Columnar microstructure of nanocrystalline Ga1-xMnxN films deposited by reactive sputtering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Resonant excitation of Mn local vibrational modes in the higher order Raman spectra of nanocrystalline Ga(1-x)Mn(x)N films

The effect of manganese on the vibrational properties of Ga(1-x)Mn(x)N (0 <= x <= 0.18) films has been investigated by Raman scattering using 488.0 and 632.8 nm photon excitations. The first-order transverse and longitudinal optical GaN vibrational bands were observed in the whole composition range using both excitations, while the corresponding overtones, as well as a prominent peak located in 1238 cm(-1) (153.5 meV) were only observed in the Mn-containing films under 488.0 nm excitation. We propose that the peak observed at 1238 cm(-1) is due to resonant Mn local vibrational modes, the excitation process being related to electronic transitions involving the Mn acceptor band.

Disorder effects produced by the Mn and H incorporations on the optical absorption edge of Ga1-xMnxAs:H nanocrystalline films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The optical absorption edge of nanocrystalline Ga(1-x)Mn(x)N films deposited by reactive sputtering

We have focused on the optical absorption edge of nanocrystalline Ga(1-x)Mn(x)N (0.00 <= x <= 0.18) films deposited by reactive RF magnetron sputtering. The films obtained are nanocrystalline with grain sizes of about 25 nm, having wurtzite structure and strong orientation texture in the c-axis direction. The optical characterizations of the absorption edges were obtained in the 190-2600 nm spectral range. The increase of the Mn content causes an increase of the absorption coefficient which can be clearly noticed at low energies, and a quasi-linear decrease of the optical gap. Broad absorption bands observed around similar to 1.3 and similar to 2.2 eV were associated with transitions between the Mn acceptor level and the valence and conduction bands, respectively. The observed changes in the optical properties due to the Mn incorporation observed in these nanocrystalline films are similar to those reported for ferromagnetic GaMnN single-crystal films.

Structural Characterization of Nanocrystalline Sb-Doped SnO2 Xerogels by Multiedge X-ray Absorption Spectroscopy

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

First order reversal curve analysis of nanocrystalline Pd80Co20 alloy films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Preparation and characterization of nanocrystalline h-BN films prepared by PECVD method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Nanocrystalline anatase thin films prepared from redispersible sol-gel powders

Transparent thin films of nanocrystalline anatase were obtained by dip-coating process using an ethanolic suspension of redispersed nanoparticles. This suspension was prepared by sol-gel route and their redispersability achieved by surface grafting of para-toluene-sulfonic acid and acetylacetone. The effects of the acetylacetone content on the powder redispersibility and on the structural evolution of films were determined by small angle X-ray scattering, X-ray reflectometry and X-ray diffraction for different firing temperatures. The results demonstrated that the porous structure of the studied films consist of agglomerates of primary particles with two levels of porosity. The control of the amount of capping ligand allows for a fine-tuning of the average pore size of the dried films. Upon increasing the firing temperature up to 500 degrees C, progressive increase in apparent density, average pore size of films and average crystallite size of powders were observed. (c) 2005 Elsevier Ltd. All rights reserved.

Structural and vibrational analysis of nanocrystalline Ga1-xMnxN films deposited by reactive magnetron sputtering

The structural and vibrational properties of nanocrystalline Ga1-xMnxN films deposited by reactive magnetron sputtering were analyzed in a wide composition range (0 < x < 0.18). The films were structurally characterized using x-ray diffraction with Rietveld refinement. The corresponding vibrational properties were investigated using micro-Raman and Fourier transform infrared spectroscopies. The films present a high crystallized fraction, crystallites having wurtzite structure, and high orientation texture with the c axis oriented perpendicular to the substrate surface. Rietveld analysis indicates that Mn atoms are incorporated substitutionally into Ga positions and show that the ionic character of cation-N bonds along the c axis is favored by the Mn incorporation. No evidence for Mn segregation or Mn rich phases was found in the composition range analyzed. Micro-Raman scattering spectra and infrared absorption experiments showed progressive changes with the increase of x and monotonic shifts of the GaN TO and LO peaks to lower frequencies. The structural and vibrational analyses are compared and the influence of Mn on the static and dynamic properties of the lattice is analyzed. (C) 2007 American Institute of Physics.

Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Microstructural investigation of the PZT films prepared from the suspension of nanocrystalline powders

PZT thin films of composition Pb(Zr0.52Ti0.48)O-3 were prepared by a novel method from the suspension of nanocrystalline PZT powders. The powders were obtained by mechanochemical synthesis. Films were deposited on silicon (100) and platinum covered silicon substrates (Pt (111) /Ti/SiO2/Si) Using spin-on technique. Substrate type has influence on films crystallinity, orientation and can react with the films changing its phase composition. Films microstructure strongly depends on thermal treatment conditions due to phase and compositional changes of the films. (C) 2003 Elsevier Ltd. All rights reserved.

Sintering and crystallite growth of nanocrystalline copper doped tin oxide

The effect of Cu2+ contents and of firing temperature on sintering and crystallite growth of nanocrystalline SnO2 xerogels was analyzed by thermoanalysis (mass loss (TG), linear shrinkage, and differential thermal analysis (DTA)), X-ray powder diffraction (XRPD), and EXAFS (extended X-ray absorption fine structures) measurements. Samples were prepared by two methods: (a) coprecipitation of a colloidal suspension from aqueous solution containing both Sn(IV) and Cu(II) ions and (b) grafting copper(II) species on the surface of tin pride gel. The thermoanalysis has shown that the shrinkage associated with the mass loss decreases by increasing the amount of copper. The EXAFS measurements carried out at the Cu K edge have evidenced the presence of copper in substitutional solid solution for the dried xerogel prepared with 0.7 mol % of copper, while for higher concentration of doping, copper has been observed also at the external surface of crystallites. The solid solution is metastable and copper migrates toward the surface during firing. The XRPD and DTA results have shown a recrystallization process near 320 degrees C, which leads to crystallite growth. The presence of copper segregated near the crystallite surface controls its growth.

Room temperature co-precipitation of nanocrystalline CeO2 and Ce0.8Gd0.2O1.9-delta powder

This paper describes a simple method to co-precipitate CeO2 and Ce0.8Gd0.2O1.9-delta with ammonium hydroxide from solvents such as: water, ethylene glycol, ethyl alcohol and isopropyl alcohol. Characterization by Raman spectroscopy and XRD evidenced the formation of a solid solution of gadolinium-doped ceria at room temperature. Nanometric particles with crystallite size of 3.1 nm were obtained during synthesis using ethyl alcohol as solvent. This is a promising result compared with those mentioned in the literature, in which the smallest crystallite size reported was, 6.5 nm. (c) 2006 Elsevier B.V. All rights reserved.

Properties and in vivo investigation of nanocrystalline hydroxyapatite obtained by mechanical alloying

Mechanical alloying has been used successfully to produce nanocrystalline powders of hydroxyapatite (HA) using three different procedures. The milled HA was studied by X-ray diffraction, Infrared, Raman scattering spectroscopy and Scanning Electron Microscopy (SEM). We obtained HA with different degrees of crystallinity and time of milling. The grain size analysis through SEM and XRD shows particles with dimensions of 36.9, 14.3 and 35.5 nm (for (R1), (R2) and (R3), respectively) forming bigger units with dimensions given by 117.2, 110.8 and 154.4 nm (for (R1), (R2) and (R3), respectively). The Energy-Dispersive Spectroscopy (EDS) analysis showed that an atomic ratio of Ca/P= 1.67, 1.83 and 1.50 for reactions (R1), (R2) and (R3), respectively. These results suggest that the R1 nanocrystalline ceramic is closer to the expected value for the ratio Ca/P for hydroxyapatite, which is 513 congruent to 1.67. The bioactivity analysis shows that all the samples implanted into the rabbits can be considered biocompatible, since they had been considered not toxic, bad not caused inflammation and reject on the part of the organisms of the animals, during the period of implantation. The samples implanted in rabbits had presented new osseous tissue formation with the presence of osteoblasts cells. (C) 2004 Elsevier B.V. All rights reserved.

Effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and their magnetic properties

The effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and on their magnetic properties was studied. The pH practically did not affect the alloy composition. Conversely, the pH showed a significant influence on the shape and size of crystallites. Two different crystallites morphology were observed depending on the bath pH. A crystallite size ranging from 18.2 to 30 nm was obtained from X-ray diffractometry (XRD) patterns using the Scherrer's method. Also from the XRD patterns the lattice strain percentage was calculated and correlated with the residual stress, which probably originated during the film electrodeposition on the substrate. Some alloy magnetic properties showed small variations. In contrast, high and unexpected coercivities were obtained reaching a maximum of 1.69 kOe at pH 5.5. The high coercivity values were attributed to the presence of residual stress at the film-substrate interface, which increased as the bath pH and crystallite size decrease, both of them contributing simultaneously to increase in coercivity. (C) 2006 Elsevier B.V. All rights reserved.