The effect of self-adhesive and self-etching resin cements on the bond strength of nonmetallic posts in different root thirds

The purpose of this study was to evaluate the effect of self-adhesive and self-etching resin cements on the bond strength of nonmetallic posts in different root regions. Sixty single-rooted human teeth were decoronated, endodontically treated, post-space prepared, and divided into six groups. Glass-fiber (GF) posts (Exacto, Angelus) and fiber-reinforced composite (FRC) posts (EverStick, StickTeck) were cemented with self-adhesive resin cement (Breeze) (SA) (Pentral Clinical) and self-etching resin cement (Panavia-F) (SE) (Kuraray). Six 1-mm-thick rods were obtained from the cervical (C), middle (M), and apical (A) regions of the roots. The specimens were then subjected to microtensile testing in a special machine (BISCO; Schaumburg, IL, USA) at a crosshead speed of 0.5 mm/min. Microtensile bond strength data were analyzed with two-way ANOVA and Tukey's tests. Means (and SD) of the MPa were: GF/SA/C: 14.32 (2.84), GF/SA/M: 10.69 (2.72), GF/SA/A: 6.77 (2.17), GF/SE/C: 11.56 (4.13), GF/SE/M: 6.49 (2.54), GF/SE/A: 3.60 (1.29), FRC/SA/C: 16.89 (2.66), FRC/SA/M: 13.18 (2.19), FRC/SA/A: 8.45 (1.77), FRC/SE/C: 13.69 (3.26), FRC/SE/M: 9.58 (2.23), FRC/SE/A: 5.62 (2.12). The difference among the regions was statistically significant for all groups (p < 0.05). The self-adhesive resin cement showed better results than the self-etching resin cement when compared to each post (p < 0.05). No statistically significant differences in bond strengths of the resin cements when comparable to each post (p > 0.05). The bond strength values were significantly affected by the resin cement and the highest values were found for self-adhesive resin cement.

Bond strength of artificial teeth attached to a microwave-polymerized denture base resin after immersion in disinfectant solutions

To evaluate the bond strength between two types of acrylic resin teeth and a microwave denture base resin after immersion in disinfectant solutions for 180 days. Eighty specimens made of acrylic resin teeth (Biotone and Biotone IPN) attached to a microwave polymerized denture base resin (Nature-Cryl MC) were divided into eight groups (n = 10) according to the treatment (distilled water-control, 2% chlorhexidine digluconate, 1% sodium hypochlorite and sodium perborate solution-Corega Tabs). The shear strength tests (MPa) were carried out using a universal testing machine with a 0.5 mm/min speed. Data analysis was performed using ANOVA and multiple comparison Student-Newman-Keuls post hoc test (α = 0.05). Biotone IPN showed similar results among the groups (distilled water, 8.25 ± 1.81 MPa; chlorhexidine, 7.81 ± 3.34 MPa; hypochlorite, 7.75 ± 3.72 MPa; and Corega Tabs, 7.58 ± 2.27 MPa, whereas Biotone showed significantly lower shear bond strength values for the groups immersed in Corega Tabs (5.25 ± 3.27 MPa) and chlorhexidine (6.08 ± 2.35 MPa). Soaking the dentures in 1% sodium hypochlorite could be recommended as a disinfectant solution for dentures fabricated with conventional acrylic resin denture teeth and microwave denture base resin. For dentures fabricated with IPN teeth and microwave denture base resin, all the soaking solutions evaluated in this study could be suggested to denture wearers.

Avaliação da resistência adesiva de diferentes sistemas resinosos de colagem ortodôntica

Recent orthodontic bonding materials have aimed to reduce the working time of the clinician, by simplifying the acid etching procedure by applying self-etching primer adhesive systems. However, the adhesion quality of these materials still demands investigation. Thus, the present study aimed to evaluate the bond strengths of three different adhesive systems. A hundred and eighty bovine lower incisors were cut and embebbed in acrylic resin matrices, in which orthodontic brackets were bonded with Transbond XT (2n = 60), Transbond XT Self Etching Primer (2n = 60) e Tyrian (2n = 60). For each composite, bond strength tests were executed immediately (n = 30) and 24 hours (n = 30) after the bonding, in the assay machine Versat 2000 (Pantec), by applying 500 Kgf of load at 1mm/min of velocity. Transbond XT, Transbond XT Self Etching Primer and Tyrian presented, respectively, average values of bond strength of 7.43, 7.09 and 3.41 MPa at the time immediately, and 7.42, 8.81 and 5.35 MPa at 24 hours after the bonding, where differences were statistically significant at 5% between Tyrian and Transbond groups at both observation times. It was concluded that Tyrian was the material that presented significant lower bond strength with regard to Transbond groups that were similar.

