Tensile bond strength of self-etching versus total-etching adhesive systems under different dentinal substrate conditions

The use of acid etchants to produce surface demineralization and collagen network exposure, allowing adhesive monomers interdiffusion and consequently the formation of a hybrid layer, has been considered the most efficient mechanism of dentin bonding. The aim of this study was to compare the tensile bond strength to dentin of three adhesive systems, two self-etching ones (Clearfil SE Bond - CSEB and One Up Bond F - OUBF) and one total-etching one (Single Bond - SB), under three dentinal substrate conditions (wet, dry and re-wet). Ninety human, freshly extracted third molars were sectioned at the occlusal surface to remove enamel and to form a flat dentin wall. The specimens were restored with composite resin (Filtek Z250) and submitted to tensile bond strength testing (TBS) in an MTS 810. The data were submitted to two-way ANOVA and Tukey's test (p = 0.05). Wet dentin presented the highest TBS values for SB and CSEB. Dry dentin and re-wet produced significantly lower TBS values when using SB. OUBF was not affected by the different conditions of the dentin substrate, producing similar TBS values regardless of the surface pretreatments.

Bond strength of acrylic teeth to denture base resin after various surface conditioning methods before and after thermocycling

This study aimed to evaluate the durability of adhesion between acrylic teeth and denture base acrylic resin. The base surfaces of 24 acrylic teeth were flatted and submitted to 4 surface treatment methods: SM1 (control): No SM; SM2: application of a methyl methacrylate-based bonding agent (Vitacol); SM3: air abrasion with 30-μm silicone oxide plus silane; SM4: SM3 plus SM2. A heat-polymerized acrylic resin was applied to the teeth. Thereafter, bar specimens were produced for the microtensile test at dry and thermocyled conditions (60 days water storage followed by 12,000 cycles). The results showed that bond strength was significantly affected by the SM (P < .0001) (SM4 = SM2 > SM3 > SM1) and storage regimens (P < .0001) (dry > thermocycled). The methyl methacrylate-based adhesive showed the highest bond strength.

Resin microtensile bond strength to feldspathic ceramic: Hydrofluoric acid etching vs tribochemical silica coating

This study aimed to compare the microtensile bond strength of resin cement to alumina-reinforced feldspathic ceramic submitted to acid etching or chairside tribochemical silica coating. Ten blocks of Vitadur-α were randomly divided into 2 groups according to conditioning method: (1) etching with 9.6% hydrofluoric acid or (2) chairside tribochemical silica coating. Each ceramic block was luted to the corresponding resin composite block with the resin cement (Panavia F). Next, bar specimens were produced for microtensile testing. No significant difference was observed between the 2 experimental groups (Student t test, P> .05). Both surface treatments showed similar microtensile bond strength values.

Microtensile bond strength of a repair composite to leucite-reinforced feldspathic ceramic

The purpose of this study was to evaluate the microtensile bond strength of a repair composite resin to a leucite-reinforced feldspathic ceramic (Omega 900, VITA) submitted to two surface conditionings methods: 1) etching with hydrofluoric acid + silane application or 2) tribochemical silica coating. The null hypothesis is that both surface treatments can generate similar bond strengths. Ten ceramic blocks (6x6x6 mm) were fabricated and randomly assigned to 2 groups (n=5), according to the conditioning method: G1- 10% hydrofluoric acid application for 2 min plus rinsing and drying, followed by silane application for 30 s; G2- airborne particle abrasion with 30 μm silica oxide particles (CoJet-Sand) for 20 s using a chairside air-abrasion device (CoJet System), followed by silane application for 5 min. Single Bond adhesive system was applied to the surfaces and light cured (40 s). Z-250 composite resin was placed incrementally on the treated ceramic surface to build a 6x6x6 mm block. Bar specimens with an adhesive area of approximately 1 ± 0.1 mm2 were obtained from the composite-ceramic blocks (6 per block and 30 per group) for microtensile testing. No statistically significant difference was observed between G1 (10.19 ± 3.1 MPa) and G2 (10.17 ± 3.1 MPa) (p=0.982) (Student's t test; á = 0.05). The null hypothesis was, therefore, accepted. In conclusion, both surface conditioning methods provided similar microtensile bond strengths between the repair composite resin and the ceramic. Further studies using long-term aging procedures should be conducted.

