Estudo da adesão de pinos endodônticos modificados superficialmente por plasma de oxigênio

The work presents the effect of plasma treatment when applied in fibers or carbon/glass posts in the adhesion fiber/resin and posts/cement. This has for objective the modification of the surface of the fibers, as well as the wettability of the posts, seeking the improvement of the adhesion and of the connection fiber/resin in the processing of polymeric composites reinforced with the same ones. 120 posts (Reforpost) were used and 30 meters of fibers of carbon and of glass (Fibrex), of the company Angelus. The samples were divided in three groups of 40 specimens: GROUP I - 20 posts of glass fiber and 20 of carbon without treatment to it shapes, GROUP II -20 posts of glass fiber and 20 of carbon treated to it shapes in the surface and GROUP III - 20 posts of glass fiber and 20 of carbon make with fibers in natura after plasma treatment. The plasma treatment was accomplished with oxygen and with temperature in the camera fixed at 200°C, for one hour of exhibition. The posts and the fibers were characterized before and after the treatment. The wettability was measure by pendent drop method, and interface fiber/resin and posts/cement were observed by optical and electronic microscopy. It was observed that both wettability and texture were increased with plasma treatment

Efeito do tratamento por plasma na proliferação de fibroblastos e esterilização de membranas de quitosana

Chitosan is being studied for use as dressing due their biological properties. Aiming to expand the use in biomedical applications, chitosan membranes were modified by plasma using the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen (H2). The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle, surface energy and water absorption test. Biological Tests were also performed, such as: test sterilization and proliferation of fibroblasts (3T3 line). Through SEM we observed morphological changes occurring during the plasma treatment, the formation of micro and nano-sized valleys. MFA was used to analyze different roughness parameters (Ra, Rp, Rz) and surface topography. It was found that the treated samples had an increase in surface roughness and sharp peaks. Methane plasma treatment decreased the hydrophilicity of the membranes and also the rate of water absorption, while the other treatments turned the membranes hydrophilic. The sterilization was effective in all treatment times with the following gases: Ar, N2 and H2. With respect to proliferation, all treatments showed an improvement in cell proliferation increased in a range 150% to 250% compared to untreated membrane. The highlights were the treatments with Ar 60 min, O2 60 min, CH4 15 min. Observing the results of the analyzes performed in this study, it appears that there is no single parameter that influences cell proliferation, but rather a set of ideal conditions that favor cell proliferation

Estudo da adesão de pinos endodônticos modificados superficialmente por plasma de oxigênio

The work presents the effect of plasma treatment when applied in fibers or carbon/glass posts in the adhesion fiber/resin and posts/cement. This has for objective the modification of the surface of the fibers, as well as the wettability of the posts, seeking the improvement of the adhesion and of the connection fiber/resin in the processing of polymeric composites reinforced with the same ones. 120 posts (Reforpost) were used and 30 meters of fibers of carbon and of glass (Fibrex), of the company Angelus. The samples were divided in three groups of 40 specimens: GROUP I - 20 posts of glass fiber and 20 of carbon without treatment to it shapes, GROUP II -20 posts of glass fiber and 20 of carbon treated to it shapes in the surface and GROUP III - 20 posts of glass fiber and 20 of carbon make with fibers in natura after plasma treatment. The plasma treatment was accomplished with oxygen and with temperature in the camera fixed at 200°C, for one hour of exhibition. The posts and the fibers were characterized before and after the treatment. The wettability was measure by pendent drop method, and interface fiber/resin and posts/cement were observed by optical and electronic microscopy. It was observed that both wettability and texture were increased with plasma treatment

Efeito do tratamento por plasma na proliferação de fibroblastos e esterilização de membranas de quitosana

Chitosan is being studied for use as dressing due their biological properties. Aiming to expand the use in biomedical applications, chitosan membranes were modified by plasma using the following gases: nitrogen (N2), methane (CH4), argon (Ar), oxygen (O2) and hydrogen (H2). The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), contact angle, surface energy and water absorption test. Biological Tests were also performed, such as: test sterilization and proliferation of fibroblasts (3T3 line). Through SEM we observed morphological changes occurring during the plasma treatment, the formation of micro and nano-sized valleys. MFA was used to analyze different roughness parameters (Ra, Rp, Rz) and surface topography. It was found that the treated samples had an increase in surface roughness and sharp peaks. Methane plasma treatment decreased the hydrophilicity of the membranes and also the rate of water absorption, while the other treatments turned the membranes hydrophilic. The sterilization was effective in all treatment times with the following gases: Ar, N2 and H2. With respect to proliferation, all treatments showed an improvement in cell proliferation increased in a range 150% to 250% compared to untreated membrane. The highlights were the treatments with Ar 60 min, O2 60 min, CH4 15 min. Observing the results of the analyzes performed in this study, it appears that there is no single parameter that influences cell proliferation, but rather a set of ideal conditions that favor cell proliferation

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.

Effect of cooling rate on properties of plasma nitrided AISI 1010 steel

In this work, AISI 1010 steel samples were plasma nitrided into 20% N 2 100 Pa and 400 Pa for N 2 and H 2 , respectively), temperatures of 500 and 580 °C, during 2 h. Three different procedures for cooling were accomplished after nitriding. In the first procedure the cooling occurred naturally, that is, the sample was kept on substrate holder. In the second one the sample was pulled off and cooling in a cold surface. Finally, in the third cooling process the sample was pulled off the substrate holder down into special reservoir filled with oil held at ambient temperature. The properties of the AISI 1010 steel samples were characterized by optical and electron microscopy, X-ray diffraction, Mössbauer spectroscopy and microhardness tests. Thermal gradient inside the sample kept on substrate holder during cooling process was measured by three inserted thermocouples at different depths. When samples were cooled rapidly the transformation of ϵ-Fe 2 − 3 N to γ′-Fe 4 N was inhibited. Such effect is indicated by the high concentration of ϵ-Fe compound zone. To get solid state solution of nitrogen in the diffusion zone, instead of precipitates of nitride phases, the cooling rate should be higher than a critical value of about 0.95 °C/s. When this value is reached at any depth of the diffusion zone, two distinct diffusion zones will appear. Temperature gradients were measured inside the samples as a consequence of the plasma treatment. It's suggested the need for standardization of the term “treatment temperature” for plasma treatment because different nitrided layer properties could be reported for the same “treatment temperature”.