Bond strength and Raman analysis of the zirconia-feldspathic porcelain interface

The test groups were experimental zirconia, Zirkonzahn zirconia, and Schuetz zirconia. Blocks of partially sintered zirconia were cut into disks (n=20) and then veneered with a feldspathic porcelain. Half of the specimens from each group (n=10) were incubated in 37°C water for 24 hours, and the other half were thermocycled. All the specimens were then subjected to shear testing. The fractured areas were analyzed with optical stereomicroscopy and classified as adhesive, cohesive, or an adhesive-cohesive failure. Spectral patterns were examined to detect bands related to the zirconia and feldspathic porcelain phases. The shear strength data were submitted to 2-way ANOVA. Results No significant differences in shear bond strength were observed among the 3 groups, regardless of whether or not the specimens were thermocycled. Adhesive failures were the most prevalent types of failure (70%). Raman spectra were clearly distinguished for all the materials, which showed the presence of tetragonal and monoclinic phases. Conclusions The controlled production of the experimental zirconia did not influence the results of the bond strength. Raman analysis suggested a process of interdiffusion by the presence of peaks associated with the zirconia and feldspathic ceramics.

Avaliação do Índice de Remanescente Adesivo utilizando braquetes com e sem tratamento na base e a interação com três sistemas de colagem

OBJETIVO: avaliar o Índice de Remanescente Adesivo (IRA) em dentes bovinos após a descolagem de braquetes com e sem tratamento na base. METODOLOGIA: foram utilizados três sistemas de colagem ortodôntica para os dois padrões de base. Os dentes bovinos foram divididos em seis grupos de 40, de acordo com a base do braquete e o sistema de colagem. Vinte e quatro horas após a colagem foram realizados os testes de compressão em uma máquina de ensaios. A avaliação do IRA foi realizada em um estereomicroscópio por três examinadores calibrados. Foi utilizado o teste não paramétrico de Kruskal-Wallis, seguido do método de Dunn, para fazer as comparações múltiplas entre todos os grupos. RESULTADOS E CONCLUSÕES: observou-se que o tratamento das bases dos braquetes com óxido de alumínio não foi determinante para o aumento da adesividade entre o braquete e o adesivo. O grupo em que se utilizou braquetes com tratamento na base e adesivo TXT (3M-Unitek) + Transbond Plus SEP (3M-Unitek) apresentou a maior parte das fraturas na interface dente-adesivo (escore 4).

Estudo in vivo e in vitro com e sem termociclagem, da resistência ao cisalhamento de braquetes colados com fonte de luz halógena

OBJETIVO: avaliar a resistência de braquetes metálicos colados em dentes humanos com resina polimerizada com luz halógena por meio de ensaios mecânicos de cisalhamento. METODOLOGIA: para este estudo foram realizados ensaios in vivo com dinamômetro portátil digital e in vitro com máquina de ensaios mecânicos universal com e sem termociclagem, complementado pelo Índice de Adesivo Remanescente (IAR). Braquetes Edgewise Standard (Abzil) foram colados utilizando adesivo Transbond Plus Self Etching Primer (SEP) e Resina Transbond XT. Foram formados 3 grupos com 10 dentes em cada um deles. No GI os braquetes foram colados nos segundos pré-molares dos pacientes. Nos GII e GIII utilizaram-se primeiros pré-molares extraídos por motivos ortodônticos. Os ensaios mecânicos do GI foram realizados 24 horas após a polimerização diretamente na boca dos pacientes com dinamômetro portátil digital. No GII os corpos-de-prova foram armazenados em água destilada e levados à estufa a 37ºC durante 24 horas e, posteriormente, submetidos à termociclagem, com 1000 ciclos a 5 e 55ºC. No GIII os corpos-de-prova foram armazenados em água destilada em temperatura ambiente por 24 horas e posteriormente submetidos aos ensaios mecânicos. RESULTADOS: os valores médios da resistência ao cisalhamento em Megapascal foram de: GI = 4,39; GII = 7,11 e GIII = 7,35. Após a descolagem foram realizadas fotografias das áreas de colagem, tanto dos dentes submetidos a testes in vivo quanto in vitro e ampliadas 5x para facilitar a visualização. As imagens obtidas foram analisadas, classificadas de acordo com o IAR e, por meio de gráficos de dispersão, foi verificada a relação entre a resistência ao cisalhamento e este índice. CONCLUSÃO: a média dos ensaios mecânicos realizados in vivo foi estatisticamente menor em relação aos ensaios in vitro. Não houve diferenças na resistência ao cisalhamento in vitro entre o grupo termociclado e o não-termociclado. Não houve relação entre tensão de ruptura e tipo de falha.

