Degradação do PMMA através da reação despolimerização uitlizando catalisadores de óxidos mistos

In this work, mixed oxides were synthesized by two methods: polymeric precursor and gel-combustion. The oxides, Niquelate of Lanthanum, Cobaltate of Lanthanum and Cuprate of Lanthanum were synthesized by the polymeric precursor method, and treated at 300 º C for 2 hours, calcined at 800 º C for 6h in air atmosphere. In gel-combustion method were produced and oxides using urea and citric acid as fuel, forming for each fuel the following oxides Ferrate of Lanthanum, Cobaltato of Lanthanum and Ferrato of Cobalt and Lanthanum, which were submitted to the combustion process assisted by microwave power maximum of 10min. The samples were characterized by: thermogravimetric analysis, X-ray diffraction; fisisorção of N2 (BET method) and scanning electron microscopy. The reactions catalytic of depolymerization of poly (methyl methacrylate), were performed in a reactor of silica, with catalytic and heating system equipped with a data acquisition system and the gas chromatograph. For the catalysts synthesized using the polymeric precursor method, the cuprate of lanthanum was best for the depolymerization of the recycled polymer, obtaining 100% conversion in less time 554 (min), and the pure polymer, was the Niquelate of Lanthanum, with 100% conversion in less time 314 (min). By gel-combustion method using urea as fuel which was the best result obtained Ferrate of Lanthanum for the pure polymer with 100% conversion in less time 657 (min), and the recycled polymer was Cobaltate of Lanthanum with 100 % conversion in less time 779 (min). And using citric acid to obtain the best result for the pure polymer, was Ferrate of Lanthanum with 100% conversion in less time 821 (min and) for the recycled polymer, was Ferrate of Lanthanum with 98.28% conversion in less time 635 (min)

Estudo do processo de combustão in-situ usando poços horizontais como produtores de óleo (Toe-to-Hell Air Injection)

The method "toe-to-heel air injection" (THAITM) is a process of enhanced oil recovery, which is the integration of in-situ combustion with technological advances in drilling horizontal wells. This method uses horizontal wells as producers of oil, keeping vertical injection wells to inject air. This process has not yet been applied in Brazil, making it necessary, evaluation of these new technologies applied to local realities, therefore, this study aimed to perform a parametric study of the combustion process with in-situ oil production in horizontal wells, using a semi synthetic reservoir, with characteristics of the Brazilian Northeast basin. The simulations were performed in a commercial software "STARS" (Steam, Thermal, and Advanced Processes Reservoir Simulator), from CMG (Computer Modelling Group). The following operating parameters were analyzed: air rate, configuration of producer wells and oxygen concentration. A sensitivity study on cumulative oil (Np) was performed with the technique of experimental design, with a mixed model of two and three levels (32x22), a total of 36 runs. Also, it was done a technical economic estimative for each model of fluid. The results showed that injection rate was the most influence parameter on oil recovery, for both studied models, well arrangement depends on fluid model, and oxygen concentration favors recovery oil. The process can be profitable depends on air rate

Análise da sensibilidade do biodiesel B5 em frotas de transporte coletivo com motorização diesel

The aim of this study was investigate the consolidation of the biodiesel fuel used in (a) engines of urban and intercity bus companies, (b) a stationary engine. It was necessary to investigate and analyze, technologically, if the biodiesel fuels were presenting troubleshooting relative to wear of parts lied to fuel and to evaluate the consumption fluctuations of this fuel. The urban and intercity bus companies, localized in Natal, Rio Grande do Norte state, Brazil, had 41 and 12 vehicles, respectively. It were analyzed datasheet of each one vehicle during three years, since 2008 until 2010 and were interviewed the management of the maintenance team of bus companies relative to aspects concerning the substitution of the diesel fuel by the B5 biodiesel. The second aim of this study was visually inspect the wear of the parts directly lied to combustion process. For this reason, it was investigated a stationary engine, manufactured by Branco BD5, 5 HP of power, fueled by (a) diesel, (b) biodiesel B5, (c) biodiesel B20 and (d) diesel or biodiesel, both contaminated by distilled water. In this engine, its power utilizing biodiesel B5 versus diesel was lower about 5.2% and, in the investigated case of B20 versus diesel, it was lower around 11.5%

Transportadores sólidos de oxigênio à base de níquel e cobre suportados em aluminatos para combustão do metano pela tecnologia de recirculação química

In recent years, solid carriers suitable oxygen have been developed for use in different chemical processes recirculation. The success of this technology is directly related to the chemical reactivity and the oxygen storage capacity of the carrier. Thus, research into the development of new materials that can be applied to the process becomes extremely important. Possible candidates are the carriers based on nickel and copper for presenting favorable thermodynamic properties. In this work, aluminates type MAl2O4 (M = Mg and Ca) and M0,9B0,1Al2O4 (B = Ni and Cu) that are used as supports were synthesized by combustion reactions assisted by microwave and calcined at 900°C/2h. Then, the carriers were impregnated with 10% (m/m) of nickel or copper, and subsequently calcined at 600°C/2h to obtain the solid oxygen carriers, which were characterized by X-ray diffraction (XRD) Microscopy scanning electron microscopy (SEM) and temperature programmed reduction (TPR). Reactions simulating the combustion process by chemical recirculation were performed by cycles reduction/oxidation, in order to evaluate the reactivity of carriers. XRD analysis revealed diffraction peaks of the spinel type structures. In the doped substrates were verified the presence of secondary phases, suggesting that all the metal was incorporated into the spinel structure. In solid oxygen carriers, the NiO and CuO phases were observed after impregnation of active phases on different media. The results of evaluations of chemical cycles reduction/oxidation revealed that TSO's impregnated with nickel in various media were more active and are potential candidates for use in the chemical recirculation technology

