uniseriate and multicellular and have their apex cell in whip form, while the glandular trichomes are multicellular, uniseriate or biseriate. The mesophyll is dorsiventral with uni-stratified palisade parenchyma in most of the cases and lacunal parenchyma formed by three to four layers of irregular cells. Only one collateral vascular bundle occurs in the midvein. Stem in transversal section is covered by epidermis with trichomes similar to leaves; the cortex is constituted by a discontinuous area of angular collenchyma, which is followed by chlorophyll parenchyma. Vascular cylinder that is delimited by pericycle shows vascular bundles of collateral type. In the secondary structure, the periderm is originated from epidermal and subepidermal tissues. In vascular region, the fascicular cambium differs into secondary xylem and phloem, while interfascicular cambium produces sclerenchymatous tissue.

O uso da serragem no processo de minicompostagem

In this work used four cylindrical PVC (polyvinyl chloride) mini compost bins, they all had the same size and were identical, with 40 cm diameter and 75 cm length, they also were opened on both sides. Each mini compost bean received 35,5 kg of solid organic wastes, which were previously crushed and 6 kg of sawdust. It was evaluated during the composting process the C/N analyses, temperature measurement, humidity and pH. Results showed that the use of sawdust as a source of high carbon inputs on the mini compost beans and using low quantities of organic solid wastes reached temperatures as high as 65° C, keeping on the thermophilic phase for almost 6 days. After 18 days the environmental temperature was reached, the organic wastes were then laid to reach full maturity for 55 more days. The C/N ratio was initially around 30/1 and after 73 days it was around 12/1.

Diametral tensile strength of dual-curing resin cements submitted exclusively to autopolymerization.

OBJECTIVES: To evaluate, at different times, the diametral tensile strength (DTS) of dual-curing resin cements that were not photopolymerized. METHOD AND MATERIALS: Equal amounts of base and catalyst pastes of Panavia F (Kuraray), Variolink II (Vivadent), Rely X (3M ESPE), and Enforce (Dentsply) were mixed and inserted into cylindrical molds (4 x 2 mm) (n = 10). Cements were not photopolymerized. DTS test was performed in a testing machine at 30 minutes, 1 hour, 24 hours, and 7 days. The specimens were stored in light-proof containers with distilled water at 37 degrees C until the time of assay. An autopolymerizing resin cement (Cement-It, Jeneric Pentron) and a zinc phosphate cement served as controls. One-way analysis of variance (ANOVA) and Tukey test were performed separately for each cement and for each time (P <.05). RESULTS: All cements showed an increase in DTS when tested at 1 and 24 hours. Tests at 24 hours and 7 days revealed no statistically significant differences. In all groups, the zinc phosphate cement had the lowest DTS mean values (2.1 MPa, 3.6 MPa, 6.5 MPa, and 6.9 MPa), while Cement-It (35.1 MPa, 33.6 MPa, 46.9 MPa, and 46.3 MPa) and Enforce (31.9 MPa, 31.7 MPa, 43.4 MPa, and 47.6 MPa) presented the highest DTS mean values. CONCLUSION: All cements presented maximal strength at 24 hours. The dual-curing resin cements, even when nonphotopolymerized, demonstrated higher DTS than the zinc phosphate cement and similar or lower values than the autopolymerizing resin cement.

Blade design and forming for fans using finite elements

The necessity of adapting the standardized fan models to conditions of higher temperature has emerged due to the growth of concerning referring to the consequences of the gas expelling after the Mont Blanc tunnel accident in Italy and France, where even though, with 100 fans in operation, 41 people died. However, since then, the defied solutions have pointed to aerodynamic disadvantages or have seemed nonappropriate in these conditions. The objective of this work is to present an alternative to the market standard fans considering a new technology in constructing blades. This new technology introduces the use of the stainless steel AISI 409 due to its good adaptation to temperatures higher than 400°C, particularly exposed to temperatures of gas exhaust from tunnels in fire situation. Furthermore, it presents a very good resistance to corrosion and posterior welding and pressing, due to its alloyed elements. The innovation is centered in the process of a deep drawing of metallic shells and posterior welding, in order to keep the ideal aerodynamic superficies for the fan ideal performance. On the other hand, the finite element method, through the elasto-plastic software COSMOS permitted the verification of the thickness and structural stability of the blade in relation to the aerodynamic efforts established in the project. In addition, it is not advisable the fabrication of blades with variable localized thickness not even, non-uniform ones, due to the verified concentration of tensions and the difficulties observed in the forming. In this way, this study recommends the construction of blades with uniform variations of thickness. © 2007 Springer.