Effect of acid etching time on the degradation of resin-dentin bonds in primary teeth

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of metal conditioners on the adhesive bonding of resin cements to cast titanium

Objective: To assess the effect of metal conditioners on the bond strength between resin cements and cast titanium. Method and Materials: Commercially pure titanium (99.56%) was cast using an arc casting machine. Surfaces were finished with 400-grit silicon carbide paper followed by air abrasion with 50-mu m aluminum oxide. A piece of double-coated tape with a 4-mm circular hole was then positioned on the metal surface to control the area of the bond. The prepared surfaces were then divided into 4 groups (n=10): G1, unprimed Panavia F; G2, Alloy Primer-Panavia F; G3, unprimed Bistite DC; G4, Metaltite-Bistite DC. Forty minutes after insertion of the resin cements, the specimens were detached from the mold and stored in water at 37 C for 24 hours. Shear bond strength was performed in a testing machine (MTS 810) at a crosshead speed of 0.5 mm/min. Data were analyzed using ANOVA and Tukey's test with a .05 significance level. The fractured surfaces were observed through an optical microscope at 10x magnification. Results: the G1 group demonstrated significantly higher shear bond strength (17.95 MPa) than the other groups. G3 (13.79 MPa) and G4 (12.98 MPa) showed similar mean values to each other and were statistically superior to G2 (9.31 MPa). Debonded surfaces generally presented adhesive failure between metal surfaces and resin cements. Conclusion: While the Metaltite conditioner did not influence the bond strength of the Bistite DC cement, the Alloy Primer conditioner significantly decreased the mean bond strength of the Panavia F cement.

Adhesive Bonding of Resin Composite to Various Ni-Cr Alloy Surfaces Using Different Metal Conditioners and a Surface Modification System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of interface characterization and adhesion of glass ceramics to commercially pure titanium and gold alloy after thermal- and mechanical-loading

Objectives. This study evaluated the effect of thermal- and mechanical-cycling on the shear bond strength of three low-fusing glassy matrix dental ceramics to commercial pure titanium (cpTi) when compared to conventional feldspathic ceramic fused to gold alloy.Methods. Metallic frameworks (diameter: 5 min, thickness: 4 mm) (N = 96, n = 12 per group) were cast in cpTi and gold alloy, airborne particle abraded with 150 mu m aluminum oxide. Low-fusing glassy matrix ceramics and a conventional feldspathic ceramic were fired onto the alloys (thickness: 4mm). Four experimental groups were formed; Gr1 (control group): Vita Omega 900-Au-Pd alloy; Gr2: Ticeram-cpTi; Gr3: Super Porcelain Ti-22-cpTi and G4: Vita Titankeramik-cpTi. While half of the specimens from each ceramic-metal combination were randomly tested without aging (water storage at 37 C for 24h only), the other half were first thermocycled (6000 cycles, between 5 and 55 C, dwell time: 13 s) and then mechanically loaded (20,000 cycles under SON load, immersion in distilled water at 37 C). The ceramic-alloy interfaces were loaded under shear in a universal test machine (cross-head speed: 0.5 mm/min) until failure occur-red. Failure types were noted and the interfaces of the representative fractured specimens from each group were examined with stereo microscope and scanning electron microscope (SEM). in an additional study (N = 16, n = 2 per group), energy dispersive X-ray spectroscopy (EDS) analysis was performed from ceramic-alloy interfaces. Data were analyzed using ANOVA and Tukey's test.Results. Both ceramic-metal combinations (p < 0.001) and aging conditions (p < 0,001) significantly affected the mean bond strength values. Thermal- and mechanical-cycling decreased the bond strength (MPa) results significantly for Gr3 (33.4 +/- 4.2) and Gr4 (32.1 +/- 4.8) when compared to the non-aged groups (42.9 +/- 8.9, 42.4 +/- 5.2, respectively). Gr1 was not affected significantly from aging conditions (61.3 +/- 8.4 for control, 60.7 +/- 13.7 after aging) (p > 0.05). Stereomicroscope images showed exclusively adhesive failure types at the opaque ceramic-cpTi interfacial zone with no presence of ceramic on the substrate surface but with a visible dark titanium oxide layer in Groups 2-4 except Gr1 where remnants of bonder ceramic was visible. EDS analysis from the interfacial zone for cpTi-ceramic groups showed predominantly 34.5-85.1% O(2) followed by 1.1-36.7% Aland 0-36.3% Si except for Super Porcelain Ti-22 where a small quantity of Ba (1.4-8.3%), S (0.7%) and Sn (35.3%) was found. In the Au-Pd alloy-ceramic interface, 56.4-69.9% O(2) followed by 15.6-26.2% Si, 3.9-10.9% K, 2.8-6% Na, 4.4-9.6% Al and 0-0.04% Mg was observed.Significance. After thermal-cycling for 6000 times and mechanical-cycling for 20,000 times, Triceram-cpTi combination presented the least decrease among other ceramic-alloy combinations when compared to the mean bond strength results with Au-Pd alloy-Vita Omega 900 combination. (c) 2008 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Análise da qualidade de adesão de diferentes bases de braquetes metálicos