Effect of ultrasonic instrumentation on the bond strength of crowns cemented with zinc phosphate cement to natural teeth. An in vitro study

Several studies have reported the benefits of sonic and/or ultrasonic instrumentation for root debridement, with most of them focusing on changes in periodontal clinical parameters. The present study investigated possible alterations in the tensile bond strength of crowns cemented with zinc phosphate cement to natural teeth after ultrasonic instrumentation. Forty recently extracted intact human third molars were selected, cleaned and stored in physiologic serum at 4°C. They received standard preparations, at a 16° convergence angle, and AgPd alloy crowns. The crowns were cemented with zinc phosphate cement and then divided into four groups of 10 teeth each. Each group was then subdivided into two subgroups, with one of the subgroups being submitted to 5,000 thermal cycles ranging from 55 ± 2 to 5 ± 2°C, while the other was not. Each group was submitted to ultrasonic instrumentation for different periods of time: group 1 - 0 min (control), group 2 - 5 min, group 3 - 10 min, and group 4 - 15 min. Tensile bond strength tests were performed with an Instron testing machine (model 4310). Statistical analysis was performed using ANOVA and Tukey's test at the 5% level of significance. A significant reduction in the tensile bond strength of crowns cemented with zinc phosphate and submitted to thermal cycles was observed at 15 min (196.75 N versus 0 min = 452.01 N, 5 min = 444.23 N and 10 min = 470.85 N). Thermal cycling and ultrasonic instrumentation for 15 min caused a significant reduction in tensile bond strength (p < .05).

Effect of light-curing units on push-out fiber post bond strength in root canal dentin

The purpose of this study was to evaluate the effectiveness of different light-curing units on the bond strength (push-out) of glass fiber posts in the different thirds of the root (cervical, middle and apical) with different adhesive luting resin systems (dual-cure total-etch; dual-cured and self-etch bonding system; and dual-cure self-adhesive cements), Disks of the samples (n = 144) were used, with approximately 1 mm of thickness of 48 bovine roots restored with glass fiber posts, that were luted with resin cements photo-activated by halogen LCU (QTH, Optilux 501) and blue LED (Ultraled), with power densities of 600 and 550 mW/cm 2, respectively. A universal testing machine (MTS 810 Material Test System) was used with a 1 mm diameter steel rod at cross-head speed of 0.5 mm/min until post extrusion, with load cell of 50 kg, for evaluation of the push-out strength in the different thirds of each sample. The push-out strength values in kgf were converted to MPa and analyzed through Analysis of Variance and Tukey's test, at significance level of 5%. The results showed that there were no statistical differences between the QTH and LED LCUs. The self-adhesive resin cement had lower values of retention. The total-etch and self-adhesive system resin cements seem to be a possible alternative for glass fiber posts cementation into the radicular canal and the LED LCU can be applied as an alternative to halogen light on photo-activation of dual-cured resin cements. © 2009 Pleiades Publishing, Ltd.

Correlation of the hybrid layer thickness and resin tags length with the bond strength of a self-etching adhesive system.

