The fucoidan from Fucus vesiculosus is known for having diverse biological properties. This study analyzed the therapeutic action of populations of commercial fucoidan (F. vesiculosus) on zymosan-induced arthritis. Three populations of fucoidan were obtained after acetone fractionation; these were denominated F1 (52.3%), F2 (36.7%) and F3 (10.7%). Chemical analyses showed that F1 contained the largest amount of sulfate ion. The electrophoretic profile shows that the commercial or total fucoidan (TF), different from the other fucoidans and from glycosaminoglycan patterns, is quite polydisperse, which indicates that it is composed of a mixture of sulfate polysaccharides. On the other hand, the fucoidans obtained from TF showed only an electrophoretic band with much lower polydispersion than that observed for TF. Fucoidan F2 showed a migration between fucoidans F1 and F3. Owing to the small amount of mass obtained from F3, we used only fucoidans F1 and F2 in the induced arthritis tests. After 1 hour of induction, we administered F1 or F2 (10, 25 and 50 mg/kg i.p.) or diclofenac sodium (10 mg/kg i.p.) or lumiracoxib (5 mg/kg o.a.) or L-NAME (30 mg/kg i.p.). After 6 hours, we performed analyses of cell influx and nitrite levels in addition to histopathological analysis. Fucoidans F1 and F2 were more potent both in decreasing the number of leukocytes and the amount of nitric oxide found in the synovial fluid. This indicates that the anti-inflammatory mechanism of these fucoidans is not only related to selectin block, but also to nitric oxide synthesis inhibition

Síntese de nanopartículas de magnetita via decomposição térmica em meio não-aquoso

This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260ºC. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface

Efeito de frações obtidas da fucoidana de Fucus vesiculosus em modelo experimental de artrite induzida por Zymosan

The fucoidan from Fucus vesiculosus is known for having diverse biological properties. This study analyzed the therapeutic action of populations of commercial fucoidan (F. vesiculosus) on zymosan-induced arthritis. Three populations of fucoidan were obtained after acetone fractionation; these were denominated F1 (52.3%), F2 (36.7%) and F3 (10.7%). Chemical analyses showed that F1 contained the largest amount of sulfate ion. The electrophoretic profile shows that the commercial or total fucoidan (TF), different from the other fucoidans and from glycosaminoglycan patterns, is quite polydisperse, which indicates that it is composed of a mixture of sulfate polysaccharides. On the other hand, the fucoidans obtained from TF showed only an electrophoretic band with much lower polydispersion than that observed for TF. Fucoidan F2 showed a migration between fucoidans F1 and F3. Owing to the small amount of mass obtained from F3, we used only fucoidans F1 and F2 in the induced arthritis tests. After 1 hour of induction, we administered F1 or F2 (10, 25 and 50 mg/kg i.p.) or diclofenac sodium (10 mg/kg i.p.) or lumiracoxib (5 mg/kg o.a.) or L-NAME (30 mg/kg i.p.). After 6 hours, we performed analyses of cell influx and nitrite levels in addition to histopathological analysis. Fucoidans F1 and F2 were more potent both in decreasing the number of leukocytes and the amount of nitric oxide found in the synovial fluid. This indicates that the anti-inflammatory mechanism of these fucoidans is not only related to selectin block, but also to nitric oxide synthesis inhibition

Síntese de nanopartículas de magnetita via decomposição térmica em meio não-aquoso

This work aims at obtaining nanoparticles of iron oxide, the magnetite one (Fe3O4), via synthesis by thermal decomposition through polyol. Thus, two routes were evaluated: a simple decomposition route assisted by reflux and a hydrothermal route both without synthetic air atmosphere using a synthesis temperature of 260ºC. In this work observed the influence of the observe of surfactants which are generally applied in the synthesis of iron oxide nanoparticles decreasing cluster areas. Further, was observed pure magnetite phase without secondary phases generally found in the iron oxide synthesis, a better control of crystallite size, morphology, crystal structure and magnetic behavior. Finally, the introduction of hydroxyl groups on the nanoparticles surface was analyzed besides its employment in the polymer production with OH radicals. The obtained materials were characterized by XRD, DLS, VSM, TEM, TG and DSC analyses. The results for the magnetite obtainment with a particle size greater than 5 nm and smaller than 11 nm, well defined morphology and good magnetic properties with superparamagnetic behavior. The reflux synthesis was more efficient in the deposition of the hydroxyl groups on the nanoparticles surface

Synthesis and characterization of lanthanum- and yttrium-doped Fe2O3 pigments

MELO, D. M. A. et al. Synthesis and charactezarion of lanthanum and yttrium doped Fe2O3 pigments. Cerâmica, São Paulo, v. 53, p. 79-82, 2007.

Synthesis and characterization of lanthanum- and yttrium-doped Fe2O3 pigments

MELO, D. M. A. et al. Synthesis and charactezarion of lanthanum and yttrium doped Fe2O3 pigments. Cerâmica, São Paulo, v. 53, p. 79-82, 2007.