Diante das diferenças existentes nas características das bases dos braquetes usados atualmente, objetivou-se neste trabalho comparar entre si três tipos de bases de braquetes metálicos (Monobloc, Equilibrium e Dynalock). Foram utilizados 36 pré-molares humanos, divididos em 3 grupos de 12 dentes. Os dentes foram incluídos em troquéis com gesso pedra tipo IV e posicionados com suas faces vestibulares perpendiculares à base do troquel. Todos os braquetes foram colados com o compósito Concise Ortodôntico e submetidos ao ensaio de cisalhamento em uma Máquina Universal com uma velocidade de 0,5 mm por minuto. O braquete Monobloc obteve o maior valor médio de resistência adesiva (x = 28,19 Kgf/cm²), sendo superior estatisticamente aos braquetes Equilibrium (x = 18,07 Kgf/cm²) e Dynalock (x = 18,24 Kgf/cm²). em relação ao ARI (Índice de Remanescente Resinoso), não foi encontrada diferença estatística entre os braquetes testados.

Adhesives with different pHs: Effect on the MTBS of chemically activated and light-activated composites to human dentin

Purpose: To evaluate the bond strength between human dentin and composites, using two light-activated single-bottle total-etch adhesive systems with different pHs combined with chemically activated and light-activated-composites. The tested hypothesis was that the dentin bond strength is not influenced by an adhesive system of low pH, combined with chemically activated or light-activated composites. Material and Method: Flat dentin surfaces of twenty-eight human third molars were allocated in 4 groups (n=7), depending on the adhesive system: (One Step Plus-OS and Prime & Bond NT-PB) and composite (light-activated Filtek Z-100 [Z100] and chemically activated Bisfil 2B [B2B]). Each adhesive system was applied on acid-etched dentin and then one of the composites was added to form a 5 mm-high resin block. The specimens were stored in tap water (37 degrees C/24 h) and sectioned into two axes, x and y. This was done with a diamond disk under coolant irrigation to obtain beams with a cross-section area of approximately 0.8 mm(2). Each specimen was then attached to a custom-made device and submitted to the microtensile test (1 mm.min(-1)). Data were analyzed using two-way ANOVA and Tukey's tests (p<0.05). Results: the anticipated hypothesis was not confirmed (p<0.0001). The bond strengths (MPa) were not statistically different between the two adhesive systems when light-activated composite was used (OS+Z100 = 24.7 +/- 7.1(a); PB+Z100 = 23.8 +/- 5.7(a)). However, with use of the chemically activated composite (B2B), PB (7.8 +/- 3.6(b) MPa) showed significantly lower dentin bond strengths than OS (32.2 +/- 7.6(a)). Conclusion: the low pH of the adhesive system can affect the bond of chemically activated composite to dentin. on the other hand, under the present conditions, the low pH did not seem to affect the bond of light-activated composites to dentin significantly.

