Avaliação do tratamento eletroquímico (direto e indireto) como alternativa de degradação do corante azul de metileno

Textile industry has been a cause of environmental pollution, mainly due to the generation of large volumes of waste containing high organic loading and intense color. In this context, this study evaluated the electrochemical degradation of synthetic effluents from textile industry containing Methylene Blue (AM) dye, using Ti/IrO2-Ta2O5 and Ti/Pt anodes, by direct and indirect (active chlorine) electrooxidation. We evaluated the influence of applied current density (20, 40 and 60 mA/cm2 ), and the presence of different concentrations of electrolyte (NaCl and Na2SO4), as well as the neutral and alkaline pH media. The electrochemical treatment was conducted in a continuous flow reactor, in which the electrolysis time of the AM 100 ppm was 6 hours. The performance of electrochemical process was evaluated by UV-vis spectrophotometry, chemical oxygen demand (COD) and total organic carbon (TOC). The results showed that with increasing current density, it was possible to obtain 100 % of color removal at Ti/IrO2-Ta2O5 and Ti/Pt electrodes. Regarding the color removal efficiency, increasing the concentration of electrolyte promotes a higher percentage of removal using 0,02 M Na2SO4 and 0,017 M NaCl. Concerning to the aqueous medium, the best color removal results were obtained in alkaline medium using Ti/Pt. In terms of organic matter, 86 % was achieved in neutral pH medium for Ti/Pt; while a 30 % in an alkaline medium. To understand the electrochemical behavior due to the oxygen evolution reaction, polarization curves were registered, determining that the presence of NaCl in the solution favored the production of active chlorine species. The best results in energy consumption and cost were obtained by applying lower current density (20 mA/cm2 ) in 6 hours of electrolysis.

Partículas inteligentes de poli (nisopropilacrilamida), quitosana e poli (ácido acrílico): efeito da temperatura e do pH sobre suas propriedades em suspensões aquosas

The present study describes the stability and rheological behavior of suspensions of poly (N-isopropylacrylamide) (PNIPAM), poly (N-isopropylacrylamide)-chitosan (PNIPAMCS), and poly (N-isopropylacrylamide)-chitosan-poly (acrylic acid) (PNIPAM-CS-PAA) crosslinked particles sensitive to pH and temperature. These dual-sensitive materials were simply obtained by one-pot method, via free-radical precipitation copolymerization with potassium persulfate, using N,N -methylenebisacrylamide (MBA) as a crosslinking agent. Incorporation of the precursor materials into the chemical networks was confirmed by elementary analysis and infrared spectroscopy. The influence of external stimuli such as pH and temperature, or both, on particle behavior was investigated through rheological measurements, visual stability tests and analytical centrifugation. The PNIPAM-CS particles showed higher stability in acid and neutral media, whereas PNIPAM-CS-PAA particles were more stable in neutral and alkaline media, both below and above the LCST of poly (Nisopropylacrylamide) (stability data). This is due to different interparticle interactions, as well as those between the particles and the medium (also evidenced by rheological data), which were also influenced by the pH and temperature of the medium. Based on the results obtained, we found that the introduction of pH-sensitive polymers to crosslinked poly (Nisopropylacrylamide) particles not only produced dual-sensitive materials, but allowed particle stability to be adjusted, making phase separation faster or slower, depending on the desired application. Thus, it is possible to adapt the material to different media