The objective of this study was to measure the thickness of the hybrid layer (HLT), length of resin tags (RTL) and bond strength (BS) in the same teeth, using a self-etching adhesive system Adper Prompt L Pop to intact dentin and to analyze the correlation between HLTand RTL and their BS. Ten human molars were used for the restorative procedures and each restored tooth was sectioned in mesio-distal direction. One section was submitted to light microscopy analysis of HLT and RTL (400x). Another section was prepared and submitted to the microtensile bond test (0.5 mm/min). The fractured surfaces were analyzed using scanning electron microscopy to determine the failure pattern. Correlation between HLT and RTL with the BS data was analyzed by linear regression. The mean values of HLT, RTL and BS were 3.36 microm, 12.97 microm and 14.10 MPa, respectively. No significant relationship between BS and HLT (R2= 0.011, p>0.05) and between BS and RTL (R2= 0.038) was observed. The results suggested that there was no significant correlation between the HLT and RTL with the BS of the self-etching adhesive to dentin.

Cementation of fiber post: influence of the cement insertion techniques on the bond strength of the fiber post-root dentin and the quality of the cement layer.

The aim of this study was to assess the influence of resin cement insertion methods on the bond strength of a fiber post to root dentin and quality of the cement layer. Forty bovine single-roots (length =16 mm) were randomly allocated into four groups, according to the cement insertion methods (N.=10): Gr1- Lentulo drill #40, Gr2- Centrix syringe, Gr3- Explorer #5, Gr4- fiber post. The root canals were prepared at 12 mm, using preparation bur # 3 of a cylinder quartz-FRC post (Aesthet post-plus, Bisco). The fiber posts were cemented using a multi-step etch-and-rinse adhesive system (All Bond 2®, Bisco) and a dual-cured resin cement (Duolink, Bisco). Each root was cut into seven samples: four samples of 1.8 mm thickness for push-out testing, and three with 0.5 mm for cement layer quality analyzing. One-way ANOVA was used for the push-out test values and the One-Way Kruskal-Wallis (P<0.05) and Dunn (10%) tests for the cement layer analyzes. ANOVA showed that the cement layer quality was affected by the cement insertion methods (P=0.0044): Gr1 (3.8 ± 1.3a), Gr2 (3.2 ± 1.3a), Gr3 (5.2 ± 1.5a,b) and Gr4 (5.2 ± 1.5b) (Dunn test), whereas the bond strength (MPa) was not affected by cement insertion methods: G1 (4.2 ± 1.3), G2 (3.2 ± 1.8), G3 (4.5 ± 0.9), G4 (3.1 ± 1.3). The fiber posts should be cemented with the assistance of the lentulo drill or centrix syringe to promote the best cement layer results.

Adhesion between fiber post and root dentin: evaluation of post surface conditioning for bond strength improvement.

The aim of this paper was to evaluate two surface conditioning methods associated with the application of adhesive on the post surface for improving the bond to resin cement. Sixty single-rooted bovine teeth were sectioned at 16 mm in length, prepared (9 mm depth), embedded in a PVC cylinder using acrylic resin, and allocated into 3 groups (N.=20) according to post surface treatment: cleaning with ethanol (control group); etching with hydrogen peroxide; etching with hydrofluoric acid. Ten posts for each group were silanized and other 10 posts were silanized and received an adhesive agent. The posts were cemented with self-adhesive resin cement (RelyX U100 resin cement). All teeth were sectioned perpendicularly to the long axis (2 mm thickness per slice), submitted to push out bond strength testing and the type of failure was recorded. The obtained data were submitted to two-way ANOVA and Turkey's test, with the level of significance set at 5%. Neither the hydrofluoric acid or hydrogen peroxide post surface treatment, nor the adhesive application, had an influence on bond strength values. The main type of failure was adhesive between cement and dentin. Etching and the application of an adhesive on the post surface did not presented a significant influence on the bond strength results for the fiber post resin cement-root dentin assembly. The cement appears to adhere very well to the fiber post surface rather than the dentin surface.

Analysis of hybrid layer thickness, resin tag length and their correlation with microtensile bond strength using a total etch adhesive to intact dentin.