Adhesive performance of dentin bonding agents applied in vivo and in vitro. Effect of intrapulpal pressure and dentin depth

The purpose of this study was to evaluate the influence of intrapulpal pressure and dentin depth on bond strengths of an etch-and-rinse and a self-etching bonding agent to dentin in vitro and in vivo. Twenty-four pairs of premolars were randomly divided into four groups (n = 6) according to the dentin bonding agent, Single Bond and Clearfil SE Bond, and intrapulpal pressure, null or positive. Each tooth of the pair was further designated to be treated in vivo or in vitro. The intrapulpal pressure was controlled in vivo by the delivery of local anesthetics containing or not a vasoconstrictor, while in vitro, it was achieved by keeping the teeth under hydrostatic pressure. Class I cavities were prepared and the dentin bonding agents were applied followed by incremental resin restoration. For the teeth treated in vitro, the same restorative procedures were performed after a 6 month-storage period. Beams with I mm 2 cross-sectional area were prepared and, microtensile tested. Clearfil SE Bond was not influenced by any of the variables of the study, while bond strengths produced in vitro were significatly higher for Single Bond. Overall, lower bond strengths were produced in deep dentin, which reached statistical significance when Single Bond was applied under physiological or simulated intrapulpal pressure. In conclusion, in vitro bonding may overestimate the immediate adhesive performance of more technique-sensitive dentin bonding systems. The impact of intrapulpal pressure on bond strength seems to be more adhesive dependent than dentin morphological characteristics related to depth. (C) 2007 Wiley Periodicals, Inc.

Microleakage and nanoleakage: Influence of laser in cavity preparation and dentin pretreatment

Objective: the purpose of this study was to verify if the application of the Nd:YAG laser following pretreatment of dentin with adhesive systems that were not light cured in class V cavities and were prepared with Er:YAG laser would promote better sealing of the gingival margins when compared to cavities prepared the conventional way. Background Data: Previous studies had shown that the pretreatment of dentin with laser irradiation after the application of an adhesive system is efficient in achieving higher shear bond and tensile bond strength. Materials and Methods: Er:YAG laser (Kavo-Key, Germany) with 350 mJ, 4 Hz, and 116.7 J/cm(2) was used for cavity preparation. The conventional preparation was made with diamond bur mounted in high-speed turbine. Dentin treatment was accomplished using an Nd:YAG laser (Pulse Master 1000, ADT. USA) at 60 mJ, 10 Hz, and 74.65/cm(2) following application of the adhesive system. The cavities were stored with Single Bond/Z100 and Prime & Bond NT/TPH. Eighty bovine incisors were used, and class V preparations were done at buccal and lingual surfaces divided into eight groups: (1) Er:YAG preparation + Prime & Bond NT + TPH; (2) Er:YAG preparation + Single Bond + Z100; (3) Er:YAG preparation + Single Bond + Nd:YAG + Z100; (4) Er:YAG preparation + Prime & Bond NT + Nd:YAG + TPH; (5) conventional preparation + Prime & Bond NT + TPH; (6) conventional preparation + Single Bond + Z100; (7) conventional preparation + Single Bond + Nd:YAG + Z100; (8) conventional preparation + Prime & Bond NT + Nd:YAG + TPH. All specimens were thermocycled for 300 full cycles between 5 degreesC +/- 2 degreesC and 55 degreesC +/- 2 degreesC (dwell time of 30 sec), and stored in 50% silver nitrate solution for 24 h soaked in photodeveloping solution and exposed to fluorescent light for 6 h. After this procedure, the specimens were sectioned longitudinally in 3 portions and the extension of microleakage at the gingival wall was determined following a criteria ranging from 0 to 4 using scanning electron microscopy (SEM). The medium portion sectioned of each specimen was polished and prepared for nanoleakage avaliation by SEM. Results: Kruskall-Wallis and Miller statistical tests determined that group 3 presented less microleakage and nanoleakage. Conclusion: Application of the Nd:YAG laser following pretreatment of dentin with adhesive Single Bond non-photocured Single Bond adhesive in cavities prepared with Er:YAG promote better sealing of the gingival margins.

An In Vitro Comparison of Different Cementation Strategies on the Pull-out Strength of a Glass Fiber Post

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)