Influence of the power level of an ultra-sonic system on dental cavity preparation

The aim of this study was to evaluate the shape of dental cavities made with the CVDentus® system using different ultrasound power levels. One standard cavity was made on the buccal aspect of 15 bovine incisors with a CVDentus® cylindrical bur (82142). The sample was divided into three groups: G1 - ultrasound with power II; G2 - ultrasound with power III; and G3 - ultrasound with power IV. A standardizing device was used to obtain standardized preparations and ultrasound was applied during one minute in each dental preparation. The cavities were sectioned in the middle, allowing observation of the cavity's profile with a magnifying glass, and width and depth measurement using the Leica Qwin program. The Kruskal-Wallis (p < 0.05) and Dunn statistical analyses demonstrated differences between the dental cavity shapes when powers III and IV were used. However, the cavities that were made with power III presented dimensions similar to those of the bur used for preparation. We concluded that the power recommended by the manufacturer (III) is the most adequate for use with the CVDentus® system.

Tijolos prensados de solo-cimento confeccionados com resíduos de concreto

In this work results are presented of laboratory tests aiming to evaluate the possibility of using concrete wastes in manufactured soil-cement pressed bricks. Tests of characterization of used soil of the composite of this soil with concrete wastes and of the mixtures of soil cement made with this composite were evaluated. According to results of tests carried out with cylindrical specimens and with soil cement pressed bricks, it was verified that the addition of the concrete wastes improved soil cement mechanical properties, favoring the a reduction of the cement consumption, obtaining pressed bricks with a better quality.

Grinding of hardened steels using optimized cooling

Grinding - the final machining process of a workpiece - requires large amounts of cutting fluids for the lubrication, cooling and removal of chips. These fluids are highly aggressive to the environment. With the technological advances of recent years, the worldwide trend is to produce increasingly sophisticated components with very strict geometric and dimensional tolerances, good surface finish, at low costs, and particularly without damaging the environment. The latter requirement can be achieved by recycling cutting fluids, which is a costly solution, or by drastically reducing the amount of cutting fluids employed in the grinding process. This alternative was investigated here by varying the plunge velocity in the plunge cylindrical grinding of ABNT D6 steel, rationalizing the application of two cutting fluids and using a superabrasive CBN (cubic boron nitride) grinding wheel with vitrified binder to evaluate the output parameters of tangential cutting force, acoustic emission, roughness, roundness, tool wear, residual stress and surface integrity, using scanning electron microscopy (SEM) to examine the test specimens. The performance of the cutting fluid, grinding wheel and plunge velocity were analyzed to identify the best machining conditions which allowed for a reduction of the cutting fluid volume, reducing the machining time without impairing the geometric and dimensional parameters, and the surface finish and integrity of the machined components.

Chronostratigraphy and radiocarbon age inversion in the Holocene regressive barrier of Paraná, southern Brazil

Twenty-two 14C datings were performed at the central sector of the Paraná coast to define Holocene regressive barrier evolution. The barrier Pleistocene substratum was ascribed an age between 40 400 and 30 000 yr BP, but it can also represent the penultimate sea level highstand during marine isotope stage 5e. The Holocene barrier samples provided ages between 8542-8279 and 2987-2751 cal yr BP, and showed at least six age inversions that were related to age differences between in situ or low-distance transported shells or trunk fragments, and high-distance transported vegetal debris, wood fragments and organic matter samples. The regressive Holocene barrier age was 4402-4135 cal yr BP near the base, and 2987-2751 cal yr BP near the top. Most of the vegetal remains were transported by ebb tidal currents from the estuaries to the inner shelf below wave base level during the mid-Holocene highstand; they were transported onshore by storm waves and littoral currents during the sea level lowering after the sea level maximum, and were deposited mainly as middle shoreface swaley cross-stratification facies. © 2008.

Biotic interaction between spionid polychaetes and bouchardiid brachiopods: Paleoecological, taphonomic and evolutionary implications