Síntese de ferritas de cobalto e níquel dopadas com zinco e caracterização de suas propriedades eletromagnéticas

This work shows that the synthesis by combustion is a prominent alternative to obtain ceramic powders of higher oxides, nanostructured and of high purity, as the ferrites of formulas Co(1-x)Zn(x)Fe2O4 e Ni(1-x)Zn(x)Fe2O4 with x ranging from 0.2 mols, in a range from 0.2 ≤ x ≥ 1.0 mol, that presents magnetic properties in coexistence of ferroelectric and ferrimagnetic states, which can be used in antennas of micro tapes and selective surfaces of low frequency in a range of miniaturized microwaves, without performance loss. The obtainment occurred through the combustion process, followed by appropriate physical processes and ordered to the utilization of the substrate sinterization process, it gave us a ceramic material, of high purity degree in a nanometric scale. The Vibrating Sample Magnetometer (VSM) analysis showed that those ferritic materials presents parameters, as materials hysteresis, that have own behavior of magnetic materials of good quality, in which the magnetization states can be suddenly changed with a relatively small variation of the field intensity, having large applications on the electronics field. The X-ray Diffraction (XRD) analysis of the ceramic powders synthesized at 900 °C, characterize its structural and geometrical properties, the crystallite size and the interplanar spacing. Other analysis were developed, as Scanning Electron Microscopy (SEM), X-ray Fluorescence (XRF), electric permittivity and the tangent loss, in high frequencies, through the equipment ZVB - 14 Vector Network Analyzer 10 MHz-14 GHz, of ROHDE & SCHWART.

Degradação do PMMA através da reação despolimerização uitlizando catalisadores de óxidos mistos

In this work, mixed oxides were synthesized by two methods: polymeric precursor and gel-combustion. The oxides, Niquelate of Lanthanum, Cobaltate of Lanthanum and Cuprate of Lanthanum were synthesized by the polymeric precursor method, and treated at 300 º C for 2 hours, calcined at 800 º C for 6h in air atmosphere. In gel-combustion method were produced and oxides using urea and citric acid as fuel, forming for each fuel the following oxides Ferrate of Lanthanum, Cobaltato of Lanthanum and Ferrato of Cobalt and Lanthanum, which were submitted to the combustion process assisted by microwave power maximum of 10min. The samples were characterized by: thermogravimetric analysis, X-ray diffraction; fisisorção of N2 (BET method) and scanning electron microscopy. The reactions catalytic of depolymerization of poly (methyl methacrylate), were performed in a reactor of silica, with catalytic and heating system equipped with a data acquisition system and the gas chromatograph. For the catalysts synthesized using the polymeric precursor method, the cuprate of lanthanum was best for the depolymerization of the recycled polymer, obtaining 100% conversion in less time 554 (min), and the pure polymer, was the Niquelate of Lanthanum, with 100% conversion in less time 314 (min). By gel-combustion method using urea as fuel which was the best result obtained Ferrate of Lanthanum for the pure polymer with 100% conversion in less time 657 (min), and the recycled polymer was Cobaltate of Lanthanum with 100 % conversion in less time 779 (min). And using citric acid to obtain the best result for the pure polymer, was Ferrate of Lanthanum with 100% conversion in less time 821 (min and) for the recycled polymer, was Ferrate of Lanthanum with 98.28% conversion in less time 635 (min)

Estudo do processo de combustão in-situ usando poços horizontais como produtores de óleo (Toe-to-Hell Air Injection)

The method "toe-to-heel air injection" (THAITM) is a process of enhanced oil recovery, which is the integration of in-situ combustion with technological advances in drilling horizontal wells. This method uses horizontal wells as producers of oil, keeping vertical injection wells to inject air. This process has not yet been applied in Brazil, making it necessary, evaluation of these new technologies applied to local realities, therefore, this study aimed to perform a parametric study of the combustion process with in-situ oil production in horizontal wells, using a semi synthetic reservoir, with characteristics of the Brazilian Northeast basin. The simulations were performed in a commercial software "STARS" (Steam, Thermal, and Advanced Processes Reservoir Simulator), from CMG (Computer Modelling Group). The following operating parameters were analyzed: air rate, configuration of producer wells and oxygen concentration. A sensitivity study on cumulative oil (Np) was performed with the technique of experimental design, with a mixed model of two and three levels (32x22), a total of 36 runs. Also, it was done a technical economic estimative for each model of fluid. The results showed that injection rate was the most influence parameter on oil recovery, for both studied models, well arrangement depends on fluid model, and oxygen concentration favors recovery oil. The process can be profitable depends on air rate