The objective of this study was to evaluate the use of a two-step total etch and rinse adhesive, the correlation between the hyybrid layer thickness (HL) and bond strength (BS), and between resin tag length (RT) and bond strength in the same teeth, and also to evaluate the fracture patterns of the tested specimens. Ten human molars were used for the restorative procedure and then sectioned in two halves (mesio-distally). The materials used were Adper Single Bond 2, 3M ESPE, Ultra etch gel, Ultradent and Filtek Z250, 3M ESPE. One half were utilized to measure the HL thickness and RT length through light microscopy analysis (400x), and the other half was subject to a microtensile test to measure the BS. The fractured surfaces were analyzed by scanning electron microscopy and fracture patterns classified. The Pearson correlation test was applied (p = 0.05). The results of the analyses of each specimen then were correlated: mean HL thickness = 4.39 (0.48) microm, mean length of RT = 9.94 (1.69) microm, mean BS = 23.98 (10.24) MPa. A statistically significant correlation between HL thickness and bond strength was found (r = 0.93). The two step etch and rinse adhesive system, showed a strong correlation between HL thickness and bond strength. The most common fractures were adhesive, followed by cohesive in resin.

Correlation between hybrid layer thickness, resin tag length and microtensile bond strength of a self-etching adhesive system

The purpose of this study was to evaluate the correlation between the hybrid layer thickness, resin tag length and resin bond strength of a self-etching adhesive system to sound dentin tissue in vivo. After performing restorative procedures and tooth extractions, ten specimens were sectioned in a mesiodistal direction. One dental section was used for light microscope analysis, in which both the resin tag length and hybrid layer thickness were measured, while the other section was analyzed using a microtensile test (0.5 mm/min). The fractured surface of the latter section was characterized using a stereoscopic magnifying glass (40x magnifcation). The results were subject to statistical analysis using the Pearson Correlation Test (a = 0.05). The hybrid layer thickness, resin tag length and resin bond strength mean values were 2.19 microm (0.34), 4.34 microm (0.28) and 9.73 MPa (5,55), respectively. In addition, correlation tests between the resin tag length and the resin bond strength (r=0.014) and also between the hybrid layer thickness and bond strength (r=0.43), showed no statistically significant correlation. The microtensile bond strength of Adper Prompt L Pop self-etching adhesive system does not depend on hybrid layer thickness or resin tag length.

Bond strength of adhesive systems with different solvents to dry and wet dentin

Aim: This study evaluates bond strength between dentin and composite using adhesives with different solvents to dry and wet dentin. Materials and methods: Ninety bovine incisors were used; the vestibular surfaces were worn by the exposure of an area with a diameter of 4 mm of dentin. The specimens were divided into 6 groups, according to the type of adhesive used and hydratation stals: Group SB-wet: Single Bond 2 in wet dentin, Group SBdry: Single Bond 2 in dry dentin, Group SL-wet: Solobond M in wet dentin, Group SL-dry: Solobond M in dentin dry. Group XPwet: XP Bond in wet dentin, Group XP-dry: XP Bond in dentin dry. They were cut to obtain specimens in the shape of stick with 1 × 1 mm and subjected to microtensile test in universal testing machine with a cross speed of 1mm/min. The data were analyzed with ANOVA and Tukey's tests (5%). Results: ANOVA showed significant differences for surface treatment and interaction, but no difference was found for adhesive factor. The Tukey's test showed that the samples with wet dentin shown higher values of bond strength. Conclusion: The adhesive did not influence in the bond strength. The groups with wet dentin showed higher values of bond strength than groups with dry dentin.