Shells of Bouchardia rosea (Brachiopoda, Rhynchonelliformea) are abundant in Late Holocene death assemblages of the Ubatuba Bight, Brazil, SW Atlantic. This genus is also known from multiple localities in the Cenozoic fossil record of South America. A total of 1211 valves of B. rosea, 2086 shells of sympatric bivalve mollusks (14 nearshore localities ranging in depth from 0 to 30 m), 80 shells of Bouchardia zitteli, San Julián Formation, Paleogene, Argentina, and 135 shells of Bouchardia transplatina, Camacho Formation, Neogene, Uruguay were examined for bioerosion traces. All examined bouchardiid shells represent shallow-water, subtropical marine settings. Out of 1211 brachiopod shells of B. rosea, 1201 represent dead individuals. A total of 149 dead specimens displayed polychaete traces (Caulostrepsis). Live polychaetes were found inside Caulostrepsis borings in 10 life-collected brachiopods, indicating a syn-vivo interaction (Caulostrepsis traces in dead shells of B. rosea were always empty). The long and coiled peristomial palps, large chaetae on both sides of the 5th segment, and flanged pygidium found in the polychaetes are characteristic of the polychaete genus Polydora (Spionidae). The fact that 100% of the Caulostrepsis found in living brachiopods were still inhabited by the trace-making spionids, whereas none was found in dead hosts, implies active biotic interaction between the two living organisms rather than colonization of dead brachiopod shells. The absence of blisters, the lack of valve/site stereotypy, and the fact that tubes open only externally are all suggestive of a commensal relationship. These data document a new host group (bouchardiid rhynchonelliform brachiopods) with which spionids can interact (interestingly, spionid-infested sympatric bivalves have not been found in the study area despite extensive sampling). The syn-vivo interaction indicates that substantial bioerosion may occur when the host is alive. Thus, the presence of such bioerosion traces on fossil shells need not imply a prolonged post-mortem exposure of shells on the sea floor. Also, none of the Paleogene and Neogene Bouchardia species included any ichnological evidence for spionid infestation. This indicates that the Spionidae/ Bouchardia association may be geologically young, although the lack of older records may also reflect limited sampling and/or taphonomic biases.

Influência dos agentes clareadores na microdureza de resina composta nanoparticulada

Objective: To assess the effect of bleaching agents on the microhardness of nanoparticle resin composite. Methods: Twenty-eight cylindrical test specimens (8× 1mm) of Filtek™ Supreme XT resin (3M/ESPE) were prepared and divided into 5 groups. The initial Vickers microhardness was measured (load of 50 grams force for 30 seconds) on the top surface of the test specimens. The groups were treated and divided as follows: G1 - artificial saliva (21 days - control); G2 - 7% hydrogen peroxide gel applied for 4h/day, for 14 days; G3 - 10% carbamide peroxide for 4h/day, for 14 days: G4 - 35% hydrogen peroxide gel applied in three sessions of 30 minutes each, with an interval of one week (21 days) between the sessions; G5 - 35% carbamide peroxide, three sessions of 30 minutes each, with an interval of one week (21 days) between the sessions. The top surfaces of the test specimens received treatment and were submitted to the Vickers microhardness test. Results: The results obtained were submitted to the Analysis of Variance at a fixed criterion, at a level of significance of p=0.05. No significant differences were observed among the treatments tested (p=0.42) when compared with G1. Significant differences (Tukey test) were found when the initial microhardness values were compared with the values after experimental treatments (p<0.01). Conclusion: The application of bleaching agents did not alter the microhardness of resin composites. Therefore, there is no need to change restorations after bleaching.

Effects of thermocycling on mechanical properties of soft lining materials.

Soft linings are materials used to reduce the tension and forces of mastication, forming all or part of the fitting surface of a denture. This study evaluated the effect of thermocycling on water absorption, solubility, Shore A hardness and color stability of permanent soft liner materials. MATERIAL AND METHODS: Two chemically activated soft liner materials (Sofreliner S; GC Reline Ultrasoft) were tested. Twenty cylindrical specimens (30.0 x 1.0 mm) were prepared for measuring water absorption and solubility and another twenty (30.0 x 3 mm) for analyzing Shore A hardness and color stability. Color was measured by a spectrophotometer before and after 2000 thermocycles. A one-way ANOVA test and Tukey test at a 5% confidence level (p<0.05) were performed. RESULTS: The results did not show statistical differences for water absorption, solubility or color stability. The post-thermocycling Shore A hardness values were significantly higher than those before the treatment. CONCLUSION: Thermocycling of soft liner materials increased Shore A hardness.

In vitro surface roughness of different glass ionomer cements indicated for ART restorations

Aim: The aim of this in vitro study was to evaluate the surface roughness of three glass ionomer cements (GICs) indicated for ART restorations. Methods: Ten cylindrical specimens of three commercial glass ionomers cements (Vidrion R - S.S. White, Maxxion R - FGM and Vitromolar DFL) were prepared (n=30) without surface finishing or protection. Twenty-four hours after preparation, the surface roughness measurements were obtained as the mean of three readings of the surface of each specimen by profilometry. The roughness values (Ra, μm) were subjected to one-way ANOVA and Tukey's test (p<0.05). Results: No statistically significant differences were observed between Vidrion R (0.18 ± 0.05) and Vitromolar (0.21 ± 0.05), whereas Maxxion R presented significantly higher roughness values than those of the other materials. Conclusions: It may be concluded that characteristics of particle size and composition of the different GICs affected their surface roughness 24 h after preparation.