Flexural strength and hardness of reline and denture base acrylic resins after different exposure times of microwave disinfection

Objectives: To evaluate the effect of microwave disinfection on the flexural strength and Vickers hardness of 4 autopolymerized resins (Kooliner [K], Tokuso Rebase Fast [T], Ufi Gel Hard [U], and New Truliner [N]) and 1 denture base resin (Lucitone 550 [L]). Method and Materials: For each material, 48 specimens (64 x 10 x 3.3 mm) were made and divided into 6 equal groups (n = 8). In the control group, specimens were untreated. Before testing, specimens were immersed in 200 mL of distilled water and submitted to disinfection for 1 of the following irradiation times: 1, 2, 3, 4, or 5 minutes. The irradiation procedure was performed twice. The flexural strength was determined using a testing machine MTS-810 and measurements of Vickers hardness were made on Micromet 2100. The values were submitted to ANOVA and Tukey's test (P = .05). Results: The K material showed a significant increase (P = .0010) in flexural strength following 5 minutes of disinfection compared to control specimens. The flexural strength mean values of materials T, U, and N were not significantly affected (P > .05) by disinfection. Compared to the control group, the K material showed a significant increase in hardness (P < .001) following disinfection for 3, 4, and 5 minutes. For material U, disinfection for 4 and 5 minutes produced specimens with significantly increased hardness values (P < .001) compared to the control group. For material N, disinfection for 5 minutes resulted in significantly higher hardness values (P < .001) than the control group. Conclusion: Regardless of the irradiation time, the flexural strength and hardness of the materials evaluated were not detrimentally affected by microwave disinfection. (Quintessence Int 2008;39:833-840)

Measurement of Interfacial Porosity at the Acrylic Resin/Denture Tooth Interface

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of water storage on the shear strength and fatigue limit of the reline resin bond to denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Weight loss and changes in surface roughness of denture base and reline materials after simulated toothbrushing in vitro

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of long-term water immersion on the fracture toughness of denture base and reline resins

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of Candida albicans adhesion and biofilm formation on a denture base acrylic resin containing silver nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

CORRELATING THE CURVE DISTANCE BETWEEN THE DISTAL of THE CANINES TO THE COMBINED WIDTH of THE SIX ANTERIOR TEETH WHEN SELECTING DENTURE TEETH FOR DIFFERENT ETHNIC GROUPS

Statement of problem. To select the width of denture teeth, the distance between the marks indicating the location of the canines is usually measured around the curvature of the wax occlusal rim; however, most manufacturers' mold charts provide the measurements of the artificial 6 anterior teeth as if they were on a straight line.Purpose. The purpose of this study was to investigate whether the curve distance between the distal surfaces of the maxillary canines can be related to the combined width (straight measurement) of the 6 anterior teeth in 4 ethnic groups.Material and methods. Maxillary stone casts were obtained for 160 dentate subjects of 4 ethnic groups (40 whites, 40 blacks, 40 multiracial - descendants of white and black parents, and 40 Asians). The width of each maxillary anterior tooth was measured on the casts with sliding calipers. The combined width of the 6 anterior teeth (CW) corresponded to the sum of the width of each anterior tooth. The curve distance between the distal surfaces of the canines (CD) was measured by using dental tape and sliding calipers. The Pearson correlation coefficient and regression analysis were used to evaluate the relationship between CD and CW in each ethnic group (alpha=.05).Results. The mean CD and CW values (in mm) obtained were: whites (CD=52.12; CW=45.65); blacks (CD=56.10; CW=48.13); multiracial (CD=53.58; CW=46.54); and Asians (CD=53.29; CW=46.60). Significant (P<.001) correlations between CD and CW measurements were observed for all ethnic groups studied (whites, r=0.957; blacks, r=0.803; multiracial, r=0.917; and Asians, r=0.881). The following linear regression equations were obtained: whites [CD=1.1(CW)+0.3]; blacks [CD=0.95(CW)+9.3]; multiracial [CD=1.2(CW)-1.1]; and Asians [CD=1.0(CW)+5].Conclusions. The curve distance between the distal surfaces of the maxillary canines can be accurately related to the combined width of the 6 anterior teeth in the selection of denture teeth for the studied ethnic groups. (J Prosthet Dent 2012;107:400-404)

The center of the incisive papilla for the selection of complete denture maxillary anterior teeth in 4 racial groups

Objectives: To evaluate the use of the center of the incisive papilla as a guide for the selection of the proper width of maxillary dentures in 4 racial groups. Method and Materials: One hundred sixty stone casts were obtained from impressions of the maxillary arch of white, black, mixed, and Asian subjects. The occlusal surfaces of the casts were photocopied and the images placed on a digitizer. The most anterior and posterior points of the papilla and cusp tips of the canines were digitized. Dentofacial Planner Plus software was used to calculate the distance from a line passing through the cusp tips of the canines to the center of the papilla, defined as the midpoint of the anterior and posterior points of the papilla. The selection error (in millimeters) due to the clinical application of the method of the incisive papilla was calculated and analyzed. Results: In all studied racial groups, there was no coincidence between the center of the incisive papilla and the canine line. The utilization of the center of the papilla would lead to the selection of wider artificial teeth. In 24.9% of the white, 19.3% of the mixed, 32.9% of the black, and 15.5% of the Asian populations, errors greater than 4 mm would be present with the utilization of the papilla. Conclusion: The method of the center of the incisive papilla is not accurate, but may aid in initial artificial teeth selection for the racial groups studied. (Quintessence Int 2008;39:841-845)