Effects of surface treatment, hydration and application method on the bond strength of a silorane adhesive and resin system to dentine

Objectives: To evaluate the effects of surface treatment, surface hydration (SH) and application method (AM) on the tensile bond strength of the Silorane Adhesive System (SAS) to dentine. Methods: Ninety bovine teeth were used. For the control group (n = 10), each dentine surface was treated according to the manufacturer's instructions of the SAS. The remaining teeth were randomly distributed into two groups (n = 40), according to the type of dentine surface treatment (ST) - 37% phosphoric acid or Er:YAG Laser prior to the application of the SAS. Each group was further divided into 2 subgroups (n = 20), according to the SH status: dry (D) or wet (W). Each subgroup was further divided into 2 subgroups (n = 10), according to the application method [AM: Active (AC) mode or Passive (PA) mode]. A coat of resin composite (Filtek P90) was applied on the surface. Artificial ageing was performed with a thermo-mechanical cycling machine. The specimens were sectioned into 1 mm × 1 mm × 10 mm sticks and stressed to failure using a universal testing machine. The remaining teeth in each group were used for Scanning Electron Microscopy to examine the fractured area. Data were subjected to a three-way ANOVA, Tukey's test and Dunnet's test (α = 0.05). Results: The ANOVA showed significant differences for SH and AM, but not for ST. For SH, the results of Tukey's test were (in MPa): D-14.9(±3.8)a, W-17.1(±4.3)b; and for AM: PA-14. 9(±4.2)a, AC-17.1(±3.9) b. Conclusions: Acid etching, when combined with a moist dentine surface and the use of primer agitation, improves the bond strength of the SAS to dentine. Clinical Significance: According to the results of the present in vitro study, modification of the application protocols for the silorane-based adhesive system may improve its clinical performance. © 2012 Published by Elsevier Ltd.

Microtensile bond strength of resin cements to caries-affected dentin

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Repair bond strength of microhybrid, nanohybrid and nanofilled resin composites: Effect of substrate resin type, surface conditioning and ageing

Objectives: This study evaluated the microtensile bond strength (MTBS) of non-aged and aged resin-based composites (RBC) (nanohybrid and nanofilled) after two surface conditioning methods, repaired using the composite of the same kind or a microhybrid composite. Materials and methods: Nanohybrid (Tetric EvoCeram-TE) and nanofilled (Filtek Supreme-FS) RBC blocks (5 × 5 × 6 mm) (N = 128) were fabricated and randomly divided into two groups: (a) no ageing (control group) and (b) ageing (5.000 thermocycling, 5-55 °C). RBC surfaces were polished by up to 1,200-grit silicone carbide papers and conditioned with either (a) air abrasion with 30-μm SiO2 particles (CoJet Sand) for 4 s + silane coupling agent (ESPE-Sil) + adhesive resin (VisioBond) (n = 16) or (b) adhesive application only (Multilink A+B for TE; Adper ScotchBond 1XT for FS) (n = 16). In half of the groups, repair resin of the same kind with the RBC and, in the other half, a different kind of composite (microhybrid, Quadrant Anterior Shine-AS) with its corresponding adhesive (Quadrant UniBond) was used. The specimens were submitted to MTBS test (0.5 mm/min). Data were analysed using three-way ANOVA and Tukey's tests. Degree of conversion (DC) of non-aged and aged resin composites (TE, FS) (n = 3 per group) was measured by micro-Raman analyses. Results: RBC type (p = 0.001) and ageing affected the MTBS results significantly (p = 0.001). Surface conditioning type did not show significant difference (p = 0.726), but less number of pre-test failures was experienced with the CoJet system compared to adhesive resin application only. Repair strength on aged TE showed significantly less (p < 0.05) MTBS than for FS. FS repaired with the same kind of RBC and adhesive resin presented the highest cohesive failures (43 %). DC was higher for TE (71 %) than for FS (58 %) before ageing. Conclusion: On the aged RBCs, less favourable repair strength could be expected especially for nanohybrid composite. For repair actions, RBC surface conditioning could be accomplished with either adhesive resin application only or with CoJet system, providing that the latter resulted in less pre-test failures. Clinical relevance: Clinicians could condition the resin surface prior to repair or relayering with either CoJet system or adhesive resin application only, depending on the availability of the system. © 2012 Springer-Verlag Berlin Heidelberg.