Surface roughness of denture base and reline materials after disinfection by immersion in chlorhexidine or microwave irradiation

Background: This study evaluated the effect of disinfection by immersion and microwave irradiation on the roughness of one denture base resin (Lucitone-L) and five relining materials, three hard (Tokuyama Rebase II-TR, New Truliner-NT, Ufigel Hard-UH) and two resilient (Trusoft-T, Sofreliner-S).Methods: Fifty specimens were made and divided into groups: CL2 specimens were brushed with 4% chlorhexidine (1 min), immersed in the same solution (10 min) and immersed in water (3 min); MW2 specimens were immersed in water and microwave irradiated (650W; 6 min); CL2 and MW2 specimens were disinfected twice; CL7 and MW7 specimens were submitted to seven cycles using chlorhexidine or microwave irradiation, respectively; W specimens were not disinfected and remained in water (37 degrees C; 7 days).Results: Results were statistically analysed (p = 0.05) and revealed that, at baseline, the highest mean value was observed for T (p < 0.001). Material NT showed increase in roughness after the first (p = 0.003), second (p = 0.001), seventh (p = 0.000) cycles of microwave disinfection and after 7 days of immersion in water (p = 0.033).Conclusions: Resilient liner S presented significant increase in roughness after the second cycle of disinfection with chlorhexidine (p = 0.003). Material T exhibited significantly decreased roughness in group W (p = 0.010), while microwaving produced severe alterations on its surface.

Effect of reline material and denture base surface treatment on the impact strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of incorporation of 2-tert-butylaminoethyl methacrylate on flexural strength of a denture base acrylic resin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Reliability of a method for evaluating porosity in denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of surface treatments on the flexural strength of denture base repair

Objective: The purpose of this study was to evaluate the flexural strength of repairs made with autopolymerising acrylic resin after different treatments of joint surfaces.Material and Methods: Fifty rectangular specimens were made with heat-polymerised acrylic resin and 40 were repaired with autopolymerising acrylic resin following joint surface treatments: group 1 (intact specimens), group 2 (chemical treatment: wetting with methyl-methacrylate for 180 s), group 3 (abraded with silicon carbide paper), group 4 (abraded and wetting with methyl-methacrylate for 180 s) and group 5 (without surface treatment). The flexural strength was measured by a three-point bending test using a universal testing machine with a 100 Kgf load cell in the centre of repair at 5 mm/min cross-head speed. All data were analysed using one-way ANOVA and Tukey HSD test for multiple comparisons (p < 0.05).Results: Among repaired specimens, groups 2 and 4 had 66.53 +/- 3.4 and 69.38 +/- 1.8 MPa mean values and were similar. These groups had superior flexural strength than groups 3 and 5 that were similar and had 54.11 +/- 3.4 and 51.24 +/- 2.8 MPa mean values, respectively. Group 1 had a mean value of 108.30 +/- 2.8 MPa being the highest result.Conclusion: It can be concluded that the treatment of the joint surfaces with methyl-methacrylate increases the flexural strength of denture base repairs, although the strength is still lower than that observed for the intact denture base resin. Abrasion with sandpaper was not able to influence the flexural strength of repaired denture bases.

Effect of microwave disinfection on the surface roughness of three denture base resins after tooth brushing

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of disinfection by microwave irradiation on the strength of intact and relined denture bases and the water sorption and solubility of denture base and reline materials

This study evaluated the influence of microwave disinfection on the strength of intact and relined denture bases. Water sorption and solubility were also evaluated. A heat-polymerized acrylic resin (Lucitone 550) was used to construct 4-mm-thick (n = 40) and 2-mm-thick (n = 160) denture bases. Denture bases (2mm) were relined with an autopolymerizing resin (Tokuso Rebase Fast, Ufi Gel Hard, Kooliner, or New Truliner). Specimens were divided into four groups (n = 10): without treatment, one or seven cycles of microwave disinfection (650 W for 6 min), and water storage at 37 degrees C for 7 days. Specimens were vertically loaded (5 mm/min) until failure. Disc-shaped specimens (50 min x 0.5 mm) were fabricated (n = 10) to evaluate water sorption and solubility. Data on maximum fracture load (N), deflection (%), and solubility (%) were analyzed by two-way analysis of variance and Student-Newman-Keuls tests (alpha = 0.05). One cycle of microwave disinfection decreased the deflection at fracture and fracture energy of Tokuso Rebase Fast and New Truliner specimens. The strength of denture bases microwaved daily for 7 days was similar to the strength of those immersed in water for 7 days. Microwave disinfection increased the water sorption of all materials and affected the solubility of the reline materials. (C) 2007 Wiley Periodicals, Inc.